    Quenched and Tempered Alloyed Engineering Steel DIN

    Uploaded by

    kazdoelah
    This document summarizes the specifications of quenched and tempered alloyed engineering steel grade 7225 (DIN 42 CrMo 4). It provides the chemical composition ranges, standards, common applications, heat treatment processes, mechanical properties, hardness levels, and a tempering hardness diagram for a 15mm diameter bar. The steel is a very common grade suitable for parts in power trains, fasteners, shafts, and gears.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd

    Quenched and Tempered Alloyed Engineering Steel DIN

    Uploaded by

    kazdoelah
    496 views2 pages
    This document summarizes the specifications of quenched and tempered alloyed engineering steel grade 7225 (DIN 42 CrMo 4). It provides the chemical composition ranges, standards, common applications, heat treatment processes, mechanical properties, hardness levels, and a tempering hardness diagram for a 15mm diameter bar. The steel is a very common grade suitable for parts in power trains, fasteners, shafts, and gears.

    Copyright

    © Attribution Non-Commercial (BY-NC)

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document summarizes the specifications of quenched and tempered alloyed engineering steel grade 7225 (DIN 42 CrMo 4). It provides the chemical composition ranges, standards, common applications, heat treatment processes, mechanical properties, hardness levels, and a tempering hardness diagram for a 15mm diameter bar. The steel is a very common grade suitable for parts in power trains, fasteners, shafts, and gears.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    496 views2 pages

    Quenched and Tempered Alloyed Engineering Steel DIN

    Uploaded by

    kazdoelah
    This document summarizes the specifications of quenched and tempered alloyed engineering steel grade 7225 (DIN 42 CrMo 4). It provides the chemical composition ranges, standards, common applications, heat treatment processes, mechanical properties, hardness levels, and a tempering hardness diagram for a 15mm diameter bar. The steel is a very common grade suitable for parts in power trains, fasteners, shafts, and gears.

    Copyright:

    Attribution Non-Commercial (BY-NC)
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    You are on page 1of 2

    Quenched and Tempered Alloyed Engineering Steel

    7225 DIN 42 CrMo 4

    Europe : DIN EN 10083-1 / DIN EN 10250-3 / DIN EN 10263-4


    Standards
    USA : ASTM A29 / ASTM A 193 / ASTM A 320 / ASTM A 322 / ASTM A 331 / SAE J 404

    C Si Mn P S Cr Mo Ni
    Chemical 0.38 - 0.45 0.15 - 0.40 0.60 - 0.90 < 0.035 < 0.035 0.90 - 1.20 0.15-0.30 < 0.25
    Composition in %
    Narrower or other tolerance ranges in chemical composition have to be agreed before order is placed.

    Material
    Very common Quenched and Tempered alloyed engineering steel grade.
    Characteristics

    On hardening in oil a bar diameter of ~22 mm and on hardening in water a bar diameter of ~30 mm will have a
    Transformation martenistic microstructure in the one of the bar dimensions. A martensitic / bainitic microstructure will be obatined
    Characteristics in the core of the bar diameters up to 100 mm on hardening in oil and up to 150 mm on hardening in water
    Transformation temperature : Acl ~ 720 o C; Ac3 : ~ 780 o C; Ms: ~350 o C

    Parts for power train applications; cold formed fastener components; Shafts; Gears; Drill collars for the oil
    Applications
    exploration.

    Hot rolled bars in Quenched and Tempered condition Hot forged bars in Quenched and Tempered
    Delivery Condition
    (DIN EN 10083-1) condition (DIN EN 10250-3)

    Hardening Tempering Annealing Jominy Test


    820-860 0C / oil or water 0
    540 - 680 C
    0
    680 - 720 C
    0
    845 - 855 C
    Heat Treatment
    Normalizing Hot Forming
    0 o
    840 - 880 C 800 - 1100 C

    1.5 mm 3 mm 5 mm 7 mm 9 mm 11 mm 13 mm 15 mm 20 mm
    53 - 61 52 - 61 52 - 61 51 - 60 49 - 60 43 - 59 40 - 59 37 - 58 34 - 56
    Jominy 25 mm 30 mm 35 mm 40 mm 45 mm 50 mm
    hardenability in
    32 - 53 31 - 51 30 - 48 30 - 47 29 - 46 29 - 45
    HRc
    If required, more limited hardenbility values on the lower range (HL) or higher range (HH) can be supplied. These
    narrower limits have to be specifically ordered.

    Quenched & Tempered


    Hardness (HB) < 16 mm 16-40 mm 40-100 mm 100-160 mm 160-320 mm 330-500 mm
    min. 310 min. 285 min. 260 min. 230 min. 205 min. 175

    Physical Properties Density at 20o C is 7.85 kg / dm3

    Mechanical Bar Reduction Impact Toughness


    0.2% Proof Stress Tensile Strength Elongation
    Properties in diameter in of Area (Z) (Av) in Joules (ISO-
    (Rp.0.2) in MPa (Rm) in Mpa (A5) in%
    Quenched and mm in % V-Notch)
    Tempered
    condition ≤ 16 > 885 1080 - 1280 > 10 > 40 > 30
    corresponding to > 16-40 > 750 980 - 1180 > 11 > 45 > 35
    DIN EN 10083-1
    (Longitudinal > 40-100 > 635 880 - 1080 > 12 > 50 > 35
    samples)
    >100-160 > 550 780 - 890 > 13 > 55 > 35
    Mechanical Bar Impact Toughness
    0.2% Proof Stress Tensile Strength
    Properties in diameter in Elongation (A5) in % (Av) in Joules (ISO-
    (Rp.0.2) in MPa (Rm) in Mpa
    Quenched and mm V-Notch)
    Tempered
    condition ≥ 15 (longitudinal) ≥ 27 (longitudinal)
    160 - 330 ≥ 460 ≥ 700
    corresponding to ≥ 10 (transverse) ≥ 14 (transverse)
    DIN EN 10250-3
    (Longitudinal ≥ 16 (longitudinal) ≥ 22 (longitudinal)
    330 - 500 ≥ 390 ≥ 600
    samples) ≥ 12 (transverse) ≥ 12 (transverse)

    Spherodized annealed + drawn


    Wire rods and bars spherodized Spherodized annealed + peeled
    Properties (wire rods < 28 mm or bars ≤ 40
    annealed (dimensions up to 40 mm) (bars : 20 - 40 mm)
    corresponding to mm )
    DIN EN 10263-4
    (longitudinal Tensile strength (Rm) ≤ 610 Mpa Tensile strength (Rm) ≤ 720 Mpa Tensile strength (Rm) ≤ 630 Mpa
    samples)
    Reduction of Area (Z) > 60% Reduction of Area (Z) > 50% Reduction of Area (Z) > 58%

    Temper-H ardness-D iagram of Steel 1.7225


    (15mm bar diameter)

    700
    600
    Hardness in HV

    500
    400
    300
    200
    100
    0
    200 300 400 500 600 700
    Te m pe ring Te m pe ra ture in °C

    ISAN METALL
    A Division of Otto Wolff Handelsgesellschaft mbH
    ThyssenKrupp Services AG
    Our official trading arm in Indonesia :

    Jl. P. Jayakarta 24/10, Jakarta 10730 Tel .(021) 639-3933 Fax. (021) 639-8906
    Website: www.krupindo.com E-mail : info@krupindo.com

    You might also like