A M E R I C A N A R C H I T E C T U R A L

AAMA 2605-05
Voluntary Specification,
Performance Requirements
and Test Procedures for
Superior Performing Organic
Coatings on Aluminum
Extrusions and Panels

M A N U F A C T U R E R S A S S O C I A T I O N
 TABLE OF CONTENTS
Preface...................................................................................1

Superceed...............................................................................1

1.0 Scope ...............................................................................1

2.0 Purpose ............................................................................1

3.0 Definitions ........................................................................1

4.0 General .............................................................................1

5.0 Test Specimens ..................................................................2

6.0 Metal Preparation And Pre-treatment.....................................2

7.0 Tests ................................................................................2

8.0 Test Reports ......................................................................6

9.0 Referenced Standards..........................................................7

AAMA. The Source of Performance Standards, Product Certification and

Educational Programs for the Fenestration Industry.

This voluntary specification was developed by representative members of AAMA

as advisory information and published as a public service. AAMA disclaims all
liability for the use, application or adaptation of materials published herein.

2005
American Architectural Manufacturers Association
1827 Walden Office Square, Suite 550, Schaumburg, IL 60173
PHONE (847)303-5664 FAX (847)303-5774
EMAIL webmaster@aamanet.org WEBSITE www.aamanet.org

All AAMA documents may be ordered at our web site in the Publications Store.

Originally Published: 1998

Preceeding Document: 2605-02
Revised And Published: 7/2005
PREFACE 2.0 PURPOSE

For years, the architectural community has recognized The specification will assist the architect, owner and
AAMA 603 and AAMA 605 as the standards for testing contractor to specify and obtain factory-applied organic
and performance of organic coatings on architectural coatings, which will provide and maintain a superior level
aluminum extrusions and panels. Significant advances of performance in terms of film integrity, exterior
have been made in technology which has created the need weatherability and general appearance over a period of
to revise these specifications. many years.

AAMA 2603, "Voluntary Specification, Performance 3.0 DEFINITIONS

Requirements and Test Procedures for Pigmented Organic
Coatings on Aluminum Extrusions and Panels;"
3.1 The terms "film" and "coating" are used
interchangeably in this specification and are defined as
AAMA 2604, "Voluntary Specification, Performance
meaning the layer of organic material applied to the
Requirements and Test Procedures for High Performance
surface of the aluminum.
Organic Coatings on Aluminum Extrusions and Panels;"
3.2 Exposed surfaces are those surfaces which are visible
AAMA 2605, "Voluntary Specification, Performance
when the coated product is installed. These may include
Requirements and Test Procedures for Superior Performing
both closed and open positions of operating sash,
Organic Coatings on Aluminum Extrusions and Panels."
ventilators, doors or panels.

SUPERCEED 3.3 Spray Coating: The process of applying a resinous

coating by atomizing it into a spray or mist, and curing it
AAMA 603, "Voluntary Performance Requirements and into a continuous film.
Test Procedures for Pigmented Organic Coatings on
Extruded Aluminum;" and 4.0 GENERAL
AAMA 605, "Voluntary Specification for High Performance
4.1 To qualify as meeting this specification, products
Organic Coatings on Architectural Extrusions and Panels;"
tested shall meet all requirements as specified herein.
as well as all revisions to these documents.
4.2 Coatings shall be visibly free from flow lines, streaks,
AAMA 2605 is a new ten-year superior performing
blisters or other surface imperfections in the dry-film state
specification with increased performance to AAMA 605.2-
on exposed surfaces when observed at a distance of 3 m
92. Significant upgrades have been made in the areas of
(10 ft) from the metal surface and inspected at an angle of
ten-year weathering performance, abrasion resistance, salt
90 degrees to the surface.
spray and humidity.
4.3 The total dry-film thickness shall be assessed utilizing
1.0 SCOPE the ASTM D 1400 method. Eighty percent of
measurements on primary exposed surfaces shall meet or
1.1 This specification describes test procedures and exceed 30 microns (1.2 mil) total film thickness. Paint
performance requirements for superior performing process capability may result in readings below 25
organic coatings applied to aluminum extrusions and microns (1.0 mil). No more than 5% of the total readings,
panels for architectural products. on primary exposed surfaces, shall be below 25 microns
(1.0 mil) (or, 85% of film thickness specified), assuming
1.2 This specification covers factory-applied spray appropriate color and hide. Film thickness specified may
coatings only. be increased to be consistent with color selection and type
of coating as recommended by the coating manufacturer.
1.3 The primary units of measure in this document are
metric. The values stated in SI units are to be regarded as NOTE: Due to the complexities of extrusion dies and
the standard. The values given in parentheses are for limitations of application equipment, it may not be
reference only. possible to achieve minimum recommended dry film
thickness on all areas of an extrusion, such as inside
corners and channels. For details of these affected areas,
contact the coating applicator prior to painting.

