    This document provides information about austenitic manganese steel grade 1.3401, including its: - Minimum mechanical properties including yield strength, tensile strength, elongation and contraction percentages, and annealed hardness. - Typical chemical composition ranges for carbon, manganese, and silicon. - Recommended hotforming and heat treatment temperatures prior to delivery. - Applications like parts for heavy pressing, knocking or blowing where work hardening increases hardness and wear resistance over time. - Forming, machining, welding, and gas cutting information. - Stock thicknesses available from 2-19mm.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd

    Manganese Steel 3401

    Uploaded by

    kazdoelah
    639 views1 page
    This document provides information about austenitic manganese steel grade 1.3401, including its: - Minimum mechanical properties including yield strength, tensile strength, elongation and contraction percentages, and annealed hardness. - Typical chemical composition ranges for carbon, manganese, and silicon. - Recommended hotforming and heat treatment temperatures prior to delivery. - Applications like parts for heavy pressing, knocking or blowing where work hardening increases hardness and wear resistance over time. - Forming, machining, welding, and gas cutting information. - Stock thicknesses available from 2-19mm.

    Original Description:

    specification of manganese steel

    Copyright

    © Attribution Non-Commercial (BY-NC)

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides information about austenitic manganese steel grade 1.3401, including its: - Minimum mechanical properties including yield strength, tensile strength, elongation and contraction percentages, and annealed hardness. - Typical chemical composition ranges for carbon, manganese, and silicon. - Recommended hotforming and heat treatment temperatures prior to delivery. - Applications like parts for heavy pressing, knocking or blowing where work hardening increases hardness and wear resistance over time. - Forming, machining, welding, and gas cutting information. - Stock thicknesses available from 2-19mm.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    639 views1 page

    Manganese Steel 3401

    Uploaded by

    kazdoelah
    This document provides information about austenitic manganese steel grade 1.3401, including its: - Minimum mechanical properties including yield strength, tensile strength, elongation and contraction percentages, and annealed hardness. - Typical chemical composition ranges for carbon, manganese, and silicon. - Recommended hotforming and heat treatment temperatures prior to delivery. - Applications like parts for heavy pressing, knocking or blowing where work hardening increases hardness and wear resistance over time. - Forming, machining, welding, and gas cutting information. - Stock thicknesses available from 2-19mm.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    You are on page 1of 1

    METAL & INDUSTRIAL SUPPLIES

    KRUPP AUSTENITIC MANGANESE STEEL


    3401 DIN X 120 Mn 12 WERKSTOFF 1.3401

    Material Properties in delivery condition (water quenched)

    Yield Tensile Elongation Contraction Annealed


    N / mm2 N / mm2 (Lo = 5 do) % Hardness
    min min min
    350 800-1100 40 40 250 HB

    Chemical C Mn Si
    Composition 1.1 - 1.3 % 12 - 13 % Max. 0.6 %

    Hotforming o
    1100 - 850 C
    Temperature

    Heat Treatment o
    1000 - 1050 C / water quenched
    Prior to Delivery

    Work Harden Up to 550 - 600 HB

    Safes, Prisons, Armoured Cars, Parts in Beater Mills, in Sand Blaster, Breaker and
    Crusher Parts, Throat Armour, Grab Crane Parts, Generally for heavy pushing,
    Range of Knocking or blowing stress. By means of these types of stress a strengthing will take
    Application e.g place and in consequence of this, the resistance to wear will go up and up enormously.
    The more this steel is knocked the higher the hardness and the resistance to wear
    will be.

    Forming Bending, flanging, punching is possible.

    Nearly impossible. For drilling a cemented carbide alloy driller is necessary and the
    Machining o
    working area must be warmed up to 200-300 C. The feed of this drill has to be started.

    The weldability of the steel is good. Welding should be done 'cold'. In order to avoid
    cracks of the welding scam, it is recommended to put a wet duster on the scam.

    Welding Material for joint welding :


    X 15 CrNiMn 18 8 Grade-Nr 1.4370, lime-basic covering.
    Material for deposit welding :
    X 120 Mn 12 Grade-Nr 1.3401. Lime-basic covering.

    Plates up to 15 mm thickness can be cut with an acetylene / oxygen blow-pipe.


    For cutting the oxygen, pressure should be higher and the cutting speed lower as
    Gas Cutting
    with normal steel grades. In some cases, the cutting edges must be ground.
    Heavler plates can be cut by means of plasma.

    Stock Available Thickness 2,3,4,5,6,8,10,12,16 and 19 mm.

    PT.Krupindo Lestari
    Head Office : Jl. P. Jayakarta No.24/10, Jakarta 10730 – Indonesia
    Telp. (021) 601-6888 (hunting), (021) 639-3933 (hunting) Fax.(021) 639-8906
    E-mail : info@krupindo.com Website : www.krupindo.com
    Branch Office : Medan, Surabaya, Semarang, Bandung, Pekanbaru, Lampung, Balikpapan

    You might also like