1. The bolts and screws will generally conform to
IS:1364, ISO 4014, ISO 4017 and DIN 931/933.
2. Threads will conform to calss 6g of IS:4218, Coarse Series.
3. Material: RITZ High grade carbon/alloy steel
4. Heat Treatment: Property Class 10.9 or 8.8 of IS:1367-III.
5. Thread Length LT:
LT1 for L ≤ 125
LT2 for L > 125 to 200
LT3 for L > 200
6. Screw Lengths equal to or shorter than those listed in row ‘LFT’ will be threa-
ded to head.
7. Sizes in brackets are non-preferred standards
8. All dimensions are in millimeters.
Length of Thread
B H R Q LENGTH
Thread Size Pitch W Max. C Min.
Max. Nom Min. Min. LT1 LT2 LT3 LFT RANGE L
M10 1.5 17.0 16.0 18.90 17.80 10.0 6.4 0.4 15.6 26 32 45 35 16-90
M12 1.75 19.0 18.0 21.10 20.03 12.0 7.5 0.6 17.4 30 36 49 40 20-280
(M14) 2.0 22.0 21.0 24.49 23.35 14.0 8.8 0.6 20.5 34 40 53 45 25-200
(M22) 2.5 32.0 34.0 35.72 37.72 22.0 14.0 0.8 30.0 50 56 69 65 50-280
M36 4.0 55.0 60.79 36.0 22.5 1.0 51.1 78 84 97 100 80-300
(M39) 4.0 60.0 66.44 39.0 25.0 1.0 55.9 84 90 103 110 90-300
M42 4.5 65.0 72.02 42.0 26.0 1.2 60.6 90 96 109 120 90-300
Yield Strength, 0.2% offset Min. 64 65.2 660 67.3 940 95.8
Elogation % on GL = 5.65A.
12% Min. 9% Min.
A=Cross Sectional Area
Recommended Thread
Stess Property Class 8.8 Property Class 10.9
M10 58.0 50.0 5.11 26360 2686 74.0 7.50 38700 3946
M12 84.3 87.0 8.90 38300 3905 128.0 13.08 56300 5735
(M14) 115.0 139.0 14.17 52300 5327 205.0 20.82 76800 7824
M16 157.0 214.0 21.82 72300 7375 315.0 32.06 106300 10832
(M18) 192.0 304.0 30.97 91200 9300 435.0 44.10 129900 13246
M20 245.0 431.0 43.91 116400 11868 615.0 62.54 165800 16903
(M22) 303.0 586.0 59.74 144000 14677 835.0 85.08 205100 20904
M24 353.0 745.0 75.94 167700 17100 1060.0 108.00 238700 24333
(M27) 459.0 1090.0 111.00 218100 22234 1550.0 158.00 310400 31640
M30 561.0 1480.0 150.00 266600 27175 2105.0 214.60 379400 38671
Note:
The tightening torques calculated (M33) 694.0 2013.0 205.20 329800 33618 2865.0 292.00 469300 47839
to induce approximate stresses as
under in screw threads: M36 817.0 2586.0 263.60 388200 39576 3680.0 375.00 552500 56318
448 N/mm2 for
PropertyClass 8.8 dia ≤ M16 (M39) 976.0 3346.0 341.10 463800 47278 4760.0 485.40 660000 67278
462 N/mm2 for
Property Class 8.8 dia > M16
M42 1120.0 4135.0 421.50 532200 54253 5880.0 599.80 757400 77205
658 N/mm2 for Property Class 10.9
Hexagon Head Bolts/Screws
Note:
1. The bolts and screws will generally conform to BS: 1768.
(Bolts/Screws made to BS:1768 will also generally conform to
American Standard ANSI B.18.2.1)
2. Threads will conform to Class 2A of BS:1580 for Unified
threads (Coarse/Fine).
3. Material: RITZ High grade carbon/alloy steel
4. Heat Treatment: As per Grade ‘S’ or ‘V’ (Bolts/Screws made to
Grades ‘S’ and ‘V’ as per BS:1768 will also generally conform to
requirements of SAE Grade ‘5’ and ‘8’ respectively)
5. Thread Length LT:
LT1 for L ≤ 6
LT2 for L > 6
6. Screw lengths equal to or shorter than those listed in row ‘LFT’
will be threaded to head.
