440C DS Carpenter
440C DS Carpenter
440C DS Carpenter
Identification
UNS Number
S44004
Type Analysis
Carbon
Phosphorus
Silicon
Molybdenum
0.95 to 1.20
0.040
1.00
0.75
%
%
%
%
Manganese
Sulfur
Chromium
Iron
1.00
0.030
16.00 to 18.00
77.98 to 80.23
%
%
%
%
General Information
Description
Carpenter Stainless Type 440C is a high-carbon chromium steel designed to provide stainless properties with maximum hardness. It
has been used primarily as a bearing steel, and is used in the hardened plus tempered condition. When heat-treated, Type 440C
attains the highest hardness of any stainless steel (about Rockwell C 60).
Applications
This stainless steel principally has been used in bearing assemblies, including bearing balls and races. In addition, it should be
considered for cutlery, needle valves, ball check valves, valve seats, pump parts, ball studs, bushings, and wear-resistant textile
components.
Elevated Temperature Use
Carpenter Stainless Type 440C is not usually recommended for elevated temperature applications since corrosion resistance is
reduced when used in the annealed condition or hardened and tempered above about 800F (427C).
Corrosion Resistance
Carpenter Stainless Type 440C resists corrosion in normal domestic environments and very mild industrial environments, including
many petroleum products and organic materials.
This grade is used in the hardened plus tempered condition. Optimum corrosion resistance is obtained by hardening from 2000F
(1093C) to ensure better carbide solution.
However, care should be taken to minimize time at 2000F (1093C) to avoid excessive grain coarsening. For best corrosion
resistance, the tempering temperature should be below about 800F (427C).
For optimum corrosion resistance, surfaces must be free of scale, lubricants, foreign particles, and coatings applied for drawing and
heading. After fabrication of parts, cleaning and/or passivation should be considered.
Important Note:The following 4-level rating scale is intended for comparative purposes only. Corrosion testing is recommended;
factors which affect corrosion resistance include temperature, concentration, pH, impurities, aeration, velocity, crevices, deposits,
metallurgical condition, stress, surface finish and dissimilar metal contact.
Nitric Acid
Phosphoric Acid
Sodium Hydroxide
Humidity
Moderate
Restricted
Moderate
Good
Sulfuric Acid
Acetic Acid
Salt Spray (NaCl)
Restricted
Restricted
Restricted
Properties
Physical Properties
Specific Gravity
7.62
Page: 1 of 5
0.2750
0.1100
5.60
168.0
29.0
361.0
lb/in
Btu/lb/F
x 10 -6 in/in/F
BTU-in/hr/ft/F
x 10 3 ksi
ohm-cir-mil/ft
Heat Treatment
Annealing
For maximum softness, this steel should be heated uniformly to 1550/1600F (843/871C). Soak and cool very slowly in the furnace.
Brinell hardness approximately 223. Intermediate or process annealing treatment-heat uniformly to 1350/1400F (732/760C). Air
cool. Brinell hardness about 255.
Hardening
Heat to 1850/1950F (1010/1066C); soak; quench in warm oil or cool in air. Do not overheat. When overheated, full hardness cannot
be obtained. See comments under corrosion resistance.
Tempering
Hardness of approximately Rockwell C 60 will be obtained. To remove peak stresses and yet retain maximum hardness, temper at
least one hour at 300/350F (149/177C).
Page: 2 of 5
Workability
Hot Working
This steel should be handled like high-speed tool steel. Preheat to 1400/1500F (760/816C), then heat slowly and uniformly to
1900/2100F (1038/1149C). Do not forge below 1700F (927C), and reheat as often as necessary. Cool in a furnace if possible or in
warm dry lime or ashes. Anneal after forging; cool to room temperature before annealing.
Cold Working
If annealed for maximum softness, this steel can be moderately cold formed or headed.
Machinability
For most machining operations, this steel cuts best when in the dead soft annealed condition. Because of its high carbon content it
machines somewhat like high-speed steel. Because chips are tough and stringy, chip curlers and breakers are important.
The following are typical feeds and speeds for Carpenter Stainless Type 440C.
Page: 3 of 5
Figures used for all metal removal operations covered are average. On certain work, the nature of the part may require adjustment of
speeds and feeds. Each job has to be developed for best production results with optimum tool life. Speeds or feeds should be
increased or decreased in small steps.
Grinding and Polishing
In cutlery applications, grinding and polishing are very important. Carpenter Stainless Steel Type 440C works well in these operations
but considerable care must be used not to overheat since both the hardness and corrosion resistance may be lowered.
Weldability
Because of its high-hardness capability, this steel is seldom welded. However, if welding is necessary, the parts should be preheated
and maintained at about 500F (260C), welded, and then immediately given a 6-8 hour anneal at 1350/1400F (732/760C) with a
slow furnace cool. The parts should not be allowed to cool below 500F (260C) between welding and annealing. High welding heat
inputs should be used. To obtain mechanical properties in the weld similar to those in the base metal, welding consumables of like
composition should be considered. Otherwise, AWS E/ER309 might also be considered.
Page: 4 of 5
AMS 5630
ASTM A276
ASTM A473
ASTM A580
QQ-S-763
Billet
Wire-Rod
Forms Manufactured
Bar-Rounds
Wire
Technical Articles
Disclaimer:
The information and data presented herein are typical or average values and are not a guarantee of maximum or minimum values. Applications specifically suggested for
material described herein are made solely for the purpose of illustration to enable the reader to make his/her own evaluation and are not intended as warranties, either