    Anchorharvey Aluminum7075 Datasheet

    Uploaded by

    mvhmoudfathy55

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Anchorharvey Aluminum7075 Datasheet

    Uploaded by

    mvhmoudfathy55
    6 views3 pages

    Original Title

    anchorharvey-aluminum7075-datasheet

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    6 views3 pages

    Anchorharvey Aluminum7075 Datasheet

    Uploaded by

    mvhmoudfathy55

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    You are on page 1of 3

    Aluminum 7075-T6; 7075-T651

    Categories: Metal; Nonferrous Metal; Aluminum Alloy; 7000 Series Aluminum Alloy
    Material General 7075 characteristics and uses (from Alcoa): Very high strength material
    Notes: used for highly stressed structural parts. The T7351 temper offers improved stress-
    corrosion cracking resistance.

    Applications: Aircraft fittings, gears and shafts, fuse parts, meter shafts and gears,
    missile parts, regulating valve parts, worm gears, keys, aircraft, aerospace and
    defense applications; bike frames, all terrain vehicle (ATV) sprockets.

    Data points with the AA note have been provided by the Aluminum Association,
    Inc. and are NOT FOR DESIGN.

    Composition Notes:
    A Zr + Ti limit of 0.25 percent maximum may be used with this alloy designation
    for extruded and forged products only, but only when the supplier or producer and
    the purchaser have mutually so agreed. Agreement may be indicated, for example,
    by reference to a standard, by letter, by order note, or other means which allow the
    Zr + Ti limit.
    Composition information provided by the Aluminum Association and is not for
    design.
    Key Words: Aluminium 7075-T6; Aluminium 7075-T651, UNS A97075; ISO AlZn5.5MgCu;
    Aluminium 7075-T6; Aluminium 7075-T651; AA7075-T6
    Vendors: Click here to view all available suppliers for this material.

    Please click here if you are a supplier and would like information on how to add
    your listing to this material.

    Physical
    Metric English Comments
    Properties
    Density 2.81 g/cc 0.102 lb/in³ AA; Typical

    Mechanical
    Metric English Comments
    Properties
    Hardness, 150 150 AA; Typical; 500 g load; 10 mm ball
    Brinell
    Hardness, 191 191 Converted from Brinell Hardness Value
    Knoop
    Hardness, 53.5 53.5 Converted from Brinell Hardness Value
    Rockwell A
    Hardness, 87 87 Converted from Brinell Hardness Value
    Rockwell B
    Hardness, 175 175 Converted from Brinell Hardness Value
    Vickers
    Ultimate Tensile 572 MPa 83.0 ksi AA; Typical
    Strength
    Tensile Yield 503 MPa 73.0 ksi AA; Typical
    Strength
    Elongation at 11.0 % 11.0 % AA; Typical; 1/16 in. (1.6 mm) Thickness
    Break
    11.0 % 11.0 % AA; Typical; 1/2 in. (12.7 mm) Diameter
    Modulus of 71.7 GPa 10400 ksi AA; Typical; Average of tension and
    Elasticity compression. Compression modulus is about
    2% greater than tensile modulus.
    Poissons Ratio 0.330 0.330
    Fatigue Strength 159 MPa 23000 psi completely reversed stress; RR Moore
    @# of Cycles @# of Cycles machine/specimen
    5.00e+8 5.00e+8
    Fracture 20.0 MPa-m½ 18.2 ksi-in½ K(IC) in S-L Direction
    Toughness
    25.0 MPa-m½ 22.8 ksi-in½ K(IC) in T-L Direction
    29.0 MPa-m½ 26.4 ksi-in½ K(IC) in L-T Direction
    Machinability 70 % 70 % 0-100 Scale of Aluminum Alloys
    Shear Modulus 26.9 GPa 3900 ksi
    Shear Strength 331 MPa 48000 psi AA; Typical

    Electrical
    Metric English Comments
    Properties
    Electrical 0.00000515 0.00000515 AA; Typical at 68°F
    Resistivity ohm-cm ohm-cm

    Thermal
    Metric English Comments
    Properties
    CTE, linear 23.6 µm/m-°C 13.1 µin/in-°F AA; Typical; average over range
    @Temperature @Temperature
    20.0 - 100 °C 68.0 - 212 °F
    25.2 µm/m-°C 14.0 µin/in-°F average
    @Temperature @Temperature
    20.0 - 300 °C 68.0 - 572 °F
    Specific Heat 0.960 J/g-°C 0.229 BTU/lb-
    Capacity °F
    Thermal 130 W/m-K 900 BTU-in/hr- AA; Typical at 77°F
    Conductivity ft²-°F
    Melting Point 477 - 635.0 °C 890 - 1175 °F AA; Typical range based on typical
    composition for wrought products 1/4 inch
    thickness or greater. Homogenization may
    raise eutectic melting temperature 20-40°F
    but usually does not eliminate eutectic
    melting.
    Solidus 477 °C 890 °F AA; Typical
    Liquidus 635.0 °C 1175 °F AA; Typical

    Processing
    Metric English Comments
    Properties
    Annealing 413 °C 775 °F
    Temperature
    Solution 466 - 482 °C 870 - 900 °F
    Temperature
    Aging 121 °C 250 °F
    Temperature

    Material
    Components Metric English Comments
    Properties
    Aluminum, Al 87.1 - 91.4 % 87.1 - 91.4 % As remainder
    Chromium, Cr 0.18 - 0.280 % 0.18 - 0.280 %
    Copper, Cu 1.20 - 2.0 % 1.20 - 2.0 %
    Iron, Fe <= 0.50 % <= 0.50 %
    Magnesium, Mg 2.10 - 2.90 % 2.10 - 2.90 %
    Manganese, Mn <= 0.30 % <= 0.30 %
    Other, each <= 0.050 % <= 0.050 %
    Other, total <= 0.15 % <= 0.15 %
    Silicon, Si <= 0.40 % <= 0.40 %
    Titanium, Ti <= 0.20 % <= 0.20 %
    Zinc, Zn 5.10 - 6.10 % 5.10 - 6.10 %