EN AW 2017A - AlCuMg1
Material available
Thickness: Sheets 1-6 mm, Plates 8-150 mm
Dimension: 1020 x 2020 mm, 1270 x 2520 mm, 1520 x 3020 mm, or as requested.
Main Usage
Main Properties
forming
forging
Mechanical Engineering
Tools
DIN 1783:
cold rolled / dimensional specification
DIN 59600
hot rolled / dimensional specification
Further Standards: ASTM; AMS; QQ-A-250
Other Norms and Admissions: On request
Fe
Cu
Mn
Mg
Cr
Zn
Ti
0,20-0,8
0,7
3,5-4,5
0,4-1,0
0,4-1,0
0,10
0,25
Other elements
0,05 (each)
0,15 (together)
Sheets
mm
0,35-12
0,35-3,0
3,0-12
12-60
Rm
MPa
Temper
Acron
Number
Description
W
F40
F39
F39
3.1325.10
3.1325.51
"
"
soft
cold hardened
"
"
Rp0,2
MPa
A50 mm
%
Hardness
HB
13
13
13
12
50
100
100
95
Remarks
Temper acc.to DIN:
.10: soft
.51: solution annealed, quenched, stretched and
tension leveled, cold hardened
Comparable Temper according to AA
.0
.T351: solution annealed, quenched, cold hardened, stress relief through defined stretching
before the hardening process
Physical properties:
Density
g/cm
Solidification range
C
Electrical conductivity
%IACS
Thermal conductivity
W/m K
Thermal expansion
(m m-1 K-1)
512-650
18-28
130-200
23,8
2,80
E - modulus
(N / mm)
-70.000
Properties and details (Rating in decreasing tendency. 1= very good; 5= bad; na= not applicable; ns= not suitable)
Durability
Seawater: 5
Weather conditions: 4
Hot forming property
Bar extrusion: 4
Die forging: 3
Hammer forging: 3
Cold formability
Upsetting, staking, flushing
(Temper Soft.): 3
Deep drawing (Temper Soft): 3
Bending (Temper Soft): 2
Pressure forming (Temper Soft): 3
Impact extruding Temper Soft): 3
weldability
Gas-fusion welding: ns
WIG-Welding: ns
MIG- Welding: ns
Resistance spot welding: 1
Flash butt welding: 2
Brazeability
Brazing with/ without melter:: ns
Soldering, abrasion soldering: 3
Soldering with melter: ns
Machinability
temper soft anneal: 4
cured: 2
General Tips
gradient solidness and hardness in the core of
thick plates, as the case may be please use
special material HOKOTOL.
If material is thicker than 250mm please use
nature hard alloys like 5083.
Only use it stretched or bulged.