    Stainless Steels 410: Martensitic

    Uploaded by

    Kiran
    This document provides information about the stainless steel grade X12Cr13 (No. 1.4006), including its standard reference, comparable standards in different countries, recommended chemical composition, and mechanical properties in various conditions such as annealed, quenched and tempered. It lists recommended maximum sizes, minimum hardness levels, tensile strengths and elongation percentages. It also provides recommended temperature ranges for hot forging deformation, annealing, quenching and tempering of this steel grade.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Stainless Steels 410: Martensitic

    Uploaded by

    Kiran
    47 views2 pages
    This document provides information about the stainless steel grade X12Cr13 (No. 1.4006), including its standard reference, comparable standards in different countries, recommended chemical composition, and mechanical properties in various conditions such as annealed, quenched and tempered. It lists recommended maximum sizes, minimum hardness levels, tensile strengths and elongation percentages. It also provides recommended temperature ranges for hot forging deformation, annealing, quenching and tempering of this steel grade.

    Original Title

    410_X12Cr13-Nr.1.4006-ENG

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides information about the stainless steel grade X12Cr13 (No. 1.4006), including its standard reference, comparable standards in different countries, recommended chemical composition, and mechanical properties in various conditions such as annealed, quenched and tempered. It lists recommended maximum sizes, minimum hardness levels, tensile strengths and elongation percentages. It also provides recommended temperature ranges for hot forging deformation, annealing, quenching and tempering of this steel grade.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    47 views2 pages

    Stainless Steels 410: Martensitic

    Uploaded by

    Kiran
    This document provides information about the stainless steel grade X12Cr13 (No. 1.4006), including its standard reference, comparable standards in different countries, recommended chemical composition, and mechanical properties in various conditions such as annealed, quenched and tempered. It lists recommended maximum sizes, minimum hardness levels, tensile strengths and elongation percentages. It also provides recommended temperature ranges for hot forging deformation, annealing, quenching and tempering of this steel grade.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 2

    STAINLESS

    X12Cr13 - Nr. 1.4006 STEELS

    STANDARD REFERENCE:
    EN 10088-3: 2014 (Hot-rolled and bright products)

    RODACCIAI REFERENCES AND COMPARABLE STANDARDS


    EUROPE ITALY GERMANY FRANCE UK USA

    EN 10088-3: 2005 (UNI 6900: 71) (DIN 17440 - 85) (NF A 35-574-90) (BS 970 pt. 3 -91) AISI

    Grade N° Werkstoff N°
    X12Cr13 1.4006 X 12 Cr 13 X12Cr13 1.4006 Z 10 C 13 410S21 410

    CHEMICAL COMPOSITION (CAST ANALYSIS) (%)


    C Si / max Mn / max P / max S / max Cr Ni / max
    0,08÷0,15 1,00 1,50 0,040 0,030 11,5÷13,5 0,75

    MECHANICAL PROPERTIES - Rough turned (1X) in the annealed condition


    Size max Heat treatment Hardness HB max* Rp 0,2 (MPa) Rm (MPa) A5 (%) min** KV (J) min
    (mm) min
    Annealed (+A) 220 - 730 max - -
    100
    Quenched + Tempered (+QT 650) - 450 650÷850 15 25
    * only for guidance

    MECHANICAL PROPERTIES - Cold drawn (2H, 2B) and ground bars (2G) in the solution annealed condition
    Annealed Quenched + Tempered
    Size max (mm)
    Rm (MPa) max HB max* Heat treatment Rp 0,2 (MPa) min Rm (MPa) max A5 (%) min** KV (J) min
    ≤ 10 880 280 550 700÷1000 9 -
    > 10 ≤ 16 880 280 500 700÷1000 9 -
    Quenched + Tempered
    > 16 ≤ 40 800 250 450 650÷930 10 25
    (+QT 650)
    > 40 ≤ 63 760 230 450 650÷880 10 25
    > 63 ≤ 100 730 220 450 650÷850 15 25
    * Values valid only for size ≥5 mm

    MECHANICAL PROPERTIES - Cold drawn wire and coils (2H)


    Tensile strength levels +C 500 +C 650 +C 800 +C900
    Rm (MPa) 500÷700 650÷850 800÷1000 900÷1100
    Note: the desired tensile strength level shall be evaluated depending on diameter required
    rev. 10/2018

    Mark Rodacciai Download APP

    STAINLESS STEELS
    410
    MARTENSITIC
    STAINLESS
    X12Cr13 - Nr. 1.4006 STEELS

    MECHANICAL PROPERTIES - Cold drawn wire and coils in the solution annealed condition (2D)
    Size 0,50 ≤ d ≤ 1,00 1,00 ≤ d ≤ 3,00 3,00 ≤ d ≤ 5,00 5,00 ≤ d ≤ 16,00
    Rm (MPa) max 1100 1050 1000 950
    A (%) max 10 10 10 15
    Note: If skin passed, Rm might be increased by up to 50 MPa

    WORKING TEMPERATURES RECOMMENDED


    Operation Hot forgings deformation Annealing Quenching Tempering
    (air) in air or oil (QT 650)
    °C 900÷1100 745÷825 950÷1000 680÷780

    TEMPERING CURVE

    Tempering temperature °C
    rev. 10/2018