    1.2379 X153Crmov12 Cppu: Chemical Composition

    Uploaded by

    Adrian Finichiu
    1. The document summarizes information about steel grade 1.2379 X153CrMoV12, including its chemical composition, properties, applications, delivery condition, and heat treatment process. 2. Key properties include high resistance to abrasive and adhesive wear due to hard carbides in the steel matrix, good toughness and dimensional stability. Applications include cutting tools, thread rolling dies, and plastic molds. 3. The steel is supplied in a soft annealed condition up to 255 HB hardness. Heat treatment involves hardening at 1000-1030°C followed by tempering between 500-550°C, resulting in a hardness over 480 HB.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    1.2379 X153Crmov12 Cppu: Chemical Composition

    Uploaded by

    Adrian Finichiu
    121 views2 pages
    1. The document summarizes information about steel grade 1.2379 X153CrMoV12, including its chemical composition, properties, applications, delivery condition, and heat treatment process. 2. Key properties include high resistance to abrasive and adhesive wear due to hard carbides in the steel matrix, good toughness and dimensional stability. Applications include cutting tools, thread rolling dies, and plastic molds. 3. The steel is supplied in a soft annealed condition up to 255 HB hardness. Heat treatment involves hardening at 1000-1030°C followed by tempering between 500-550°C, resulting in a hardness over 480 HB.

    Original Description:

    zbd

    Original Title

    1.2379 - X153CrMoV12

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    1. The document summarizes information about steel grade 1.2379 X153CrMoV12, including its chemical composition, properties, applications, delivery condition, and heat treatment process. 2. Key properties include high resistance to abrasive and adhesive wear due to hard carbides in the steel matrix, good toughness and dimensional stability. Applications include cutting tools, thread rolling dies, and plastic molds. 3. The steel is supplied in a soft annealed condition up to 255 HB hardness. Heat treatment involves hardening at 1000-1030°C followed by tempering between 500-550°C, resulting in a hardness over 480 HB.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    121 views2 pages

    1.2379 X153Crmov12 Cppu: Chemical Composition

    Uploaded by

    Adrian Finichiu
    1. The document summarizes information about steel grade 1.2379 X153CrMoV12, including its chemical composition, properties, applications, delivery condition, and heat treatment process. 2. Key properties include high resistance to abrasive and adhesive wear due to hard carbides in the steel matrix, good toughness and dimensional stability. Applications include cutting tools, thread rolling dies, and plastic molds. 3. The steel is supplied in a soft annealed condition up to 255 HB hardness. Heat treatment involves hardening at 1000-1030°C followed by tempering between 500-550°C, resulting in a hardness over 480 HB.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    Material No.

    Code:

    DE - Brand:

    1.2379 X153CrMoV12
    Chemical composition:
    (Typical analysis in %)

    CPPU
    Cr

    Mo

    1,55 12,00 0,80

    V
    0,90

    Steel properties:

    Ledeburitic 12% chrome steel, very high resistance


    against abrasive and adhesive wear due to a high
    volume of hard carbides in the steel matrix, good
    toughness, very good dimensional stability, high
    compressive strength, very good base material for
    PVD/CVD coating as well as nitriding due to its
    secondary hardening properties. Similar to AISI D2.

    Applications:

    Cutting, punching, stamping tools, shear blades, thread


    rolling dies, cold extrusion dies, drawing and bending
    tools, flanging and straightening rolls, fine cutting tools,
    deep drawing tools, plastic moulds for abrasive polymers.

    Condition of delivery:

    Soft annealed to max. 255 HB

    Physical properties:
    Thermal expansion coefficient

    Thermal conductivity

    10-6 m

    20-100C 20-200C 20-300C 20-400C

    m K

    10,5

    11,5

    11,9

    13,0

    20C

    350C

    700C

    m K

    16,7

    20,5

    24,2

    Heat treatment:
    Soft annealing

    Stress relief annealing

    11/04

    Hardening

    Temperature

    Cooling

    Hardness

    820 - 850C

    furnace

    max. 255 HB

    Temperature

    Cooling

    600 - 650C

    furnace

    Temperature

    Cooling

    Tempering

    1000 - 1030C

    oil, pressure gas (N2),


    air or hot bath
    500 - 550C

    see tempering
    diagram
    usually < 300C

    1040 - 1080C

    oil, pressure gas (N2),


    air or hot bath
    500 - 550C

    see tempering
    diagram
    usually > 480C

    Drrenberg Edelstahl GmbH Hammerweg 7 D-51766 Engelskirchen


    Tel.: +49 22 63 / 79 1 Fax: +49 22 63 / 79 20 5 www.doerrenberg.de

    A company of the
    GESCO group

    (1.2379) Thermal Cycle Diagram


    Hardening

    600-650C

    Finish
    machining

    cooling slowly
    in furnace

    Tempering

    hardening temperature
    3rd preheating
    step
    min. / mm
    ~850C
    cooling
    2nd preheating
    oil, air, pressure
    step
    gas (N2)
    min. / mm
    ~650C

    Intermediate
    machining

    Rough
    machining

    Temperature

    Stress relief annealing

    1st tempering
    1 h / 20 mm
    at least 2 h

    hot bath
    500-550C

    2nd tempering
    1 h / 20 mm
    at least 2 h

    3rd tempering
    1 h / 20 mm
    at least 2 h

    1st preheating
    step
    min. / mm
    ~400C

    equalisation
    1 h / 100 mm

    Time

    Continuous Cooling Transformation Diagram (CCT)


    Austenitizing temperature: 1030C

    1200

    Austenitizing temperature: 1080C

    1200

    1000

    1000

    600

    88

    A+C

    400

    B
    15

    200
    M
    0
    0,1

    Ac1b

    100

    Ac1e
    Temperature [C]

    800

    891

    10

    10

    891
    2

    65

    Ac1b

    10

    230 HV

    10

    10

    600

    96

    A+C

    400

    M
    0
    0,1

    100

    200 Ms

    780 623 435


    3

    10
    Time [s]

    800

    782 772

    10

    10

    782
    3

    10
    Time [s]

    724

    297 245 HV

    10

    Tempering Diagram
    70
    65
    1

    60
    Hardness [HRc]

    Temperature [C]

    Ac1e

    55
    2

    50
    45

    40 Test specimen:

    = 30 mm, h = 40 mm

    35 quenched from 1010C


    in oil

    30
    0

    100

    2
    Test specimen:
    = 30 mm, h = 40 mm
    quenched from 1075C
    in oil

    200
    300
    400
    500
    Tempering temperature [C]

    Remarks: All technical information is for reference only.