Location via proxy:   [ UP ]  
[Report a bug]   [Manage cookies]                
Scribd Logo
Upload

Welcome to Scribd!

  • 154 views

    20160323093435-52CrMoV4 (51CrMoV4)

    Uploaded by

    Martin Hristov
    This document provides information on the material 52CrMoV4, including its chemical composition, applications, heat treatment processes, and mechanical properties. 52CrMoV4 is a hot rolled steel suitable for quenching and tempering into highly strained springs. It has a carbon content of 0.5% and contains chromium, molybdenum, and vanadium. Its applications include leaf springs, helical vehicle springs, and stabilizers. Heat treatments include normalizing, soft annealing, hardening, and tempering. After hardening and tempering, it has a minimum 0.2% proof stress of 1200 MPa, tensile strength between 1400-1700 MPa, and specified ductility and impact resistance

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    20160323093435-52CrMoV4 (51CrMoV4)

    Uploaded by

    Martin Hristov
    154 views1 page
    This document provides information on the material 52CrMoV4, including its chemical composition, applications, heat treatment processes, and mechanical properties. 52CrMoV4 is a hot rolled steel suitable for quenching and tempering into highly strained springs. It has a carbon content of 0.5% and contains chromium, molybdenum, and vanadium. Its applications include leaf springs, helical vehicle springs, and stabilizers. Heat treatments include normalizing, soft annealing, hardening, and tempering. After hardening and tempering, it has a minimum 0.2% proof stress of 1200 MPa, tensile strength between 1400-1700 MPa, and specified ductility and impact resistance

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides information on the material 52CrMoV4, including its chemical composition, applications, heat treatment processes, and mechanical properties. 52CrMoV4 is a hot rolled steel suitable for quenching and tempering into highly strained springs. It has a carbon content of 0.5% and contains chromium, molybdenum, and vanadium. Its applications include leaf springs, helical vehicle springs, and stabilizers. Heat treatments include normalizing, soft annealing, hardening, and tempering. After hardening and tempering, it has a minimum 0.2% proof stress of 1200 MPa, tensile strength between 1400-1700 MPa, and specified ductility and impact resistance

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    154 views1 page

    20160323093435-52CrMoV4 (51CrMoV4)

    Uploaded by

    Martin Hristov
    This document provides information on the material 52CrMoV4, including its chemical composition, applications, heat treatment processes, and mechanical properties. 52CrMoV4 is a hot rolled steel suitable for quenching and tempering into highly strained springs. It has a carbon content of 0.5% and contains chromium, molybdenum, and vanadium. Its applications include leaf springs, helical vehicle springs, and stabilizers. Heat treatments include normalizing, soft annealing, hardening, and tempering. After hardening and tempering, it has a minimum 0.2% proof stress of 1200 MPa, tensile strength between 1400-1700 MPa, and specified ductility and impact resistance

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    Material specification sheet

    Saarstahl - 52CrMoV4 (51CrMoV4)


    Material No.: Former brand name: International steel grades:

    1.7701 F4K BS:


    AFNOR: 51CDV4
    SAE:

    Material group: Hot rolled steel for springs suitable for quenching and tempering ac-
    cording to DIN 17221

    Chemical C Si Mn Cr Mo V
    composition:
    (Typical analysis in %) 0,50 0,25 0,90 1,10 0,25 0,10

    Application: Hot rolled steel for springs for highly strained springs suitable for
    quenching and tempering, as leaf springs and helical vehicle
    springs, stabilisers vehicle, torsion bars, cup springs.

    Hot forming and Hot forming: 1050 - 850°C


    heat treatment: Hot deformation: 920 - 830°C
    Normalising: 850 - 880°C/air
    Soft annealing: 640 - 680°C/furnace
    Hardening: 830 - 860°C/oil
    Tempering: 430 - 500°C/air

    Mechanical Treated for cold shearability +S: max. 280 HB


    Properties: Soft annealed +A: max. 248 HB
    Spheroidized annealed - GKZ (+AC) max. 225 HB
    Core hardness after quenching: min. 54 HRC

    Hardened and tempered, H+A, 16 mm flat steel bars, 25 mm bars

    0,2% proof stress


    Rp0,2 [N/mm²] min. 1200

    Tensile strength Rm [N/mm²] 1400 - 1700

    Fracture elongation A5 [%] min. 6

    Reduction of area Z [%] min. 30

    Notch impact energy ISO-V [J] min. 6