4.4 Cleaning and metal preparation shall be in compliance

with Section 6 of this document.

AAMA 2605-05 Page 1

4.5 Minor scratches and blemishes shall be repairable 6.2 CHEMICAL CONVERSION COATING WEIGHT
with the coating manufacturer's recommended product or
system. Such repairs shall match the original finish for 6.2.1 Procedure
color and gloss and shall adhere to the original finish Measure in accordance with the latest issue of ASTM D
when tested as outlined in Section 7.4.1.1, Dry Adhesion. 5723 using x-ray fluorescence or other standard methods
After application, allow the repair coating to dry for at for determining coating weights.
least 72 hours at 18C to 27C (65F to 80F) before
conducting the film adhesion test. 6.2.2 Performance
Chrome containing conversion coating weights should be
NOTE: The size and number of touch-up repairs should a minimum of 431 mg/m2 (40 mg/ft2).
be kept to a minimum.
Non-chrome conversion coating weights should be
4.6 Sealant used in contact with an organic coating shall maintained according to suppliers recommendations.
be compatible with the organic coating and meet the
performance requirements of AAMA 800 sealant NOTE: Frequent in-plant testing and control of
specification. There shall be no evidence of deleterious pretreatment is required to insure satisfactory
effects in the organic coating such as staining, coating performance of the coating system.
separation, lifting, discoloration or loss of adhesion of the
coating from the substrate. 7.0 TESTS
NOTE: It is strongly recommended that the fabricator of
7.1 COLOR UNIFORMITY
the finished products consult with the sealant
manufacturer in the selection of the appropriate sealant.
7.1.1 Procedure
Pell adhesion testing as described in AAMA 800 is
Check random samples visually under a uniform light
suggested. It is important to understand that the AAMA
source. Viewing should be done at multiple angles. In
800 sealant specification does not ensure adhesion to a
conjunction, instrumental methods are imperative.
specific coating. The best way to ensure adhesion is to
submit panel specimens of the specific coating to the
7.1.2 Performance
sealant manufacturer or an AAMA accredited
Color uniformity shall be consistent with the color range
independent laboratory for tests and recommendations.
or numerical value established between the approval
source and the applicator. Suggested range is 2E per
5.0 TEST SPECIMENS ASTM D 2244, Section 6.3, from agreed upon color
standard.
5.1 Test specimens shall consist of finished panels or
extrusions representative of the production coated NOTE: Color and finish appearance may vary upon
aluminum. A sufficient number of specimens on which to factory application due to differences in spray equipment,
conduct instrument measurements with flat coated line conditions or day-to-day process variations. It is
surfaces of at least 150 mm (6 in) long and 75 mm (3 in) strongly recommended that final color approval be made
wide, shall be submitted to the testing laboratory. The with actual production line samples or mock-ups, not
coating applicator or fabricator shall indicate exposed laboratory prepared panels
surfaces or submit drawings. Tests shall be performed on
exposed areas as indicated on drawings or as marked on Pearlescent mica and metallic flakes reflect and scatter
test specimens. light in random patterns; therefore, exact color uniformity
should not be expected. Slight color shifting should also
6.0 METAL PREPARATION AND PRE- be expected when viewing from varying angles and
distances. Equipment considerations affect color and are
TREATMENT especially critical with multiple applicators.
NOTE: A multi-stage cleaning and pre-treatment system 7.2 SPECULAR GLOSS
is required to remove organic and inorganic surface soils,
remove residual oxides, and apply a chemical conversion 7.2.1 Procedure
coating to which organic coatings will firmly adhere. Measure in accordance with the latest issue of ASTM D
523 using a 60 degree gloss meter. Samples must meet
6.1 The pre-treatment when used in conjunction with a minimum dry film thickness requirements.
baked organic coating shall produce a total finishing
system capable of meeting impact, adhesion, detergent, 7.2.2 Performance
humidity and salt spray performance as specified in the Gloss values shall be within 5 units of the manufacturer's
appropriate test method. specification.

