Designation: B 168 – 01 Used in USDOE-NE Standards

Standard Specification
Nickel-Chromium-Iron Alloys (UNS N06600, N06601, N06603,
N06690, N06693, N06025, and N06045) and Nickel-
Chromium-Cobalt-Molybdenum Alloy (UNS N06617) Plate,
Sheet, and Strip1
This standard is issued under the fixed designation B 168; the number immediately following the designation indicates the year of
original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A
superscript epsilon (e) indicates an editorial change since the last revision or reapproval.

This standard has been approved for use by agencies of the Department of Defense.

1. Scope E 18 Test Methods for Rockwell Hardness and Rockwell

1.1 This specification2 covers rolled nickel-chromium-iron Superficial Hardness of Metallic Materials4
alloys (UNS N06600, N06601, N06603, N06690, N06693, E 29 Practice for Using Significant Digits in Test Data to
N06025, and N06045)* and nickel-chromium-cobalt- Determine Conformance with Specifications5
molybdenum alloy (UNS N06617) plate, sheet, and strip. E 38 Methods for Chemical Analysis of Nickel-Chromium
1.2 The values stated in inch-pound units are to be regarded and Nickel-Chromium-Iron Alloys6
as the standard. The values given in parentheses are for E 112 Test Methods for Determining the Average Grain
information only. Size4
1.3 The following precautionary caveat pertains only to the E 140 Hardness Conversion Tables for Metals4
test methods portion, Section 12, of this specification: This E 1473 Test Methods for Chemical Analysis of Nickel,
standard does not purport to address all of the safety concerns, Cobalt, and High-Temperature Alloys7
if any, associated with its use. It is the responsibility of the user F 155 Test Method for Temper of Strip and Sheet Metals for
of this standard to establish appropriate safety and health Electronic Devices (Spring-Back Method)8
practices and determine the applicability of regulatory limita- 2.2 Federal Standards:9
tions prior to use. Fed. Std. No. 102 Preservation, Packaging and Packing
Levels
2. Referenced Documents Fed. Std. No. 123 Marking for Shipment (Civil Agencies)
2.1 ASTM Standards: Fed. Std. No. 182 Continuous Identification Marking of
B 166 Specification for Nickel-Chromium-Iron Alloys Nickel and Nickel-Base Alloys
(UNS N06600, N06601, N06603, N06690, N06693, 2.3 Military Standard:9
N06025, and N06045) and Nickel-Chromium-Cobalt- MIL-STD-129 Marking for Shipment and Storage
Molybdenum Alloy (UNS N06617) Rod, Bar, and Wire3
3. Terminology
B 880 Specification for General Requirements for Chemical
Check Analysis Limits for Nickel, Nickel Alloys and 3.1 Descriptions of Terms Specific to This Standard—The
Cobalt Alloys3 terms given in Table 1 shall apply.
E 8 Test Methods for Tension Testing of Metallic Materials4
4. Ordering Information
E 10 Test Method for Brinell Hardness of Metallic Materi-
als4 4.1 It is the responsibility of the purchaser to specify all
requirements that are necessary for the safe and satisfactory
performance of material ordered under this specification.
Examples of such requirements include, but are not limited to,
1
This specification is under the jurisdiction of ASTM Committee B02 on the following:
Nonferrous Metals and Alloys and is the direct responsibility of Subcommittee 4.1.1 Alloy —Name or UNS number (see Table 2),
B02.07 on Refined Nickel and Cobalt and Their Alloys.
Current edition approved Nov. 10, 2001. Published January 2002. Originally
published as B 168 – 41. Last previous edition B 168 – 00.
2 5
For ASME Boiler and Pressure Code applications, see related Specification Annual Book of ASTM Standards, Vol 14.02.
6
SB-168 in Section II of that Code. Discontinued; see 1989 Annual Book of ASTM Standards, Vol 03.05.
7
* New designation established in accordance with Practice E 527 and SAE Annual Book of ASTM Standards, Vol 03.05.
8
J1086, Practice for Numbering Metals and Alloys (UNS). Discontinued; see 1983 Annual Book of ASTM Standards, Vol 10.04.
3 9
Annual Book of ASTM Standards, Vol 02.04. Available from Standardization Documents Order Desk, Bldg. 4 Section D, 700
4
Annual Book of ASTM Standards, Vol 03.01. Robbins Ave., Philadelphia, PA 19111-5094, Attn: NPODS.

Copyright © ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.

1
 B 168
TABLE 1 Product Description
Product Thickness, in. (mm) Width, in. (mm)
Hot-rolled plateA ⁄ and over (Table 5
3 16 and Table 6) (Table 8)B
Hot-rolled sheetA 0.018 to 0.250 (0.46 to 6.4), incl (Table 7) (Table 10)
Cold-rolled sheetC 0.018 to 0.250 (0.46 to 6.4), incl (Table 7) (Table 10)
Cold-rolled stripC 0.005 to 0.250 (0.13 to 6.4), incl (Table 7) (Table 10)
A
Material 3⁄16 to 1⁄4 in. (4.8 to 6.4 mm), incl, in thickness may be furnished as sheet or plate provided the material meets the specification requirements for the condition
ordered.
B
Hot-rolled plate, in widths 10 in. (254 mm) and under, may be furnished as hot-finished rectangles with sheared or cut edges in accordance with Specification B 166,
provided the mechanical property requirements of this specification are met.
C
Material under 48 in. (1219 mm) in width may be furnished as sheet or strip provided the material meets the specification requirements for the condition ordered.

TABLE 2 Chemical Requirements

Composition Limits, %
Element
Alloy N06600 Alloy N06601 Alloy N06617 Alloy N06690 Alloy N06693 Alloy N06025 Alloy N06045 Alloy N06603
Nickel 72.0 min 58.0–63.0 44.5 min 58.0 min remainderA remainderA 45.0 min remainderA
Chromium 14.0–17.0 21.0–25.0 20.0–24.0 27.0–31.0 27.0–31.0 24.0–26.0 26.0-29.0 24.0–26.0
Cobalt ... ... 10.0–15.0 ... ... ... ...
Molybdenum ... ... 8.0–10.0 ... ... ... ... ...
Niobium ... ... ... ... 0.5–2.5 ... ... ...
Iron 6.0–10.0 remainderA 3.0 max 7.0–11.0 2.5–6.0 8.0–11.0 21.0–25.0 8.0–11.0
Manganese 1.0 max 1.0 max 1.0 max 0.5 max 1.0 max 0.15 max 1.0 max 0.15 max
Aluminum ... 1.0–1.7 0.8–1.5 ... 2.5–4.0 1.8-2.4 ... 2.4-3.0
Carbon 0.15 max 0.10 max 0.05–0.15 0.05 max 0.15 max 0.15–0.25 0.05–0.12 0.20-0.40
Copper 0.5 max 1.0 max 0.5 max 0.5 max 0.5 max 0.1 max 0.3 max 0.50 max
Silicon 0.5 max 0.5 max 1.0 max 0.5 max 0.5 max 0.5 max 2.5-3.0 0.50 max
Sulfur 0.015 max 0.015 max 0.015 max 0.015 max 0.01 max 0.010 max 0.010 max 0.010 max
Titanium ... ... 0.6 max ... 1.0 max 0.1–0.2 0.01-0.25
Phosphorus ... ... ... ... 0.020 max 0.020 max 0.020 max
Zirconium ... ... ... ... 0.01–0.10 0.01–0.10
Yttrium ... ... .. ... 0.05–0.12 0.01–0.15
Boron ... ... 0.006 max ... ... ... ...
Nitrogen ... ... ... ... ... ... ...
Cerium ... ... ... ... ... 0.03–0.09 ...
A
Element shall be determined arithmetically by difference.

