Article
Walnut and Hazelnut Shells: Untapped Industrial
Resources and Their Suitability in
Lignocellulosic Composites
Marius Cătălin Barbu 1,2 , Thomas Sepperer 1 , Eugenia Mariana Tudor 1,2, * and
Alexander Petutschnigg 1
1 Forest Products Technology and Timber Construction Department, Salzburg University of Applied Sciences,
Markt 136a, 5431 Kuchl, Austria; cmbarbu@unitbv.ro (M.C.B.); thomas.sepperer@fh-salzburg.ac.at (T.S);
alexander.petutschnigg@fh-salzburg.ac.at (A.P.)
2 Faculty of Wood Engineering, University of Transilvania in Brasov, Romania, Bld. Eroilor nr.29,
500036 Brasov, Romania
* Correspondence: eugenia.tudor@fh-salzburg.ac.at

Received: 24 August 2020; Accepted: 10 September 2020; Published: 11 September 2020 

Abstract: Walnut and hazelnut shells are agricultural by-products, available in high quantities
during the harvest season. The potential of using these two agricultural residues as raw materials in
particleboard production has been evaluated in this study. Different panels with either walnut or
hazelnut shells in combination with melamine-urea formaldehyde or polyurethane at the same level
of 1000 kg/m3 density were produced in a laboratory hot press and mechanical properties (modulus
of elasticity, bending strength, and Brinell hardness) and physical properties (thickness swelling and
water absorption) were determined, together with formaldehyde content. Although Brinell hardness
was 35% to 65% higher for the nutshell-based panels, bending strength and modulus of elasticity
were 40% to 50% lower for the melamine-urea formaldehyde bonded nutshells compared to spruce
particleboards, but was 65% higher in the case of using polyurethane. Water absorption and thickness
swelling could be reduced significantly for the nutshell-based boards compared to the spruce boards
(the values recorded ranged between 58% to 87% lower as for the particleboards). Using polyurethane
as an adhesive has benefits for water uptake and thickness swelling and also for bending strength
and modulus of elasticity. The free formaldehyde content of the lignocellulosic-based panels was
included in the E0 category (≤2.5 mg/100 g) for both walnut and hazelnut shell raw materials and the
use of polyurethane improved these values to super E0 category (≤1.5 mg/100 g).

Keywords: hazelnut; walnut; shells; lignocellulosic composites; UF; PUR; formaldehyde content

1. Introduction
The continuous interest in the efficient use and reuse of resources in the wood and agricultural
sector for upcycled applications [1] is of great interest nowadays [2,3] in the context of the circular
economy [4].
Steered by the paucity of non-renewable resources, the interest for wood could exceed its
sustainable supply within the next few decades [5]. The wood demand has increased steadily, not
only in the industry or for energy production (more than 50%), while the supply of wood is limited in
specific regions of the world [6]. This leads to the need for substitutes for wood in engineered wood
products (e.g., particleboards, PB). A promising alternative for wood in composites is provided by
agricultural residues. A lot of research on agricultural waste has been carried out for PB based on
wheat straw [7,8], rice straw [9,10], rapeseed [11], hemp shives [12,13], cotton dust [14], or sunflower
stalks [15] and topinambour [16]. Brewer’s spent grain is also a raw material for PB [17] together

Appl. Sci. 2020, 10, 6340; doi:10.3390/app10186340 www.mdpi.com/journal/applsci


Appl. Sci. 2020, 10, 6340 2 of 11

with tree bark [18–20]. The advantages of these agricultural and forestry by-products include reduced
costs, ample availability, biodegradability, and renewability, followed by an enlarged flexibility and
sound insulation [21,22]. Some drawbacks in using agricultural residues in lignocellulosic composites
include unequal availability over the year, the manufacture of products with these raw materials
cannot run year-round, no industrialized processing yet, big storage facilities, and different necessary
pre-treatments [23–25]. Walnut and hazelnut shells are agricultural residues available in high quantities,
but despite their thermal utilization [26], with no industrial use yet. Nut shells can exhibit high
hardness and toughness [27]. Worldwide walnut production in 2019/2020 was roughly 965,400 tons
and 528,070 tons for hazelnut [28]. Taking in account that roughly 67 % of the total fruit weight is
comprised of the shell leads to 646,818 tons of walnut shells and roughly 353,807 tons of hazelnut shells
each year [29]. Especially in Iran and Turkey research on the solely use of nutshells and nutshells in
combination with wood has been done. The authors in [30] studied the properties of particleboard
from hazelnut husks and combined with European black pine (Pinus nigra Arnold) [31,32]. Walnut
shells were studied by [33,34]. Other research refers to particleboards manufactured with peanut hulls
mixed with European black pine [35], peanut shell flour [36], and almond shells [37–39].
The aim of this study was to compare and evaluate the influence of the nutshell type (hazelnut
and walnut) and resin (bonded with melamine urea formaldehyde (MUF) and polyurethane (PUR) 10%
each) on the mechanical and physical properties and on the free formaldehyde content of particleboards
produced solely from the above-mentioned nutshells. Other studies have dealt with PB bonded only
with UF, so this study brings a novel process of gluing the nut shell panels with MUF and PUR as the
properties of these boards including the Brinell hardness and formaldehyde content have not been
reported yet.