AAMA 2605-05 Page 2

NOTE: Standard gloss range reference values are: 7.5 IMPACT RESISTANCE

Gloss Colors Specular Gloss Value 7.5.1 Procedure

Using a 16 mm (5/8 in) diameter round-nosed impact
High 80-Over tester 18 N-m (160 in-lb) range such as a Gardner impact
Medium 20-79 tester, apply a load directly to the coated surface of
Low 19 or less sufficient force to deform the test sample a minimum of 3
mm 0.3 mm (0.10 in 0.01 in). Apply tape (Permacel
7.3 DRY FILM HARDNESS 99 or equivalent) 20 mm (3/4 in) wide over area of
deformation by pressing down firmly against coating to
7.3.1 Procedure eliminate voids and air pockets. Sharply pull tape off at a
Strip the wood from a Berol Eagle Turquoise pencil or right angle to the plane of the surface being tested. Test
equivalent, grade F minimum hardness, leaving a full pieces should be at ambient temperature approximately
diameter of lead exposed to a length of 6 mm minimum to 18C to 27C (65F to 80F).
10 mm maximum (1/4 in minimum to 3/8 in maximum).
Flatten the end of the lead 90 degrees to the pencil axis 7.5.2 Performance
using fine-grit sand or emery paper. Hold the pencil at a No removal of film from substrate.
45 degree angle to the film surface and push forward
about 6 mm (1/4 in) using as much downward pressure as NOTE: Minute cracking at the perimeter of the concave
can be applied without breaking the lead. Reference area of the test panel is permissible but no coating pick-
ASTM D 3363. off should be apparent.
7.3.2 Performance 7.6 ABRASION RESISTANCE
No rupture of film per ASTM D 3363.
7.6.1 Procedure
7.4 FILM ADHESION Using the falling sand test method, ASTM D 968, the
Abrasion Coefficient shall be calculated according to the
7.4.1 Procedure formula which follows.
7.4.1.1 Dry Adhesion ABRASION COEFFICIENT - LITERS PER MIL = V/T
Make 11 parallel cuts, 1 mm (1/16 in) apart through the
film. Make 11 similar cuts at 90 degrees to and crossing where: V = volume of sand used in liters
the first 11 cuts. Apply tape (Permacel 99 or equivalent) T = thickness of coating in mils
20 mm (3/4 in) wide over area of cuts by pressing down
firmly against the coating to eliminate voids and air 7.6.2 Performance
pockets. Sharply pull the tape off at a right angle to the The Abrasion Coefficient Value of the coating shall be 40
plane of the surface being tested. Test pieces should be at minimum.
ambient temperature [approximately 18C to 27C (65F
to 80F)]. 7.7 CHEMICAL RESISTANCE
7.4.1.2 Wet Adhesion 7.7.1 Muriatic Acid Resistance
Make cuts as outlined in Section 7.4.1.1. Immerse the (15-Minute Spot Test)
sample in distilled or deionized water at 38C (100F) for
24 hours. Remove and wipe the sample dry. Repeat the 7.7.1.1 Procedure
test specified in Section 7.4.1.1 within five minutes. Apply 10 drops of 10% (by volume) solution of muriatic
acid (37% commercial grade hydrochloric acid) in tap
7.4.1.3 Boiling Water Adhesion water and cover it with a watch glass, convex side up. The
Make cuts as outlined in Section 7.4.1.1. Immerse the acid solution and test shall be conducted at 18C to 27C
sample in boiling distilled or deionized water 99C to (65F to 80F). After a 15-minute exposure, wash off with
100C (210F to 212F) for 20 minutes. The water shall running tap water.
remain boiling throughout the test. Remove the sample
and wipe it dry. Repeat the test specified in Section 7.7.1.2 Performance
7.4.1.1 within five minutes. No blistering and no visual change in appearance when
examined by the unaided eye.
7.4.2 Performance
No removal of film under the tape within or outside of the 7.7.2 Mortar Resistance
cross-hatched area or blistering anywhere on the test (24-Hour Pat Test)
specimen. Report loss of adhesion as a percentage of
squares affected, (i.e., 10 squares lifted is 10% failure).

