    Aluminum 5182-H34: Metal Nonferrous Metal Aluminum Alloy 5000 Series Aluminum Alloy

    Uploaded by

    Luis Badoff
    This document provides information on the aluminum alloy 5182-H34. It lists the alloy's typical physical properties including density, mechanical properties like hardness and tensile strength, electrical and thermal properties, and its chemical composition ranges. Processing information is also given such as recommended annealing and hot-working temperatures.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Aluminum 5182-H34: Metal Nonferrous Metal Aluminum Alloy 5000 Series Aluminum Alloy

    Uploaded by

    Luis Badoff
    29 views2 pages
    This document provides information on the aluminum alloy 5182-H34. It lists the alloy's typical physical properties including density, mechanical properties like hardness and tensile strength, electrical and thermal properties, and its chemical composition ranges. Processing information is also given such as recommended annealing and hot-working temperatures.

    Original Description:

    especificación tapa latita de aluminio

    Original Title

    AA5182 TAPA

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides information on the aluminum alloy 5182-H34. It lists the alloy's typical physical properties including density, mechanical properties like hardness and tensile strength, electrical and thermal properties, and its chemical composition ranges. Processing information is also given such as recommended annealing and hot-working temperatures.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    29 views2 pages

    Aluminum 5182-H34: Metal Nonferrous Metal Aluminum Alloy 5000 Series Aluminum Alloy

    Uploaded by

    Luis Badoff
    This document provides information on the aluminum alloy 5182-H34. It lists the alloy's typical physical properties including density, mechanical properties like hardness and tensile strength, electrical and thermal properties, and its chemical composition ranges. Processing information is also given such as recommended annealing and hot-working temperatures.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    Aluminum 5182-H34 Página 1 de 2

    Aluminum 5182-H34
    Categories: Metal; Nonferrous Metal; Aluminum Alloy; 5000 Series Aluminum Alloy

    Material Data points with the AA note have been provided by the Aluminum Association, Inc. and
    Notes: are NOT FOR DESIGN.

    Composition Notes:
    Composition information provided by the Aluminum Association and is not for design.

    Key Words: UNS A95182; Aluminium 5182-H34; AA5182-H34


    Vendors: No vendors are listed for this material. Please click here if you are a supplier and would
    like information on how to add your listing to this material.

    Physical Metric English Comments


    Properties
    Density 2.65 g/cc 0.0957 lb/in³ AA; Typical

    Mechanical Metric English Comments


    Properties
    Hardness, 91 91 500 kg load with 10 mm ball. Calculated
    Brinell value.
    Hardness, 115 115 Converted from Brinell Hardness Value
    Knoop
    Hardness, 38.5 38.5 Converted from Brinell Hardness Value
    Rockwell A
    Hardness, 57 57 Converted from Brinell Hardness Value
    Rockwell B
    Hardness, 102 102 Converted from Brinell Hardness Value
    Vickers
    Tensile 340 MPa 49300 psi
    Strength,
    Ultimate
    Tensile 240 MPa 34800 psi
    Strength,
    Yield
    Elongation at 10 % 10 % In 5 cm
    Break @Thickness 1.60 mm @Thickness 0.0630 in
    Modulus of 69.6 GPa 10100 ksi In Tension
    Elasticity
    Compressive 70.9 GPa 10300 ksi
    Modulus
    Poissons 0.33 0.33
    Ratio
    Shear 26.0 GPa 3770 ksi Calculated
    Modulus
    Shear 200 MPa 29000 psi Calculated value.
    Strength

    Electrical Metric English Comments


    Properties
    Electrical 0.00000560 ohm-cm 0.00000560 ohm-cm
    Resistivity

    Thermal Metric English Comments


    Properties
    22.2 µm/m-°C 12.3 µin/in-°F
    @Temperature -50.0 - 20.0 °C @Temperature -58.0 - 68.0 °F

    Create PDF files without this message by purchasing novaPDF printer (http://www.novapdf.com)
    file:///C:/Users/lbadoff/Documents/ALUMINIO/NORMAS/LATITAS/Aluminum%2... 07/06/2017
    Aluminum 5182-H34 Página 2 de 2

    CTE, linear

    23.9 µm/m-°C 13.3 µin/in-°F


    @Temperature 20.0 - 100 °C @Temperature 68.0 - 212 °F
    24.1 µm/m-°C 13.4 µin/in-°F
    @Temperature 20.0 - 100 °C @Temperature 68.0 - 212 °F
    25.0 µm/m-°C 13.9 µin/in-°F
    @Temperature 20.0 - 200 °C @Temperature 68.0 - 392 °F
    26.0 µm/m-°C 14.4 µin/in-°F
    @Temperature 20.0 - 300 °C @Temperature 68.0 - 572 °F
    Specific Heat 0.904 J/g-°C 0.216 BTU/lb-°F
    Capacity
    Thermal 126 W/m-K 874 BTU-in/hr-ft²-°F
    Conductivity
    Melting 577 - 638 °C 1070 - 1180 °F
    Point
    Solidus 577 °C 1070 °F
    Liquidus 638 °C 1180 °F

    Processing Metric English Comments


    Properties
    Annealing 343 °C 650 °F
    Temperature
    Hot-Working 260 - 510 °C 500 - 950 °F
    Temperature

    Component Metric English Comments


    Elements
    Properties
    Aluminum, 93.2 - 95.8 % 93.2 - 95.8 % As remainder
    Al
    Chromium, <= 0.10 % <= 0.10 %
    Cr
    Copper, Cu <= 0.15 % <= 0.15 %
    Iron, Fe <= 0.35 % <= 0.35 %
    Magnesium, 4.0 - 5.0 % 4.0 - 5.0 %
    Mg
    Manganese, 0.20 - 0.50 % 0.20 - 0.50 %
    Mn
    Other, each <= 0.05 % <= 0.05 %
    Other, total <= 0.15 % <= 0.15 %
    Silicon, Si <= 0.20 % <= 0.20 %
    Titanium, Ti <= 0.10 % <= 0.10 %
    Zinc, Zn <= 0.25 % <= 0.25 %

    References for this datasheet.

    Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a
    consistent format. Users requiring more precise data for scientific or engineering calculations can click on the property value to see the
    original value as well as raw conversions to equivalent units. We advise that you only use the original value or one of its raw conversions in
    your calculations to minimize rounding error. We also ask that you refer to MatWeb's terms of use regarding this information. Click here to
    view all the property values for this datasheet as they were originally entered into MatWeb.

    Create PDF files without this message by purchasing novaPDF printer (http://www.novapdf.com)
    file:///C:/Users/lbadoff/Documents/ALUMINIO/NORMAS/LATITAS/Aluminum%2... 07/06/2017