2. Materials and Methods


The raw materials used for the particleboard production consisted of walnut and hazelnut shells.
The hazelnut (Corylus avellana L.) shells were provided by the Faculty of Forestry at the University
of Zagreb (Croatia). The walnut (Juglans regia L.) shells were provided by a family-owned walnut
cracking company in Carinthia (Maria Rojach, Austria). Melamine urea formaldehyde (MUF) resin
(Prefere 10G268) was provided by metaDynea (Krems, Austria) and polyurethane (PUR 501.0) was
provided by Kleiberit Klebchemie (Kleiberit Klebchemie M. G. Becker GmbH & Co. KG, Weingarten,
Germany).
A total of 40 kg walnut shells and 30 kg hazelnut shells were available for the project. The shells
were at first manually cleaned from impurities and afterward shredded in an R40 industrial four shaft
shredder at Untha Company (Kuchl, Austria) using an 8-mm screen. The shredded nutshells were
dried in a Brunner-Hildebrand High VAC-S, HV-S1 (Hannover, Germany) kiln dryer for three days
to reach a moisture content of about 5%. After drying, the particles were sorted into three main size
classes (fine-grained, middle-grained and coarse-grained) using a sieve shaker Retsch AS 200 (Haan,
Deutschland). Particles in the middle-sized (3–6 mm) and fine (<3 mm) fraction were used for the
board production. The percentage of particles in each group and nutshell type is listed in Table 1.

Table 1. Weight distribution according to the fraction size of the raw material.

Raw Material % Fine-Grained % Middle-Sized Grained % Coarse-Grained


Hazelnut 13.4 67.1 19.5
Walnut 12.4 73.4 14.2

A total of twelve boards (two for each group) was produced, of which the compositions are listed
in Table 2.
Appl. Sci. 2020, 10, x FOR PEER REVIEW 3 of 11

The
Appl. Sci. 320
2020, 10,mm
6340 ×
320 mm boards were produced with a thickness of 10 mm and a density of 1000
3 of 11
kg/m3 for nutshells and 700 kg/m3 for the spruce control boards. The density of 1000 kg/m3 could not
be reached with wood particles due to the technical limitations of the hydraulic press Höfer HLOP
Table
280. The 2. Manufacturing
walnut and hazelnutparameters of particleboards
boards were composed made from
of 70% hazelnut, walnut,
middle-sized and spruce.
and 30% coarse-grained
particles.
Board Adhesive Raw Material Density (kg/m )3 Press Time (min) Press Temp. (◦ C)
A MUF Hazelnut 1000 6 160
Table 2. Manufacturing parameters of particleboards made from hazelnut, walnut, and spruce.
B MUF Walnut 1000 6 160
C MUF Spruce 1000
Density Press Time 6 Press Temp.160
D Board
PUR Adhesive Raw Material 1000 3
Hazelnut 20 60
(kg/m ) (min) (°C)
E PUR Walnut 1000 20 60
F A UF MUF SpruceHazelnut 7001000 6 6 160 180
B MUF Walnut 1000 6 160
C MUF Spruce 1000 6 160
The 320 mm × 320 mm boards were produced with a thickness of 10 mm and a density of
D PUR Hazelnut 1000 20 60
1000 kg/m3 for nutshells and 700 kg/m3 for the spruce control boards. The density of 1000 kg/m3
E PUR Walnut 1000 20 60
could not be reached with wood particles due to the technical limitations of the hydraulic press
F UF Spruce 700 6 180
Höfer HLOP 280. The walnut and hazelnut boards were composed of 70% middle-sized and 30%
coarse-grained particles.
For all panels, the particles were mixed with resin manually and then formed into a mat and
For all panels, the particles were mixed with resin manually and then formed into a mat and
pre-compressed. This mat was pressed afterward in a hydraulic laboratory press (Höfer HLOP 280,
pre-compressed. This mat was pressed afterward in a hydraulic laboratory press (Höfer HLOP 280,
Taiskirchen, Austria) with a pressure of 3 N/mm 2
2. For the UF and MUF bonded boards, 10% resin
Taiskirchen, Austria) with a pressure of 3 N/mm . For the UF and MUF bonded boards, 10% resin
based on weight was used including 1% ammonium sulfate as a hardener. These boards (Figure 1)
based on weight was used including 1% ammonium sulfate as a hardener. These boards (Figure 1)
were pressed at 160 °C for 6 min. The PUR bonded boards were also produced with 10% adhesive,
were pressed at 160 ◦ C for 6 min. The PUR bonded boards were also produced with 10% adhesive, but
but these were pressed at 60 °C for 20 min. After pressing, the panels were conditioned at 20 °C and
these were pressed at 60 ◦ C for 20 min. After pressing, the panels were conditioned at 20 ◦ C and 65%
65% relative air humidity for one week before cut to test specimen size, which was done according
relative air humidity for one week before cut to test specimen size, which was done according to [40].
to [40].

Figure1. 1.
Figure Hazelnut
Hazelnut andand walnut
walnut 10 mm10thick
mmsamples
thick samples bonded
bonded with PUR; with PUR;
1000 kg/m 1000 kg/m
3 density; 3 density;
composition:
composition: 70% fine-grained particles (<3 mm) and 30% coarse-grained particles
70% fine-grained particles (<3 mm) and 30% coarse-grained particles (3–6 mm). (3–6 mm).