AAMA 2605-05 Page 3

7.7.2.1 Procedure Parts by
Prepare mortar by mixing 75 g (2.6 oz) of building lime Weight
(conforming to ASTM C 207) and 225 g (7.9 oz) of dry Tetrasodium pyrophosphate (Na4P2O7)
sand, both passing through a 10-mesh wire screen with 53.0
anhydrous
sufficient water, approximately 100 g (3.5 oz), to make a Sodium sulfate (Na2SO4), anhydrous 19.0
soft paste. Immediately apply wet pats of mortar about Sodium metasilicate (Na2SiO3), anhydrous 7.0
1300 mm2 (2 in2) in area and 12 mm (1/2 in) in thickness Sodium carbonate (Na2CO3), anhydrous 1.0
to coated aluminum specimens which have been aged at
Sodium salt of a linear alkylarylsulfonate
least 24 hours after coating. Immediately expose test 20.0
(90% flake grade)
sections for 24 hours to 100% relative humidity at 38C
Total 100.0
(100F).

7.7.2.2 Performance 7.7.4.2 Performance

Mortar shall dislodge easily from the painted surface, and No loss of adhesion of the film to the metal. No blistering
any residue shall be removable with a damp cloth. Any and no significant visual change in appearance when
lime residue should be easily removed with the 10% examined by the unaided eye.
muriatic acid solution described in Section 7.7.1.1. There
shall be no loss of film adhesion or visual change in 7.7.5 Window Cleaner Resistance
appearance when examined by the unaided eye.
7.7.5.1 Procedure
NOTE: A slight staining or discoloration may be apparent Prepare a solution of glass cleaner. Apply 10 drops of the
on orange, yellow or metallic coatings. This should be window cleaner to the painted surface and immediately
discussed with the specifying source prior to selection of cover it with a watch glass, convex side up. Let the test sit
color. for 24 hours, then rinse the specimen with running tap
water. Record visual appearance. Let the specimen sit for
7.7.3 Nitric Acid Resistance four hours before conducting the dry adhesion test outlined
in Section 7.4.1.1
7.7.3.1 Procedure
Fill an eight-ounce wide-mouth bottle one-half full of nitric All purpose glass cleaner composition is as follows:
acid, 70% ACS reagent grade(1). Place the test panel
completely over the mouth of the bottle painted side down, Raw Materials % By Weight
for 30 minutes. Rinse the sample with tap water, wipe it Dowanol PM* 5
dry, and measure any color change after a one-hour Propylene glycol 5
recovery period. Isopropanol 35
(1)
Water 55
The assay of the nitric acid (HNO3) should be Fisher A- *Dow Chemical, propylene glycol methyl ether
200 or equivalent; minimum 69.0%, maximum 71.0%.
The solution and test should be conducted at 18C to 27C
7.7.3.2 Performance
(65F to 80F).
Not more than 5E Units (Hunter) of color change,
calculated in accordance with ASTM D 2244, when
7.7.5.2 Performance
comparing measurements on the acid-exposed painted
There shall be no blistering or noticeable change in
surface and the unexposed surface.
appearance when examined by the unaided eye and no
removal of film under the tape within or outside of the
7.7.4 Detergent Resistance cross-hatched area.
7.7.4.1 Procedure
7.8 CORROSION RESISTANCE
Prepare a 3% (by weight) solution of detergent as
prescribed in ASTM D 2248, and distilled water. Immerse
7.8.1 Humidity Resistance
at least two test specimens in the detergent solution at 38C
(100F) for 72 hours. Remove and wipe the samples dry.
7.8.1.1 Procedure
Immediately apply tape (Permacel 99 or equivalent) 20 mm
Expose the sample in a controlled heat-and-humidity
(3/4 in) wide by pressing down firmly against the coating to
cabinet for 4,000 hours at 38C (100F) and 100% RH
eliminate voids and air pockets. Place the tape
with the cabinet operated in accordance with ASTM D
longitudinally along the entire length of the test specimens.
2247 or ASTM D 4585.
If blisters are visible, then the blistered area must be taped
and rated. Sharply pull off at a right angle to the plane of
the surface being tested, per ASTM D 3359. A typical
solid detergent composition is as follows:

