Steel Joint Bars, Low, Medium, and High Carbon (Non-Heat-Treated)

Download as pdf or txt
Download as pdf or txt
You are on page 1of 3

Designation: A 3 01

Standard Specication for

Steel Joint Bars, Low, Medium, and High Carbon (Non-HeatTreated)1


This standard is issued under the xed designation A 3; the number immediately following the designation indicates the year of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A superscript epsilon (e) indicates an editorial change since the last revision or reapproval. This standard has been approved for use by agencies of the Department of Defense.

1. Scope 1.1 This specication covers steel joint bars for connecting steel rails in mine, industrial, and standard railroad track. 1.2 Three grades of joint bars are dened for applications where non-heat treated bars are suitable: 1.2.1 Grade 1, low-carbon, primarily for industrial and mine use. 1.2.2 Grade 2, medium-carbon, primarily for industrial and mine use. 1.2.3 Grade 3, high-carbon, for general use in standard railroad track. They may be used in the production of insulated track joints. 1.3 The values stated in inch-pound units are to be regarded as the standard. The values given in parentheses are for information only. 2. Referenced Documents 2.1 ASTM Standards: A 370 Test Methods and Denitions for Mechanical Testing of Steel Products2 A 700 Practices for Packaging, Marking, and Loading Methods for Steel Products for Domestic Shipment3 3. Ordering Information 3.1 Orders for joint bars under this specication shall include the following information as appropriate: 3.1.1 Quantitynumber of pairs of bars, 3.1.2 Typedesign or type bar along with section designation and weight of rails being joined,

3.1.3 Gradein accordance with 1.2 and Table 1 and Table 2, 3.1.4 Dimensionoverall length, 3.1.5 Punchingtype (elliptical, oval, round, or combinations), size, number, location, spacing, and elevation of punched holes, with dimensional drawing if necessary, 3.1.6 Special Requirementsnotching, shearing, bundling, etc., including details, and 3.1.7 Certication and Test Report Requirements(Section 11). 4. Manufacture 4.1 The steel shall be made by one or both of the following processes: basic-oxygen or electric-furnace. 4.1.1 The steel may be cast by a continuous process, or in ingots. 4.2 Grade 2, medium-carbon, joint bars may be punched, slotted, and shaped in the case of special designs, either hot or cold. Joint bars that are punched, slotted, or shaped cold shall be subsequently annealed. 4.3 Grade 3, high-carbon, joint bars shall be uniformly heated for punching, slotting, and shaping. 5. Chemical Requirements 5.1 The steel shall conform to the requirements as to chemical composition prescribed in Table 1. 5.2 Heat or Cast AnalysisAn analysis of each heat or cast shall be made by the manufacturer to determine the percentages of carbon, manganese, phosphorus, and sulfur. The analysis shall be made from a test sample taken preferably during the pouring of the heat or cast. The chemical composition thus determined shall conform to the requirement in Table 1. Manganese and sulfur determinations are for information only. 5.3 Product AnalysisWhen ladle tests are not available, nished material representing the heat may be product tested. The product analysis allowance beyond the limits of the specied ladle analysis shall be within the limits for product analyses specied in Table 2.

1 This specication is under the jurisdiction of ASTM Committee A01 on Steel, Stainless Steel and Related Alloys, and is the direct responsibility of Subcommittee A01.01 on Steel Rails and Accessories. Current edition approved April 10, 2001. Published May 2001. Originally published as A3 1901. Last previous edition A3 87 (1995). 2 Annual Book of ASTM Standards, Vol 01.03. 3 Annual Book of ASTM Standards, Vol 01.05.

Copyright ASTM, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959, United States.

A3
TABLE 1 Chemical Requirements
Elements Grade 1 Carbon, min Phosphorus, max ... 0.05 Composition, % Grade 2 0.30 0.05 Grade 3 0.45 0.04

7.3 Any variation from a straight line in a vertical plane shall be such as will make the bars high in the center. 7.4 For girder rail applications only, any variation from a straight line in a horizontal plane shall be such as will make the bars convex towards the web of the rail. 8. Workmanship, Finish, and Appearance 8.1 The joint bars shall be straight, subject to the variations prescribed in 7.3, 7.4, and Table 4. 8.2 The general appearance with respect to soundness and surface nish shall be consistent with good commercial practice as determined by visual inspection. 9. Inspection 9.1 The manufacturer shall afford the purchasers inspector all reasonable facilities necessary to satisfy that the material is being produced and furnished in accordance with this specication. Mill inspection by the purchaser shall not interfere unnecessarily with the manufacturers operations. All tests and inspections shall be made at the place of manufacture, unless otherwise agreed upon. 10. Rejection and Rehearing 10.1 Material that fails to conform to the requirements of this specication may be rejected. Rejections shall be reported to the manufacturer or supplier promptly and in writing. In case of dissatisfaction with the test results, the manufacturer or supplier may make claim for a rehearing. 11. Certication and Test Report 11.1 When specied in the purchase order or contract, a manufacturers certication shall be furnished to the purchaser that the material was produced and tested in accordance with this specication and has been found to meet the requirements. 11.2 When specied in the purchase order or contract, a report of the chemical and mechanical test results shall be furnished. 11.3 A Material Test Report, Certicate of Inspection, or similar document printed from or used in electronic form from an electronic data interchange (EDI) transmission shall be regarded as having the same validity as a counterpart printed in the certiers facility. The content of the EDI transmitted document must meet the requirements of the invoked ASTM standard(s) and conform to any existing EDI agreement between the purchaser and the supplier. 11.4 Notwithstanding the absence of a signature, the organization submitting either a printed document (Material Test Report, Certicate of Inspection or similar document) or an EDI transmission is responsible for the content of the report. 12. Product Marking 12.1 The name or brand of the manufacturer and the year of manufacture shall be rolled in raised letters and gures on the side of the rolled bars, and a portion of this marking shall appear on each nished joint bar. 12.2 In addition to the markings in 12.1, the following markings shall appear on Grade 3, high-carbon joint bars: 12.2.1 The section designation shall be included with the rolled raised characters.
2