4.1.2 ASTM designation, including year of issue, 4.1.10 Purchaser Inspection—If the purchaser wishes to
4.1.3 Condition—See 6.1 and 6.2 and Appendix X1, witness tests or inspection of material at the place of manu-
4.1.4 Finish—Appendix X1, facture, the purchase order must so state indicating which tests
4.1.5 Dimensions—Thickness, width, and length, or inspections are to be witnessed (Section 13).
4.1.6 Quantity,
4.1.7 Optional Requirements: 5. Chemical Composition
4.1.7.1 Sheet and Strip— Whether to be furnished in coil, in
cut straight lengths, or in random straight lengths, 5.1 The material shall conform to the requirements as to
4.1.7.2 Strip—Whether to be furnished with commercial slit chemical composition prescribed in Table 2.
edge, square edge, or round edge, 5.2 If a product (check) analysis is performed by the
4.1.7.3 Plate—Whether to be furnished specially flattened purchaser, the material shall conform to the product (check)
(see 7.7.2); also how plate is to be cut (see 7.2.1 and 7.3.2), analysis variations prescribed in Specification B 880.
4.1.8 Certification— State if certification or a report of test
results is required (Section 15), 6. Mechanical Properties and Other Requirements
4.1.9 Samples for Product (Check) Analysis—Whether
samples for product (check) analysis should be furnished (see 6.1 Mechanical Properties—The material shall conform to
5.2), and the mechanical properties prescribed in Table 3.

TABLE 3 Mechanical Properties for Plate, Sheet, and Strip (All Thicknesses and Sizes Unless Otherwise Indicated)

Elongation in 2 in. or 50 mm
Yield StrengthA (0.2 % offset), min, psi
Condition (Temper) Tensile Strength, min, psi (MPa) Rockwell HardnessB,C
(MPa)
(or 4D), min,%
Hot-Rolled Plate
UNS N06600:
Annealed 80 000 (550) 35 000 (240) 30 ...
As-rolledD,E 85 000 (586) 35 000 (240) 30 ...
UNS N06601:
Annealed 80 000 (550) 30 000 (205) 30 ...

2
 B 168

TABLE 3 Continued
Elongation in 2 in. or 50 mm
Yield StrengthA (0.2 % offset), min, psi
Condition (Temper) Tensile Strength, min, psi (MPa) Rockwell HardnessB,C
(MPa)
(or 4D), min,%
UNS N06603:
Annealed 94 000 (650) 43 000 (300) 25 ...
UNS N06617:
Annealed 95 000 (655) 35 000 (240) 35 ...
UNS N06690:
Annealed 85 000 (586) 35 000 (240) 30 ...
As-rolledD,E 85 000 (586) 35 000 (240) 30 ...
AnnealedF 75 000 (514) 30 000 (206) 30 ...
UNS N06693
Annealed 85 000 (586) 40 000 (275) 30 ...
UNS N06025
Annealed 98 000 (680) 39 000 (270) 30 ...
UNS N06045
Annealed 90 000 (620) 35 000 (240) 35 ...
Hot-Rolled Sheet
UNS N06600:
Annealed 80 000 (550) 35 000 (240) 30 ...
UNS N06601:
Annealed 80 000 (550) 30 000 (205) 30 ...
UNS N06603:
Annealed 94 000 (650) 43 000 (300) 25 ...
UNS N06617:
Annealed 95 000 (655) 35 000 (240) 30 ...
UNS N06690:
Annealed 85 000 (586) 35 000 (240) 30 ...
UNS N06693
Annealed 85 000 (586) 40 000 (275) 30 ...
UNS N06025
Annealed 98 000 (680) 39 000 (270) 30 ...
UNS N06045
Annealed 90 000 (620) 35 000 (240) 35 ...
Cold-Rolled Plate
UNS N06603
Annealed 94 000 (650) 43 000 (300) 25 ...
UNS N06025
Annealed 98 000 (680) 39 000 (270) 30 ...
UNS N06045
Annealed 90 000 (620) 35 000 (240) 35 ...
Cold-Rolled Sheet
UNS N06600:
Annealed 80 000 (550)G 35 000 (240) 30G ...
Hard 125 000 (860)G 90 000 (620) 2G ...
UNS N06601:
Annealed 80 000 (550)G 30 000 (205) 30G ...
UNS N06603:
G
Annealed 94 000 (650) 43 000 (300) 25 ...
UNS N06617:
Annealed 95 000 (655)G 35 000 (240) 25G ...
UNS N06690:
Annealed 85 000 (586)G 35 000 (240) 30G ...
Hard 125 000 (860)G 90 000 (620) 2G ...
UNS N06693
Annealed 85 000 (586) 40 000 (275) 30 ...
UNS N06025
Annealed 98 000 (680) 39 000 (270) 30 ...
UNS N06045
Annealed 90 000 (620) 35 000 (240) 35 ...
Cold-Rolled Strip
UNS N06600:
Annealed 80 000 (550)G 35 000 (240) 30G ...
Skin-hard ... ... ... B 85 to B88
Quarter-hard ... ... ... B 88 to B94
Half-hard ... ... ... B 93 to B98
Three-quarter-hard ... ... ... B 97 to C25
Hard 125 000 (860)G 90 000 (620) 2G ...
Spring ... ... ... C 30 min
UNS N06601:
Annealed 80 000 (550)G 30 000 (205) 30G ...

