Steel Wire, Cold-Drawn For Mechanical Springs
Steel Wire, Cold-Drawn For Mechanical Springs
Steel Wire, Cold-Drawn For Mechanical Springs
This standard has been approved for use by agencies of the Department of Defense.
1
A 227/A 227M
TABLE 1 Tensile Requirements, SI UnitsA TABLE 2 Tensile Requirements, Inch-Pound UnitsA
Class I Class II Class I Class II
Diameter,B
Tensile Strength, MPa Tensile Strength MPa Diameter, in. Tensile Strength, ksi Tensile Strength, ksi
mm
min max min max min max min max
0.50 1960 2240 2240 2520 0.020 283 323 324 364
0.55 1940 2220 2220 2500 0.023 279 319 320 360
0.60 1920 2200 2200 2480 0.026 275 315 316 356
0.65 1900 2180 2180 2460 0.029 271 311 312 352
0.70 1870 2140 2140 2410 0.032 266 306 307 347
0.80 1830 2100 2100 2370 0.035 261 301 302 342
0.90 1800 2070 2070 2340 0.041 255 293 294 332
1.00 1770 2040 2040 2310 0.048 248 286 287 325
1.10 1740 2000 2000 2260 0.054 243 279 280 316
1.20 1720 1980 1980 2240 0.062 237 272 273 308
1.40 1670 1930 1930 2180 0.072 232 266 267 301
1.60 1640 1880 1880 2120 0.080 227 261 262 296
1.80 1600 1840 1840 2080 0.092 220 253 254 287
2.00 1580 1810 1810 2040 0.106 216 248 249 281
2.20 1550 1780 1780 2010 0.120 210 241 242 273
2.50 1510 1730 1730 1960 0.135 206 237 238 269
2.80 1480 1700 1700 1920 0.148 203 234 235 266
3.00 1460 1680 1680 1900 0.162 200 230 231 261
3.50 1420 1630 1630 1840 0.177 195 225 226 256
4.00 1380 1590 1600 1700 0.192 192 221 222 251
4.50 1350 1550 1550 1750 0.207 190 218 219 247
5.00 1320 1510 1510 1700 0.225 186 214 215 243
5.50 1300 1490 1490 1670 0.250 182 210 211 239
6.00 1280 1470 1470 1650 0.312 174 200 201 227
6.50 1250 1440 1440 1630 0.375 167 193 194 220
7.00 1220 1410 1410 1600 0.438 165 190 191 216
7.50 1200 1390 1390 1580 0.500 156 180 181 205
8.00 1190 1370 1370 1550 0.562 152 176 177 201
9.00 1160 1340 ... ... 0.625 147 170 171 294
10.00 1130 1310 ... ... A
Tensile strength values for intermediate diameters shall be interpolated.
11.00 1110 1280 ... ...
12.00 1090 1260 ... ...
14.00 1050 1210 ... ...
16.00 1010 1170 ... ...
7.1.4 Test Method—The tension test shall be made in
A
accordance with Test Methods and Definitions A 370.
Tensile strength values for intermediate diameters may be interpolated.
B
Preferred sizes. For a complete list, refer to ANSI B32.4M, Preferred Metric 7.2 Wrap Test:
Sizes for Round, Square, Rectangle, and Hexagon Metal Products. 7.2.1 Requirements—The material as represented by the
wrap test specimens shall conform to the requirements speci-
composition prescribed in Table 3.
fied in Table 4 or Table 5. Wrap test on wires over 8.5 mm or
6.2 Cast or Heat Analysis—Each cast or heat of steel shall
0.312 in. in diameter is not applicable. Since the conventional
be analyzed by the manufacturer to determine the percentage of
methods will not accommodate over 8.5 mm or 0.312 in., an
elements prescribed in Table 3. This analysis shall be made
alternative test procedure shall be agreed upon between pur-
from a test specimen preferably taken during the pouring of the
chaser and producer.
cast or heat. When requested, this shall be reported to the
7.2.2 Number of Tests—One test specimen shall be taken for
purchaser and shall conform to the requirements of Table 3.
each ten coils, or fraction thereof, in a lot. Each cast or heat in
6.3 Product Analysis—An analysis may be made by the
a given lot shall be tested.
purchaser from finished wire representing each cast or heat of
7.2.3 Location of Test—Test specimens shall be taken from
steel. The chemical composition thus determined, as to ele-
either end of the coil.
ments required or restricted, shall conform to the product
7.2.4 Test Method—The wrap test shall be made in accor-
analysis requirements specified in Table 10 of Specification
dance with Test Methods and Definitions A 370, Supplement
A 510 or A 510M.
IV.
6.4 For referee purposes, Test Methods, Practices and Ter-
minology, A 751 shall be used. 8. Metallurgical Requirements
7. Mechanical Properties 8.1 Surface Condition:
7.1 Tension Test:
7.1.1 Requirements—The material as represented by tension TABLE 3 Chemical Requirements
test specimens shall conform to the requirements prescribed in Element Composition, %
Table 1 or Table 2. Carbon 0.45–0.85A
7.1.2 Number of Tests—One test specimen shall be taken for Manganese 0.30–1.30B
Phosphorus, max 0.040
each ten coils or fraction thereof, in a lot. Each cast or heat in Sulfur, max 0.050
a given lot shall be tested. Silicon 0.15–0.35
7.1.3 Location of Tests—Test specimens shall be taken from A
Carbon in any one lot shall not vary more than 0.13 %.
either end of the coil. B
Manganese in any one lot shall not vary more than 0.30 %.
