FOR INDUCTION MELTING AND MASS HEATING, the early induction heating coils
were manufactured from copper tubing wrapped in multiple turns around a mandrel. The first induction heat treating coils were developed for
crankshaft hardening in the 1930s (Fig. 1, 2) (Ref 1–4). Unlike the melting and mass heating
coils, the heat treating induction coils were machined. These inductors consisted of two
parts with a hinge on one side that would open and shut around the crankshaft journal. Quench holes were drilled on the inner diameter of the induction coil to deliver quench to the part afterheating. This pioneering development was the culmination of many years of hard work by a large team and clearly demonstrated the different requirements for induction heat treating as compared to melting and mass heating.
Copyright 2014, ASM International, www.asminternational.org. This article was published in ASM Handbook, Volume 4C: Induction Heating and Heat Treatment and is made available as an electronic reprint with the permission of ASM International. One print or electronic copy may be made for personal use only. Systematic or multiple reproduction, distribution to multiple locations via electronic or other means, duplications of any material in this article for a fee or for commercial purposes, or modification of the content of this article is prohibited.
Copyright 2014, ASM International, www.asminternational.org. This article was published in ASM Handbook, Volume 4C: Induction Heating and Heat Treatment and is made available as an electronic reprint with the permission of ASM International. One print or electronic copy may be made for personal use only. Systematic or multiple reproduction, distribution to multiple locations via electronic or other means, duplications of any material in this article for a fee or for commercial purposes, or modification of the content of this article is prohibited.
Report
Share
Report
Share
1 of 18
Download to read offline
More Related Content
Design and Fabrication of Inductors for Induction Heat Treating
1. Design and Fabrication of Inductors for
Induction Heat Treating
Rob Goldstein, Fluxtrol
William Stuehr, Induction Tooling
Micah Black, Tucker Induction Systems
FOR INDUCTION MELTING AND MASS
HEATING, the early induction heating coils
were manufactured from copper tubing wrapped
in multiple turns around a mandrel. The first
induction heat treating coils were developed for
crankshaft hardening in the 1930s (Fig. 1, 2)
(Ref 1–4). Unlike the melting and mass heating
coils, the heat treating induction coils were
machined. These inductors consisted of two
parts with a hinge on one side that would open
and shut around the crankshaft journal. Quench
holes were drilled on the inner diameter of the
induction coil to deliver quench to the part after
heating. This pioneering development was the
culmination of many years of hard work by a
large team and clearly demonstrated the different
requirements for induction heat treating as com-
pared to melting and mass heating.
During the infancy of induction heat treating
coil development, the specific features of the in-
duction coil primarily were determined through
an analytical-, experience-, and experimental-
based method. Concepts for induction coils were
created by physicists. Calculations of coil para-
meters were determined by manually solving
complex equations. Induction coil designs initi-
ally were made by draftsmen on blueprints.
Most inductors were manufactured by crafts-
men using a combination of copper tubing,
manually machined components, and copper
plates brazed together. Coil optimization was
made based on experimental results through
the trial-and-error method, because tests and
modifications took much less time than the
calculations did (Ref 1, 5).
While many induction heat treating coils are
still manufactured in this way, the tools for
the design and fabrication of complex induction
heat treating inductors have evolved greatly
over the years. For many types of applications,
the preferred induction coil style already is
known based on years of empirical data. In
many cases, comparisons to known results can
even determine induction coil dimensions that
will lead to a successful heat treating pattern,
greatly limiting experimental testing times and
shortening development cycles (Ref 1, 5–9).
For newer applications or optimization of
existing ones, computer modeling tools are being
incorporated into the induction coil design
procedure. Sophisticated software running on
personal computers is capable of making cal-
culations in seconds, minutes, or hours that
would have taken days, weeks, or months to
solve manually. In many cases, no analytical
formula exists for complex coils, and the only
way to make calculations prior to tests is with
a computer modeling program. Induction coil
designs and process recipes are “virtually”
tested to determine resulting heat patterns. In
many cases today (2013), virtual tests and eva-
luations can be made more quickly and at a
lower cost than physical ones (Ref 10–12).