InInterms
termsofofmechanical
mechanicalproperties,
properties,bending
bendingstrength
strength(MOR)
(MOR)and andmodulus
modulusofofelasticity
elasticity(MOE)
(MOE)
accordingtoto[41]
according [41]and
andBrinell
BrinellHardness
Hardness[42] [42]were
weretested.
tested.
Forthe
For thebending
bendingproperties
properties[41],
[41],the
thethree-point
three-pointbending
bendingtest
testwas
wasemployed.
employed.
Thephysical
The physicalproperties
propertiessuch
suchasasthickness
thicknessswelling
swellingand
andwater
waterabsorption
absorption after
after 24
24hhwater
water
immersion[43]
immersion [43]and
anddensity
density[44]
[44]were
werealso
alsomeasured.
measured.
Appl. Sci. 2020, 10, 6340 4 of 11

To determine the formaldehyde content of the panels, 250 mm × 250 mm boards with fine-grained
particles (<3 mm) and 10 mm thickness and a density of 1000 kg/m3 were manufactured with walnut
and hazelnut shells. Moisture content (m.c.) was measured for each type of board (Table 3).

Table 3. Moisture content of the nutshell boards prior to determining the formaldehyde content with
the perforator method.

Board Glue m.c. (%) Particle Size (mm)


Walnut UF 1.79 <3 mm
Walnut PUR 5.25 <3 mm
Hazelnut UF 2.28 <3 mm
Hazelnut PUR 6.28 <3 mm

Each board was cut into 2.5 × 2.5 mm samples after cooling. The test specimens were placed in
airtight bags and delivered to the Kaindl Company, Wals, Salzburg, Austria, where formaldehyde
content was measured according to [45]. This method is recommended for nonlaminated and uncoated
wood-based panels.

3. Results
For all boards described earlier, the mechanical and physical properties were evaluated according
to the corresponding standard and statistically analyzed using mean separation tests and ANOVA.

3.1. Mechanical Properties


In terms of mechanical properties, MOE, MOR and Brinell hardness have been evaluated. The mean
value, standard deviation, and minimal and maximal values are listed in Table 4. Results of ANOVA
are indicated by letters a–e and u–z. The first letter refers to the different raw material (for values
with the same letter, the raw material has no significant influence), the second letter refers to the used
adhesive (again, and for values with the same letter, the adhesive has no influence).

Table 4. Mechanical properties of the hazelnut, walnut, and spruce particle boards.

Properties Board Mean Std. Dev. Min Max


MOE [GPa] A 1.13 a,u 0.42 0.73 1.79
B 1.15 b,v 0.29 1.20 1.96
C 2.57 c,w 0.36 2.12 3.00
D 1.32 d,u 0.30 0.92 1.60
E 1.30 d,x 0.44 0.68 1.70
F 0.86 e,y 0.13 0.65 1.00
MOR [N/mm2 ] A 4.25 a,u 1.21 2.55 5.47
B 5.20 a,w 1.02 3.79 6.53
C 13.26 b,y 2.04 11.09 16.26
D 7.43 c,v 1.34 5.36 8.65
E 8.86 c,x 2.75 5.35 12.18
F 5.47 d,z 0.75 4.33 6.32
Brinell hardness [N/mm2 ] A 62.50 a,u 12.55 39.95 82.65
B 43.70 b,v 7.07 36.57 57.72
C 28.00 c,x 5.48 22.26 35.39
D 53.90 d,u 12.70 27.82 70.59
E 55.50 d,w 8.51 37.30 63.89
F 18.00 e,y 3.08 15.26 22.82
a,b,c,d,e values with the same letter were not significantly different (raw material),u,v,w,x,y,z values with the same letter

were not significantly different (adhesive).


Appl. Sci. 2020, 10, 6340 5 of 11

3.1.1. MOE and MOR


For the MUF bonded boards, the walnut shell ones (B) performed better in terms of MOE (1.51 GPa)
and a MOR of 5.20 N/mm2 compared to boards made from hazelnut shells (A) with an MOE of 1.30 GPa
and a MOR of 4.25 N/mm2 (Table 4). Although ANOVA showed that the material had a statistically
significant influence in terms of MOE, it did not have an influence on the MOR. When PUR was used
as an adhesive, it did not make a difference whether the boards were made of hazelnut (D) or walnut
(E) shells. MOE was roughly 1.3 GPa for both, MOR 7.43 and 8.86 N/mm2 for hazelnut and walnut
shell boards, respectively. Furthermore, ANOVA showed that for walnut shell boards, it did not make
a difference if MUF or PUR (both at a concentration of 10 w.t. %) was used as an adhesive when it
came to MOE, while it did influence the MOR. When hazelnut shells were used as a raw material, the
adhesive had a statistically significant influence on both MOE and MOR. The reference boards made
from spruce and MUF (C) achieved the highest values for MOE and MOR (2.57 GPa and 13.26 N/mm2 ,
respectively). Surprisingly, the PUR bonded spruce boards (F) performed weaker than the nutshell
panels (0.87 GPa for MOE and 5.47 N/mm2 for MOR). The results for both hazelnut and walnut panels
bonded with PUR were similar to the values obtained by [34], namely a MOR between 6 and 9 N/mm2
and an MOE between 0.8 and 1.3 GPa. When the same amount of hazelnut shells was mixed with
wood particles (50% + 50%), the values of the MOE and MOR increased significantly [32].
In terms of MOE (Table 4), the walnut shell boards showed higher values than the ones produced
by [46], which reached 1.15 GPa on average compared to 1.51 GPa and might have been caused by
the adhesive used. The study by [46] applied UF, while for these boards was utilized a less brittle
MUF [47]. Another reason might be that [46] produced boards with a density of 700 kg/m3 while those
boards had a target density of 1000 kg/m3 [48].
The results for MOE and MOR of the nutshell boards were expected to range below the results of
spruce particleboards. This can be traced back to the fact that the mechanical properties are strongly
influenced by different properties of the raw material like density, chemical composition, and particle
size. A low-density raw material allows a higher compression in the panel, leading to improved
performance in bending tests [49]. Given that the density of the used nutshells was very high (between
700 and 1030 kg/m3 depending on the fraction) and spruce particles have a density of 450 kg/m3 , the
lower performance of the MUF bonded nutshell boards can be traced back to a lower compression
rate [50]. The weak behavior of the PUR bonded spruce boards can be traced back to unsatisfying
bonding, caused by an insufficient moisture content of the raw material (3%) for the adhesive to
react [51].