AAMA 2605-05 Page 4

7.8.1.2 Performance specimen to get a percentage figure as used in the
No formation of blisters to extent greater than "Few" tabulation. In some instances, the rating numbers may be
blisters Size No. 8, as shown in Figure No. 4, ASTM D used as factors with exposure time intervals related thereto,
714. to produce a performance index number which very
accurately indicates relative quality.
7.8.2 Salt Spray Resistance
7.9 WEATHERING
7.8.2.1 Procedure
Score the film sufficiently deep to expose the base metal 7.9.1 South Florida Exposure
using a sharp knife or blade instrument. Expose the The coating shall maintain its film integrity and at a
sample for 4,000 hours according to ASTM B 117 using a minimum meet the following color retention, chalk
5% salt solution. Remove and wipe sample dry. resistance, gloss retention and erosion resistance
Immediately apply tape (Permacel 99 or equivalent) 20 properties. The architect, owner or contractor should
mm (3/4 in) wide over scored area by pressing down request data relative to the long-term durability of the
firmly against the coating to eliminate voids and air color(s) selected. Access to exposure panels must be
pockets. Sharply pull the tape off at a right angle to the made available to the architect and/or owner upon
plane of the surface being tested. request.

7.8.2.2 Performance 7.9.1.1 Test Site and Duration

Minimum rating of 7 on scribe or cut edges, and a Test sites for on-fence testing are acceptable as follows:
minimum blister rating of 8 within the test specimen field, Florida exposure South of latitude 27 degrees North at a 45
in accordance with the following Table 1 and Table 2 degree angle facing South for a minimum of ten (10) years.
(Reference ASTM D 1654). Time elapsed when the coating is off the test fence for
evaluation, or other purposes, shall not be counted as part
TABLE 1 Rating of Failure at Scribe (Procedure A) of the 10-year exposure minimum.
Representative Mean Creepage From Scribe
Millimeters Inches (Approx.) Rating Number 7.9.1.2 Color Retention
Zero 0 10
Over 0 to 0.5 0 to 1/64 9 7.9.1.2.1 Performance
Over 0.5 to 1.0 1/64 to 1/32 8 Maximum of 5E Units (Hunter) of color change as
Over 1.0 to 2.0 1/32 to 1/16 7 calculated in accordance with ASTM D 2244, Section 6.3
Over 2.0 to 3.0 1/16 to 1/8 6 after the minimum 10-year exposure test per Section
Over 3.0 to 5.0 1/8 to 3/16 5 7.9.1.1. Color change shall be measured on the exposed
Over 5.0 to 7.0 3/16 to 1/4 4 painted surface which has been cleaned of external deposits
Over 7.0 to 10.0 1/4 to 3/8 3 with clear water and a soft cloth and corresponding values
Over 10.0 to 13.0 3/8 to 1/2 2 shall be measured on the original retained panel or the
Over 13.0 to 16.0 1/2 to 5/8 1 unexposed flap area of the panel. A portion of the exposed
Over 16.0 Over 5/8 0 panel may be washed lightly to remove surface dirt only.
Heavy scrubbing or any polishing to remove chalk
TABLE 2 Rating of Unscribed Areas (Procedure B) formation or restore the surface is not permitted where
Area Failed, % Rating Number color measurements are made. New colors, whether
No Failure 10 formulated by a paint manufacturer or blended by an
0 to 1 9 applicator according to a paint manufacturer's
2 to 3 8 specifications, may be qualified without the exposure test
4 to 6 7 per Section 7.9.1.1, provided that they are produced with
7 to 10 6 the same pigments in the same coating resin system as a
11 to 20 5 color on which acceptable ten (10) year test data is
21 to 30 4 available and which is within the 10 Hunter Units in
31 to 40 3 lightness (L).
41 to 55 2
56 to 75 1 7.9.1.3 Chalk Resistance
Over 75 0
7.9.1.3.1 Performance
NOTE: The use of a ruled plastic grid is recommended as Chalking shall be no more than that represented by a No. 8
an aid in evaluating this type of failure. A 6 mm (1/4 in) rating for colors, No. 6 for whites, based on ASTM D 4214,
grid is suggested as most practical for the usual specimen. Test Method A (Method D 659) after test site (weathering)
In using the grid, the number of squares in which one or exposure (per Section 7.9.1.1) for ten (10) years. Chalking
more points of failure are found is related to the total shall be measured on an exposed, unwashed painted
number of squares covering the significant area of the surface.

