    Chi Mei Polylac® PA-757 ABS

    Uploaded by

    nayeemhumayun
    This document provides information on the properties of Chi Mei Polylac® PA-757 ABS. It lists various physical, mechanical, and thermal properties. Key properties include a density of 1.05 g/cc, tensile strength of 37.0 MPa, flexural strength of 76.0 MPa, and Vicat softening point of 100°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Chi Mei Polylac® PA-757 ABS

    Uploaded by

    nayeemhumayun
    142 views1 page
    This document provides information on the properties of Chi Mei Polylac® PA-757 ABS. It lists various physical, mechanical, and thermal properties. Key properties include a density of 1.05 g/cc, tensile strength of 37.0 MPa, flexural strength of 76.0 MPa, and Vicat softening point of 100°C.

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides information on the properties of Chi Mei Polylac® PA-757 ABS. It lists various physical, mechanical, and thermal properties. Key properties include a density of 1.05 g/cc, tensile strength of 37.0 MPa, flexural strength of 76.0 MPa, and Vicat softening point of 100°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    142 views1 page

    Chi Mei Polylac® PA-757 ABS

    Uploaded by

    nayeemhumayun
    This document provides information on the properties of Chi Mei Polylac® PA-757 ABS. It lists various physical, mechanical, and thermal properties. Key properties include a density of 1.05 g/cc, tensile strength of 37.0 MPa, flexural strength of 76.0 MPa, and Vicat softening point of 100°C.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    You are on page 1of 1

    5/12/24, 4:11 PM Chi Mei Polylac® PA-757 ABS

    Chi Mei Polylac® PA-757 ABS


    Categories: Polymer; Thermoplastic; ABS Polymer; Acrylonitrile Butadiene Styrene (ABS), Molded

    Material High gloss, medium impact


    Notes:
    Vendors: No vendors are listed for this material. Please click here if you are a supplier and would like information
    on how to add your listing to this material.

    Physical Properties Metric English Comments


    Density 1.05 g/cc 0.0379 lb/in³ ISO 1183
    Linear Mold Shrinkage 0.0030 - 0.0070 cm/cm 0.0030 - 0.0070 in/in ASTM D955
    Melt Flow 1.8 g/10 min 1.8 g/10 min ASTM D1238
    @Load 5.00 kg, @Load 11.0 lb,
    Temperature 200 °C Temperature 392 °F
    22 g/10 min 22 g/10 min ISO-1133
    @Load 10.0 kg, @Load 22.0 lb,
    Temperature 220 °C Temperature 428 °F

    Mechanical Properties Metric English Comments


    Hardness, Rockwell R 116 116 ASTM D785
    Ball Indentation Hardness 110 MPa 16000 psi H358/30; ISO 2039-1
    Tensile Strength at Break 37.0 MPa 5370 psi 50 mm/min; ISO 527
    Tensile Strength, Yield 54.0 MPa 7830 psi 50 mm/min; ISO 527
    Elongation at Break 20 % 20 % 50 mm/min; ISO 527
    Flexural Strength 76.0 MPa 11000 psi 2 mm/min; ISO 178
    Flexural Modulus 2.20 GPa 319 ksi 2 mm/min; ISO 178
    Izod Impact, Notched 1.83 J/cm 3.43 ft-lb/in ASTM D256
    @Thickness 6.35 mm @Thickness 0.250 in
    2.05 J/cm 3.84 ft-lb/in ASTM D256
    @Thickness 3.17 mm @Thickness 0.125 in
    Izod Impact, Notched 14.0 kJ/m² 6.66 ft-lb/in² ISO 180/1A
    (ISO)
    Izod Impact, Unnotched NB NB ISO 180/1C
    (ISO)
    Charpy Impact Unnotched NB NB ISO 179
    Charpy Impact, Notched 1.50 J/cm² 7.14 ft-lb/in² ISO 179
    Impact 11 11 Impact Flexural Test Notched (KJ/m²)
    NB NB Impact Flexural Test Unnotched (KJ/m²)

    Thermal Properties Metric English Comments


    Deflection Temperature at 88.0 °C 190 °F unannealed; ISO 75
    1.8 MPa (264 psi)
    98.0 °C 208 °F annealed; ISO 75
    Vicat Softening Point 100 °C 212 °F 50°C/hr; ISO 306
    @Load 5.00 kg @Load 11.0 lb
    101 °C 214 °F 120°C/hr; ISO 306
    @Load 5.00 kg @Load 11.0 lb
    104 °C 219 °F 50°C/hr; ISO 306
    @Load 1.00 kg @Load 2.20 lb
    105 °C 221 °F 120°C/hr; ISO 306
    @Load 1.00 kg @Load 2.20 lb
    Flammability, UL94 HB HB UL 94
    @Thickness 1.59 mm @Thickness 0.0625 in

    Some of the values displayed above may have been converted from their original units and/or rounded in order to display the information in a consistent format.
    Users requiring more precise data for scientific or engineering calculations can click on the property value to see the original value as well as raw conversions to
    equivalent units. We advise that you only use the original value or one of its raw conversions in your calculations to minimize rounding error. We also ask that you
    refer to MatWeb's terms of use regarding this information. Click here to view all the property values for this datasheet as they were originally entered into MatWeb.

    https://www.matweb.com/search/datasheet_print.aspx?matguid=8bcaa49130724c86b74cca85da32daac 1/1