3.1.2. Brinell Hardness


Boards made from hazelnut shells and MUF (A) showed the highest average Brinell hardness
with 62.5 N/mm2 while the lowest hardness value was achieved by PUR bonded spruce particles with
only 18 N/mm2 (Table 4). The highest value was achieved by hazelnut with 82.6 N/mm2 while the
lowest for those panels was 39.9 N/mm2 . The big difference between the highest and lowest value
and the high standard deviation can be explained as a result of the different measuring spots and the
manual scattering of raw material in the press mold. This showed that the hardness was very high
when measured on a big piece of the nutshells, while it was much lower when determined on the
fine-grained particles that are filling the gaps between the coarse ones. This was not only valid for
MUF, but also for PUR. The highest Brinell hardness value for a hazelnut board glued with PUR (D)
was 70.59 N/mm2 while the lowest was 27.82 N/mm2 . The mean was determined at 54 N/mm2 . Walnut
panels showed similar results this time, PUR bonded boards (E) performed a little better with an
average Brinell hardness of 55.5 N/mm2 , while MUF boards (B) only reached 43.7 N/mm2 . The highest
value for the walnut boards was 63.9 N/mm2 for those produced with PUR. ANOVA showed that
when it came to PUR bonded boards, the nutshell type had no influence. There was also no statistically
significant difference for hazelnut boards concerning the adhesive. Compared to spruce particleboards
that showed an average result of 18 N/mm2 for PUR and 28 N/mm2 for MUF, the nutshells were much
Appl. Sci. 2020, 10, 6340 6 of 11

harder. However, the results for the wood-based boards were closely distributed to the mean value,
with a standard deviation of only 3 N/mm2 . This means that the spot where the force is applied is less
relevant compared to the nutshell boards.

3.2. Physical Properties


In terms of physical properties, thickness swelling (TS) and water absorption (WA) both after 24 h
water immersion were evaluated.
Thickness swelling after 24 h water immersion for MUF bonded hazelnut husk panels (A) was
determined with 17.5% while it was a little lower for walnut shells (B) with 13.2% (Table 5). Compared
to the spruce reference board (C) with an average of 52%, the increase in thickness was much lower.
The results for hazelnut (A) glued with MUF were a little better compared to those obtained by [31]
and [35] (29.3% TS with a standard deviation of 3.5%), while the results for walnut (B) were higher
compared to [34], who evaluated the thickness swelling with 10.2%.

Table 5. Physical properties of the hazelnut, walnut, and spruce particle boards.

Properties Board Mean Std. dev. Min Max


TS 24 h [%] A 17.47 a,u 2.88 13.56 21.91
B 13.23 b,w 1.35 10.98 15.21
C 52.09 c,y 7.84 42.69 64.84
D 9.66 d,v 1.48 8.33 12.66
E 8.37 d,x 1.26 6.48 10.29
F 44.48 e,z 11.01 30.92 64.39
WA 24 h [%] A 26.96 a,u 2.96 23.32 32.54
B 24.54 a,w 3.55 19.29 28.78
C 64.00 b,y 9.64 45.24 75.02
D 12.44 c,v 2.05 9.60 15.28
E 11.49 c,x 2.56 7.40 14.40
F 89.99 d,z 7.04 81.49 104.09
a,b,c,d,e values with the same letter were not significantly different (raw material), u,v,w,x,y,z values with the same letter

were not significantly different (adhesive).

Thickness swelling after 24 h was significantly reduced when PUR was used to produce the
boards. This means that it was only 9.7% for hazelnut (D) and 8.4% for walnut (E). The spruce boards
showed an increase in thickness of nearly 52% for MUF and still 44.5% for PUR. The nutshells in
combination with PUR performed better compared to the spruce particles. It was found that when
MUF was used as the adhesive, there was a significant difference between the walnut and hazelnut
shells, while the material did not have a big influence when bonded with PUR.
The results for water absorption after 24 h water submersion were similar to those for thickness
swelling after 24 h (Table 5). This means that the nutshell boards glued with MUF had a higher water
uptake, namely 27% for hazelnut (A) and 25% for walnut (B), compared to the PUR bonded ones with
12.5% (D) and 11.5% (E), respectively. The values were much lower compared to the results of spruce
particles with 64% for MUF (C) and almost 90% for PUR (F). Regarding water uptake over 24 h, there
was no influence of the used nutshell type in combination with either MUF or PUR.
The same trend of blocking and reduction of TS and WA was observed in the case of using
hazelnut shells combined with wood particles [32], with a mean of 20% for TS and 70% for WA and
from [34], in the case of walnut shells with the same value for TS as reported by [32] and lower WA
of 37%.
It was expected that thickness swelling and water absorption will be lower, compared to the
spruce particleboards. The water uptake of lingo-cellulosic materials is strongly influenced by the
number of free hydroxyl groups where water is bonded to. These hydroxyl groups are mainly present
in the natural polymer cellulose. Hemicellulose is amorphous and has a hydrophilic character that is
Appl. Sci. 2020, 10, x FOR PEER REVIEW 7 of 11

