1. Scope
1.1 This specification covers grades of hot-formed welded
and seamless high-strength low-alloy square, rectangular,
round, or special shape structural tubing for welded, riveted, or
bolted construction of bridges and buildings and for general
structural purposes. When the steel is used in welded construction, the welding procedure shall be suitable for the steel and
the intended service.
1.2 Grade II has atmospheric corrosion resistance equivalent to that of carbon steel with copper (0.20 minimum Cu)
Grades Ia and Ib have atmospheric corrosion resistance substantially better than that of Grade II (Note 1). When properly
exposed to the atmosphere, Grades Ia and Ib can be used bare
(unpainted) for many applications. When enhanced corrosion
resistance is desired, Grade III, copper limits may be specified.
NOTE 1For methods of estimating the atmospheric corrosion resistance of low alloy steels see Guide G 101 or actual data.
4. Process
4.1 The steel shall be made by one or more of the following
processes: open-hearth, basic-oxygen, or electric-furnace.
4.2 Steel may be cast in ingots or may be strand cast. When
steels of different grades are sequentially strand cast, identification of the resultant transition material is required. The
producer shall remove the transition material by any established procedure that positively separates the grades.
5. Manufacture
5.1 The tubing shall be made by the seamless, furnacebuttwelded (continuous-welded), or hot-stretch-reduced
electric-resistance-welded process.
6. Chemical Composition
6.1 When subjected to the heat and product analysis, respectively, the steel shall conform to the requirements prescribed in
Table 1.
6.1.1 For Grades Ia and Ib, the choice and use of alloying
elements, combined with carbon, manganese, and sulfur within
the limits prescribed in Table 1 to give the mechanical
properties prescribed in Table 2 and to provide the atmospheric
corrosion resistance of 1.2, should be made by the manufacturer and included and reported in the heat analysis for
information purposes only to identify the type of steel applied.
For Grades Ia and Ib material, the atmospheric corrosionresistance index, calculated on the basis of the chemical
3. Ordering Information
3.1 Orders for material under this specification should
include the following as required to describe the material
adequately:
1
This specification is under the jurisdiction of ASTM Committee A-1 on Steel,
Stainless Steel, and Related Alloys and is the direct responsibility of Subcommittee
A01.09 on Carbon Steel Tubular Products.
Current edition approved Mar. 10, 1999. Published May 1999. Originally
published as A 618 68. Last previous edition A 618 97.
2
Annual Book of ASTM Standards, Vol 01.03.
3
Annual Book of ASTM Standards, Vol 01.05.
4
Annual Book of ASTM Standards, Vol 03.02.
A 618
TABLE 1 Chemical Requirements
Element
Composition, %
Grade Ia
Carbon, max
Manganese
Phosphorus
Sulfur, max
Silicon, max
Copper, min
Vanadium, min
Grade Ib
Grade II
Grade III
Heat
Product
Heat
Product
Heat
Product
Heat
Product
0.15
1.00 max
0.070.15
0.025
...
0.20
...
0.18
1.04 max
0.070.16
0.045
...
0.18
...
0.20
1.35 max
0.025 max
0.025
...
0.20B
...
...
1.40 max
0.035 max
0.035
...
0.18B
...
0.22
0.851.25
0.025 max
0.025
0.30
0.20
0.02
0.26
1.30 max
0.035 max
0.035
0.33
0.18
0.01
0.23A
1.35 maxA
0.025 max
0.025
0.30
...
0.02C
0.27A
1.40 maxA
0.035 max
0.035
0.35
...
0.01
A
For each reduction of 0.01 % C below the specified carbon maximum, an increase of 0.05 % manganese above the specified maximum will be permitted up to 1.45 %
for the heat analysis and up to 1.50 % for the product analysis.
B
If chromium and silicon contents are each 0.50 % min, then the copper minimums do not apply.
C
For Grade III, columbium may be used in conformance with the following limits: 0.005 %, min (heat) and 0.004 %, min (product).
70
50
22
19
(485)
(345)
67
46
22
18
(460)
(315)
7. Mechanical Requirements
7.1 Tensile Properties:
7.1.1 The material, as represented by the test specimen,
shall conform to the requirements prescribed in Table 2.
7.1.2 Elongation may be determined on a gage length of
either 2 in. (50 mm) or 8 in. (200 mm) at the manufacturers
option.
