water cement ratio
Recently Published Documents

Abstract: This research paper represents the experimental study on use of ceramic waste material as an aggregate in concrete. To reach the goal of sustainable development utilization of waste materials in concrete production is very much useful. The ceramic aggregate used in this study was recycled from industrial ceramic tile waste in India. From the results it can be seen that it is possible to produce a concrete with good strength by using ceramic waste as an aggregate in .It is also seen from the results that the compressive strength characteristics of ceramic aggregate concrete met the required criteria set by various international standards and codes, which shows the ability of ceramic waste to be used as a substitute to the conventional aggregates in concrete. We replaced the coarse aggregate in concrete by 100% to thewaste ceramic aggregate of size 10mm. The water cementratio taken was 0.30 for concrete production and compared it with normal aggregate concrete of M20 grade. By the decrease in water/cement ratio, high strength concrete canbe obtained. But it is found that the workability will be very low. In our project the required workability was achieved by the use of maximum water-cement ratio .To overcome this use of several admixtures like super-plasticizers and silica fume are recommended to add in the mixing so that the workability can be improved. Keywords: Sustainable development, Ceramic waste as aggregate

At present, the research on the high temperature degradation of concrete usually focuses on only the degradation of concrete itself without considering the effect of the plastering layer. It is necessary to take into account the influence of the plastering layer on the high temperature degradation of concrete. With an increase in the water/cement ratio, the explosion of concrete disappeared. Although increasing the water/cement ratio can alleviate the cracking of concrete due to lower pressure, it leads to a decrease in the mechanical properties of concrete after heating. It is proved that besides the water/cement ratio, the apparent phenomena and mechanical properties of concrete at high temperature can be affected by the plastering layer. The plastering layer can relieve the high temperature cracking of concrete, and even inhibit the high temperature explosion of concrete with 0.30 water/cement ratio. By means of an XRD test, scanning electron microscope test and thermogravimetric analysis, it is found that the plastering layer can promote the rehydration of unhydrated cement particles of 0.30 water/cement ratio concrete at high temperature and then promote the mechanical properties of concrete at 400 °C. However, the plastering layer accelerated the thermal decomposition of C-S-H gel of concrete with a water/cement ratio of 0.40 at high temperature, and finally accelerate the decline of mechanical property of concrete. To conclude, the low water/cement ratio and plastering layer can delay the deterioration of concrete at high temperature.

Abstract In the recent decade, supplementary cementing ingredients have become an essential part of various strength ranges of concrete and cement-mortar mix design. Examples are natural materials, by-products, industrial wastes, and materials that require less energy and time to generate. Fly ash is one of the most widely utilized additional cementing ingredients. Fly ash is a by-product substance produced by coal combustion. It's being used in cement mortar and concrete as a pozzolanic substance. It has demonstrated significant influence in improving liquid and solid properties of cement mortar, such as compressive strength. Multi Expression Programming (MEP) is employed in this study to estimate the compressive strength (CS) of cement mortar modified with fly ash. The outcomes of this model were compared and evaluated with several other models such as the Nonlinear Regression model (NLR), Artificial Neural Network (ANN), and M5P-tree models that have been used in the construction fields. The input parameters included water/cement ratio (w/c), curing time (t days), and fly ash content (FA %), while the target property was compressive strength up to 360 days of curing. Four hundred fifty (450) data are collected from previous literature on modifying cement mortar with fly ash for that purpose. The water/cement ratio ranged from 0.24 to 1.2, and the fly ash was used to replace cement up to 55% (%wt. of dry cement). Based on the Coefficient of Determination (R2), Root Mean Squared Error (RMSE), Scatter Index (SI), Objective (OBJ), Mean Absolute Error (MAE), t-test value, the uncertainty of 95%, Performance Index (ρ), and boxplot for actual and predicted compressive strength. The MEP model performed better than other developed models according to evaluation tools. The compressive strength was also correlated with flexural and splitting tensile strengths using different nonlinear models.