Appl. Sci. 2020, 10, 6340 7 of 11


in the natural polymer cellulose. Hemicellulose is amorphous and has a hydrophilic character that is
additionally increasing the water uptake. Lignin, however, is totally hydrophobic, which means that
water cannotincreasing
additionally be absorbed within
the water [52]. The
uptake. high
Lignin, amountisof
however, lignin
totally in the walnut
hydrophobic, shells
which (49.1%)
means that
compared
water cannottoberoughly
absorbed35% in [52].
within softwood indicated
The high amount ofa lignin
decreased
in the amount of water
walnut shells (49.1%)absorption.
compared
Furthermore,
to roughly 35%hazelnut husks
in softwood containaalmost
indicated 42%amount
decreased of ligninofand
wateronly 55% of holocellulose
absorption. Furthermore,compared
hazelnut
to 65%contain
husks in softwood.
almost 42% of lignin and only 55% of holocellulose compared to 65% in softwood.
PUR is more hydrolytically stable than MUF, which explains the big differences for thickness
swelling and water absorption when these two adhesives are compared. compared. The high value for water
absorption for
absorption forthe
thePUR
PUR glued
glued spruce
spruce particleboards
particleboards was was
againagain
caused caused
by theby the
low low
(3%) (3%) moisture
moisture content
content
of of the
the raw raw material
material and a non-complete
and a non-complete reaction reaction of the adhesive.
of the adhesive.

3.3. Formaldehyde Content


3.3. Formaldehyde Content
The
The corrected
corrected values
values of
of free
free formaldehyde
formaldehyde content
content varied
varied depending on the
depending on the type
type of
of adhesive
adhesive
formulation for the board (Figures
(Figures 22 and
and 3).
3).

Appl.Figure 2. Free
2. 10,
Sci. 2020, Free formaldehyde
formaldehyde
x FOR content for
content
PEER REVIEW for both
both the measured and corrected perforator values (EN 8 of 11
120:2011) of samples of walnut and hazelnut shell boards compared with larch bark panels from [53].

The values for walnut and hazelnut shell panels were compared with similar 10 mm boards
manufactured with the same adhesives reported by [53]. The lowest formaldehyde content of 0.07
mg/100 g oven dry was measured for the board with larch bark bonded with PUR (PUR_bark). This
is included in the super E0 classification (≤1.5 mg/100 g). In the same category were comprised the
values of the walnut (PUR_WN) and hazelnut (PUR_HN) shell boards glued with PUR and the larch
bark board bonded with UF. To the E0 class (≤2.5 mg/100 g) belonged the values for the nutshell
boards bonded with UF (UF_HN and UF_WN). These results are consistent with those obtained by
[54] regarding formaldehyde release from low-emission wood-based panels using the perforator
method, which ranged from 0.71 to 2.99 mg/100 g and was slightly lower than that of [34].
The role of bark to decrease the formaldehyde content of wood-based composites was also
studied by [55,56]. It was expected that the level of free formaldehyde content of the panels glued
with PUR would be significantly lower than that of the boards bonded with UF, but the combination
of both adhesives
Figure and raw materials
3. Free formaldehyde contentresulted
measuredin panels that
according to ENreached
120:2011at
of least
10 mm the E0 classification.
walnut and hazelnut
Figure 3. Free formaldehyde content measured according to EN 120:2011 of 10 mm walnut and
panels bonded
hazelnut with
panels UF and
bonded MUF
with UF and
and compared with the values
MUF and compared of larch
with the bark
values boards
of larch glued
bark withglued
boards the
same adhesives from [53].
with the same adhesives from [53].

4. Conclusions
This study has shown that the nutshells can be used for the manufacture of PBs with improved
performances in terms of physical properties (dimensional stability), but also with higher Brinell
hardness compared to the spruce particleboards.
MOR and MOE are lower by roughly 50% and cannot meet the requirements for P1 or P2 PBs,
Appl. Sci. 2020, 10, 6340 8 of 11

The values for walnut and hazelnut shell panels were compared with similar 10 mm boards
manufactured with the same adhesives reported by [53]. The lowest formaldehyde content of 0.07
mg/100 g oven dry was measured for the board with larch bark bonded with PUR (PUR_bark). This
is included in the super E0 classification (≤1.5 mg/100 g). In the same category were comprised the
values of the walnut (PUR_WN) and hazelnut (PUR_HN) shell boards glued with PUR and the larch
bark board bonded with UF. To the E0 class (≤2.5 mg/100 g) belonged the values for the nutshell
boards bonded with UF (UF_HN and UF_WN). These results are consistent with those obtained by [54]
regarding formaldehyde release from low-emission wood-based panels using the perforator method,
which ranged from 0.71 to 2.99 mg/100 g and was slightly lower than that of [34].
The role of bark to decrease the formaldehyde content of wood-based composites was also studied
by [55,56]. It was expected that the level of free formaldehyde content of the panels glued with PUR
would be significantly lower than that of the boards bonded with UF, but the combination of both
adhesives and raw materials resulted in panels that reached at least the E0 classification.