The process of mechanical induction coil
design also has evolved over the years. While
the initial drawings were made by hand, induction
coils now are drawn and detailed using computer-
aided design (CAD) packages. Over the past sev-
eral years, CAD packages have increased their
interactivity with computer-aided manufacturing
(CAM) software packages. In many instances,
induction coil drawings can be transferred from
a CAD drawing to a CAM program into the com-
puter numerically controlled machine. This cre-
ates the possibility for greater repeatability of
complex machined induction coils (Ref 13, 14).
Methods of Induction Heat Treating
Today (2014), there are many different types
of induction heat treating coils. The induction
heat treating coil style depends on the induction
heat treating process. All induction heat treating
processes can be classified in two categories:
single shot and scanning, based on whether the
induction coil is moving (excluding rotation)
relative to the part during the heating process.
A brief description is given subsequently, because
more in-depth information on induction heat
treating equipment is discussed in other sections
in this article.
In single-shot (Fig. 3) induction heat treating
applications, the position of the induction
coil relative to the heated length of the part
does not move. In many single-shot heating
ASM Handbook, Volume 4C, Induction Heating and Heat Treatment
V. Rudnev and G.E. Totten, editors
Copyright # 2014 ASM InternationalW
All rights reserved
www.asminternational.org
Fig. 1 Tocco coil. Source: Ref 1 Fig. 2 Vologdin coil
2. applications, the part rotates while heating and
quenching occur to ensure uniformity of pattern.
Within the family of single-shot heat treating
applications, there are several varieties of in-
duction coil configurations, depending on the
quench-delivery mechanism.
Machined integral quench (MIQ) installations
have quench integrated right into the induction
coil itself. The most common method is for the
quench to be delivered through the coil copper
itself. These inductors typically have separate
pockets for water cooling and quench delivery.
In some other cases, the quench may be deliv-
ered through a magnetic flux concentrator.
Another type of single-shot heat treating instal-
lation is quenching in place (Fig. 4). Quenching in
place is similar to MIQ, because the quench ring is
a part of the induction coil assembly. What differ-
entiates quenching in place from MIQ installa-
tions is that the quench is not designed to be an
active component of the induction circuit.
The final single-shot induction heat treating
coil style is separate quenching (Fig. 5). In
these installations, the quench is not part of
the induction coil assembly. In separate-quench
installations, the quenching often is delivered in
a different station or position in the machine.
These systems are common when a delay
between heating and quenching for heat soak-
ing is desirable.
Besides single shot, the other type of induc-
tion machine is scanning (Fig. 6) (Ref 5, 9). In
scan-hardening applications, the induction coil
moves relative to the part. Similar to single-shot
inductors, scanning inductors can be either MIQ
or quenching in place. They also may be sepa-
rate quenching, but this is less common.
Considerations for Inductor Design
Induction heat treating coils are available in
many shapes and sizes and must perform a vari-
ety of tasks in a given induction heat treating
application. Depending on the application, the
induction coil design requirements include:
Meet heat treatment specifications in desired
production rates
Be robust enough to tolerate manufacturing
variations
Mount into the induction machine
Have electrical parameters that match the
induction power supply
Deliver quench
Have a satisfactory lifetime
Have satisfactory efficiency
Be repeatable from inductor to inductor
In developing a new induction heat treating
coil and process, the first question is whether
the component will be produced on an existing
system or if a new machine must be built. In
many cases, the part producer’s desire is to
develop new tooling for an existing machine
with spare capacity. This reduces the degree
of freedom and can make the induction coil
design procedure more complicated, because
a less-than-optimal frequency or coil style will
be necessitated to fit the existing machine
(Ref 16).
To determine the ability to use existing
equipment, it is necessary to make an analysis
of the part to be heat treated. Part material,
prior processing, geometry, production rate,
and heat treatment specifications all play roles.
