At a glance
Powered by AI
The document describes reference photographs that represent various conditions of steel surfaces before and after abrasive blast cleaning to supplement written surface preparation standards.

The initial conditions described are: Condition A (mill scale), Condition B (mill scale and rust), Condition C (100% rust with little pitting), Condition D (100% rust with pitting), and Condition G (previously painted steel that is weathered, blistered, or stained).

The degrees of surface cleaning described are: SSPC-SP 7/NACE No. 4 (Brush-Off Blast Cleaning), SSPC-SP 14/NACE No. 8 (Industrial Blast Cleaning), SSPC-SP 6/NACE No. 3 (Commercial Blast Cleaning), SSPC-SP 10/NACE No. 2 (Near-White Blast Cleaning), and SSPC-SP 5/NACE No. 1 (White Metal Blast Cleaning).

Guide to SSPC-VIS 1

June 1, 2002
Editorial Revisions November 1, 2004

SSPC: The Society for Protective Coatings

GUIDE TO SSPC-VIS 1
Guide and Reference Photographs for Steel Surfaces
Prepared by Dry Abrasive Blast Cleaning

1. Scope
Condition C: Steel surface completely covered with
rust; little or no pitting visible
This guide describes the use of reference photographs
Condition D: Steel surface completely covered with
depicting the appearance of both previously unpainted and
rust; pitting visible
previously painted and partially rusted hot-rolled carbon
Condition G: Coating system applied over mill scale
steel prior to and after abrasive blast cleaning. These pho-
bearing steel; system thoroughly weath-
tographs are intended to be used to supplement the written
ered, thoroughly blistered, or thoroughly
SSPC/NACE International blast cleaning surface preparation
stained
standards. The written standards are the primary means to
Condition G1 In this series of photographs, exten-
determine conformance with blast cleaning requirements. The
sive pinpoint rusting is present.
photographs shall not be used as a substitute for the written
Condition G2 In this series of photographs, moder-
standards (see Note 7.1).
ate pitting is present
Condition G3 In this series of photographs, severe
2. Description
pitting is present.
The reference photographs consist of a series of 1:1 (actual
4.2 These reference photographs illustrate surfaces
size) color photographs that represent various conditions of
prepared by abrasive blast cleaning using silica sand with the
unpainted and painted steel surfaces prior to and after surface
exception of those in Appendix A (see Section 4.3).
preparation by abrasive blast cleaning. The photographs were
taken under controlled studio lighting designed to show the
The various degrees of cleaning represented are:
maximum detail possible.

SSPC-SP 7/NACE No. 4 Brush-Off Blast Cleaning


3. Referenced Standards
SSPC-SP 14/NACE No. 8 Industrial Blast Cleaning
3.1 SSPC AND NACE INTERNATIONAL JOINT SSPC-SP 6/NACE No. 3 Commercial Blast Cleaning
STANDARDS: SSPC-SP 10/NACE No. 2 Near-White Blast Cleaning
SSPC-SP 5/NACE No. 1 White Metal Blast Cleaning
SP 5/NACE No. 1 White Metal Blast Cleaning
SP 6/NACE No. 3 Commercial Blast Cleaning 4.3 Appendix A: Photographs illustrative of some varia-
SP 7/NACE No. 4 Brush-Off Blast Cleaning tions in color, texture, and general appearance that can result
SP 10/NACE No. 2 Near-White Blast Cleaning from the choice of abrasive are provided in Appendix A (also
SP 14/NACE No. 8 Industrial Blast Cleaning see Note 7.2). These photographs represent Condition A (ad-
herent mill scale) surfaces blast cleaned to SSPC-SP 5/NACE
4. Conditions Depicted No. 1 (white metal) by mineral, slag, and metallic abrasives.
The variations in appearance are depicted only for white metal;
4.1 These reference photographs illustrate ve initial rust
however, these same variations should be considered when
conditions before surface preparation, covering the range from
assessing steel prepared to other degrees of cleaning.
intact mill scale to rusted and pitted steel, as well as previously
painted steel.1 The rust conditions are:
4.4 Appendix B: These photographs illustrate how varia-
tions in surface prole, view angle, and lighting can affect the
Condition A: Steel surface completely covered with
appearance of G1 and G3 surfaces blast cleaned to SSPC-SP
adherent mill scale; little or no rust visible
5/NACE No. 1.
Condition B: Steel surface covered with both mill
4.4.1 Prole Variations: The photographs labeled P
scale and rust
show G1 SP 5 and G3 SP 5 surfaces with a prole height of 4