4. Conclusions
This study has shown that the nutshells can be used for the manufacture of PBs with improved
performances in terms of physical properties (dimensional stability), but also with higher Brinell
hardness compared to the spruce particleboards.
MOR and MOE are lower by roughly 50% and cannot meet the requirements for P1 or P2 PBs,
according to EN 310:2005. Future research should consider the improvement potentials by choosing
the proper percentage of nutshells chips, combining the coarse-grained particles with the fine-grained
ones, in order to fill voids in-between, combined with a proper bonding system.
This study has also shown that, when MUF is used to bond the boards, the raw material has
no influence on MOR and water absorption, when PUR is used, the raw material has no influence
on MOE, but with an improvement in terms of MOR (35% higher compared to spruce particles),
Brinell hardness (up to 67%), thickness swelling (65–75% lower), and water absorption (58–87% lower).
There is no statistically significant influence of the adhesive for hazelnut shells in terms of MOE and
Brinell hardness.
The values of the formaldehyde content are all included in the E0 emission class. In the case of
the panels bonded with PUR, the measured values were less than 1.5 mg/100 g, which means that the
super E0 category was reached. All these perforator results for the panels manufactured with hazelnut
and walnut shells recommend them as low-emissions lignocellulosic composites.
The nutshells, utilized only for energy purposes [57], could be considered as a raw material in
particleboard production. Further research can focus on the properties of improved formulations
for adhesives and lignocellulosic particles, eventually with reinforcements [58] to achieve similar
properties to P1 and P2 [59].

Author Contributions: Conceptualization, T.S.; Methodology, T.S. and E.M.T. Validation, E.M.T.; Formal analysis,
A.P. and M.C.B.; Investigation, T.S.; Resources, T.S.; Writing—original draft preparation, T.S. and E.M.T.;
Writing—review and editing, T.S. and E.M.T.; Visualization, T.S., and M.C.B.; Supervision, A.P. and M.C.B. All
authors have read and agreed to the published version of the manuscript.
Funding: This research received no external funding.
Acknowledgments: The authors would like to thank Frederick Kamke from Oregon State University (Oregon,
USA) for making the project possible and his support throughout the project; Danijela Domljan from the University
of Zagreb (Croatia) for providing the hazelnut shells used for the board production in this project and to Kaindl
Co. in Salzburg for supporting this research with the determination of the formaldehyde content of the walnut
and hazelnut samples.
Conflicts of Interest: The authors declare no conflict of interest.
Appl. Sci. 2020, 10, 6340 9 of 11

References
1. Tudor, E.M.; Zwicl, C.; Eichinger, C.; Petutschnigg, A.; Barbu, M.C. Performance of softwood bark
comminution technologies for determination of targeted particle size in further upcycling applications. J.
Clean. Prod. 2018, 269, 122412. [CrossRef]
2. Queirós, C.; Cardoso, S.; Lourenço, A.; Ferreira, J.M.I.; Lourenço, M.; Pereira, H. Characterization of walnut,
almond, and pine nut shells regarding chemical composition and extract composition. Biomass Convers.
Biorefinery 2019, 10. [CrossRef]
3. de Carvalho Araújo, C.; Salvador, R.; Piekarski, C.; Sokulski, C.; de Francisco, A.; Camargo, S. Circular
Economy Practices on Wood Panels: A Bibliographic Analysis. Sustainability 2019, 11, 1057. [CrossRef]
4. Fan, Y.; Lee, C.; Lim, J.; Klemeš, J. Cross-disciplinary approaches towards smart, resilient and sustainable
circular economy. J. Clean. Prod. 2019, 232, 1482–1491. [CrossRef]
5. Risse, M.; Weber-Blaschke, G.; Richter, K. Resource efficiency of multifunctional wood cascade chains using
LCA and exergy analysis, exemplified by a case study for Germany. Resour. Conserv. Recycl. 2017, 126,
141–152. [CrossRef]
6. Eurostat. Wood Products-Production and Trade. Available online: https://ec.europa.eu/eurostat/statistics-
explained/index.php/Wood_products_-_production_and_trade (accessed on 19 August 2020).
7. Boquillon, N.; Elbez, G.; Schönfeld, U. Properties of wheat straw particleboards bonded with different types
of resin. J. Wood Sci. 2004, 50, 230–235. [CrossRef]
8. Wang, D.; Sun, S. Low density particleboard from wheat straw and corn pith. Ind. Crop. Prod. 2002, 50, 43–50.
[CrossRef]
9. Luo, P.; Yang, C.; Li, M.; Wang, Y. Manufacture of thin rice straw particleboards bonded with various
polymeric methane diphenyl diisocyanate/ urea formaldehyde resin mixtures. BioResources 2020, 15, 935–944.
10. Yasina, M.; Waheed Bhutto, A.; Bazmi, A.; Karim, S. Efficient Utilization of Rice-wheat Straw to Produce
Value-added Composite Products. J. Environ. Chem. Eng. 2010, 1, 1–8.
11. Dukarska, D.; Czarnecki, R.; Dziurka, D.; Mirski, R. Construction particleboards made from rapeseed straw
glued with hybrid pMDI/PF resin. Eur. J. Wood Prod. 2017, 75, 175–184. [CrossRef]
12. Balducci, F.; Harper, C.; Meinlschmidt, P.; Dix, B.; Sanasi, A. Development of Innovative Particleboard Panels.
Drv. Ind. 2008, 59, 131–136.
13. Réh, R.; Vrtielka, J. Modification of the core layer of particleboard with hemp shives and its influence on the
particleboard properties. Acta Fac. Xylologiae 2013, 55, 51–59.
14. Nemli, G.; Odabas Serin, Z.; Özdemir, F.; Ayrılmış, N. Potential use of textile dust in the middle layer of
three-layered particleboards as an eco-friendly solution. BioResources 2019, 14, 120–127.
15. Bektas, I.; Guler, C.; Kalaycioğlu, H.; Mengeloglu, F.; Nacar, M. The Manufacture of Particleboards using
Sunflower Stalks (Helianthus annuus L.) And Poplar Wood (Populus alba L.). J. Compos. Mater. 2005, 39,
467–473. [CrossRef]
16. Klímek, P.; Meinlschmidt, P.; Wimmer, R.; Plinke, B.; Schirp, A. Using sunflower (Helianthus annuus L.),
topinambour (Helianthus tuberosus L.) and cup-plant (Silphium perfoliatum L.) stalks as alternative raw
materials for particleboards. Ind. Crop. Prod. 2016, 92, 157–164. [CrossRef]
17. Klímek, P.; Wimmer, R.; Mishra, P.; Kúdela, J. Utilizing brewer’s-spent-grain in wood-based particleboard
manufacturing. J. Clean. Prod. 2017, 141, 812–817. [CrossRef]
18. Wang, X.; Fang, H.; Feng, M.; Zhang, Y.; Yan, N. Manufacturing Medium-Density Particleboards from
Wood–Bark Mixture and Different Adhesive Systems. For. Prod. J. 2015, 65, 20–25. [CrossRef]
19. Lakreb, N.; As, N.; Gorgun, V.; Sen, U.; Gomes, G.; Pereira, H. Production and characterization of
particleboards from cork-rich Quercus cerris bark. Eur. J. Wood Prod. 2018, 76, 989–997. [CrossRef]
20. Medved, S.; Tudor, E.M.; Barbu, M.C.; Jambreković, V.; Španić, N. Effect of Pine (Pinus Sylvestris) Bark Dust
on Particleboard Thickness Swelling and Internal Bond. Drv. Ind. 2019, 70, 141–147. [CrossRef]
21. Merkel, K.; Rydarowski, H.; Kazimierczak, J.; Bloda, A. Processing and characterization of reinforced
polyethylene composites made with lignocellulosic fibres isolated from waste plant biomass such as hemp.
Compos. B Eng. 2014, 67, 138–144. [CrossRef]
22. Yu, X.; Xu, H. Lightweight Composites Reinforced by Agricultural Byproducts. In Lightweight Materials from
Biopolymers and Biofibers; American Chemical Society: Omaha, NE, USA, 2014; pp. 209–238.
Appl. Sci. 2020, 10, 6340 10 of 11