The part material and prior processing deter-
mine what the minimum heat treatment temper-
ature should be, along with how much time is
allowed for cooling. The part geometry and
heat treatment specifications indicate how
much energy is required, what the preferred
frequency ranges are, and what type of induc-
tion method (i.e., single shot, scanning) is best
suited for the application. Finally, the produc-
tion rate determines how much power and/or
how many spindles or stations are required.
More details on this topic are given later in
this and other articles in this Volume. The dis-
cussion in this article is limited to the relation-
ship between these factors and the induction
coil design.
Current Flow in the Part
Eddy currents are the primary source of
power dissipation in most induction heat treat-
ing applications. Eddy currents, just like all
other electrical currents, must form a closed
contour. In most cases, the current flow in the
workpiece follows the shape of the induction
heating coil, due to the proximity effect. The
power density in a given section of the work-
piece depends on the current density. The
current density can be influenced by electro-
magnetic effects (end effect, edge effect, etc.),
the presence of magnetic flux concentrators,
the width of the copper, the geometry of the
part, and the distance between the coil and the
workpiece (coupling gap).
The next step in the coil design process is
determining how the current will flow in the
part. This is critical, especially in cases where
the geometry changes. Some common geometry
changes encountered in induction heat treating
are fillets, undercuts, corners, shoulders, cham-
fers, splines, keyways, and oil holes. The heat-
ing of these critical areas relative to adjacent
ones is strongly dependent on the induction coil
style and frequency of heating.
The first primary choices for current flow,
either in the plane of the geometry change or
perpendicular to the geometry change, are dis-
cussed here. When current flow is perpendicu-
lar to the direction of a geometry change, the
natural tendency is for the current to concen-
trate on the part surface that is closer to the
Fig. 3 Single-shot induction heat treating application
Fig. 4 Quench-in-placeinductorforhardeningofaspindle
Fig. 6 Machined integral quench scanning inductor
with magnetic flux concentrator
Fig. 5 Separate quenching. Source: Ref 15
590 / Equipment
3. induction coil, due to the proximity effect. An
additional consideration is that near the ends of
the closer section to where the distance increases,
there is either a decrease or an increase in heat-
ing, depending on whether the part is magnetic
or nonmagnetic due to the electromagnetic end
effect. For hardening applications, there is some
increase, and for tempering there is a decrease.
The magnitude of the change depends on the
frequency (Fig. 7) (Ref 12).
When the current flow is in the direction of a
geometry change, the current flows under the
inductor in a width approximating that of the
induction coil. When the dimension change
occurs, the current flow follows the contour of
the part through this dimensional change. At
the point of the dimension change, the change
in heating is governed by the electromagnetic
edge effect. The edge effect tends to be smaller
than the end effect, hence meaning a smaller
temperature differential in this area. As the dis-
tance between the coil and part increases, the
amount of current remains nearly the same,
but the current begins to flow over a wider
length. The less concentrated heating leads to
lower power densities (Fig. 8). The difference
between the power densities tends to be smaller
than when current flow is in the direction of the
geometry change than when it is perpendicular.
To illustrate the concept, consider the case of
a simple spindle with one bearing race and a
shoulder (Fig. 9). The heat treating pattern is
the light-gray area. This part could be heated
either by scanning or single shot. The scanning
inductor almost certainly would be an encir-
cling inductor with a length less than the pat-
tern length. Within single shot, it also could
be hardened by a machined encircling inductor
or a so-called encircling/nonencircling inductor.
