Categories: Material Notes:: Aluminum 295.0-T6, Sand Cast
Categories: Material Notes:: Aluminum 295.0-T6, Sand Cast
Categories: Material Notes:: Aluminum 295.0-T6, Sand Cast
Material Notes:
Key Words:
Vendors:
Physical Properties
Density
Mechanical Properties
Hardness, Brinell
Hardness, Knoop
Hardness, Vickers
Tensile Strength, Ultimate
Tensile Strength, Yield
Elongation at Break
Tensile Modulus
Compressive Yield Strength
Poissons Ratio
Fatigue Strength
Machinability
Shear Modulus
Shear Strength
Electrical Properties
Electrical Resistivity
Thermal Properties
Heat of Fusion
CTE, linear
Processing Properties
Melt Temperature
Solution Temperature
Aging Temperature
Casting Temperature
Data points with the AA note have been provided by the Aluminum Association, Inc. and are NOT
FOR DESIGN.
Composition Notes:
Composition information provided by the Aluminum Association and is not for design.
Metric
2.81 g/cc
Metric
60 - 90
98
85
>= 221 MPa
>= 138 MPa
@Strain 0.200 %
>= 3.0 %
70.0 GPa
170 MPa
0.33
52.0 MPa
@# of Cycles 5.00e+8
70%
25.9 GPa
205 MPa
Metric
0.00000490 ohm-cm
Metric
389 J/g
22.9 µm/m-°C
@Temperature 20.0 - 100 °C
24.8 µm/m-°C
@Temperature 20.0 - 300 °C
0.963 J/g-°C
138 W/m-K
521 - 643 °C
521 °C
643 °C
Metric
677 - 816 °C
513 - 518 °C
152 - 157 °C
677 - 788 °C
Metric
91.3 - 95.3 %
4.0 - 5.0 %
<= 1.0 %
<= 0.03 %
<= 0.35 %
<= 0.05 %
<= 0.15 %
0.70 - 1.5 %
<= 0.25 %
<= 0.35 %
English Comments
0.102 lb/in³ AA; Typical
English Comments
60 - 90 AA; Typical; 500 g load; 10 mm ball
98 Estimated from Brinell Hardness.
85 Estimated from Brinell Hardness.
>= 32000 psi AA
>= 20000 psi AA
@Strain 0.200 %
English Comments
0.00000490 ohm-cm AA; Typical 35% IACS Conductivity
English Comments
167 BTU/lb
12.7 µin/in-°F AA; Typical
@Temperature 68.0 - 212 °F
0.230 BTU/lb-°F
957 BTU-in/hr-ft²-°F AA; Typical at 25°C
970 - 1190 °F AA; Typical
970 °F AA; Typical
1190 °F AA; Typical
English Comments
1250 - 1500 °F
955 - 965 °F hold at temperature for 12 hr; cool in water at 150 to 212°F
305 - 315 °F From solution treated material, hold at temperature for 3 - 5 hours
1250 - 1450 °F
English Comments
91.3 - 95.3 % As remainder
4.0 - 5.0 %
<= 1.0 %
<= 0.03 %
<= 0.35 %
<= 0.05 %
<= 0.15 %
0.70 - 1.5 %
<= 0.25 %
<= 0.35 %