    Axalta - NapGard 7-1888 CAV - PDS - V.may2016

    Uploaded by

    marjory ferrer

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Axalta - NapGard 7-1888 CAV - PDS - V.may2016

    Uploaded by

    marjory ferrer
    5 views3 pages

    Original Title

    Axalta - NapGard 7-1888 CAV - PDS - v.May2016

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    5 views3 pages

    Axalta - NapGard 7-1888 CAV - PDS - V.may2016

    Uploaded by

    marjory ferrer

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 3

    Technical Data Sheet

    Description

    Nap-Gard® 7-1888 CAV is a variation of Nap-Gard® 7-1888 that allows application with Regular Airless Spray
    equipment. The properties are similar to Nap-Gard® 7-1888, based on the latest Novolac Technology that
    produces a highly dense crosslinked coating for high temperature service in the Oil and Gas Industry (cathodic
    disbonding resistance up to 150°C / 302°F).

    Color: Brown

    Advantages & Uses

    Advantages
     100% Solids – No VOCs.
     Isocyanate free.
     Excellent resistance to high temperature cathodic disbonding up to 150°C (302°F).
     Excellent adhesion to grit blasted steel surfaces, Fusion Bond Epoxy (FBE), and
     Fiber Reinforced Plastic (FRP).
     Excellent impact resistance.
     Good flexibility.
     Ideal for areas where Plural Component Airless Spray equipment cannot be used.

    Uses
     Exterior coating of pipelines for high temperature service.

    Application

    Spray Grade: Airless Spray 56:1 minimum pump ratio. Remove the pump’s suction tube and place the lower
    pump assembly in a 5-gallon material pail. Hoses should be ½” ID maximum (no longer than 100 ft.) and ending
    with a 10 ft., 3/8” ID whip hose.
    Tip Size: 0.0523-0.527 reversible tip.
    Brush or roller for touch-up or repairs of small areas.

    Surface Preparation
    Steel Substrate:
    Cleanliness: Near White
    Standards: NACE 2, Sa 2½ (Swedish Scale, ISO 8501-1) SSPC SP-10 (The Society for Protective Coatings)
    Profile: 62.5 microns minimum to 125 microns maximum (2.5 mils to 5.0 mils)

    FBE: Profile: 6.25 microns (2.5 mils) minimum

    Mixing Ratio
     By Volume: 3 Parts Base to 1 Part Hardener.
    Technical Data Sheet

    Recommended Film Thickness


     0.75 mm (30 mils).

    Recoat Intervals
    @ 25°C (77°F) Maximum: 3 Hours
    @ 50°C (122°F) Maximum: 20 Minutes
    @ 60°C (140°F) Maximum: 8 Minutes

    Compatibly with other anticorrosion coatings


    Nap-Gard® 7-1888 CAV is compatible with all Axalta and fusion bonded epoxy (FBE) anti-corrosion coatings.
    For compatibility with other anti-corrosion coatings, please consult with Axalta.

    Handling Properties

    Spray Grade
    Pot Life [100 gm (3.5 oz) mass @ 25°C (77°F)] 30 min
    Dry Time (ASTM D1640)
    [0.60 mm (25 mils) coating thickness @ 25°C (77°F)]
    Touch Dry Time 3 min
    Dry Hard Time 6 hours

    Ambient Temperature Minimum 10°C (50°F)


    Substrate Temperature The acceptable substrate (metal surface) temperature range for the application
    of Nap-Gard® 7-1888 CAV is 10°C (50°F) to 100°C (212°F). Preheating of the
    substrate is required if the surface to be coated is below 10°C (50°F). The
    substrate temperature must be a minimum of 3°C (5°F) above the dew point
    temperature before proceeding with the coating operation. Post-heating may
    also be required when over-coating polyolefin substrates. Refer to the Curing
    Table.
    Storage / Shelf Life Store in a cool, dry, well-ventilated area at temperatures between 5°C (41°F) and
    40°C (104°F). Keep the lids sealed when not in use. The Shelf Life is a maximum
    of 24 months from the date of manufacture if the materials are in unopened
    containers.

    Liquid Properties

    Base Hardener
    Appearance Dark Brown Viscous Liquid Amber Mobile Liquid
    Solids Content (%) 100 100
    Specific Gravity (ASTM D1475) 1.42 ± 0.03 1.03 ± 0.03
    Coverage (Theoretical) Base & Hardener Mixed: 39.0 m2/Litre/25 microns

    Physical / Mechanical / Electrical Properties

    Adhesion to Steel:
    Dry Adhesion (Pull-off Strength) [(psi)] (ASTM D4541-95-A4)
    > 4,300
    (Self-Alignment Adhesion Tester, Type IV) [25°C (77°F)]
    Wet Adhesion (Hot Water Soak) (CSA-Z245.20-10, Clause 12.14, 28 Days)
    Rating # 1
    [95°C (203°F)]
    Technical Data Sheet

    Wet Adhesion (Hot Water Soak) (CSA-Z245.20-10, Clause 12.14, 120 Days) Rating # 1
    [75°C ± 3°C (167°F ± 5°F)]
    Cathodic Disbonding Test [Average Radius (mm)]
    6.50
    (CSA-Z245.20-10, Clause 12.8, Modified, 28 Days) [95°C (203°F)]
    Cathodic Disbonding Test [Average Radius (mm)]
    9.40
    (CSA-Z245.20-10, Clause 12.8, Modified, 28 Days) [135°C (275°F)]
    Flexibility (° PPD) (CSA Z245.20-02, Clause 12.11) (25°C / 77°F) 1.00
    Flexibility (° PPD) (CSA Z245.20-02, Clause 12.11) (0°C / 32°F) 0.75
    Flexibility (° PPD) (CSA Z245.20-02, Clause 12.11) (-30°C / -22°F) 0.50
    Hardness (Shore D) (ASTM D2240-91) [25°C (77°F)] 85
    Impact [Joules (ft-lbf)] (CSA-Z245.20-10, Clause 12.12) [21°C (70°F)] 4.20
    Impact [Joules (ft-lbf)] (CSA-Z245.20-10, Clause 12.12) [0°C (32°F)] 3.50
    Impact [Joules (ft-lbf)] (CSA-Z245.20-10, Clause 12.12) [-30°C (-22°F)] 2.00