Materials Science: Fatigue Life

Fatigue is the weakening of a material caused by repeatedly applied loads, even if the loads are less than the material's strength. It occurs when microscopic cracks form in a material from loads applied above a certain threshold. These cracks grow with each load cycle until a critical size is reached, causing sudden fracture. The shape of a structure affects its fatigue life, with sharp corners and holes increasing local stresses and reducing fatigue strength. Fatigue life is defined as the number of stress cycles before failure and can be estimated using methods like the stress-life or strain-life approaches.

Uploaded by

Ishwarya Srikanth
Copyright
© © All Rights Reserved
Available Formats
Download as DOCX, PDF, TXT or read online on Scribd
28 views

Materials Science: Fatigue Life

Fatigue is the weakening of a material caused by repeatedly applied loads, even if the loads are less than the material's strength. It occurs when microscopic cracks form in a material from loads applied above a certain threshold. These cracks grow with each load cycle until a critical size is reached, causing sudden fracture. The shape of a structure affects its fatigue life, with sharp corners and holes increasing local stresses and reducing fatigue strength. Fatigue life is defined as the number of stress cycles before failure and can be estimated using methods like the stress-life or strain-life approaches.

Uploaded by

Ishwarya Srikanth
Copyright
© © All Rights Reserved
Available Formats
Download as DOCX, PDF, TXT or read online on Scribd
You are on page 1/ 3

In materials science, fatigue is the weakening of a material caused by

repeatedly applied loads. It is the progressive and localised structural


damage that occurs when a material is subjected to cyclic loading. The
nominal maximum stress values that cause such damage may be much less
than the strength of the material typically quoted as the ultimate tensile
stress limit, or the yield stress limit.
Fatigue occurs when a material is subjected to repeated loading and
unloading. If the loads are above a certain threshold, microscopic cracks will
begin to form at the stress concentrators such as the surface, persistent slip
bands (PSBs), and grain interfaces. Eventually a crack will reach a critical
size, the crack will propagate suddenly, and the structure will fracture. The
shape of the structure will significantly affect the fatigue life; square holes or
sharp corners will lead to elevated local stresses where fatigue cracks can
initiate. Round holes and smooth transitions or fillets will therefore increase
the fatigue strength of the structure.
Fatigue life
ASTM defines fatigue life, Nf, as the number of stress cycles of a specified
character that a specimen sustains before failure of a specified nature
occurs. For some materials, notably steel and titanium, there is a theoretical
value for stress amplitude below which the material will not fail for any
number of cycles, called a fatigue limit, endurance limit, or fatigue strength.
Engineers have used any of three methods to determine the fatigue life of a
material: the stress-life method, the strain-life method, and the linear-elastic
fracture mechanics method. One method to predict fatigue life of materials is
the Uniform Material Law (UML). UML was developed for fatigue life
prediction of aluminium and titanium alloys by the end of 20th century and
extended to high-strength steels, and cast iron.
Characteristics of fatigue

Fracture of an aluminium crank arm. Dark area of striations: slow crack


growth. Bright granular area: sudden fracture.

In metal alloys, when there are no macroscopic or microscopic


discontinuities, the process starts with dislocation movements, which
eventually form persistent slip bands that become the nucleus of short
cracks.

Macroscopic and microscopic discontinuities as well as component


design features which cause stress concentrations (holes, keyways, sharp
changes of direction etc.) are common locations at which the fatigue
process begins.

Fatigue is a process that has a degree of randomness (stochastic),


often showing considerable scatter even in well controlled environments.

Fatigue is usually associated with tensile stresses but fatigue cracks


have been reported due to compressive loads.[8]

The greater the applied stress range, the shorter the life.

Fatigue life scatter tends to increase for longer fatigue lives.

Damage is cumulative. Materials do not recover when rested.

Fatigue life is influenced by a variety of factors, such


as temperature, surface finish, metallurgical microstructure, presence
of oxidizing or inert chemicals, residual
stresses,
scuffing
contact
(fretting), etc.

Some materials (e.g., some steel and titanium alloys) exhibit a


theoretical fatigue limit below which continued loading does not lead to
fatigue failure.

High cycle fatigue strength (about 104 to 108 cycles) can be described
by stress-based parameters. A load-controlled servo-hydraulic test rig is
commonly used in these tests, with frequencies of around 2050 Hz.
Other sorts of machineslike resonant magnetic machinescan also be
used, to achieve frequencies up to 250 Hz.

Low cycle fatigue (loading that typically causes failure in less than
10 cycles) is associated with localized plastic behavior in metals; thus, a
strain-based parameter should be used for fatigue life prediction in
metals. Testing is conducted with constant strain amplitudes typically at
0.015 Hz.
4