3
 B 168

TABLE 3 Continued
Elongation in 2 in. or 50 mm
Yield StrengthA (0.2 % offset), min, psi
Condition (Temper) Tensile Strength, min, psi (MPa) Rockwell HardnessB,C
(MPa)
(or 4D), min,%
UNS N06603:
Annealed 94 000 (650) 43 000 (300) 25G ...
UNS N06617:
Annealed 95 000 (655)G 35 000 (240) 30G ...
UNS N06690:
G G
Annealed 85 000 (586) 35 000 (240) 30 ...
Skin-hard ... ... ... B 85 to B88
Quarter-hard ... ... ... B 88 to B94
Half-hard ... ... ... B 93 to B98
Three-quarter-hard ... ... ... B 97 to C25
Hard 125 000 (860)G 90 000 (620) 2G ...
Spring ... ... ... C 30 min
UNS N06693
Annealed 85 000 (586) 40 000 (275) 30 ...
UNS N06025
Annealed 98 000 (680) 39 000 (270) 30 ...
UNS N06045
Annealed 90 000 (620) 35 000 (240) 35 ...
A
Yield strength requirements do not apply to material under 0.020 in. (0.51 mm) in thickness.
B
For Rockwell or equivalent hardness conversions, see Hardness Conversion Tables E140.
C
Caution should be served in using the Rockwell test on thin material, as the results may be affected by specimen thickness. For thicknesses under 0.050 in. (1.3 mm),
the use of the Rockwell superficial or the Vickers hardness test is suggested.
D
As-rolled plate may be given a stress relieving heat treatment subsequent to final rolling.
E
As-rolled plate specified “suitable for hot forming” shall be furnished from heats of known good hot-malleability characteristics (see X1.2.2). There are no applicable
tensile or hardness requirements for such material.
F
Annealed at 1850°F (1010°C) minimum.
G
Not applicable for thickness under 0.010 in. (0.25 mm).

6.2 Deep Drawing and Spinning Quality Sheet and Strip— 7.1.1 Plate—For plate up to 2 in. (50.8 mm), inclusive, in
The material shall conform to the grain size and hardness thickness, the permissible variation under the specified thick-
requirements as prescribed in Table 4. ness and permissible excess in overweight shall not exceed the
6.2.1 The mechanical properties of Table 3 do not apply to amounts prescribed in Table 5.
deep drawing and spinning quality sheet and strip. 7.1.1.1 For use with Table 5, plate shall be assumed to
weigh 0.304 lb/in.3(8.415 g/cm3).
7. Dimensions and Permissible Variations 7.1.2 Plate—For plate over 2 in. (50.8 mm) in thickness, the
7.1 Thickness and Weight: permissible variations over the specified thickness shall not
exceed the amounts prescribed in Table 6.
7.1.3 Sheet and Strip— The permissible variations in thick-
TABLE 4 Grain Size and Hardness for Cold-Rolled, Deep-
Drawing, and Spinning-Quality Sheet and Strip ness of sheet and strip shall be as prescribed in Table 7. The
Calculated
thickness of strip and sheet shall be measured with the
Corresponding micrometer spindle 3⁄8in. (9.5 mm) or more from either edge
Diameter of
Thickness, in. ASTM Rockwell BA,B
(mm)
Average Grain
MicroGrain Hardness, max for material 1 in. (25.4 mm) or over in width and at any place
Section, max, in.
(mm)
Size No. on the strip under 1 in. in width.
Sheet (56 in. (1.42 m) Wide and Under) 7.2 Width or Diameter:
0.050 (1.3) and less 0.0030 (0.075) 4.5 86
Over 0.050 to 0.250 0.0043 (0.110) 3.5 86
7.2.1 Plate—The permissible variations in width of rectan-
(1.3 to 6.4), incl gular plates and diameter of circular plates shall be as
Strip (12 in. (305 mm) Wide and Under)C prescribed in Table 8 and Table 9.
0.005D to 0.010 0.0009 (0.022) 8E 88E
(0.13 to 0.25), 7.2.2 Sheet and Strip— The permissible variations in width
incl for sheet and strip shall be as prescribed in Table 10.
Over 0.010 to 0.125 0.0030 (0.075) 4.5 86
(0.25 to 3.2), incl
7.3 Length:
A
For Rockwell or equivalent hardness conversions, see Hardness Conversion
7.3.1 Sheet and strip of all sizes may be ordered to cut
Tables E140. lengths, in which case a variation of 1⁄8 in. (3.2 mm) over the
B
Caution should be observed in using the Rockwell test on thin material, as the specified length shall be permitted.
results may be affected by specimen thickness. For thicknesses under 0.050 in.
(1.3 mm), the use of the Rockwell superficial or the Vickers hardness test is 7.3.2 Permissible variations in length of rectangular plate
suggested. shall be as prescribed in Table 11.
C
Sheet requirements (above) apply to strip thicknessess over 0.125 in. (3.2
mm), and for all thicknessess of strip over 12 in. (305 mm) in width.
7.4 Straightness:
D
For ductility evaluations for strip under 0.005 in. (0.13 mm) in thickness, the 7.4.1 The edgewise curvature (depth of chord) of flat sheet,
springback test, such as described in Test Method F 155, is often used and the strip, and plate shall not exceed 0.05 in. multiplied by the
manufacturer should be consulted.
E
Accurate grain size and hardness determinations are difficult to make on strip length in feet (0.04 mm multiplied by the length in centime-
under 0.005 in. (0.13 mm) in thickness and are not recommended. tres).

4
 B 168
TABLE 5 Permissible Variations in Thickness and Overweight of Rectangular Plates

NOTE 1—All plates shall be ordered to thickness and not to weight per square foot (cm). No plates shall vary more than 0.01 in. (0.3 mm) under the
thickness ordered, and the overweight of each lotA in each shipment shall not exceed the amount in the table. Spot grinding is permitted to remove surface
imperfections, such spots not to exceed 0.01 in. under the specified thickness.
Permissible Excess in Average WeightB,C per Square Foot of Plates for Widths Given in Inches (Millimetres) Expressed in
Percentage of Nominal Weights

Specified Thickness, 108 to 120 to 132 to 144 to

48 to 60 60 to 72 72 to 84 84 to 96 96 to 108
in. (mm) 120 132 144 160
Under 48 (1220 to (1520 to (1830 to (2130 to (2440 to
(2740 to (3050 to (3350 to (3660 to
(1220) 1520), 1830), 2130), 2440), 2740),
3050), 3350), 3660), 4070),
excl excl excl excl excl
excl excl excl excl
⁄ to 5⁄16 (4.8 to 7.9), excl
3 16 9.0 10.5 12.0 13.5 15.0 16.5 18.0 ... ... ...
⁄ to 3⁄8 (7.9 to 9.5), excl
5 16 7.5 9.0 10.5 12.0 13.5 15.0 16.5 18.0 ... ...
3⁄8 to 7⁄16 (9.5 to 11.1),excl 7.0 7.5 9.0 10.5 12.0 13.5 15.0 16.5 18.0 19.5
7⁄16 to 1⁄2 (11.1 to 12.7), excl 6.0 7.0 7.5 9.0 10.5 12.0 13.5 15.0 16.5 18.0
1⁄2 to 5⁄8 (12.7 to 15.9), excl 5.0 6.0 7.0 7.5 9.0 10.5 12.0 13.5 15.0 16.5
5⁄8 to 3⁄4 (15.9 to 19.1), excl 4.5 5.5 6.0 7.0 7.5 9.0 10.5 12.0 13.5 15.0
3⁄4 to 1 (19.1 to 25.4), excl 4.0 4.5 5.5 6.0 7.0 7.5 9.0 10.5 12.0 13.5
1 to 2 (25.4 to 50.8), incl 4.0 4.0 4.5 5.5 6.0 7.0 7.5 9.0 10.5 12.0
A
The term “lot” applied to this table means all of the plates of each group width and each group thickness.
B
The permissible overweight for lots of circular and sketch plates shall be 25 % greater than the amounts given in this table.
C
The weight of individual plates shall not exceed the nominal weight by more than 11⁄4 times the amount given in the table and Footnote B.