AAMA 2605-05 Page 5

7.9.1.4 Gloss Retention 8.0 TEST REPORTS
7.9.1.4.1 Procedure
8.1 Test reports on file with the applicator shall include the
After weathering exposure (per Section 7.9.1.1), measure
following information:
60 degree gloss of exposed and unexposed areas of a test
site exposure panel following ASTM D 523. The
8.1.1 Date when tests were performed and date of issue of
exposure panel may be washed lightly with clear water
report.
and a soft cloth to remove loose surface dirt. Heavy
scrubbing or any polishing to restore the surface is not
8.1.2 Identification of organic coating and/or coating
permitted where gloss measurements are made.
system tested, including production date, batch or lot
number, cure conditions, pre-treatment data, manufacturer's
7.9.1.4.2 Performance
name and name of company submitting coated samples
Gloss retention shall be a minimum of 50% after the 10 year
used in test.
exposure test per Section 7.9.1.1 expressed as:
8.1.3 Copy of drawings submitted showing exposed
60 gloss exposed surfaces.
% Retention = X 100%
60 gloss unexposed
8.1.4 Test results.
7.9.1.5 Resistance to Erosion
8.1.5 A statement indicating that the organic coating and/or
coating system tested passed all tests or failed one or more.
7.9.1.5.1 Procedure
After weathering exposure (per Section 7.9.1.1), measure
8.1.6 In the case of a failure, which test(s) and a description
dry film thickness of exposed and adjacent unexposed areas
of the failure(s).
of exposure panels using an Eddy Current Meter as defined
in ASTM B 244 or other instrumental methods of equal
8.1.7 Statement that all tests were conducted in accordance
precision.
with this standard.
7.9.1.5.2 Performance
8.1.8 Name and address of the laboratory which
conducted tests and issued the report.
Less than 10 percent film loss after the exposure test per
Section 7.9.1.1 expressed as a percent loss of total film:

Loss = 100% Dry film thickness exposed X 100%

Dry film thickness unexposed

AAMA 2605-05 Page 6

9.0 REFERENCED STANDARDS AMERICAN SOCIETY FOR TESTING AND
MATERIALS (ASTM)
References to the standards listed below shall be to the ASTM B 117-03, Standard Practice for Operating Salt
edition indicated. Any undated reference to a code or Spray (Fog) Apparatus
standard appearing in the requirements of this standard
shall be interpreted as to referring to the latest edition of ASTM B 244-97(2002), Standard Test Method for
that code or standard. Measurement of Thickness of Anodic Coatings on
Aluminum and of Other Nonconductive Coatings on
AMERICAN ARCHITECTURAL Nonmagnetic Basis Metals with Eddy-Current Instruments
MANUFACTURERS ASSOCIATION (AAMA)
ASTM C 207-05, Standard Specification for Hydrated
AAMA 800-05, Voluntary Specifications and Test Lime for Masonry Purposes
Methods for Sealants
ASTM D 523-89(1999), Standard Test Method for
Specular Gloss

ASTM D 714-02, Standard Test Method for Evaluating

Degree of Blistering of Paints

ASTM D 968-93(2001), Standard Test Methods for

Abrasion Resistance of Organic Coatings by Falling
Abrasive

ASTM D 1400-00, Standard Test Method for

Nondestructive Measurement of Dry Film Thickness of
Nonconductive Coatings Applied to a Nonferrous Metal
Base

ASTM D 1654-05, Standard Test Method for Evaluation of

Painted or Coated Specimens Subjected to Corrosive
Environments

ASTM D 1730-03, Standard Practices for Preparation of

Aluminum and Aluminum-Alloy Surfaces for Painting

ASTM D 2244-02e1, Standard Practice for Calculation of

Color Tolerances and Color Differences from
Instrumentally Measured Color Coordinates

ASTM D 2247-02, Standard Practice for Testing Water

Resistance of Coatings in 100% Relative Humidity

ASTM D 2248-01a, Standard Practice for Detergent

Resistance of Organic Finishes

ASTM D 3359-02, Standard Test Methods for Measuring

Adhesion by Tape Test

ASTM D 3363-05, Standard Test Method for Film

Hardness by Pencil Test

ASTM D 4214-98, Standard Test Methods for Evaluating

the Degree of Chalking of Exterior Paint Films

ASTM D 4585-99, Standard Practice for Testing Water

Resistance of Coatings Using Controlled Condensation

ASTM D 5723-95(2002), Standard Practice for

Determination of Chromium Treatment Weight on Metal
Substrates by X-Ray Fluorescence

AAMA 2605-05 Page 7

American Architectural Manufacturers Association
1827 Walden Office Square, Suite 550
Schaumburg, IL 60173
PHONE (847)303-5664 FAX (847)303-5774
EMAIL webmaster@aamanet.org
WEBSITE www.aamanet.org