For an encircling inductor (scanning or single
shot), the current flow in the coil and part tend
to take the shortest path and flow along the
inductor inside diameter and bearing surface
diameter. To compensate for this tendency,
it is necessary to vary the gap between the
coil and part to use the proximity effect to
compensate for the shorter length for current
flow. In the area of the radius, there is a transi-
tion from the smaller gaps on the flange to the
larger gaps on the diameter. For a single-turn
machined inductor, the coil design in this area
involves a delicate balance to achieve sufficient
depth in the fillet without heating too deeply in
the bearing area just above the fillet. For case
depths that are large relative to the cross sec-
tion, this becomes more difficult because core
temperatures increase, resulting in reduced con-
ductive heat extraction. For a shorter scanning
coil, this task is made easier by using a mag-
netic flux concentrator to drive current down
from the shaft and into the radius of the part
(Fig. 10).
Encircling/nonencircling inductors consist of
multiple partial loops connected by copper rails
that are contoured to the part surface (Fig. 11).
For these inductors, the part must rotate to
ensure even heating. For a simple part such as
this, likely only one top and one bottom partial
loop would be required. In this case, current
flows under the coil turns and follows the con-
tour of the coil in the part. In this way, the top
and bottom of the pattern are controlled by the
end loops, and the rails determine the pattern in
the central area. By following the rails along the
part surface, the current flows through the radius.
Fig. 7 End-effect drawing
Fig. 8 Edge-effect drawing
Fig. 9 Heat pattern for spindle
Fig. 10 Encircling drawing for spindle
Design and Fabrication of Inductors for Induction Heat Treating / 591
4. This makes achieving a more uniform contour
easier with a linear inductor than with an encir-
cling one for this type of part (Fig. 12).
The Influence of Frequency
The frequency of the induction heating cur-
rent has a strong influence on the induction coil
and process design. It affects the power
required, heating time, coil losses, local distri-
bution of power in the part, and the structural
support required. A brief overview of the effect
of frequency is given in this section, because it
is covered in more depth in other articles in this
Volume.
Often, the same case depth can be achieved
over a wide range of frequencies. For large
parts in either the completely magnetic (cold
steel) or nonmagnetic (hot steel) state, current
density is highest at the surface and falls off
exponentially in depth. There is a value used
by induction heating practitioners called the
reference or skin depth related to this behavior.
The formula for reference depth is:
d ¼ k
ffiffiffiffiffi
r
mf
r
(Eq 1)
where d is the reference depth, k is a constant
depending on units, r is the electrical resis-
tivity, m is the magnetic permeability, and f is
frequency.
In large bodies, 63% of the current and 86%
of the power reside in the first reference depth
(Fig. 13) (Ref 6, 17). This leads to the assump-
tion commonly made in estimating parameters
that all of the power is generated in the d layer.
In induction hardening applications, the
distribution of current and power density is dif-
ferent than that predicted by the reference
depth, because the magnetic steel below the
Curie point still interacts with the magnetic
field behind the nonmagnetic hot surface layer
(Ref 17). To achieve the same case depth on
parts with lower frequencies, one can expect
higher power levels, shorter heating times, and
lower surface temperatures. As the frequency
is increased, power levels must be decreased
and heating times increased to achieve the same
case depth without overheating the surface. The
amount of energy required depends on the bal-
ance between thermal losses (heat soaking), coil
efficiency, and power induced in the subcase-
depth material.
Besides the process, the frequency also influ-
ences how the current is flowing in the induc-
tion coil itself. In practice, the most effective
thickness of the conductive part of the tubing
wall (d1) is assumed to be d1 ffi 1.6d1. This
ratio is based on solution of a one-dimensional
problem. An induction coil tubing wall smaller
than 1.6d1 results in reduction in coil effi-
ciency; furthermore, in some cases the tubing
wall can be much thicker compared to the
aforementioned ratio. This is because it may
not be mechanically practical to use a tubing
wall thickness of 0.25 mm (0.01 in.). Some
guidelines for wall thickness are shown in
Table 1 (Ref 9).
The frequency also affects the electrody-
namic forces, which influence the mechanical
design of the induction coil. Electrodynamic
forces in induction heating have two compo-
nents: static and dynamic. The static component
initially pulls the inductor in toward the part in
the cold magnetic state and then pushes it away
from the part when it is nonmagnetic. The
dynamic component oscillates around the static
component at double the electric frequency
(Fig. 14). The level of force in the system is
proportional to the square of the coil current;
that is, the forces are directly proportional to
the power (Ref 17).