TABLE 6 Permissible Variations in Thickness for Rectangular Plates Over 2 in. (51 mm) in Thickness

NOTE 1—Permissible variation under specified thickness, 0.01 in. (0.3 mm)
Permissible Variations, in. (mm), over Specified Thickness for Widths Given, in. (mm)
60 to 84 84 to 120 120 to 132
Specified Thickness, in. (mm) To 36 (915), 36 to 60 (915 132 (3350)
(1520 to (2130 to (3050 to
excl to 1520), excl and over
2130), excl 3050), excl 3350), excl
Over 2 to 3 (51 to 76), excl ⁄
1 16 (1.6) 3⁄32 (2.4) 7⁄64 (2.8) 1⁄8 (3.2) 1⁄8 (3.2) ⁄
9 64 (3.6)
3 to 4 (76 to 102), incl ⁄
5 64 (2.0) 3⁄32 (2.4) 7⁄64 (2.8) 1⁄8 (3.2) 1⁄8 (3.2) ⁄
9 64 (3.6)

7.4.2 Straightness for coiled material is subject to agree- 8. Workmanship, Finish, and Appearance
ment between the manufacturer and the purchaser. 8.1 The material shall be uniform in quality and temper,
7.5 Edges: smooth, commercially straight or flat, and free of injurious
7.5.1 When finished edges of strip are specified in the imperfections.
contract or order, the following descriptions shall apply: 8.2 Sheet, Strip, and Plate—Sheet, strip, and plate supplied
7.5.1.1 Square-edge strip shall be supplied with finished in the conditions and finishes as listed in the appendix may be
edges, with sharp, square corners, without bevel or rounding. ground or machined to remove surface imperfections, provided
7.5.1.2 Round-edge strip shall be supplied with finished such removal does not reduce the material below the minimum
edges, semicircular in form, the diameter of the circle forming specified dimensions. Surface eliminated depressions shall be
the edge being equal to the strip thickness. faired smoothly into the surrounding material. The removal of
7.5.1.3 When no description of any required form of strip a surface imperfection shall be verified by the method origi-
edge is given, it shall be understood that edges such as those nally used to detect the imperfection.
resulting from slitting or shearing will be acceptable.
7.5.1.4 Sheet shall have sheared or slit edges. 9. Sampling
7.5.1.5 Plate shall have sheared or cut (machined, abrasive- 9.1 Lot—Definition:
cut, powder-cut, or inert-arc cut) edges, as specified. 9.1.1 A lot for chemical analysis shall consist of one heat.
7.6 Squareness (Sheet)—For sheets of all thicknesses, the 9.1.2 A lot for mechanical properties, hardness, and grain
angle between adjacent sides shall be 90 6 0.15° (1⁄16in. in 24 size testing shall consist of all material from the same heat,
in. (1.6 mm in 610 mm)). nominal thickness, and condition.
7.7 Flatness: 9.1.2.1 Where material cannot be identified by heat, a lot
7.7.1 There shall be no flatness requirements for “deep- shall consist of not more than 500 lb (227 kg) of material in the
drawing quality,” “spinning quality,” or “as rolled” sheet and same thickness and condition, except for plates weighing over
strip (see X1.4). 500 lb, in which case only one specimen shall be taken.
7.7.2 Standard flatness tolerances for plate shall conform to 9.2 Test Material Selection:
the requirements of Table 12. “Specially flattened” plate, when 9.2.1 Chemical Analysis—Representative samples from
so specified, shall have permissible variations in flatness as each lot shall be taken during pouring or subsequent process-
agreed upon between the manufacturer and the purchaser. ing.

5
 B 168
TABLE 7 Permissible Variations in Thickness of Sheet and Strip
(Permissible Variations, Plus and Minus, in Thickness, in. (mm), for Widths Given in in. (mm))
SheetA
Hot-Rolled Cold-Rolled
Specified Thickness, in. (mm)
Over 48 to 60 Over 48 to 60
48 (1220) 48 (1220)
(1220 to 1520), (1220 to 1520),
and Under and Under
incl incl
0.018 to 0.025 (0.5 to 0.6), incl 0.003 (0.08) 0.004 (0.10) 0.002 (0.05) 0.003 (0.08)
Over 0.025 to 0.034 (0.6 to 0.9), incl 0.004 (0.10) 0.005 (0.13) 0.003 (0.08) 0.004 (0.10)
Over 0.034 to 0.043 (0.9 to 1.1), incl 0.005 (0.13) 0.006 (0.15) 0.004 (0.10) 0.005 (0.13)
Over 0.043 to 0.056 (1.1 to 1.4), incl 0.005 (0.13) 0.006 (0.15) 0.004 (0.10) 0.005 (0.13)
Over 0.056 to 0.070 (1.4 to 1.8), incl 0.006 (0.15) 0.007 (0.18) 0.005 (0.13) 0.006 (0.15)
Over 0.070 to 0.078 (1.8 to 1.9), incl 0.007 (0.18) 0.008 (0.20) 0.006 (0.15) 0.007 (0.18)
Over 0.078 to 0.093 (1.9 to 2.4), incl 0.008 (0.20) 0.009 (0.23) 0.007 (0.18) 0.008 (0.20)
Over 0.093 to 0.109 (2.4 to 2.8), incl 0.009 (0.23) 0.010 (0.25) 0.007 (0.18) 0.009 (0.23)
Over 0.109 to 0.125 (2.8 to 3.2), incl 0.010 (0.25) 0.012 (0.31) 0.008 (0.20) 0.010 (0.25)
Over 0.125 to 0.140 (3.2 to 3.6), incl 0.012 (0.31) 0.014 (0.36) 0.008 (0.20) 0.010 (0.25)
Over 0.140 to 0.171 (3.6 to 4.3), incl 0.014 (0.36) 0.016 (0.41) 0.009 (0.23) 0.012 (0.31)
Over 0.171 to 0.187 (4.3 to 4.8), incl 0.015 (0.38) 0.017 (0.43) 0.010 (0.25) 0.013 (0.33)
Over 0.187 to 0.218 (4.8 to 5.5), incl 0.017 (0.43) 0.019 (0.48) 0.011 (0.28) 0.015 (0.38)
Over 0.218 to 0.234 (5.5 to 5.9), incl 0.018 (0.46) 0.020 (0.51) 0.012 (0.31) 0.016 (0.41)
Over 0.234 to 0.250 (5.9 to 6.4), incl 0.020 (0.51) 0.022 (0.56) 0.013 (0.33) 0.018 (0.46)
Cold-Rolled StripA,B
Specified Thickness, in. (mm) Widths 12 in. (305 mm) and under, plus and minus