23. Bowyer, J.; Stockmann, V. Agricultural residues: An exciting bio-based raw material for the global panels
industry. Forest Prod. J. 2001, 51, 10–21.
24. Siti Suhaily, S.; Khalil, A.; Asniza, M.; Nurul Fazita, M.; Mohamed, A.; Dungani, R.; Zulqarnain, W.; Syakir, M.
Design of green laminated composites from agricultural biomass. In Lignocellulosic Fibre and Biomass-Based
Composite Materials; Elsevier: Sawston, UK, 2017; pp. 291–311.
25. Papadopoulou, E.; Chrissafis, C. Particleboards from agricultural lignocellulosics and biodegradable polymers
prepared with raw materials from natural resources. In Natural Fiber-Reinforced Biodegradable and Bioresorbable
Polymer Composites; Woodhead Publishing: Sawston, UK, 2017; pp. 19–30.
26. Figen-Antmen, Z. Exploitation of Peanut and Hazelnut Shells as Agricultural Industrial Wastes for Solid
Biofuel Production. Fresenius Environ. Bull. 2019, 28, 2340–2347.
27. Flores-Johnson, E.; Carrillo, J.; Zhai, C.; Gamboa, R.; Gan, Y.S.L. Microstructure and mechanical properties of
hard Acrocomia mexicana fruit shell. Sci. Rep. 2018, 8, 9668. [CrossRef] [PubMed]
28. Statista. Production of Tree Nuts Worldwide in 2019/2020, by Type (in 1,000 Metric Tons). Available online:
https://www.statista.com/statistics/1030790/tree-nut-global-production-by-type/ (accessed on 19 August
2020).
29. Martínez, M.; Moiraghi, L.; Agnese, M.; Guzman, C. Making and some properties of activated carbon
produced from agricultural industrial residues from Argentina. J. Argent. Chem. Soc. 2003, 91, 104–108.
[CrossRef]
30. Gürü, M.; Aruntaş, Y.; Tüzün, F.; Bilici, I. Processing of urea-formaldehyde-based particleboard from hazelnut
shell and improvement of its fire and water resistance. Fire Mater. 2009, 33, 413–419. [CrossRef]
31. Güler, C.; Çöpür, Y.; Büyüksari, U. Producing particleboards from hazelnut (Corylus avellana L.) husk and
European Black Pine (Pinus nigra Arnold). Wood Res. 2009, 54, 125–132.
32. Kowaluk, G.; Kadziela,
˛ J. Properties of particleboard produced with use of hazelnut shells. Ann. WULS
SGGW Wood Technol. 2014, 85, 131–134.
33. Gürü, M.; Atar, M.; Yıldırım, R. Production of polymer matrix composite particleboard from walnut shell
and improvement of its requirements. Mater. Des. 2008, 29, 284–287. [CrossRef]
34. Pirayesh, H.; Khanjanzadeh, H.; Salarib, H. Effect of using walnut/almond shells on the physical, mechanical
properties and formaldehyde emission of particleboard. Compos. Part. B Eng. 2013, 45, 858–863. [CrossRef]
35. Güler, C.; Cöpur, Y.; Tascioglu, C. The manufacture of particleboards using mixture of peanut hull (Arachis
hypoqaea L.) and European Black pine (Pinus nigra Arnold) wood chips. Bioresour. Technol. 2008, 99, 2893–2897.
[CrossRef]
36. Batalla, L.; Nuñez, A.; Marcovich, N. Particleboards from peanut-shell flour. J. Appl. Polym. Sci. 2005, 97,
916–923. [CrossRef]
37. Gürü, M.; Tekeli, S.; Bilici, I. Manufacturing of urea–formaldehyde-based composite particleboard from
almond shell. Mater. Des. 2006, 27, 1148–1151. [CrossRef]
38. Pirayesh, H.; Khazaeian, A. Using almond (Prunus amygdalus L.) shell as a bio-waste resource in wood-based
composite. Compos. Part. B Eng. 2012, 43, 1475–1479. [CrossRef]
39. Chaudhary, A.; Gope, P.; Singh, V. Effect of Almond Shell Particles on Tensile Property of Particleboard. J.
Mater. Environ. Sci. 2013, 4, 109–112.
40. EN 326:2012. Wood-Based Panels—Sampling, Cutting and Inspection—Part 1: Sampling and Cutting of Test Pieces
and Expression of Test Results; European Committee for Standardization: Brussels, Belgium, 2012.
41. EN 310:2005. Wood-Based Panels: Determination of Modulus of Elasticity in Bending and of Bending Strength;
European Committee for Standardization: Brussels, Belgium, 2005.
42. EN 1534:2010. Wood flooring—Determination of Resistance to Indentation—Brussels, Belgium; European
Committee for Standardization: Brussels, Belgium, 2010.
43. EN 317:2005. Particleboards and fibreboards—Determination of Swelling in Thickness after Immersion in Water;
European Committee for Standardization: Brussels, Belgium, 2005.
44. EN 323:2015. Wood-based Panels—Determination of Density; European Committee for Standardization: Brussels,
Belgium, 2015.
45. EN 120:2011. Wood-Based Panels—Determination of Formaldehyde Release—Extraction Method (Called Perforator
Method); European Committe for Standardization: Brussels, Belgium, 2011.
46. Pirayesh, H.; Khazaeian, A.; Tabarsa, T. The potential for using walnut (Juglans regia L.) shell as a raw material
for wood-based particleboard manufacturing. Compos. Part. B Eng. 2012, 43, 3276–3280. [CrossRef]
Appl. Sci. 2020, 10, 6340 11 of 11

