    TDS Epicon HB-300 20190822

    Uploaded by

    sankaung1992120
    technical

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    TDS Epicon HB-300 20190822

    Uploaded by

    sankaung1992120
    30 views1 page
    technical

    Original Title

    TDS EPICON HB-300 20190822

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    technical

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    30 views1 page

    TDS Epicon HB-300 20190822

    Uploaded by

    sankaung1992120
    technical

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    You are on page 1of 1

    Technical Data Sheet

    EPICON HB-300

    Standard Paint specifications of "Handbook for corrosion protection of steel road bridges", March 2014, by Japan Road Association

    Type of paint High-build epoxy resin paint


    Characteristics 1) Good durability.
    2) High build type and good workability.
    3) Good adhesion property and physical property to shock resistance.

    Paint properties Mixing ratio : Base : Hardener = 85 : 15 by weight


    Base : Hardener = 75 : 25 by volume
    Color : N-7.0, N-8.5
    Density : 1.54 ± 0.05 g/mL
    by Roller, brush by Airless spray
    Coverage : 500 g/㎡ X 2 1100 g/㎡
    0.325 L/㎡ X 2 0.714 L/㎡
    Dry Film Thickness : DFT : 150 μm X 2 DFT : 300 μm
    Wet Film Thickness : WFT : 215 μm X 2 WFT : 430 μm

    Drying time : Temp. 5℃ 10 ℃ 20 ℃ 30 ℃


    Set-to-touch 3 hrs. 2.5 hrs. 1.5 hrs. 1 hr.
    Tack free 20 hrs. 15 hrs. 8 hrs. 6 hrs.
    Pot life (20℃) 3 hrs.
    Painting interval (min) (20℃) 1 day
    Painting interval (max) (20℃) 10 days

    Painting conditions Weather conditions : Atomospheric temperature : Minimum 5 ℃


    Relative humidity : Maximum 85 %
    Painting method : Roller, Burush, Airless spray
    For airless spray : Tip No. : Graco 623 - 723
    Paint output pressure : 14.7 - 17.7 MPa (150 - 180 kgf/c㎡)
    Spray gun speed : 60 - 80 cm/sec.
    Thinner : EPOXY THINNER A
    CHUGOKU THINNER CMP-31
    Thinning ratio : For roller / brush : Maximum 10% by weight
    For airless spray : Maximum 20% by weight
    Surface preparation The surface to be painted shall be clean (free from rust, dust, oil and other foreign materials) and dry.
    The surface temperature shall be higher than 3 ℃ or more against the due point.

    Packing style 20L set

    Shelf life Base : 12 months from production date


    Hardener : 12 months from production date
    Note 1) Please refer to Safety Data Sheet (SDS) for the further information.
    2) Fire shall be noted. Ventilation shall be maintained during painting and drying time until full cured.
    3) Base and Hardener shall be mixed in according to the above mixing ratio. Firstly, Base shall be stirred until
    becoming uniform. Secondly, Hardener is added. The mixed paint shall be stirred until the both of Base and
    Hardener become uniform. After then, Thinner is added and stirred until the mixed paint become uniform.
    4) It is recommended to be diluted by thinner as less as possible in order to get the sufficient DFT.
    5) It is recommended to mix the necessary quantity because of pot life.
    6) In case of the painting interval to be exceeded, all the surface to be painted shall be cleaned and roughened by
    sand paper.

    7) Coverage indicaed is based on "Handbook for corrosion protection of steel road bridges", March 2014, by Japan Road Association.

    8) This data sheet contains the best and latest of our knowledge according to the "Handbook for corrosion protection of steel road bridges"
    ,March 2014, by Japan Road Association, and subject to change witout notice.