Dispersed silver nanoparticles (AgNPs) on the surface of titanium alloy (Ti6Al4V) and titanium alloy modified by titania nanotube layer (Ti6Al4V/TNT) substrates were produced by chemical vapor deposition method (CVD) using novel precursor of the formula [Ag₅(O₂CC₂F₅)₅(H₂O)₃]. The structure and volatile properties of this compound were determined using single crystal X-ray diffractometry, variable temperature IR spectrophotometry (VT IR), and electron inducted mass spectrometry (EI MS). The morphology and the structure of the produced Ti6Al4V/AgNPs, and Ti6Al4V/TNT/AgNPs composites were characterized by scanning electron microscopy (SEM) and atomic force microscopy (AFM). Moreover, measurements of hardness, Young’s modulus, adhesion, and surface free energy have been carried out. The ability to release silver ions from the surface of produced nanocomposite materials immersed in PBS solution has been estimated using inductively coupled plasma mass spectrometry (ICP MS). The wettability and the surface free energy of samples were estimated on the base of contact angle studies with the use of water and diiodomethane. Among the studied surface-modified titanium alloy implants, the best nano-mechanical properties were noticed for the Ti6Al4V/TNT15/AgNPs composite. The location of silver nanoparticles inside of titania nanotubes caused their lowest release rate, which may indicate on suitable properties above mentioned type of the composite for the construction of implants with a long term of antimicrobial activity.

Research on titanium oxo complexes (TOCs) are usually focused on their structure and photocatalytic properties. Findings from these investigations spurred our interest in exploring also their potential biological activities. In this study, we focused on the synthesis and structure of a compound with the general formula [Ti8O2(OiPr)20(man)4] (1), which was isolated from the reaction mixture of titanium(IV) isopropoxide with mandelic acid (Hman) in a molar ratio of 4:1. The structure (1) was determined using single-crystal X-ray diffraction, while spectroscopic studies provided insights into its physicochemical properties. To assess the potential practical applications of (1), its microcrystals were incorporated into a polymethyl methacrylate (PMMA) matrix, yielding composite materials of the type PMMA + (1) (2 wt.%, 5 wt.%, 10 wt.%, and 20 wt.%). The next stage of our research involved the antimicrobial activity evaluation of the obtained materials. Investigations carried out demonstrated antimicrobial activity of pure (1) and its composites (PMMA + (1)) against both Gram-positive and Gram-negative strains. Furthermore, MTT tests conducted on the L929 murine fibroblast cell line confirmed the lack of cytotoxicity of these composites. Our study identified (1) as a promising antimicrobial agent, also for producing composite coatings.