AMS5772
AMS5772
1.1 Form:
This specification covers a corrosion and heat-resistant cobalt alloy in the form of bars, forgings,
flash welded rings, and stock for forging or flash welded rings.
1.2 Application:
These products have been used typically for parts requiring high strength up to 1800 F (982 C)
and oxidation resistance up to 2000 F (1093 C), but usage is not limited to such applications.
2. APPLICABLE DOCUMENTS:
The issue of the following documents in effect on the date of the purchase order forms a part of
this specification to the extent specified herein. The supplier may work to a subsequent revision
of a document unless a specific document issue is specified. When the referenced document
has been cancelled and no superseding document has been specified, the last published issue
of that document shall apply.
2.1 SAE Publications:
Available from SAE, 400 Commonwealth Drive, Warrendale, PA 15096-0001 or www.sae.org.
AMS 2261 Tolerances, Nickel, Nickel Alloy, and Cobalt Alloy Bars, Rods, and Wire
AMS 2269 Chemical Check Analysis Limits, Nickel, Nickel Alloys, and Cobalt Alloys
AMS 2371 Quality Assurance Sampling and Testing, Corrosion and Heat-Resistant Steels and
Alloys, Wrought Products and Forging Stock
AMS 2374 Quality Assurance Sampling and Testing, Corrosion and Heat-Resistant Steel
and Alloy Forgings
AMS 2750 Pyrometry
AMS 2806 Identification, Bars, Wire, Mechanical Tubing, and Extrusions, Carbon and Alloy
Steels and Corrosion and Heat-Resistant Steels and Alloys
AMS 2808 Identification, Forgings
AMS 7490 Rings, Flash Welded, Corrosion and Heat-Resistant Austenitic Steels and
Austenitic-Type Alloys, or Precipitation-Hardenable Alloys
2.2 ASTM Publications:
Available from ASTM, 100 Barr Harbor Drive, West Conshohocken, PA 19428-2959 or
www.astm.org.
Composition
min
0.05
-0.20
--20.00
20.00
13.00
0.02
--remainder
max
0.15
1.25
0.50
0.020
0.015
24.00
24.00
16.00
0.12
0.015
3.00
3.1.1 Check Analysis: Composition variations shall meet the applicable requirements of AMS
2269.
3.2 Condition:
The product shall be supplied in the following condition:
3.2.1 Bars: Hot finished and solution heat treated; round bars shall be ground or turned.
3.2.2 Forgings and Flash Welded Rings: Solution heat treated. Surface finish shall be as agreed
upon by purchaser and the forging or flash welded ring manufacturer.
3.2.2.1 Flash welded rings shall not be supplied unless specified or permitted on purchaser's
part drawing. When supplied, rings shall be manufactured in accordance with AMS 7490.
3.2.3 Stock for Forging or Flash Welded Rings: As ordered by the forging or flash welded ring
manufacturer.
16 hours thereafter, the stress shall be increased in increments of 2.0 ksi (14 MPa). Time to
rupture and elongation requirements shall be as specified in 3.4.1.3.
3.4.1.4 Oxidation Resistance: Shall be as follows, determined in accordance with 4.4.1:
3.4.1.4.1 Metal converted to oxide scale plus any continuous intergranular oxidation shall not
exceed an average of 0.0015 inch (0.038 mm) on each side or 0.003 inch (0.08 mm) on each
specimen.
3.4.1.4.2 Specimens displaying localized areas greater than 0.062 inch (1.57 mm) in diameter
with excessive oxidation attack, unless such attack can be attributed to contact with ceramic
supports, shall be considered invalid and the test repeated. If the condition is duplicated, the
product is not acceptable.
3.4.2 Forging Stock: When a sample of stock is forged to a test coupon and solution heat
treated as in 3.3, specimens taken from the heat treated coupon shall conform to the
requirements of 3.4.1.1, 3.4.1.2.2, 3.4.1.3, and 3.4.1.4. If specimens taken from the stock after
heat treatment as in 3.3 conform to the requirements of 3.4.1.1, 3.4.1.2.2, 3.4.1.3, and 3.4.1.4,
the tests shall be accepted as equivalent to tests of a forged coupon.