7. All dimensions are in inches.
5/16” 18 24 0.500 0.577 0.313 0.206 0.015 0.473 7/8 - 1-1/8 1/2-4
7/16” 14 20 0.625 0.722 0.438 0.286 0.015 0.595 1-1/8 - 1-3/8 3/4-3-1/2
1/2” 13 20 0.750 0.866 0.500 0.318 0.015 0.720 1-1/4 1-1/2 1-1/2 3/4-3-1/2
5/8” 11 18 0.938 1.083 0.625 0.398 0.020 0.908 1-1/2 1-3/4 1-7/8 1-8
3/4” 10 16 1.125 1.300 0.750 0.473 0.020 1.090 1-3/4 2 2-1/8 1-1/2-8
7/8” 9 14 1.313 1.515 0.875 0.553 0.040 1.275 2 2-1/4 2-3/8 1-1/2-8
1” 8 12 1.500 1.732 1.000 0.617 0.060 1.463 2-1/4 2-1/2 2-5/8 1-1/2-8
Hexagon Head Bolts/Screws
Note:
1. The nuts will generally conform to IS: 1364, ISO 4032, DIN 934.
2. Threads will conform to Class 6H of IS:4218 for Coarse Series.
3. Material & Heat Treatment:
To achieve mechanical properites of Property Class 8 or 10 of IS:1367-VI.
4. Nuts of Property Class 8 are used with bolts of Property Class 8.8.
Nuts of Property Class 10 are used with bolts of Property Class 10.9
(In general, nut of a higher property class can replace nuts of a lower
property class in a joint).
5. In Bolt/Nut assembly, tightening should be done by rotation of nut.
Torque values as recommended in tables for bolts (p:5).
6. Sizes in brackets are non-preferred standards.
7. All dimensions are in millimeters.
Dimensions: Thread
Pitch W Max. C Min. H Max.
size
M4 0.7 7.0 7.66 3.20
M5 0.8 8.0 8.79 4.00 4.70
M6 1.0 10.0 11.05 5.00 5.20
Note:
1. The nuts will generally conform to BS:1768. (Nuts made as per
BS:1768 will also generally conform to American Standard ANSI
B:18.2.2)
2. Threads will conform to Class 2B of BS:1580 for Unifined threads,
(Coarse/Fine).
3. Material and Heat Treatment:
To achieve mechanical properties of Grade ‘1’ or ‘5’ of BS:1768. (Nuts
made to Grade ‘1’ and ‘5’ as per BS:1768 will also generally conform
to requirements of SAE Grade ‘5’ and ‘8; respectively).
4. In Bolt/Nut assembly, tightening should be done by rotation of nut.
Torque values as recommended in tables for bolts (p.7)