7.1.3 For material under 516 in. (7.94 mm) in thickness, a
deduction from the percentage elongation of 1.25 percentage
points in 8 in. specified in Table 2 shall be made for each
decrease of 132in. (0.79 mm) of the specified thickness under
516 in. (7.94 mm).
7.2 Bend TestThe bend test specimen shall stand being
bent cold through 180 without cracking on the outside of the
bent portion, to an inside diameter which shall have a relation
to the thickness of the specimen as prescribed in Table 3.
7.3 Number of TestsTwo tension and two bend tests, as
specified in 7.4.2, and 7.4.3, shall be made from tubing
representing each heat. However, if tubing from one heat
differs in the ordered nominal wall thickness, one tension test
and one bend test shall be made from both the heaviest and
lightest wall thicknesses processed.
7.4 Test Specimens:
7.4.1 The test specimens required by this specification shall
conform to those described in the latest issue of Test Methods
and Definitions A 370.
7.4.2 The tension test specimen shall be taken longitudinally from a section of the finished tubing, at a location at least
90 from the weld in the case of welded tubing, and shall not
be flattened between gage marks. If desired, the tension test
may be made on the full section of the tubing; otherwise, a
longitudinal strip test specimen shall be used as prescribed in
Test Methods and Definitions A 370, Annex A2. The specimens
shall have all burrs removed and shall not contain surface
imperfections that would interfere with the proper determination of the tensile properties of the metal.
7.4.3 The bend test specimen shall be taken longitudinally
from the tubing, and shall represent the full wall thickness of
Grade lll
65
50
20
18
(450)
(345)
A
For Grade II, when the material is normalized, the minimum yield strength and
minimum tensile strength required shall be reduced by 5 ksi (35 MPa).
A 618
tubing having a periphery in excess of 14 in. the mass tolerance
is applicable to the individual length.
8.2.3 LengthStructural tubing is commonly produced in
random mill lengths of 16 to 22 ft (4.9 to 6.7 m) or 32 to 44 ft
(9.8 to 13.4 m), in multiple lengths, and in definite cut lengths
(Section 3). When cut lengths are specified for structural
tubing, the length tolerances shall be in accordance with Table
5.
8.2.4 StraightnessThe permissible variation for straightness of structural tubing shall be 18 in. times the number of feet
of total length divided by 5 (2.08 mm times length in metres).
8.2.5 Squareness of SidesFor square or rectangular structural tubing, adjacent sides may deviate from 90 by a
tolerance of 62, maximum.
8.2.6 Radius of CornersFor square or rectangular structural tubing, the radius of any outside corner of the section
shall not exceed three times the specified wall thickness.
8.2.7 Twist:
8.2.7.1 The tolerance for twist, or variation with respect to
axial alignment of the section for square, rectangular, or special
shape structural tubing, shall be as prescribed in Table 6.
8.2.7.2 Twist is measured by holding down one end of a
square or rectangular tube on a flat surface plate with the
bottom side of the tube parallel to the surface plate, and noting
the height that either corner at the opposite end of the bottom
side of the tube extends above the surface plate. The difference
in the height of the corners shall not exceed the values in Table
6.
material. The sides of the bend test specimen may have the
corners rounded to a maximum radius of 116 in. (1.59 mm).
7.5 Test Methods:
7.5.1 The yield strength shall be determined in accordance
with one of the alternatives described in Test Methods and
Definitions A 370.
7.5.2 The bend test shall be made on square or rectangular
tubing manufactured in accordance with this specification.
7.6 Retests:
7.6.1 If the results of the mechanical tests representing any
heat do not conform to a requirement, as specified in 7.1 and
7.2, retests may be made on additional tubing of double the
original number from the same heat, each of which shall
conform to the requirement specified, or the tubing represented
by the test is subject to rejection.
7.6.2 In case of failure on retest to meet the requirements of
7.1 and 7.2, the manufacturer may elect to retreat, rework, or
otherwise eliminate the condition responsible for failure to
meet the specified requirements. Thereafter, the material remaining from the respective heat originally represented may be
tested, and shall comply with all requirements of this specification.
8. Dimensions and Permissible Variations
8.1 The dimensions of square, rectangular, round, and
special shape structural tubing to be ordered under this
specification shall be subject to prior negotiation with the
manufacturer. The dimensions agreed upon shall be indicated
in the purchase order.