When the part is electrically thick (i.e., the
diameter or thickness is much greater than
the reference depth), the current required for
the same power is proportional to the inverse
fourth root of the ratio of frequencies (Eq 2).
From this equation, it can be seen that the cur-
rent required for the same amount of power
decreases with increasing frequency:
I2 ¼ I1
ffiffiffiffi
f1
f2
4
s
(Eq 2)
Fig. 11 Encircling/nonencircling drawing for spindle
Fig. 12 Linear/single-shot drawing for spindle
Fig. 13 Distribution of current (S) and power density
(Pv) in the depth of a large workpiece.
Source: Ref 17
Table 1 Standard wall thickness of copper
tubing
Copper wall thickness
Frequency, kHzmm in.
0.75–1 0.032–0.048 450–50
1–2 0.048–0.090 25–8.3
1.5–4 0.062–0.156 10–3
4–6.5 0.156–0.250 3–1
Source: Ref 7
592 / Equipment
5. Due to this, the electrodynamic forces are
higher at lower frequencies. Additionally,
power levels generally tend to be higher at
lower frequencies, increasing the electrody-
namic forces even more. Therefore, the lower
the frequency, the more robust the mechanical
design of the induction coil should be. In addi-
tion to heavier copper wall thicknesses, the coil
supporting structure also must be stronger to
withstand the mechanical loading to which
the coil is exposed. This is especially true on
single-shot coils.
Control of Heating in Different
Areas of the Part
In many induction heat treating applications,
there is a requirement to selectively harden
some areas of the workpiece and not harden
others. In other instances, different case depths
are desired in different areas of the part. Often,
it is necessary to achieve these various targets
in the same induction heat treating operation.
For scan hardening applications, these varia-
tions typically are compensated for by adjusting
the power and scan speed as the part traverses
through the induction coil. For single-shot
induction coils, it is necessary to accommodate
these changes in the coil design. There are three
main tools for adjustment of the coil design:
coupling gap, coil copper profile, and magnetic
flux controllers.
The coupling gap is the most straightforward
way to control the heat pattern. The closer the
coil is to the part, the greater the intensity of heat-
ing in this area relative to other areas. This is
because the current in the part flows in a nar-
rower band more closely approximating that in
the induction heating coil. With increasing cou-
pling gap, the current spreads out over a longer
length, resulting in lower current density and
power density.
Another method to control the heat pattern is
to change the cross-sectional profile of the cop-
per coil. The section(s) of the coil turn that
faces the part and carries the majority of the
current is referred to as the heat face of the
coil. For induction coils with a single heat
face, power profiling is achieved by varying
the geometry of the heat face (Fig. 15). For
instance, to shorten the transition zones at the
ends of the coil, it is common to have a larger
gap in the middle of the coil than on the ends.
This method is commonly used for controlling
the end of a heat treating pattern where it is de-
sirable to keep the pattern out of an undercut or
a snap ring groove. This helps to compensate
for the divergence of magnetic flux and the
additional thermal losses near the end of the
coil.
An example of this is hardening the bearing
of a crankshaft using an encircling coil (clam-
shell or sharp-C technology, Ref 9). Using the
Flux 2D computer simulation program, it is
possible to make a comparison to see the effect
of the copper profiling on the temperature dis-
tribution. Figure 16 shows a simplified example
of a coil for this technology. The lines on the
part represent the minimum and maximum case
depth. The frequency for this comparison is
50 kHz. The coupling gap is 2 mm (0.08 in.),
and the coil has thin plates of Fluxtrol 50 con-
centrator on both sides to prevent coupling with
the sidewalls. At 2.5 mm (0.10 in.) from each
end of the coil, the copper is recessed 1 mm
(0.04 in.). This coil is compared to a coil with
the exact same geometry, except the central
section of the inductor is not recessed. The
heating time for both cases is 4 s.