Up to 0.050 (1.27), incl 0.0015 (0.038)

Over 0.050 to 0.093 (1.27 to 2.39), incl 0.0025 (0.063)
Over 0.093 to 0.125 (2.39 to 3.18), incl 0.004 (0.11)
A
Measured 3⁄8in. (9.5 mm) or more from either edge except for strip under 1 in. (25.4 mm) in width which is measured at any place.
B
Standard sheet tolerances apply for thicknesses over 0.125 in. (3.2 mm) and for all thicknesses of strip over 12 in. (305 mm) wide.

9.2.1.1 Product (Check) Analysis shall be wholly the re- 11.3.2 The largest possible round specimen shown in Test
sponsibility of the purchaser. Methods E 8 for material 1⁄2 in. (12.7 mm) and over.
9.2.2 Mechanical Properties, Hardness, and Grain Size—
Samples of the material to provide test specimens for mechani- 12. Test Methods
cal properties, hardness, and grain size shall be taken from such 12.1 The chemical composition, mechanical, and other
locations in each lot as to be representative of that lot. properties of the material as enumerated in this specification
shall be determined, in case of disagreement, in accordance
10. Number of Tests with the following methods:
10.1 Chemical Analysis—One test per lot. Test ASTM Designation
10.2 Mechanical Properties—One test per lot.
10.3 Hardness—One test per lot. (Required only as speci- Chemical Analysis E 38,A E 1473
Tension E8
fied in Table 3 and Table 4.) Brinell hardness E 10
10.4 Grain Size—One test per lot. (Required only as speci- Rockwell hardness E 18
fied in Table 4.) Hardness conversion E 140
Grain size E 112
Rounding procedure E 29
11. Specimen Preparation Spring-back F 155
11.1 Tension test specimens shall be taken from material in A
Methods E 38 are to be used only for elements not covered by Test Methods
the final condition (temper) and tested transverse to the E 1473.
direction of rolling when width will permit. 12.2 The measurement of average grain size may be carried
11.2 Tension test specimens shall be any of the standard or out by the planimetric method, the comparison method, or the
subsize specimens shown in Test Methods E 8. intercept method described in Test Methods E 112. In case of
11.3 In the event of disagreement, referee specimens shall dispute, the referee method for determining average grain size
be as follows: shall be the planimetric method.
11.3.1 Full thickness of the material, machined to the form 12.3 For purposes of determining compliance with the
and dimensions shown for the sheet-type specimen in Test specified limits for requirements of the properties listed in the
Methods E 8 for material under 1⁄2in. (12.7 mm) in thickness. following table, an observed value or a calculated value shall

6
 B 168
TABLE 8 Permissible variationsA of Sheared, Plasma-Torch-Cut, and Abrasive-Cut Rectangular PlateB,C
Permissible Variations in Widths for Widths Given, in. (mm)
Up to 30 (760), Over 30 to 72 Over 72 to 108 Over 108 to 144 Over 144 to 160
Specified Thickness incl (760 to 1830), (1830 to 2740), (2740 to 3660), (3660 to 4070),
incl incl incl incl
+ − + − + − + − + −
Inches
Sheared:D
3⁄16 to 5⁄16, excl ⁄
3 16 ⁄
18 ⁄
14 ⁄
18 ⁄
38 ⁄
18 ⁄
12 ⁄
18 ... ...
5⁄16 to 1⁄2, excl ⁄
14 ⁄
18 ⁄
38 ⁄
18 ⁄
38 ⁄
18 ⁄
12 ⁄
18 ⁄
58 ⁄
18

1⁄2 to 3⁄4, excl 3⁄8 1⁄8 3⁄8 1⁄8 1⁄2 1⁄8 5⁄8 1⁄8 3⁄4 1⁄8

3⁄4 to 1, excl 1⁄2 1⁄8 1⁄2 1⁄8 5⁄8 1⁄8 3⁄4 1⁄8 7⁄8 1⁄8

1 to 11⁄4, incl 5⁄8 1⁄8 5⁄8 1⁄8 3⁄4 1⁄8 7⁄8 1⁄8 1 1⁄8

Abrasive cut:E,F
3⁄16 to 11⁄4, incl 18 ⁄ ⁄
18 18 ⁄ ⁄
18 18 ⁄ ⁄
18 18 ⁄ 18 ⁄ 18 ⁄ ⁄
18

Over 11⁄4 to 23⁄4, incl ⁄

3 16 ⁄
18 ⁄
3 16 ⁄
18 ⁄
3 16 ⁄
18 ⁄
3 16 18 ⁄ ⁄
3 16 ⁄
18

Plasma-torch-cut:G
3⁄16 to 2, excl 12 ⁄ 0 12 ⁄ 0 12 ⁄ 0 12 ⁄ 0 12 ⁄ 0
2 to 3, incl 58 ⁄ 0 58 ⁄ 0 58 ⁄ 0 58 ⁄ 0 58 ⁄ 0
Millimetres
Sheared:D
4.8 to 7.9, excl 4.8 3.2 6.4 3.2 9.5 3.2 12.7 3.2 ... ...
7.9 to 12.7, excl 6.4 3.2 9.5 3.2 9.5 3.2 12.7 3.2 15.9 3.2
12.7 to 19.1, excl 9.5 3.2 9.5 3.2 12.7 3.2 15.9 3.2 19.1 3.2
19.1 to 25.4, excl 12.7 3.2 12.7 3.2 15.8 3.2 19.1 3.2 22.2 3.2
25.4 to 31.8, incl 15.9 3.2 15.9 3.2 19.1 3.2 22.2 3.2 25.4 3.2
Abrasive cut:E,F
4.8 to 31.8, incl 3.2 3.2 3.2 3.2 3.2 3.2 3.2 3.2 3.2 3.2
Over 31.8 to 4.8 3.2 4.8 3.2 4.8 3.2 4.8 3.2 4.8 3.2
69.8, incl
Plasma-torch-cut:G
4.8 to 50.8, excl 12.7 0 12.7 0 12.7 0 12.7 0 12.7 0
50.8 to 76.2, incl 15.9 0 15.9 0 15.9 0 15.9 0 15.9 0

A
Permissible variations in width for powder- or inert-arc-cut plate shall be as agreed upon between the manufacturer and the purchaser.
B
Permissible variations in machined, powder-, or inert-arc-cut circular plate shall be as agreed upon between the manufacturer and the purchaser.
C
Permissible variations in plasma-torch-cut sketch plates shall be as agreed upon between the manufacturer and the purchaser.
D
The minimum sheared width is 10 in. (254 mm) for material 3⁄4in. (19.1 mm) and under in thickness and 20 in. (508 mm) for material over 3⁄4 in. (19.1 mm) in thickness.
E
The minimum abrasive-cut width is 2 in. (50.8 mm) and increases to 4 in. (101.6 mm) for thicker plates.
F
These tolerances are applicable to lengths of 240 in. (6100 mm), max. For lengths over 240 in., an additional 1⁄16 in. (1.6 mm) is permitted, both plus and minus.
G
The tolerance spread shown for plasma-torch cutting may be obtained all on the minus side, or divided between the plus and minus side if so specified by the
purchaser.