8.2 Permissible Variations:
8.2.1 Outside Dimensions:
8.2.1.1 For round tubing 2 in. and over in nominal diameter,
the outside diameter shall not vary more than 61 % from the
specified outside diameter. For sizes 112 in. (38.1 mm) and
under, the outside diameter shall not vary more than 164 in.
(0.40 mm) over and more than 132 in. (0.79 mm) under the
specified outside diameter.
8.2.1.2 The specified dimensions, measured across the flats
at positions at least 2 in. (50.8 mm) from either end of square
and rectangular tubing and including an allowance for convexity and concavity, shall not exceed the plus and minus tolerance
shown in Table 4.
8.2.2 MassThe mass of structural tubing shall not be less
than the specified value by more than 3.5 %. The mass
tolerance shall be determined from individual lengths or for
round tubing sizes 412 in. (114 mm) in outside diameter and
under and square and rectangular tubing having a periphery of
14 in. (356 mm) and under shall be determined from masses of
the customary lifts produced by the mill. On round tubing sizes
over 412 in. in outside diameter and square and rectangular
Tolerance 6,
in. (mm)
0.020 (0.51)
0.025 (0.64)
0.030 (0.76)
1%
22 ft (6.71 m) and
Under
Over
Under
12
14
(12.7)
(6.35)
Over 22 to 44 ft (6.71
to 13.42 m), incl
Over
Under
34
14
(19.05)
(6.35)
A 618
TABLE 6 Twist Tolerances for Square, Rectangular, or Special
Shape Structural Tubing
Specified Dimension of Longest
Outside Side, in. (mm)
112 (38.1) and under
Over 112 to 212(38.1 to 63.5),
incl
Over 212 to 4 (63.5 to 101.6),
incl
Over 4 to 6 (101.6 to 152.4),
incl
Over 6 to 8 (152.4 to 203.2),
incl
Over 8 (203.2)
Maximum Twist
per 3 ft of
Length, in.
Maximum Twist
per Meter of
Length, mm
0.050
0.062
1.39
1.72
0.075
2.09
0.087
2.42
0.100
2.78
0.112
3.11
forming or installation, or both, conditions involved. Disposition shall be a matter for agreement.
12. Certification
12.1 Upon request of the purchaser in the contract or order,
a manufacturers certification that the material was manufactured and tested in accordance with this specification (including year of issue) together with a report of the chemical and
tensile tests shall be furnished.
13. Packaging, Package Marking, and Loading
13.1 Except as noted in 13.2, each length of structural
tubing shall be legibly marked by rolling, die stamping, ink
printing, or paint stenciling to show the following information:
manufacturers name, brand, or trademark; size and wall
thickness; steel grade; and the specification number (year of
issue not required).
13.2 For structural tubing 112 in. (38.1 mm) and under in
nominal size or the greatest cross sectional dimension less than
2 in. (50.8 mm), the information listed in 10.1 may be marked
on a tag securely attached to each bundle.
13.3 When specified in the order, contract, etc., packaging,
marking, and loading shall be in accordance with the procedures of Practices A 700.
13.4 Bar CodingIn addition to the requirements in 13.1,
13.2, and 13.3, bar coding is acceptable as a supplemental
identification method. The purchaser may specify in the order
a specific bar coding system to be used.
10. Inspection
10.1 All tubing shall be subject to an inspection at the place
of manufacture to assure conformance with the requirements of
this specification.
11. Rejection
11.1 Each length of tubing received from the manufacturer
may be inspected by the purchaser and, if it does not meet the
requirements of this specification based on the inspection and
test method as outlined in the specification, the length may be
rejected and the manufacturer shall be notified. Disposition of
rejected tubing shall be a matter of agreement between the
manufacturer and the purchaser.
11.2 Tubing found in fabrication or in installation to be
unsuitable for the intended use, under the scope and requirements of this specification, may be set aside and the manufacturer notified. Such tubing shall be subject to mutual investigation as to the nature and severity of the deficiency and the
14. Keywords
14.1 high-strength low-alloy steel; seamless steel tube; steel
tube; structural steel tubing; welded steel tubing
The American Society for Testing and Materials takes no position respecting the validity of any patent rights asserted in connection
with any item mentioned in this standard. Users of this standard are expressly advised that determination of the validity of any such
patent rights, and the risk of infringement of such rights, are entirely their own responsibility.
This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM Headquarters. Your comments will receive careful consideration at a meeting of the responsible
technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should make your
views known to the ASTM Committee on Standards, 100 Barr Harbor Drive, West Conshohocken, PA 19428.