This document provides information on ADEKIT A140, a high performance structural epoxy adhesive. It has excellent mechanical and thermal properties up to 100°C and is suitable for bonding car bodies and metallic structures. The adhesive has a pot life of 30 minutes, cures at room temperature, and achieves full strength within 4.5 hours. It maintains high lap shear strength even after exposures like thermal shocks, moisture, oils and acids.
This document provides information on ADEKIT A140, a high performance structural epoxy adhesive. It has excellent mechanical and thermal properties up to 100°C and is suitable for bonding car bodies and metallic structures. The adhesive has a pot life of 30 minutes, cures at room temperature, and achieves full strength within 4.5 hours. It maintains high lap shear strength even after exposures like thermal shocks, moisture, oils and acids.
This document provides information on ADEKIT A140, a high performance structural epoxy adhesive. It has excellent mechanical and thermal properties up to 100°C and is suitable for bonding car bodies and metallic structures. The adhesive has a pot life of 30 minutes, cures at room temperature, and achieves full strength within 4.5 hours. It maintains high lap shear strength even after exposures like thermal shocks, moisture, oils and acids.
This document provides information on ADEKIT A140, a high performance structural epoxy adhesive. It has excellent mechanical and thermal properties up to 100°C and is suitable for bonding car bodies and metallic structures. The adhesive has a pot life of 30 minutes, cures at room temperature, and achieves full strength within 4.5 hours. It maintains high lap shear strength even after exposures like thermal shocks, moisture, oils and acids.
ADEKIT H 9940 STRUCTURAL EPOXY ADHESIVE HIGH PERFORMANCES
DESCRIPTION Bonding of car body, bonding metallic structures (racing vehicles, aeronautics), bonding inserts and composite structures
PROPERTIES
2 component high performance room temperature Excellent mechanical and thermal performances up cured epoxy adhesive to 100°C Non sagging paste product suitable for vertical Excellent strength to dynamic loads (vibrations and applications and to fill irregular joints impacts) Product adapted to stringent ageing and aggressive environments
PHYSICAL PROPERTIES Composition RESIN HARDENER MIXED Mix ratio by weight 100 90 Mix ratio by volume at 25°C 100 100 beige beige Colour brown beige brown black black Viscosity at 25°C (Pa.s) BROOKFIELD LVT 400 450 430 3 Specific gravity at 25°C (g/cm ) ISO 1675 : 1985 1.38 1.23 1.30 Pot life at 25°C on 100 g (min) Gel Timer TECAM - - 30 Open time (min) - - - 40
THERMAL AND MECHANICAL PROPERTIES (1)
Hardness ISO 868 : 2003 Shore D1 / D15 80 / 77 Tensile strength ISO 527 : 1993 MPa 30 Elongation at break ISO 527 : 1993 % 2 Glass transition temperature (tg) ISO 11359 : 2002 °C 70 Coefficient of thermal expansion (CTE) -6 -1 ISO 11359: 1999 10 K 70 (-30°C to +60°C) Working temperature - °C -40 ; +100°C
EQUIPMENT ADEKIT 140 packaged in 50 and 400 ml cartridges and requires a manual or pneumatic gun. Please consult our technical department for applications needing a machine.
SUBSTRATE PREPARATION
The item to be bonded must be free of all dirt, oil or other foreign matter. A clean, dry surface is a must. Consult our Technical Support and refer to the technical data sheet about surface preparations to choose adapted degreaser or cleaner
Page 1/3- TDS09F0114 – December 1st 2009
GERMANY SPAIN & PORTUGAL SLOVAKIA NORTH AMERICA JAPAN INDIA
Time to obtain 1 MPa lap shear strength at 25°C ISO 4587 : 2003 hr 4 hrs 30 Time to obtain 50% final lap shear strength at 25°C ISO 4587 : 2003 hr 20 Lap shear strength on aluminium ISO 4587 : 2003 MPa 21 CF(3) Floating roller peel resistance (2) ISO 4578 : 1997 kN/m 5 CF Lap shear strength after moist cataplasm 15 days at 80°C ISO 4587 : 2003 MPa 20 CF Lap shear strength after a thermal shock ageing cycle ISO 4587 : 2003 MPa 20 CF 15 cycles D3 (see annex) Lap shear strength after ageing in immersion for 3 weeks : motor oil at 70°C 16 CF hydrochloric acid (0.1 N) at 23°C 17 CF soda (0.1 N) at 23°C 21 CF seawater at 23°C ISO 4587 : 2003 21 CF ISO 175 : 1999 MPa gasoil at 23°C 19 CF gas at 23°C 21 CF Lap shear strength after thermal ageing 3 weeks at 100°C ISO 4587 : 2003 MPa 21 CF (1) Lap shear strength on aluminium2017A etched in sulfochromic bath (2) Hardening conditions: 8 hrs at 80°C + 48 hrs at room temperature (3) According to ISO 10365:1992 : CF = Cohesive failure, AF = Adhesive failure, SAF = Superficial adhesive failure, SF := Support failure
HANDLING PRECAUTIONS It is recommended to use the product at a temperature between +18°C and +35°C. Normal health and safety precautions should be observed when handling these products : ensure good ventilation wear gloves and safety glasses wear waterproof clothes For further information, please consult the product safety data sheet.
STORAGE CONDITIONS
Shelf life of ADEKIT A140/ H9940 is 12 months stored in its original unopened packaging at a temperature between +15°C and +25°C.
PACKAGING
BLACK BEIGE BROWN
A 140/50 NR H 9940 NR A 140/400 BE H 9940 BE A 140/50 MN H 9940 MN A 140/400 NR 5 + 4.5 kg 12 cartridges 6(0.5+0.45)kg 12 cartridges 5 + 4.5 kg 12 cartridges 40 + 36 kg 40 + 36 kg GUARANTEE
The information contained in this technical data sheet result from research and tests conducted in our Laboratories under precise conditions. It is the responsibility of the user to determine the suitability of AXSON products, under their own conditions before commencing with the proposed application. AXSON guarantee the conformity of their products with their specifications but cannot guarantee the compatibility of a product with any particular application. AXSON disclaim all responsibility for damage from any incident which results from the use of these products. The responsibility of AXSON is strictly limited to reimbursement or replacement of products which do not comply with the published specifications. Page 2/3- TDS09F0114 – December 1st 2009
GERMANY SPAIN & PORTUGAL SLOVAKIA NORTH AMERICA JAPAN INDIA