TABLE 9 Permissible Variations in Diameter for Circular Plates

Sheared Plate
Permissible Variations over Specified Diameter for
Specified Diameter, in. (mm) Thickness Given, in. (mm)A
To 3⁄8 ( 9.5), incl
20 to 32 (508 to 813), excl 1⁄4 (6.4)

32 to 84 (813 to 2130), excl 5⁄16 (7.9)

84 to 108 (2130 to 2740), excl 3⁄8 (9.5)

108 to 140 (2740 to 3580), incl 7⁄16 (11.1)

Plasma-Torch-Cut PlateB
Permissible Variations in Specified Diameter for Thickness Given, in. (mm)C
Specified Diameter, in. (mm) Thickness, max, ⁄
3 16 to 2 (4.8 to 50.8), excl 2 to 3 (50.8 to 76.2), incl
in. (mm) + − + −
19 to 20 (483 to 508), excl 3 (76.2) ⁄ (12.7)
12 0 ⁄ (15.9)
58 0
20 to 22 (508 to 559), excl 23⁄4 (69.8) 1⁄2 (12.7) 0 5⁄8 (15.9) 0
22 to 24 (559 to 610), excl 21⁄2 (63.5) 1⁄2 (12.7) 0 5⁄8 (15.9) 0
24 to 28 (610 to 711), excl 21⁄4 (57.3) 1⁄2 (12.7) 0 5⁄8 (15.9) 0
28 to 32 (711 to 812), excl 2 (50.8) 1⁄2 (12.7) 0 5⁄8 (15.9) 0
32 to 34 (812 to 864), excl 13⁄4 (44.5) 1⁄2 (12.7) 0 ... ...
34 to 38 (864 to 965), excl 11⁄2 (38.1) 1⁄2 (12.7) 0 ... ...
38 to 40 (965 to 1020), excl 11⁄4 (31.8) 1⁄2 (12.7) 0 ... ...
40 to 140 (1020 to 3560), incl 3 (76.2) 1⁄2 (12.7) 0 5⁄8 (15.9) 0
A
No permissible variations under.
B
Permissible variations in plasma-torch-cut sketch plates shall be as agreed upon between the manufacturer and the purchaser.
C
The tolerance spread shown may also be obtained all on the minus side or divided between the plus and minus sides if so specified by the purchaser.

7
 B 168
TABLE 10 Permissible Variations in Width of Sheet and Strip
Permissible Variations in Specified Width, in. (mm)
Specified Thickness, in. (mm) Specified Width, in. (mm)
+ −
Sheet
Up to 0.250 (6.35) all 0.125 (3.18) 0
A
Strip
Under 0.075 (1.9) Up to 12 (305), incl 0.007 (0.18) 0.007 (0.18)
Over 12 to 48 (305 to 1219), incl 0.062 (1.6) 0
0.075 to 0.100 (1.9 to 2.5), incl Up to 12 (305), incl 0.009 (0.23) 0.009 (0.23)
Over 12 to 48 (305 to 1219), incl 0.062 (1.6) 0
Over 0.100 to 0.125 (2.5 to 3.2), incl Up to 12 (305), incl 0.012 (0.30) 0.012 (0.30)
Over 12 to 48 (305 to 1219), incl 0.062 (1.6) 0
Over 0.125 to 0.160 (3.2 to 4.1), incl Up to 12 (305), incl 0.016 (0.41) 0.016 (0.41)
Over 12 to 48 (305 to 1219), incl 0.062 (1.6) 0
Over 0.160 to 0.187 (4.1 to 4.7), incl Up to 12 (305), incl 0.020 (0.51) 0.020 (0.51)
Over 12 to 48 (305 to 1219), incl 0.062 (1.6) 0
Over 0.187 to 0.250 (4.7 to 6.4), incl Up to 12 (305), incl 0.062 (1.6) 0.062 (1.6)
Over 12 to 48 (305 to 1219), incl 0.062 (1.6) 0.062 (1.6)
A
Rolled round or square-edge strip in thicknesses of 0.071 to 0.125 in. (1.80 to 3.18 mm), incl, in widths 3 in. (76.2 mm) and under, shall have permissible width
variations of 60.005 in. (60.13 mm). Permissible variations for other sizes shall be as agreed upon between the manufacturer and the purchaser.

TABLE 11 Permissible Variations in LengthA of Sheared, Plasma-Torch-Cut,B and Abrasive-Cut Rectangular PlateC
Permissible Variation in Length for Lengths Given, in. (mm)
Over 60 to 96 Over 96 to 120 Over 120 to 240 Over 240 to 360 Over 360 to 450 Over 450 to 540
Up to 60 Over 540
Specified Thickness (1520 to 2440), (2440 to 3050), (3050 to 6096), (6096 to 9144), (9144 to (11 430 to
(1520), incl (13 716)
incl incl incl incl 11 430), incl 13 716), incl
+ − + − + − + − + − + − + − + −
Inches
Sheared:D
3⁄16 to 5⁄16, excl ⁄
3 16 ⁄
18 ⁄
14 ⁄
18 ⁄
38 ⁄
18 ⁄
12 ⁄
18 ⁄
58 ⁄
18 ⁄
34 ⁄
18 ⁄
78 ⁄
18 ... ...
5⁄16 to 1⁄2, excl ⁄
38 ⁄
18 ⁄
12 ⁄
18 ⁄
12 ⁄
18 ⁄
12 ⁄
18 ⁄
58 ⁄
18 ⁄
34 ⁄
18 ⁄
78 ⁄
18 1 ⁄
18

1⁄2 to 3⁄4, excl 1⁄2 1⁄8 1⁄2 1⁄8 5⁄8 1⁄8 5⁄8 1⁄8 3⁄4 1⁄8 7⁄8 1⁄8 11⁄8 1⁄8 13⁄8 1⁄8

