    This welding procedure qualification certificate certifies that welder Jacek Nakonieczny successfully welded and tested a V-joint between 4mm thick parent materials made of material group 8.1 using the TIG welding process. The weld metal thickness was 4mm and the throat thickness ranged from 2-3.5mm. The filler material was Thermanit GE-316L wire with a diameter of 2mm. Shielding and backing gases used were argon. Welding was performed in the PC and PF positions with a heat input between 0.4-1.08 kJ/mm.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    VP16 PDF

    Uploaded by

    Kara White
    149 views13 pages
    This welding procedure qualification certificate certifies that welder Jacek Nakonieczny successfully welded and tested a V-joint between 4mm thick parent materials made of material group 8.1 using the TIG welding process. The weld metal thickness was 4mm and the throat thickness ranged from 2-3.5mm. The filler material was Thermanit GE-316L wire with a diameter of 2mm. Shielding and backing gases used were argon. Welding was performed in the PC and PF positions with a heat input between 0.4-1.08 kJ/mm.

    Original Description:

    Original Title

    VP16.pdf

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This welding procedure qualification certificate certifies that welder Jacek Nakonieczny successfully welded and tested a V-joint between 4mm thick parent materials made of material group 8.1 using the TIG welding process. The weld metal thickness was 4mm and the throat thickness ranged from 2-3.5mm. The filler material was Thermanit GE-316L wire with a diameter of 2mm. Shielding and backing gases used were argon. Welding was performed in the PC and PF positions with a heat input between 0.4-1.08 kJ/mm.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    149 views13 pages

    VP16 PDF

    Uploaded by

    Kara White
    This welding procedure qualification certificate certifies that welder Jacek Nakonieczny successfully welded and tested a V-joint between 4mm thick parent materials made of material group 8.1 using the TIG welding process. The weld metal thickness was 4mm and the throat thickness ranged from 2-3.5mm. The filler material was Thermanit GE-316L wire with a diameter of 2mm. Shielding and backing gases used were argon. Welding was performed in the PC and PF positions with a heat input between 0.4-1.08 kJ/mm.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 13

    Certificate no: HAM 1571024/2

    Page 1 of 

    Welding Procedure Qualification Certificate


    (EN ISO 15614-1)
    Energy - Downstream, Power and Manufacturing
    Manufacturers Welding Procedure Qualification Examining body
    VP16E /
    Record No.: Reference No:

    Manufacturer: Ruhfus Systemhydraulik GmbH


    Address: Neuss / Germany
    Welders Name Jacek Nakonieczny

    Code/Testing Standard: EN ISO 15614, Lloyd's Register Rules and Regulations


    Date of Welding: 22 May 2015
    Range of Qualification

    Welding Process(es): 141 (TIG)


    Type of joint and weld: V-Joint 40-60
    Parent material group(s) and sub- 8.1 / 8.1
    ()
    Parent Material Thickness (mm): 4,0
    Weld Metal Thickness (mm): 4,0
    Throat Thickness (mm) 2,0-3,5
    Single Run/Multi Run Multi Run
    Outside Pipe Diameter (mm): 30,0
    Filler Material Designation: Thermanit GE-316 L
    Filler Material Make: Bhler
    Filler Material Size: 2,0 mm
    Designation of Shielding Gas/Flux: EN ISO 14175-I1-Ar
    Designation of Backing Gas: EN ISO 14175-I1-Ar
    Type of Welding Current and Polarity: direct current (-)
    Mode of Metal Transfer: ---
    Heat Input: 0,4-1,08 kJ/mm
    Welding Positions: PC+PF
    Preheat Temperature: 15,0C
    Interpass Temperature: 150,0C
    Post-Heating: ---
    Post-Weld Heat Treatment and/or ---
    A i
    Other Information
    For further details see WPS VO16E PC+PH and Techno Labor test report.

    Certified that test welds were prepared, welded and tested satisfactorily in accordance with the requirements of the code/testing standard indicated
    above.
    Location: Dortmund Date of Issue: 18 June 2015
    Surveyor Thomas Aschert
    Hamburg Office

    For K. Nebel: Lloyd's Register EMEA


    Surveyor to Lloyd'sLR031.1.2013.12
    Register EMEA

    A subsidiary of Lloyd's Register Group Limited

    Examining Body

    Lloyd's Register Group Limited, its affiliates and subsidiaries and their respective officers, employees or agents are, individually and collectively, referred to in this clause as
    'Lloyd's Register'. Lloyd's Register assumes no responsibility and shall not be liable to any person for any loss, damage or expense caused by reliance on the information or
    advice in this document or howsoever provided, unless that person has signed a contract with the relevant Lloyd's Register entity for the provision of this information or
    advice and in that case any responsibility or liability is exclusively on the terms and conditions set out in that contract.

    Form 4102 (2013.12)