back to chapter overview / all chapters

1 STICK ELECTRODES
TYPE EN -ISO and ASME -AWS MECHANICAL
PROPERTIES
ANALYSIS APPLICATION

CEWELD 9606-1: FM6 T > 690 MPa C < 0,10 E NiCrMo 686 CPT electrode is suitable for welding duplex, super-duplex and
E NiCrMo Sect IX QW-432: F-No. 43 Y > 350 MPa Mn < 1,0 super-austenitic stainless steels as well as nickel-chromium-molybdenum alloys
686 CPT 14172: E > 30% Fe < 5,0 such as UNS N06059 and N06022, Inconel alloy C-276 and Inconel alloys 622, 625
E Ni 6686 Si < 0,25 and 686. Joining Duplex, Superduplex, super austenitic stainless steel, nickel
(NiCr21Mo16W4) Ni > 49 alloys, N06059, N06022, Hastelloy C276, alloy C22, Inconel 622, 625, 686, chemical
A 5.11: Ti < 0,3 and petrochemical industry, 2.4605, 2.4610, 2.4602, 2.4819, NICr23Mo16Al, Ni-
E NiCrMo-14 Cr 19 - 23 Mo16Cr15Ti, NiCr21Mo14W, NiMo16Cr15W, alloy 59, alloy C4, alloy 276
Mo 15 - 17
W 3,0 - 4,4
CEWELD 9606-1: FM6 T > 620 MPa C 0,05 - 0,15 E NiCrCo 617 is used for welding of nickel-chromium-cobalt-molybdenum alloys
E NiCrCo Sect IX QW-432: F-No. 43 Y > 400 MPa Mn 0,3 - 2,5 (UNS Number N06617). This electrode can also be used for overlay cladding
617 14172: E > 25% Fe < 5,0 in case its alloy properties are required. Weld metal provides optimum strength and
E Ni 6117 I > 120J (20 °C) Si < 0,75 oxidation resistance above up to 1150 °C, especially when welding on base metals of
(NiCr22Co12Mo) Ni > 45 nickel-iron-chromium alloys.
A 5.11: Co 9,0 -15 Inconel alloys 600 and 601, Incoloy alloys 800 HT and 802 and cast alloys such
E NiCrCoMo-1 Cu < 0,5 as HK-40, HP and HP-45 Modified. UNS Number N06617, 2.4663, 1.4952, 1.4958,
Cr 21 - 26 1.4959, NiCr21Co12Mo, X6CrNiNbN 25 20, X5NiCrAlTi 31 20, X8NiCrAlTi 32 21,
Nb+Ta < 1,0 Alloy 617, N08810, N08811
Mo 8,0 –10
12. SHOCK AND ABRASION RESISTANT
CEWELD 14700: 320 HB C ~ 0,1 E DUR 300 Kb is an exceptional easy to apply alloy without any risk for cracks and
E DUR 300 E Fe1 (up from 3rd layer) Mn ~ 1,0 can also be applied on austenitic manganese steels, 300 HB is usually almost obtained
Kb (DIN 8555: E 1-UM-300-P) 300 HB Si ~ 0,5 in the first layer. The weld deposit is machinable with tungsten carbide tool tips. Very
(up from 2nd layer) Cr ~ 1,2 good weld deposit appearance and outstanding welding properties on both AC and
280 HB Fe Rest DC+.
(up from 1st layer)
(275-325HB)
CEWELD 14700: 370 HB C ~ 0,15 E DUR 350 Kb is an exceptional easy to apply alloy without any risk for cracks and
E DUR 350 E Fe1 (up from 3rd layer) Mn ~ 1,1 can also be applied on austenitic manganese steels, 350 HB is usually almost obtained
Kb (DIN 8555: E 1-UM-350-P) 350 HB Si ~ 0,7 in the first layer. The weld deposit is machinable with tungsten carbide tool tips. Very
(up from 2nd layer) Cr ~ 3,0 good weld deposit appearance and outstanding welding properties on both AC and
320 HB Fe Rest DC+.
(up from 1st layer)
(325-375HB)
CEWELD 14700: 420 HB C ~ 0,18 E DUR 400 Kb is an exceptional easy to apply alloy without any risk for cracks and
E DUR 400 E Fe1 (up from 3rd layer) Mn ~ 1,2 can also be applied on austenitic manganese steels, 400 HB is usually almost obtained
Kb (DIN 8555: E 1-UM-400-P) 400 HB Si ~ 0,7 in the first layer. The weld deposit is machinable with tungsten carbide tool tips. Very
(up from 2nd layer) Cr ~ 3,5 good weld deposit appearance and outstanding welding properties on both AC and
375HB Fe Rest DC+.
(up from 1st layer)
(375-450HB)
CEWELD 14700: 42 HRC C ~ 0,1 E DUR 400 CrMo is an exceptional easy to apply alloy without any risk for cracks
E DUR 400 E Fe3 (up from 3rd layer) Mn ~ 0,6 and can also be applied on austenitic manganese steels, 39 HRc is usually almost
CrMo (DIN 8555: E 3-UM-40-PT) 39 HRC Si ~ 0,4 obtained in the first layer. The weld deposit has a high impact resistance combined with
(up from 2nd layer) Cr ~ 6,5 abrasion resistance, including metal to metal friction resistance, and increased working
36 HRC Mo ~ 3,0 temperatures up to 550°C.
(up from 1st layer) Fe Rest
(37-42HRC)
CEWELD 14700: 57-62 HRC C ~ 0,5 E DUR 600 Kb is a basic coated electrode with approximately 130% recovery that
E DUR 600 E Fe8 Mn < 3,0 results in a fine rippled seam surface with excellent impact and wear properties. The
Kb (DIN 8555: E 6-UM-60) Cr ~ 9,0 weld deposit shows a martensitic structure with good high temperature properties and
Mo < 5,0 can resist oxidation up to 800°C. The deposit is heat treatable and offers excellent
V < 2,0 sliding and rolling properties.
W < 2,0
Nb < 10
Fe Rest
CEWELD 14700: 57-62 HRC C ~ 0,7 E DUR 600 AC electrode has a soft but intensive welding character, a fine-structured
E DUR 600 E Fe8 Mn ~ 0,5 seam surface and excellent slag-removal properties.
AC (DIN 8555: E6-UM-60-GP) Si ~ 1,9 Suitable for : Rollers, dredger chains, conveyors, hammers, dredger equipment, mining
Cr ~ 10,0 and earth-moving equipment.
Fe Rest Can be welded on current DC+ and AC
13. HIGH WEAR RESISTANT
CEWELD Sect IX QW-432: F-No. 71 48-50 HRC C ~ 4,5 E DUR 55 is a heavy coated high efficiency hardfacing electrode with 160 % recovery.
E DUR 55 14700: Si ~ 1,0 Suitable for applications subject to strong abrasive wear by minerals.
E Fe7 Mn ~ 1,0
(DIN 8555: E3-UM-50- Cr ~ 25
CKRTZ ) Fe Rest
A 5.13:
E FeCr-A1

1/14