3⁄4 to 1, excl 5⁄8 1⁄8 5⁄8 1⁄8 5⁄8 1⁄8 3⁄4 1⁄8 7⁄8 1⁄8 11⁄8 1⁄8 13⁄8 1⁄8 15⁄8 1⁄8

1 to 11⁄4, incl 3⁄4 1⁄8 3⁄4 1⁄8 3⁄4 1⁄8 7⁄8 1⁄8 11⁄8 1⁄8 13⁄8 1⁄8 15⁄8 1⁄8 ... ...
Abrasive-cut:E
3⁄16 to 11⁄4, incl 18 ⁄ ⁄
18 18 ⁄ ⁄
18 18 ⁄ ⁄
18 18 ⁄ ⁄
18 18 ⁄ 18⁄ 18 ⁄ ⁄
18 ... ... ... ...
Over 11⁄4 to 2 ⁄
3 16 ⁄
18 ⁄
3 16 ⁄
18 ⁄
3 16 ⁄
18 ⁄
3 16 ⁄
18 ⁄
3 16 18⁄ ⁄
3 16 ⁄
18 ... ... ... ...
3⁄4, incl

Plasma torch-cut:F
3⁄16 to 2, excl 12 ⁄ 0 12 ⁄ 0 12 ⁄ 0 12 ⁄ 0 12 ⁄ 0 12 ⁄ 0 ⁄
12 0 ⁄
12 0
2 to 3, incl 58 ⁄ 0 58 ⁄ 0 58 ⁄ 0 58 ⁄ 0 58 ⁄ 0 58 ⁄ 0 ⁄
58 0 ⁄
58 0
Millimetres
Sheared:D
4.8 to 7.9, excl 4.8 3.2 6.4 3.2 9.5 3.2 12.7 3.2 15.9 3.2 19.0 3.2 22.2 3.2 ... ...
7.94 to 12.7, excl 9.5 3.2 12.7 3.2 12.7 3.2 12.7 3.2 15.9 3.2 19.0 3.2 22.2 3.2 25.4 3.2
12.7 to 19.0, excl 12.7 3.2 12.7 3.2 15.9 3.2 15.9 3.2 19.0 3.2 22.2 3.2 28.6 3.2 34.9 3.2
19.0 to 25.4, excl 15.9 3.2 15.9 3.2 15.9 3.2 19.0 3.2 22.2 3.2 28.6 3.2 34.9 3.2 41.3 3.2
25.4 to 31.8, incl 19.0 3.2 19.0 3.2 19.0 3.2 22.2 3.2 28.6 3.2 34.9 3.2 41.3 3.2 ... ...
Abrasive-cut:E
4.8 to 31.8, incl 3.2 3.2 3.2 3.2 3.2 3.2 3.2 3.2 3.2 3.2 3.2 3.2 ... ... ... ...
Over 31.8 to 69.9, 4.8 3.2 4.8 3.2 4.8 3.2 4.8 3.2 4.8 3.2 4.8 3.2 ... ... ... ...
incl
Plasma torch-cut:F
4.8 to 50.8, excl 12.7 0 12.7 0 12.7 0 12.7 0 12.7 0 12.7 0 12.7 0 12.7 0
50.8 to 76.2, incl 15.9 0 15.9 0 15.9 0 15.9 0 15.9 0 15.9 0 15.9 0 15.9 0
A
Permissible variations in length for powder- or inert-arc-cut plate shall be agreed upon between the manufacturer and the purchaser.
B
The tolerance spread shown for plasma-torch-cutting may be obtained all on the minus side, or divided between the plus and minus sides if so specified by the
purchaser.
C
Permissible variations in machined, powder- or inert-arc-cut circular plate shall be as agreed upon between the manufacturer and the purchaser.
D
The minimum sheared length is 10 in. (254 mm).
E
Abrasive cut applicable to a maximum length of 144 to 400 in. (3658 to 10 160 mm) depending on the thickness and width ordered.
F
The tolerance spread shown for plasma-torch-cut sketch plates shall be as agreed upon between the manufacturer and the purchaser.

8
 B 168
TABLE 12 Permissible Variations from Flatness of Rectangular, Circular, and Sketch Plates

NOTE 1—Permissible variations apply to plates up to 12 ft (3660 mm) in length, or to any 12 ft (3660 mm) of longer plates.
NOTE 2—If the longer dimension is under 36 in. (914 mm), the permissible variation is not greater than 1⁄4 in. (6.4 mm).
NOTE 3—The shorter dimension specified is considered the width, and the permissible variation in flatness across the width does not exceed the tabular
amount of that dimension.
NOTE 4—The maximum deviation from a flat surface does not customarily exceed the tabular tolerance for the longer dimension specified.
Permissible Variations from a Flat Surface for Thickness and Widths Given, in. (mm)
48 to 60 60 to 72 72 to 84 84 to 96 96 to 108 108 to 120 120 to 144
Specified Thickness To 48 144
(1220 to (1520 to (1830 to (2130 to (2440 to (2740 to (3050 to
(1220), (3660),
1520), 1830), 2130), 2440), 2740), 3050), 3660),
excl and over
excl excl excl excl excl excl excl
Inches
⁄ to ⁄ , excl
3 16 14 ⁄
34 1⁄
1 16 1⁄14 1⁄
38 15⁄8 15⁄8 ... ... ...
⁄ to 3⁄8, excl
14 11 16⁄ 3⁄4 15⁄16 11⁄8 13⁄8 17⁄16 19⁄16 17⁄8 ...
3⁄8 to 1⁄2, excl ⁄
12 9⁄16 11⁄16 3⁄ 4 15⁄16 11⁄8 11⁄4 17⁄16 13⁄4
1⁄2 to 3⁄4, excl ⁄
12 9⁄16 5⁄8 5⁄8 13⁄16 11⁄8 11⁄8 11⁄8 13⁄8
3⁄4 to 1, excl 1⁄2 9⁄16 5⁄8 5⁄8 3⁄4 13⁄16 15⁄16 1 11⁄8
1 to 2, excl 1⁄2 9⁄16 9⁄16 9⁄16 11⁄16 11⁄16 11⁄16 3⁄4 1
2 to 4, incl 1⁄4 5⁄16 3⁄8 7⁄16 1⁄2 9⁄16 5⁄8 3⁄4 7⁄8