The temperature distribution in the coil
without profiling is shown in Fig. 17. The area
of high temperature begins to taper off well
before the end of the heat face and the mini-
mum required length of the pattern. The surface
temperature already is high, so it is not possible
to increase heating to lengthen the pattern.
Figure 18 shows the temperature distribution
for the coil with a profiled face. It is clear from
this image that the area of high temperature
extends significantly longer than for the coil
without profiling. The minimum heat treatment
width is met with a lower maximum surface
temperature. For better comparison between
the two cases, Fig. 19 compares the surface
temperature in length.
For coils with multiple heat faces or sec-
tions, in addition to the coupling gap, the heat
pattern also can be controlled by changing the
width of the heat face from section to section.
Power density in the part is proportional to
the current density squared. If it is assumed
that all of the current in the coil is transferred
to the part and is flowing directly under the
heat face of the induction coil, then the cur-
rent density will be inversely proportional
to the width of the heat face. This means
Fig. 15 Drawing showing inductor heat face
Fig. 16 Nonrotational inductor cross section used for simulation
Fig. 14 Diagram showing relationship between current
(i), static component of force (Fc), and dynamic
force (F). Source: Ref 17
Design and Fabrication of Inductors for Induction Heat Treating / 593
6. that power density will be proportional to the
inverse square of the width of the heat face.
The real effect is significantly less, because
not all of the current is on the heat face, and
some of the flux outside the coil couples with
the part.
For heating of a round part with a linear coil,
the effect is not as strong due to the nonuniform
gap between the rectangular coil and the round
part.
To demonstrate the effect of the heat face
width, a comparison is made for heating a
12.7 mm (0.5 in.) thick plate with a 9.5 by
12.7 mm (⅜ by 0.5 in.) tube and a 12.7 mm
(0.5 in.) square copper tube. Computer simula-
tion program Flux 2D is used for calculation
of the electromagnetic problem. The top half
of the plate has the properties of steel above
the Curie point, and the bottom half has
the properties of cold steel. The frequency is
10 kHz, and the coupling gap is set to 3.2 mm
(⅛ in.). The same current, 3000 A, is used for
both coils. The magnetic field and power den-
sity distributions for both cases are shown in
Fig. 20. Ideally, the power density would be
78% higher for the 9.5 mm (⅜ in.) heat face
compared to the 12.7 mm (0.5 in.) one. In real-
ity, this difference in maximum power density
is only approximately 17%. This is due to the
large amount of current that is flowing in the
part outside the heat face of the coil.
A more effective way to control the distribu-
tion of heat in the length of an inductor is to use
magnetic flux controllers. For induction heat
treating applications, the most common materi-
als used as magnetic flux controllers are silicon
steel laminations and soft magnetic composite
materials. Magnetic flux concentrators provide
a low reluctance path for the magnetic field to
flow. The result is that the magnetic field goes
from being widely distributed in space to being
concentrated around the coil. This causes nearly
all of the current flowing on the sidewalls of the
copper coil to be pushed down to the heat face.
This results in the current in the part being con-
centrated more strongly underneath the heat
face of the coil.
To demonstrate the effect of the concentrator,
a comparison is made for heating a 12.7 mm
(0.5 in.) thick plate with a 12.7 mm (0.5 in.)
square copper tube, with and without a C-shaped
concentrator applied. The flux-concentrating
material used is Fluxtrol A. The other condi-
tions are the same as in the case for the heat
face variation study. The magnetic field and
power density distributions for the coil with
concentrator are shown in Fig. 21.
