ProblemSheet - Unit 1
ProblemSheet - Unit 1
1. A steel rod 6 mm in diameter is under the action of a tensile force of 800 Newtons. Calculate the tensile stress in the bar.
2. A 30-mm gauge length is marked on an aluminium test piece. The test piece is strained in tension so that the gauge length becomes
32.3 mm. Calculate the strain.
3. A steel wire, 0.5 mm2 in cross-sectional area, and 10m long is extended elastically 1.68 mm by a force of 18 N. Calculate the modulus
of elasticity for the steel.
4. A 200-mm-long strip of metal is stretched in two steps, first to 300 mm and then to 400 mm. Show that the total true strain is the sum
of the true strains in each step; in other words, the true strains are additive. Show that, in the case of engineering strains, the strains
cannot be added to obtain the total strain.
5. A paper clip is made of wire 0.7 mm in diameter. If the original material from which the wire is made is a rod 25 mm in diameter,
calculate the longitudinal engineering and true strains that the wire has undergone during processing.
6. A steel rod having 0.1 mm diameter and 1.5 m length is subjected to an axial pull of 1 kN. Find (a) stress (b) strain and (c) elongation.
7. A short timber post of rectangular cross section has one side of section twice the other. When the timber post is subjected to compressive
load of 10 kN it contracts by 0.0521 mm for 1 m length. If the modulus of elasticity of timber is 12 GPa, calculate the dimensions of
the post.
8. A tensile test uses a test specimen that has a gage length of 50 mm and an area = 200 mm2. During the test the specimen yields under a
load of 98,000 N. The corresponding gage length = 50.23 mm. This is the 0.2 percent yield point. The maximum load = 168,000 N is
reached at a gage length = 64.2 mm. Determine: (a) yield strength Y, (b) modulus of elasticity E, and (c) tensile strength TS.
9. A copper wire of diameter 0.80 mm fails at an engineering stress = 248.2 MPa. Its ductility is measured as 75% reduction of area.
Determine the true stress and true strain at failure.