TABLE 2 Product Analysis


Allowance Beyond Limits of Specied Chemical Analysis Percent under min limit Carbon Phosphorus 0.04 ... Percent over max limit 0.04 0.008

5.3.1 An analysis may be made by the purchaser from a sample taken from a nished joint bar representing each heat or cast. The chemical composition thus determined shall conform to the requirements in Table 1. 6. Tensile Requirements 6.1 PropertiesThe material as represented by a tension test specimen shall conform to the tensile properties prescribed in Table 3. 6.2 Test SpecimenThe tension test specimen shall be taken from the middle of the head at the center of a nished joint bar. The specimen shall be machined to the form and dimensions for a standard round tension test specimen with 2-in. or (50- mm) gage length, as described in Test Methods and Denitions A 370. 6.3 Number of TestsOne tension test shall be made from each heat or cast of steel. 6.4 RetestsIf the results of the tension test fail to meet the requirements specied, a retest shall be permitted on two random specimens from the lot. Both shall conform to the requirements specied in Table 3. 6.4.1 If any test specimen fails because of mechanical reasons such as failure of testing equipment or improper specimen preparation, it may be discarded and another specimen taken. 7. Dimensions and Permissible Variations 7.1 The joint bars shall be true to template, and shall accurately t the rails for which they are intended. 7.2 The joint bars shall be either sheared or sawed to length, punched to the dimensions specied by the purchaser and alignment adjusted, all subject to the permissible variations prescribed in 7.3, 7.4, and Table 4.
TABLE 3 Tensile Requirements
Grade 1 ksi Tensile strength, min Elongation in 2 in. or 50 mm, min 55 22 MPa 380 Grade 2 ksi 68 20 MPa 470 Grade 3 ksi 85 15 MPa 585

A3
12.2.2 A serial number representing the heat or cast shall be hot-stamped on the outside of the web of each bar, near one end. 12.3 Bar Coding: 12.3.1 The Automotive Industry Action Group (AIAG) Bar Code Standard for Primary Metals for Steel Products may be considered as a possible auxiliary method of identication. Use of this method shall be by agreement between purchaser and supplier. 13. U.S. Government Procurement 13.1 When specied in the contract or purchase order, material shall be prepared for shipment and storage in accordance with the requirements of Practices A 700. 14. Keywords 14.1 rail; railway applications; steel joint bars

TABLE 4 Permissible Variations in Dimensions


Specied size of holes Specied location of holes Specied length of bar Maximum camber in either planetee rail applications (see 7.3) Grades 1, 2 116 in. (1.6 mm) 24-in. (610-mm) bars 18 in. (3.2 mm) 36-in. (914-mm) bars Maximum vertical camber-girder rail applications (see 7.3) (Grades 1 and 2 only) 364 in. (1.2 mm) 24-in. (610-mm) bars 332 in. (2.4 mm) 36-in. (914-mm) bars Maximum horizontal camber-girder rail applications (see 7.4) (Grades 1 and 2 only) 116 in. (1.6 mm) 24-in. (610-mm) bars 18 in. (3.2 mm) 36-in. (914-mm) bars Grade 3 in. (0.8 mm) 116 in. (1.6 mm)
1 32

6132 in. (0.8 mm) 6116 in. (1.6 mm) 618 in. (3.2 mm)

The American Society for Testing and Materials takes no position respecting the validity of any patent rights asserted in connection with any item mentioned in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk of infringement of such rights, are entirely their own responsibility. This standard is subject to revision at any time by the responsible technical committee and must be reviewed every ve years and if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards and should be addressed to ASTM Headquarters. Your comments will receive careful consideration at a meeting of the responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should make your views known to the ASTM Committee on Standards, at the address shown below. This standard is copyrighted by ASTM, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above address or at 610-832-9585 (phone), 610-832-9555 (fax), or service@astm.org (e-mail); or through the ASTM website (www.astm.org).