Millimetres
4.8 to 6.4, excl 19.0 27.0 31.8 34.9 41.3 41.3 ... ... ...
6.4 to 9.5, excl 17.5 19.0 23.8 28.6 34.9 36.5 39.7 47.6 ...
9.5 to 12.7, excl 12.7 14.3 17.5 19.0 23.8 28.6 31.8 36.5 44.4
12.7 to 19.0, excl 12.7 14.3 15.9 15.9 20.6 28.6 28.6 28.6 34.9
19.0 to 25.4, excl 12.7 14.3 15.9 15.9 19.0 20.6 23.8 25.4 28.6
25.4 to 50.8, excl 12.7 14.3 14.3 14.3 17.5 17.5 17.5 19.0 25.4
50.8 to 101.6, incl 6.4 7.9 9.5 11.1 12.7 14.3 15.9 19.0 22.2

be rounded as indicated in accordance with the rounding to the producer or supplier promptly and in writing. In case of
method of Practice E 29. dissatisfaction with the results of the test, the producer or
Test Rounded Unit for Observed supplier may make claim for a rehearing.
Or Calculated Value

Chemical composition, nearest unit in the last right-

15. Certification
hardness, and toler- hand place of figures of the 15.1 When specified in the purchase order or contract, a
ances (when ex- specified limit. If two choices
pressed in decimals) are possible, as when the digits
manufacturer’s certification shall be furnished to the purchaser
dropped are exactly a 5, or a stating that material has been manufactured, tested, and in-
5 followed only by zeros, spected in accordance with this specification, and that the test
choose the one ending in an
even digit, with zero defined results on representative samples meet specification require-
as an even digit. ments. When specified in the purchase order or contract, a
Tensile strength and nearest 1000 psi (6.9 MPa) report of the test results shall be furnished.
yield strength
Elongation nearest 1 %
Grain Size: 16. Product Marking
0.0024 in. (0.060 mm) nearest multiple of 0.0002 in.
or larger (0.005 mm) 16.1 Each bundle or shipping container shall be marked
less than 0.0024 in. nearest multiple of 0.0001 with the name of the material or UNS number; condition
(0.060 mm) in. (0.002 mm) (temper); this specification number; the size; gross, tare, and
13. Inspection net weight; consignor and consignee address; contract or order
13.1 Inspection of the material shall be made as agreed upon number; or such other information as may be defined in the
between the manufacturer and the purchaser as part of the contract or order.
purchase contract.
17. Keywords
14. Rejection and Rehearing 17.1 plate; sheet; strip; UNS N06025; UNS N06045; UNS
14.1 Material that fails to conform to the requirements of N06600; UNS N06601; UNS N06603; UNS N06617; UNS
this specification may be rejected. Rejection should be reported N06690; UNS N06693

9
 B 168
SUPPLEMENTARY REQUIREMENTS

The following supplementary requirements shall apply only when specified by the purchaser in the
inquiry, contract, or order, for agencies of the U. S. Government.

S1. Referenced Documents S4. Preparation for Delivery

S1.1 The following documents of the issue in effect on date S4.1 Preservation, Packaging, Packing:
of material purchased form a part of this specification to the S4.1.1 Military Agencies—The material shall be separated
extent referenced herein: Federal Standards 102, 123, and 182
by size, composition, grade, or class and shall be preserved and
and Military Standard MIL-STD-129.
packaged, Level A or C or packed, Level A, B, or C as specified
S2. Quality Assurance in the contract or purchase order.
S2.1. Responsibility for Inspection—Unless otherwise S4.1.2 Civil Agencies—The requirements of Fed. Std. No.
specified in the contract or purchase order, the manufacturer is 102 shall be referenced for definitions of the various levels of
responsible for the performance of all inspection and test packaging protection.
requirements specified. Except as otherwise specified in the S4.2 Marking:
contract or purchase order, the manufacturer may use his own
S4.2.1 Military Agencies—In addition to any special mark-
or any other suitable facilities for the performance of the
ing required by the contract or purchase order, marking for
inspection and test requirements unless disapproved by the
shipment shall be in accordance with MIL-STD-129.
purchaser at the time the order is placed. The purchaser shall
have the right to perform any of the inspections or tests set S4.2.2 Civil Agencies—In addition to any special marking
forth when such inspections and tests are deemed necessary to required by the contract or purchase order, marking for
ensure that the material conforms to prescribed requirements. shipment shall be in accordance with Fed. Std. No. 123.
S3. Identification Marking
S3.1 All material shall be properly marked for identification
in accordance with Fed. Std. No. 182, except that the ASTM
specification number and the alloy number shall be used.

APPENDIX

(Nonmandatory Information)

X1. CONDITIONS AND FINISHES

X1.1 Scope X1.4 Sheet, Hot-Rolled

X1.1.1 This appendix lists the conditions and finishes in X1.4.1 Annealed and Pickled—Soft with a pickled matte
which plate, sheet, and strip are normally supplied. These are finish. Properties similar to X1.5.1 but with broader thickness
subject to change, and the manufacturer should be consulted tolerances. Not suggested for applications where the finish of a
for the latest information available. cold-rolled sheet is considered essential, or for deep drawing or
X1.2 Plate, Hot-Rolled spinning.
X1.2.1 Annealed—Soft with an oxide surface, and suitable
for heavy cold forming. Available with a descaled surface, X1.5 Sheet and Strip, Cold-Rolled
when so specified. X1.5.1 Annealed—Soft with a pickled or bright annealed
X1.2.2 As-Rolled—With an oxide surface. Available with a finish.
descaled surface, when so specified. Suitable for flat work, X1.5.2 Deep-Drawing or Spinning Quality——Similar to
mild forming, or tube sheets. When intended for tube sheets, X1.5.1, except furnished to controlled hardness and grain size
specify that plates are to be specially flattened. When intended and lightly leveled.
for hot forming, this should be indicated on the purchase order
so that the manufacturer may select appropriate material. X1.5.3 Skin-Hard—Similar to X1.5.1, but given a light cold
reduction to hardness range shown in Table 3.
X1.3 Plate, Cold–Rolled X1.5.4 Quarter-Hard— Cold rolled to the hardness range
X1.3.1 Annealed—Soft with an oxide surface; available in a indicated in Table 3, bright finish. Out-of-flatness must be
descaled surface when so specified. expected and will vary with temper and thickness.

10
 B 168
X1.5.5 Half-Hard—Cold rolled to the hardness range indi- X1.5.7 Hard—Cold rolled to the tensile requirements indi-
cated in Table 3, bright finish. Out-of-flatness must be expected cated in Table 3, bright finish. Out-of-flatness must be expected
and will vary with temper and thickness. and will vary with temper and thickness.
X1.5.6 Three-Quarter Hard—Cold rolled to the hardness X1.5.8 Spring Temper— Cold rolled to the minimum hard-
range indicated in Table 3, bright finish. Out-of-flatness must ness indicated in Table 3, bright finish. Out-of-flatness must be
be expected and will vary with temper and thickness. expected and will vary with temper and thickness.

ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned
in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk
of infringement of such rights, are entirely their own responsibility.

This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the
responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should
make your views known to the ASTM Committee on Standards, at the address shown below.

This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,
United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above
address or at 610-832-9585 (phone), 610-832-9555 (fax), or service@astm.org (e-mail); or through the ASTM website
(www.astm.org).

11