5. All dimensions are in inches.
7/16”
16
14
24
20
0.563
0.625
0.650
0.722
0.328
0.375
Physical Properties:
For use with Proof Load Brinell Hard- Rockwell Hard-
Grade
Bolts of Grade Stress ness HB ness
50 tonf/in2
1 5 180-240 RB 89 - RC 23
78.9 kgf/mm2
65 tonf/in2
5 8 270-335 RC 28 - 36
102.6 kgf/mm2
Socket Head Cap Screws
M1.6 0.35 3.0 1.6 1.6 1.5 0.8 15 0.2 2.01 1.27
M10 1.50 16.0 10.0 10.0 8.0 5.0 32 0.6 78.5 58.0
M12 1.75 18.0 12.0 12.0 10.0 6.0 36 1.0 113.0 84.3
M14 2.00 21.0 14.0 14.0 12.0 7.0 40 1.0 154.0 115.0
M16 2.00 24.0 16.0 16.0 14.0 8.0 44 1.0 201.0 157.0
M20 2.50 30.0 20.0 20.0 17.0 10.0 52 1.2 314.0 245.0
M24 3.00 36.0 24.0 24.0 19.0 12.0 60 1.2 452.0 353.0
M30 3.50 45.0 30.0 30.0 22.0 15.0 72 1.5 707.0 561.0
M36 4.00 54.0 36.0 36.0 27.0 18.0 84 1.5 1018.0 817.0
M42 4.50 63.0 42.0 42.0 32.0 21.0 96 1.6 1385.0 1120.0
Note:
1. Material - Hegh Grade Alloy Steel
2. Hardness - Rc 38-45 (alloy steel)
3. Tensile Stress - (alloy steel)
1300 MPa up to M10 1250 MPa over M10
4. Shear Stress - (alloy steel)
780 MPa up to M10 750 MPa over M10
5. 0.2% Yield Stress - (alloy steel)
1170 MPa up to M10 1125 MPa over M10
APPLICATION DATA
Body
Tensile Strength Double Recommended
Yield Strength min. Hole Dimensions (mm)
Thread min. Shear Seating Torque
Strength
Size
body c/bore
MPa KN Mpa KN KN N-m Inch-lbf Tap drill
drill drill
*M1.6 1300 1.65 1170 1.49 3.14 0.29 2.5 1.25 1.9 3.3
*M2.5 1300 4.41 1170 3.97 7.66 1.21 11 2.05 2.9 5.4
M6 1300 26.10 1170 23.5 44.10 16.00 140 5.0 6.8 11.25
M8 1300 47.60 1170 42.8 78.40 39.00 350 6.75 8.8 14.25
M10 1300 75.40 1170 67.9 122.00 77.00 680 8.5 10.8 17.25
M12 1250 105.00 1125 95 170.00 135.00 1200 10.25 12.8 19.25
M14 1250 144.00 1125 129 231.00 215.00 1900 12.0 15 22.25
M16 1250 196.00 1125 177 300.00 330.00 2900 14.0 17 25.5
M20 1250 306.00 1125 276 470.00 650.00 5750 17.5 21 31.5
M24 1250 441.00 1125 397 680.00 1109.00 9700 21.0 25 37.5
M30 1250 701.00 1125 631 1060.00 2250.00 19900 28.5 31.5 47.5
M36 1250 1021.00 1125 919 1530.00 3850.00 34100 32.0 37.5 56.5
M42 1250 1400.00 1125 1260 2080.00 6270.00 55580 37.5 44 66.0
*Micro-Sizes
Note:
1KN = approx. 102 kgf (or 225 lbf) 1MPa = 1 N/mm2 or approx. 145 psi
Tap drill sizes based on approx. 70% thread height.
Seating torques based on 800 Mpa induced stress in screw threads.
Comparison of Different Strength Grades
UNIFIED INCH
METRIC PRODUCTS B.S. INCH PRODUCTS
PRODUCTS
THREAD PITCH & T.P.I.
Major Major Major
Major Dia. T.P.I. T.P.I. T.P.I.
Dia. Dia. Dia.
SIZE COARSE FINE SIZE SIZE
PTICH PTICH
T.P.I. T.P.I. mm inch UNC UNF inch BSW BSF inch BA inch
mm mm
M10
1.25
1.5
20.0
17.0
1.00
1.25
25
20
8.00
10.00
0.315
0.394
5/16
3/8
18
16
24
24
0.313
0.375
0BA
5/16
3/8
18
16
22
20
0.313
0.375
25.4 0.236
7/16 14 18 0.438
M12 1.75 14.5 1.25 20 12.00 0.472 1/2 13 20 0.500 1/2 12 16 0.500
M16 2.0 12.5 1.50 17 16.00 0.630 5/8 11 18 0.625 5/8 11 14 0.625
M20 2.5 10.0 1.50 17 20.00 0.787 3/4 10 16 0.750 3/4 10 12 0.750
(M22) 2.5 10.0 1.50 17 22.00 0.866 7/8 9 14 0.875 7/8 9 11 0.875
M30 3.5 7.25 2.00 13 30.00 1.181 1-1/4 7 12 1.250 1-1/4 7 9 1.250
M36 4.0 6.4 3.00 8.5 36.00 1.417 1-1/2 6 12 1.500 1-1/2 6 8 1.500