2
A 227/A 227M
TABLE 4 Wrap Test Requirements, SI Units TABLE 6 Permissible Variations in Wire Diameter, SI UnitsA
Mandrel Size Permissible
Diameter, mm
Class I Class II Variations,
Diameter, mm
0.50 to 4.0, incl 1XA 2X plus and minus, Permissible Out-of
Over 4.0 to 8.0, incl 2X 4X mm Round, mm
A
For 1X mandrel, wire shall be wrapped on itself. To 0.70, incl 0.02 0.02
Over 0.70 to 2.00, incl 0.03 0.03
Over 2.00 to 9.00, incl 0.05 0.05
8.1.1 The surface of the wire as-received shall be free of Over 9.00 0.08 0.08
A
rust, excessive scale, die marks, pits and scratches detrimental For purposes of determining conformance with this specification, all specified
limits are absolute as defined in Practice E 29.
to the end application. Seams shall not exceed 3.5 % of the
wire diameter or 0.25 mm [0.010 in.], whichever is less.
8.1.2 Location of Test—Test specimens shall be taken from 13.2 The material shall be adequately protected and cor-
either or both ends of the coil. rectly identified in order that the manufacturer may make a
proper investigation.
9. Dimensions and Permissible Variations
14. Certification
9.1 The permissible variations in the diameter of the wire
14.1 When specified in the purchase order or contract, a
shall be as specified in Table 6 or Table 7.
manufacturer’s or supplier’s certification shall be furnished to
10. Workmanship and Appearance the purchaser that the material was manufactured, sampled,
tested, and inspected in accordance with this specification and
10.1 Workmanship—The wire shall not be kinked or im-
has been found to meet the requirements. When specified in the
properly cast. To test for cast, a few convolutions of wire shall
purchase order or contract, a report of the test results shall be
be cut from the coil and placed on a flat surface. The wire shall
furnished.
lie flat on itself and not spring up excessively nor show a wavy
14.2 The certification shall include the specification num-
condition.
ber, year date of issue, and revision letter, if any.
10.1.1 Each coil shall be one continuous length of wire,
properly coiled and firmly tied. Welds made prior to cold 15. Packaging, Marking, and Loading for Shipment
drawing are permitted. 15.1 The coil mass, dimensions, and the method of packag-
11. Retests ing shall be agreed upon between the manufacturer and
purchaser.
11.1 If any test specimen exhibits obvious defects or shows 15.2 A tag shall be securely attached to each coil of wire
the presence of a weld, it shall be discarded and another with identifying information as agreed upon by the purchaser
specimen substituted. and manufacturer.
15.3 Unless otherwise specified in the purchaser’s order,
12. Inspection
packaging, marking, and loading for shipments shall be in
12.1 Unless otherwise specified in the contract or purchase accordance with those procedures recommended by Practices
order, the manufacturer is responsible for the performance of A 700.
all inspection and test requirements specified in this specifica- 15.4 For Government Procurement—Packaging, packing,
tion. Except as otherwise specified in the contract or purchase and marking of material for military procurement shall be in
order, the manufacturer may use his own or any other suitable accordance with the requirements of MIL-STD-163, Level A,
facilities for the performance of the inspection and test Level C, or commercial as specified in the contract or purchase
requirements unless disapproved by the purchaser at the time order. Marking for shipment of material for civil agencies shall
the order is placed. The purchaser shall have the right to be in accordance with Fed. Std. No. 123.
perform any of the inspections and tests set forth in this 15.5 Bar Coding—In addition to the previously stated
specification when such inspections and tests are deemed identification requirements, bar coding is acceptable as a
necessary to assure that the material conforms to prescribed supplementary identification method. Bar coding should be
requirements. consistent with AIAG Standard 02.00, Primary Metals Identi-
fication Tag Application. The bar code may be applied to a
13. Rejection and Rehearing
substantially affixed tag.
13.1 Unless otherwise specified, any rejection based on tests
made in accordance with this specification shall be reported to TABLE 7 Permissible Variations in Wire Diameter, Inch-Pound
the manufacturer as soon as possible so that an investigation UnitsA
may be initiated. Permissible Permissible
Diameter, in. Variations, plus and Out-of-Round, in.
minus, in.
TABLE 5 Wrap Test Requirements, Inch-Pound Units
0.020 to 0.028, incl 0.0008 0.0008
Mandrel Size Over 0.028 to 0.075, incl 0.001 0.001
Diameter, in.
Class I Class II Over 0.075 to 0.375, incl 0.002 0.002
0.020 to 0.162, incl 1XA 2X Over 0.375 to 0.625, incl 0.003 0.003
Over 0.162 to 0.312, incl 2X 4X A
For purposes of determining conformance with this specification, all specified
A
For 1X mandrel, wire shall be wound on itself. limits are absolute as defined in Practice E 29.
3
A 227/A 227M
16. Keywords
16.1 cold-drawn; springs; wire
The American Society for Testing and Materials takes no position respecting the validity of any patent rights asserted in connection
with any item mentioned in this standard. Users of this standard are expressly advised that determination of the validity of any such
patent rights, and the risk of infringement of such rights, are entirely their own responsibility.
This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM Headquarters. Your comments will receive careful consideration at a meeting of the responsible
technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should make your
views known to the ASTM Committee on Standards, 100 Barr Harbor Drive, West Conshohocken, PA 19428.