3.4.3 Stock for Flash Welded Rings: Specimens taken from the stock after solution heat
treatment as in 3.3 shall conform to the requirements of 3.4.1.1, 3.4.1.2.2, 3.4.1.3, and 3.4.1.4.
3.5 Quality:
The product, as received by purchaser, shall be uniform in quality and condition, sound, and free
from foreign materials and from imperfections detrimental to usage of the product.
3.5.1 Grain flow of die forgings, except in areas which contain flash-line end grain, shall follow
the general contour of the forgings showing no evidence of reentrant grain flow.
3.6 Tolerances:
Bars shall conform to all applicable requirements of AMS 2261.
4. QUALITY ASSURANCE PROVISIONS:
4.1 Responsibility for Inspection:
The vendor of the product shall supply all samples for vendor's tests and shall be responsible for
the performance of all required tests. Purchaser reserves the right to sample and to perform any
confirmatory testing deemed necessary to ensure that the product conforms to specified
requirements.
4.2 Classification of Tests:
4.2.1 Acceptance Tests: Composition (3.1), tensile properties (3.4.1.1), hardness (3.4.1.2),
stressrupture properties (3.4.1.3), and oxidation resistance (3.4.1.4) are acceptance tests and
shall be performed on each heat or lot as applicable.
4.2.2 Periodic Tests: Tests of forging stock (3.4.2) and of stock for flash welded rings (3.4.3) to
demonstrate ability to develop required properties and grain flow of die forgings (3.5.1) are
periodic tests and shall be performed at a frequency selected by the vendor unless frequency of
testing is specified by purchaser.
4.3 Sampling and Testing:
Shall be as follows:
4.3.1 Bars, Flash Welded Rings, and Stock for Forging or Flash Welded Rings: In accordance
with AMS 2371.
4.3.2 Forgings: In accordance with AMS 2374.
4.4 Test Methods:
4.4.1 Oxidation Resistance:
4.4.1.1 Specimen Preparation: Specimens shall have surface area not less than 1.5 square
inches (9.7 cm2) available for exposure in excess of material required for fixturing. Both sides of
the specimen shall have a 120-grit surface finish. Specimens' dimensions shall be measured
within 0.0003 inch ( 0.008 mm). Specimens shall be degreased.
4.4.1.2 Testing: Specimens shall be subjected to four cycles, each cycle consisting of heating to
2000 to 2100 F (1093 to 1149 C), holding at the selected temperature within 25 F (14 C)
for 25 hours 1, and cooling in air to 300 F (149 C) or lower between each cycle for a total of
100 hours 4 at heat. Specimens may be partially inserted into inert ceramic bricks or
suspended from inert ceramic rods or suitable metallic rods, but shall not be placed in crucibles.
The specimens may be tested in a muffle or comparable furnace providing air flow is such that
the required surface areas are equally exposed to the flowing air and temperature.
4.4.1.3 Examination: Test specimens shall be cross sectioned and examined metallographically
in the as-polished condition at not lower than 500X magnification. Not less than eight randomly
selected surface areas, 0.008 inch (0.20 mm) in length, shall be measured and the values
averaged to determine compliance with 3.4.1.4.
4.5 Reports:
The vendor of the product shall furnish with each shipment a report showing the following
results of tests and relevant information:
4.5.1 For each heat: Composition.
4.5.2 For each lot of bars, forgings, and flash welded rings:
Tensile Properties
Hardness
Stress-rupture properties
Oxidation resistance.
4.5.3 A statement that the product conforms to the other technical requirements.
8. NOTES:
8.1 A change bar (|) located in the left margin is for the convenience of the user in locating areas
where technical revisions, not editorial changes, have been made to the previous issue of a
specification.
An (R) symbol to the left of the document title indicates a complete revision of the specification,
including technical revision. Change bars and (R) are not used in original publications, nor in
specifications that contain editorial changes only.
8.2 Hardness conversion tables for metals are presented in ASTM E 140.
8.3 Terms used in AMS are clarified in ARP1917.
8.4 Dimensions and properties in inch/pound units and the Fahrenheit temperatures are
primary; dimensions and properties in SI units and the Celsius temperatures are shown as the
approximate equivalents of the primary units and are presented only for information.
8.5 Purchase documents should specify not less than the following:
AMS 5772D
Form and size or part number of product desired
Quantity of product desired.