Stellite 6 Final
6 ALLOY
Nominal Composition (mass %) and Physical Properties
TIG & OXY-ACETYLENE WELDING MMA WELD DEPOSITION MIG WELD DEPOSITION PTA & LASER WELD DEPOSITION HVOF & PLASMA SPRAY DEPOSITION
T E C H N I C A L DATA
Scanning Electron Micrograph of Cast Stellite 6 at 1000x magnifcation.
Nominal Thermal Expansion Coefcient (from 20C/68F to stated temperature)
100C
(212F)
200C
(392F)
300C
(572F)
400C
(752F)
500C
(932F)
600C
(1112F)
700C
(1292F)
800C
(1472F)
900C
(1652F)
1000C
(1832F)
m/m.K 11.35 12.95 13.6 13.9 14.2 14.5 14.7 15.05 15.5 17.5
-inch/inch.F 6.31 7.20 7.56 7.72 7.89 8.06 8.17 8.36 8.61 9.72
Nominal Tensile Properties at Room Temperature
Ultimate Tensile Strength Rm Yield Stress Rp(0.2%) Elongation Elastic Modulus
ksi MPa ksi MPa A(%) psi GPa
Castings 123 850 101.5 700 <1 30.3x10
6
209
Stellite