47. Pizzi, A.; Mittal, K. Handbook of Adhesive Technology; Dekker: New York, MY, USA, 1994.
48. Dunky, M.; Niemz, P. Holzwerkstoffe und Leime: Technologie und Einflussfaktoren, Mit 150 Tabellen; Springer:
Berlin, Germany, 2002.
49. Tabarsa, T.; Ashori, A.; Gholamzadeh, M. Evaluation of surface roughness and mechanical properties of
particleboard panels made from bagasse. Comp. Part. B Eng. 2011, 42, 1330–1335. [CrossRef]
50. Kollmann, F. Technologie des Holzes und der Holzwerkstoffe, 2nd ed.; Springer: Berlin, Germany, 1982.
51. Zeppenfeld, G.; Grunwald, D. Klebstoffe in der Holz- und Möbelindustrie, 2nd ed.; Weinbrenner, DRW-Verlag:
Leinfelden-Echterdingen, Germany, 2005.
52. Gwon, J.; Lee, S.; Chun, S.; Doh, G.; Kim, J. Effects of chemical treatments of hybrid fillers on the physical
and thermal properties of wood plastic composites. Compos. Part. A Appl. Sci. Manuf. 2010, 41, 1491–1497.
[CrossRef]
53. Tudor, E.M.; Barbu, M.C.; Petutschnigg, A.; Réh, R.; Krišt’ák, L’. Analysis of Larch-Bark Capacity for
Formaldehyde Removal in Wood Adhesives. Int. J. Environ. Res. Public Health 2020, 17, 764. [CrossRef]
54. Roffael, E.; Johnsson, B.; Engström, B. On the measurement of formaldehyde release from low-emission
wood-based panels using the perforator method. Wood Sci. Technol. 2010, 44, 369–377. [CrossRef]
55. Medved, S.; Gajšek, U.; Tudor, E.M.; Barbu, M.C.; Antonović, A. Efficiency of bark for reduction of
formaldehyde emission from particleboards. Wood Res. 2019, 64, 307–316.
56. Réh, R.; Igaz, R.; Krišt’ák, L’.; Ružiak, I.; Gajtanska, M.; Božíková, M.; Kučerka, M. Functionality of Beech
Bark in Adhesive Mixtures Used in Plywood and Its Effect on the Stability Associated with Material Systems.
Materials 2019, 12, 1298. [CrossRef] [PubMed]
57. Şenol, H. Biogas potential of hazelnut shells and hazelnut wastes in Giresun City. Biotechnol. Rep. 2019, 24,
e00361. [CrossRef] [PubMed]
58. Nicolao, E.S.; Leiva, P.; Chalapud, M.C.; Ruseckaite, R.A.; Ciannamea, E.M.; Stefani, P.M. Flexural and
tensile properties of biobased rice husk-jute-soybean protein particleboards. J. Build. Eng. 2020, 30, 101261.
[CrossRef]
59. EN 312:2005. Particleboards—Specifications—Part 3: Requirements for Boards for Use in Interior Fitments (Including
Furniture) in Dry Conditions; European Committee for Standardization: Brussels, Belgium, 2005.

© 2020 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access
article distributed under the terms and conditions of the Creative Commons Attribution
(CC BY) license (http://creativecommons.org/licenses/by/4.0/).