LUPOY EU5002W

Injection Molding, PC/ASA, Non-flame Retardancy

Application
Industrial Goods / Others / Electric

Typical
Properties Condition Method Unit
Value

Physical
Specific Gravity 23℃ ASTM D792 1.14
Shrinkage 1 ASTM D955 1 ,
Flow 2.0mm 1 % 0.6~0.8
Cross-flow 2.0mm 1 % 0.6~0.8
Melt Flow Rate 250℃, 2.16kg ASTM D1238 g/10min 5.0
Specific Gravity 23℃ ISO 1183 1.14
Shrinkage 1 ISO 294-4 1 ,
Flow 2.0mm 1 % 0.6~0.8
Cross-flow 2.0mm 1 % 0.6~0.8
Melt Flow Rate 260℃, 5kg ISO 1133 g/10min 22

Mechanical
Tensile Strength 1 ASTM D638 1 ,
@Break 3.2mm, 50mm/min 1 kgf/cm² 580
Tensile Elongation 1 ASTM D638 1 ,
@Yield 3.2mm, 50mm/min 1 % 5.4
@Break 3.2mm, 50mm/min 1 % 110
Tensile Modulus 3.2mm, 50mm/min ASTM D638 kgf/cm² 18,320
Flexural Strength 3.2mm, 10mm/min ASTM D790 kgf/cm² 840
IZOD Impact Strength 1 ASTM D256 1 ,
3.2mm, Notched 23℃ 1 kgf·cm/cm 60
1 -30℃ 1 kgf·cm/cm 25
6.4mm, Notched 23℃ 1 kgf·cm/cm 52
1 -30℃ 1 kgf·cm/cm 17
1 -40℃ 1 kgf·cm/cm 14
Rockwell Hardness R-Scale ASTM D785 118
Tensile Strength 1 ISO 527 1 ,
@Yield 4.0mm, 50mm/min 1 MPa 52
@Break 4.0mm, 50mm/min 1 MPa 56
Tensile Elongation 1 ISO 527 1 ,
@Yield 4.0mm, 50mm/min 1 % 5.4
@Break 4.0mm, 50mm/min 1 % 93
Tensile Modulus 4.0mm, 1mm/min ISO 527 MPa 1,860
Flexural Strength 4.0mm, 2.0mm/min ISO 178 MPa 75
Flexural Modulus 4.0mm, 2.0mm/min ISO 178 MPa 2,050
IZOD Impact Strength 1 ISO 180 1 ,
4.0mm, Notched 23℃ 1 kJ/m² 53
1 -30℃ 1 kJ/m² 20
1 -40℃ 1 kJ/m² 18
Charpy Impact Strength 1 ISO 179 1 ,
4.0mm, Notched 23℃ 1 kJ/m² 60
 1 -30℃ 1 kJ/m² 22
1 -40℃ 1 kJ/m² 18
Rockwell Hardness R-Scale ISO 2039 118

Thermal
Heat Deflection Temperature 1 ASTM D648 1 ,
4.6kgf 6.4mm, Unannealed 1 ℃ 127
18.6kgf 6.4mm, Unannealed 1 ℃ 113
Coefficient of Linear Thermal Expansion 1 ASTM D696 1 ,
Flow -30℃ ∼ 80℃ 1 10⁻⁶m/m·℃ 89
Cross-flow -30℃ ∼ 80℃ 1 10⁻⁶m/m·℃ 92
Heat Deflection Temperature 1 ISO 75 1 ,
0.45MPa 4.0mm, Flatwise Unannealed 1 ℃ 124
1.8MPa 4.0mm, Flatwise Unannealed 1 ℃ 101
Coefficient of Linear Thermal Expansion 1 ISO 11359 1 ,
Flow -30℃ ∼ 80℃ 1 10⁻⁶m/m·℃ 89
Cross-flow -30℃ ∼ 80℃ 1 10⁻⁶m/m·℃ 92

Electrical
Surface Resistivity 23℃ ASTM D257 Ohm 1E+15
Dielectric Constant 23°C ASTM D150 2.8
Dielectric Strength 23℃, 2.0mm ASTM D149 kV/mm 16
Surface Resistivity 23℃ IEC60093 Ohm 1E+15
Note) Typical values can be used only for the purpose of selecting material, and there can be variation within normal tolerances for various colors.
Values given should not be interpreted as specification and not be used for designing part or tool.
All properties, except melt flow rate are measured by injection molded specimens after 48 hours storage at 23℃, 50% relative humidity.

Issued Date : 2022-10-26

The information contained herein, including, but not limited to, data, statements and typical values, are given in good faith. LG Chem makes no warranty or guarantee, expressed or implied, (i) that the
result described herein will be obtained under end - use conditions, or (ii) as to the effectiveness or safety of any design incorporating LG Chem materials, products, recommendations or advice.
Further, any information contained herein shall not be construed as a part of legally binding offer. Especially, the typical values should be regarded as reference values only and not as binding
minimum values. Each user bear full responsibility for making its own determination as to the suitability of LG Chem's materials, products, recommendations, or advice for its own particular use. Each
user must identify and perform all tests and analyses necessary to assure that its finished parts incorporating LG Chem material or products will be safe and suitable for use under end - use
conditions. The data contained herein can be changed without notice as a result of the quality improvement of the products.
LUPOY EU5002W
Injection Molding, PC/ASA, Non-flame Retardancy

Application
Industrial Goods / Others / Electric

Processing Conditions (Injection Molding)

Processing Parameters Unit Value

Drying Temperature ℃
Drying Time hrs
Maximum Moisture Content %
Melt Temperature ℃
Rear ℃
Cylinder Temperature Middle ℃
Front ℃
Nozzle Temperature ℃
Mold Temperature ℃
Note) These guides may not apply directly or need adjustment in specific situations such as low shot sizes, thin wall molding and gas-assist molding and so on.