1
Conditions E and F are described and illustrated in SSPC-VIS 4/NACE VIS 7.

Copyright The Society for Protective Coatings


--`,```,`,,`,``,,,,`,``,,,`,,,-`-`,,`,,`,`,,`---
2-33
Provided by IHS under license with SSPC Licensee=ChevronTexaco-Petro Chem 9 loc/9 usr Part 2/1000001106
No reproduction or networking permitted without license from IHS Not for Resale, 03/16/2006 03:56:19 MST
Guide to SSPC-VIS 1
June 1, 2002
Editorial Revisions November 1, 2004

mils (100 m). For comparison, a single photo of the same 6. Disclaimer
surface condition with a prole height of 1 mil (25 m) is also
shown. The lighting conditions were the same as those used 6.1 While every precaution is taken to ensure that all
in the G1 and G3 series. information furnished in SSPC guides and standards is as
accurate, complete, and useful as possible, SSPC cannot
4.4.2 Angle of View: The photographs labeled H, L assume any responsibility nor incur any obligation resulting
and D show variations in appearance of the 4-mil (25 m) from the use of any materials or methods specied therein, or
G1 SP 5 P and G3 SP 5 P specimens caused by differences in of the guides or standards themselves.
the angle at which the surface is viewed. Photographs labeled
H were taken at a high (i.e., nearly perpendicular) camera 6.2 This guide does not attempt to address problems
angle. Photographs labeled L were taken at a lower (more concerning safety associated with its use. The user of this
acute) camera angle. specication, as well as the user of all products or practices
described herein, is responsible for instituting appropriate
4.4.3 Diffusion of Light: The photographs labeled D health and safety practices and for ensuring compliance with
were taken using diffused lighting, as may occur on a completely all governmental regulations.
overcast day. Due to the diffused light, no strong shadows ap-
pear on the surface, regardless of the angle of view. However, 7. Notes
these photographs show that diffused light may result in an
overall color cast to the surface. 7.1 This edition of SSPC-VIS 1 contains all of the pho-
tographs contained in the 1989 edition. The written surface
5. Procedure preparation standards, such as SSPC-SP 5, are joint stan-
dards of SSPC and NACE International and are identied as
5.1 Select the photograph of the condition (A, B, C, D, such in Section 3.3. This revised edition also contains pho-
G1 G2 or G3) that most closely represents the appearance of tographs of previously painted steel that has been abrasive
the steel to be cleaned. The steel to be cleaned may contain blast cleaned.
more than one initial condition.
7.2 The photographs of nonmetallic abrasives in Appendix
5.2 Determine the degree of cleaning that is specied A illustrate the range of appearance produced by nonmetallic
(SSPC-SP 7, SP 14, SP 6, SP 10, or SP 5). abrasives as a class. Among the abrasives included in this
class are silica sand, olivine sand, garnet, int shot, copper
5.3 Use Table 1 to determine which photograph depicts slag, coal slag, and nickel slag. The abrasive used for each
the nished surface. For example, if the initial condition is C photograph is not specically identied because noticeable

--`,```,`,,`,``,,,,`,``,,,`,,,-`-`,,`,,`,`,,`---
and SSPC-SP 6 (commercial blast cleaning) is specied, use variations in appearance were observed among the abrasives
photograph C SP 6 (also see Note 7.3). within a given generic class (e.g., copper slag).

5.4 Compare the prepared surface with the photograph A similar set of photographs illustrates the range of ap-
selected in Section 5.3 to evaluate the degree of cleaning. pearance produced by metallic abrasives as a class, which
includes steel shot, steel grit, and combinations and modica-
5.5 These reference photographs shall be used only in tions of these two abrasive media.
conjunction with the written SSPC/NACE International surface
preparation standards, as the reference photographs are based 7.3 In addition to the photographs prepared from pre-
upon appearance only and do not address other factors neces- viously painted steel shown in the Condition G series, the
sary for compliance with the written specication. Steel surfaces photographs in the Conditions A through D series prepared
from unpainted steel are often found to be representative of
show variations in texture, shade, color, tone, pitting, aking,
the appearance of blast cleaned steel that was previously
mill scale, etc., which should be considered when making a painted.
comparison with the reference photographs.