The physical and mechanical properties of grouting materials greatly affect the friction resistance and the bearing performance of a non-soil-squeezing PHC pipe pile. Orthogonal tests for four factors at five levels were carried out to optimize the proportion of the water–cement mixture by using Portland cement as a raw material and a water-reducing agent, expansion agent and early-strength agent as additives. The following conclusions were obtained: (1) Both the water–cement ratio and the dosage of water-reducing agent are positively correlated with the fluidity of the water–cement mixture and have the greatest influence on the fluidity, followed by the expansion agent and early-strength agent. The saturation point of the water-reducing agent is 1.5%. (2) The strength of the grouting body decreases linearly with the increase of the water–cement ratio, and the dosage of the water-reducing agent has no obvious effect on the strength. As the dosage of expansion agent increases, the strength of the grouting body decreases rapidly. The expansion agent mainly plays a key role in the middle and late stages of the hardening process of the slurry. Early-strength agents have a greater impact on the early strength, but less on the later strength. When the slurry is solidified for 3 h, the early-strength agent has the greatest impact on the strength with an optimal dosage of 5%. (3) The volume of the grouting body has an inverse relationship with the water–cement ratio, and the optimal amount of expansion agent is 12%. The incorporation of an expansion agent makes the volume increase of the grouting body exceed the volume shrinkage ratio caused by the hardening of the grouting body with a curing time of more than 3 days, ensuring a slight increase in the volume of the grouting body. After 3 days, even though the effect of the expansion agent is gradually weakened, it can still ensure that the volume of the grouting body does not shrink. With the increase of the amount of water-reducing agent, the volume of the grouting body gradually decreases. When the amount of water-reducing agent exceeds 1.5%, the volume of the grouting body no longer decreases. (4) The early-strength agent has almost no effect on the volume of the grouting body. When the curing time is 3 h, the water–cement ratio has the greatest influence on the volume of the grouting body, followed by the water-reducing agent, and, finally, the expansion agent. After 3 h, the water–cement ratio still has the greatest influence, and the influence of the expansion agent gradually exceeds that of the water-reducing agent. The water-reducing agent mainly affects the volume of the grouting body in the water separation stage, and the expansion agent mainly plays a role in the middle and late stages of the slurry solidification. After optimized ratio analysis, the fluidity of the water–cement mixture can be improved, the volume shrinkage ratio rate can be lowered and the early strength can be increased.

The paper presents data on the study of the polycondensation of 2-furaldehyde and 1,3,5-trihydroxybenzene in an alkaline medium to obtain a plasticizing additive. Results are presented on the study of the products of the separate interaction of 1,3,5-trioxybenzene and 2-furaldehyde with NaOH, and the joint polycondensation of 1,3,5-trioxybenzene with 2-furaldehyde with NaOH by UV spectroscopy. The structure of the product of the interaction of 1,3,5-trioxybenzene with 2-furaldehyde in an alkaline medium was studied by IR spectroscopy. Stronger C–H bonds appear in the IR spectrum and stretching vibrations of the C = O group are not observed, which confirms the production of a new compound. The optimal dosage of the developed plasticizing additive has been established as 0.3% of the cement mass (calculated on dry matter). The developed plasticizing additive can significantly reduce the water-cement ratio while maintaining the strength characteristics of cement compositions. In addition, when using the additive, the strength characteristics are significantly increased with a reduced water-cement ratio.

This research focused on laboratory tests that was conducted using locally available 10mm washed all-in gravel, quarry dust with varying water cement ratio. The research was carried-out using 108 (150 x 150 x 150) mm standard cubes that were all tested from three designed concrete mixes. In the present study, the role of water-cement ratio in compressive strength of concrete was investigated. The mixed concrete samples with water-cement ratios of 0.3, 0.35 and 0.40 were experimented for 3, 7, 21 and 28 days of curing. The results of compressive strength experiment showed that due to increase in water-cement ratio from 0.3 to 0.40, the compressive strength improved from 22 N/mm2 to 24.33 N/mm2 for 1:1.5:3 design mix, the compressive strength improved from 22.88 N/mm2 to 24 N/mm2 for 1:2:1 design mix, while compressive strength improved from 24 N/mm2 to 25.3 N/mm2 for 1:1:2 design mix   respectively. The results for compressive strength experiments showed that the 0.4 water-cement ratio resulted in the optimum compressive strength for all three design mixes.      

Jet grouting is one of the most widely applied soil improvement techniques. It is suitable for most geotechnical problems, including improving bearing capacity, decreasing settlement, forming seals, and stabilizing slopes. One of the difficulties faced by designers is determining the strength and geometry of elements created using this method. Jet grouted soil-cement columns in soil are a complicated issue because they are dependent on a number of parameters such as soil type, grout and water flow rate, rotation and lifting speed of monitor, nozzle jetting force, and water to cement ratio of slurry. This paper discusses the effect of the water-cement ratio on the physical and mechanical characteristics of soilcrete. In the laboratory, sandy soil mixed with cement grout with water-cement ratio varies from (0.7:1 to 1.4:1). To evaluate the characteristics of soilcrete, 96 specimens were prepared in the laboratory and tested at different curing times. The results indicate that the Uniaxial Compressive Strength (UCS) of soilcrete decreases with increasing the (W/C) ratio of the grout, where the soilcrete strength of W/C ratio of 0.7 is higher about 237% of W/C ratio of 1.4 at 28-day; the evolution of the (UCS) is proportional to the logarithm of the curing time; the ratio between the modulus of elasticity (Etg50) to the maximum UCS varies from 113 to 175; when the water-cement ratio increases, the dry density of soilcrete decreases, as a result, the (USC) of soilcrete decreases.