Specific Mechanical Tests Performed Test Method / Standard Against Which Tests Are Performed Range of Testing / Limits of Detection Accuracy ( )

Download as docx, pdf, or txt
Download as docx, pdf, or txt
You are on page 1of 1

Specific Mechanical Tests performed

Test method / standard against which tests are performed IS 16081995 ASTM A 370 2002

Range of testing / Limits of detection Up to 20kN = 100N Up to 40kN = 200N Upto100kN (upto10MT) = 500N (50kg) Up to 100kN(upto20MT)=1000N (100 kg) Up to 400kN(upto40MT) = 2000N (200 kg) Up to 100MT = 500 kg 15.625 to 187.5 5 30kg HRB, HRC15 T, 30 T 200 gm to less than 5Kg less than 200 gm 40 mm Thickness Mandrel Dia 250 mm 216 ft. lbs. Up to 30 kg. m Up to 16.52 kg. m Up to 500mm ID Up to 80mm Up to 2mm Thickness

Accuracy ()

Tensile Test

1%

Hardness Test Brinell Hardness Vickers Hardness Rockwell Hardness Superficial Rockwell Hardness Micro Hardness Vickers Bend Test Impact Test Charpy Impact IZOD Impact Flattening Test Flaring / Drift Test Erichsen Cupping Test

ASTM A 3702002 IS 150096 IS 1501 Pt.199 IS 15862001 IS 5072 88 IS 1501 Pt.299 IS 1501 Pt.399 IS 159991 ASTM A 370 2002 ASTM A 3702002 ASTM E 23 IS 175799 IS 159899 ASTM A 3702002 IS 232891 ASTM A 3702002 IS 233591 IS 10175( PI) 1993

3%

NA 5% 5% 5% NA 1% 2%

Micro Examination ASTM E 407 / 112 1989 ASTM 1 10 Grain Size General Structure Phase Determination such as Ferrite / Pearlite / Retained Austenite in Steel Nodularity/Carbide in SGI Iron Cast Iron Grain Size, Decarburization, Case Depth, Thickness of Coating Phase determination in Duplex Steel ASTM A 923 98. Hydraulic Test Macroetch Test Proof Load Test ASTM A 530/ 450 / 999 2001

ASTM 1 10 Grain Size

-----

Up to 300 kg/cm

2% ---- 1%

ASTM E 340 / E3811989 -----IS 1367Pt .VI 1991 IS 1367Pt . 3 1992 0 100 MT ASTM A 370 2002