Copyright The Society for Protective Coatings 2-34


Provided by IHS under license with SSPC Licensee=ChevronTexaco-Petro Chem 9 loc/9 usr Part 2/1000001106
No reproduction or networking permitted without license from IHS Not for Resale, 03/16/2006 03:56:19 MST
Guide to SSPC-VIS 1
June 1, 2002
Editorial Revisions November 1, 2004

TABLE 1
INITIAL CONDITIONS

--`,```,`,,`,``,,,,`,``,,,`,,,-`-`,,`,,`,`,,`---
Condition G1
Condition G2 Condition G3
Weathered
Weathered Weathered
Condition Condition Condition Coating Sys-
Condition Coating Sys- Coating
Degree of A B D tem Over Mill
C tem Over Mill System Over
Cleaning 100% Mill Mill Scale 100% Rust Scale with
100% Rust Scale with Mill Scale
Scale and Rust with Pits Extensive
Moderate with Severe
Pinpoint
Pitting Pitting
Rusting

Brush-Off See
B SP 7 C SP 7 D SP 7 G1 SP 7 G2 SP 7 G3 SP 7
Blast Cleaning Footnote 1
(SSPC-SP 7)

Industrial See See See See


G1 SP 14 G2 SP 14 G3 SP 14
Blast Cleaning Footnote 2 Footnote 2 Footnote 2 Footnote 2
(SSPC-SP 14)

Commercial See
B SP 6 C SP 6 D SP 6 G1 SP 6 G2 SP 6 G3 SP 6
Blast Cleaning Footnote 3
(SSPC-SP 6)

Near-White
A SP 10 B SP 10 C SP 10 D SP 10 G1 SP 10 G2 SP 10 G3 SP 10
Blast Cleaning
(SSPC-SP 10)
G1 SP 5 G3 SP 5
G1 SP 5 P5 G3 SP 5 P5
White Metal
A SP 5 B SP 5 C SP 5 D SP 5 G1 SP 5 H G3 SP 5 H
Blast Cleaning G2 SP 5
G1 SP 5 L G3 SP 5 L
(SSPC-SP 5)
G1 SP 5 D G3 SP 5 D

1
No photograph provided. The initial condition has only tightly adherent mill scale, which, according to the SSPC-SP 7 denition, is not removed by
brush-off blast cleaning.
2
SSPC-SP 14 can be achieved from these conditions, but photographs are not available.
3
No photograph provided. The effort required to remove mill scale on Condition A steel typically results in less staining than the maximum 33% allowed
by SP 6, approaching the photograph provided for A SP 10.
4
The photographs contained in Appendix A depict the appearance of previously unpainted steel surfaces after blast cleaning to white metal with alternate
abrasives (see Note 7.2).
Alternate nonmetallic abrasives A SP 5 N1, A SP 5 N2, A SP 5 N3
Alternate metallic abrasives: A SP 5 M1, A SP 5 M2, A SP 5 M3.
5
The photographs contained in Appendix B illustrate the effect of variations in prole height (P), viewing angle (H, L), and diffusion of light (D) on the
appearance of a pitted surface and a nonpitted surface.

Copyright The Society for Protective Coatings 2-35


Provided by IHS under license with SSPC Licensee=ChevronTexaco-Petro Chem 9 loc/9 usr Part 2/1000001106
No reproduction or networking permitted without license from IHS Not for Resale, 03/16/2006 03:56:19 MST
--`,```,`,,`,``,,,,`,``,,,`,,,-`-`,,`,,`,`,,`---

Copyright The Society for Protective Coatings


Provided by IHS under license with SSPC Licensee=ChevronTexaco-Petro Chem 9 loc/9 usr Part 2/1000001106
No reproduction or networking permitted without license from IHS Not for Resale, 03/16/2006 03:56:19 MST