The magnetic field and power density are
much more concentrated when the magnetic
flux controller is applied. The surface power
density curves from the left to the right side
of the part are shown in Fig. 22 for all three
cases. It is clear that the application of a mag-
netic flux controller is a stronger method of
controlling the heat pattern in the length of a
coil than the use of copper profiling. It also is
possible to more smoothly distribute the pattern
between different areas by profiling the poles of
the concentrator rather than having steps in the
induction coil. For linear coils heating a round
part, the influence of both heat face width and
a magnetic flux controller is less dramatic than
in the case of a flat plate, due to the divergence
of the part from the coil. More information on
magnetic flux controller selection and uses is
contained in the article “Magnetic Flux Con-
trollers in Induction Heating and Melting” in
this Volume.
Presentation of the Part to the
Inductor
During the initial inductor design, a method of
holding the part and presenting it to the inductor
must be addressed. Some considerations are:
What is the part size and weight?
What is the process hardening or tempering?
Is it to be scanned or single shot?
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 4 Phase (Deg): 0
Scale / Color
20.06464 / 86.92299
86.92299 / 153.78134
153.78134 / 220.63969
220.63969 / 287.49805
287.49805 / 354.35638
354.35638 / 421.21478
421.21478 / 488.07312
488.07312 / 554.93146
554.93146 / 621.78986
621.78986 / 688.64819
688.64819 / 755.50653
755.50653 / 822.36487
822.36487 / 889.22321
889.22321 / 956.0816
956.0816 / 1.02294E3
1.02294E3 / 1.0898E3
Fig. 17 Temperature distribution with a nonprofiled heat face
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 4 Phase (Deg): 0
Scale / Color
20.08923 / 83.79922
83.79922 / 147.50919
147.50919 / 211.21918
211.21918 / 274.92917
274.92917 / 338.63913
338.63913 / 402.34912
402.34912 / 466.05911
466.05911 / 529.7691
529.7691 / 593.47913
593.47913 / 657.18909
657.18909 / 720.89905
720.89905 / 784.60907
784.60907 / 848.31903
848.31903 / 912.02905
912.02905 / 975.73901
975.73901 / 1.03945E3
Fig. 18 Temperature distribution with a profiled heat face
594 / Equipment
7. Is the part to be rotated during processing?
What is the rate of production?
What type of materials handling equipment
is needed?
How and where on the part can it be held?
What is the kilowatt requirement and power
supply frequency?
How is it to be loaded into the inductor:
manually or mechanically?
What is the quench method: spray, dunk,
agitated bath, still air, or air blast?
What types of holding devices are to be used:
centers, chuck, or special grippers?
Depending on the process, there could be
several mechanical methods to grip and present
a part to the inductor. In high-production appli-
cations, an entire machine may be designed and
built for a specific materials handling process.
In limited-production runs, however, a simple
lift-and-rotate device within a quench tank may
be employed. Either way, a decision must be
made on how to hold the part.
Part holding and presentation can be as easy
as chucking the part or as complicated as hav-
ing to hold and rotate the part while it is heated
entirely. In any scenario, the electromagnetic
fields from the induction coil should be consid-
ered in the design of the holding device and its
effect on the part. Magnetic steels in close pro-
ximity to the inductor will heat; therefore, suffi-
cient air space around the inductor is prudent.
Common nonmagnetic part-holding materials,
such as 300-series stainless steels, aluminum,
and brass, can be heated when in close prox-
imity to the inductor, but with a less significant
effect. When designed specific to an applica-
tion, certain ceramics also make excellent part-
holding devices.
For example, typical to induction hardening
applications is the lift-and-rotate method within
a quench tank. A part of reasonable size and
shape, such as an automotive wheel spindle, is
mounted onto a part holder made from nonmag-
netic stainless steel. An upper center of the
same material is used to stabilize the part dur-
ing rotation. An inductor designed to heat treat
the wheel spindle is installed onto the power
supply mounting foot within the tank. A spray
quench is integral to the inductor. The wheel
spindle is loaded in the holder and raised to
the inductor. Rotation starts, the induction
power is applied, the wheel spindle is heated
and then immediately quenched, and the spin-
dle is lowered and unloaded. This entire process
takes less than 30 s. In a high-production appli-
cation, throughput would be multiplied with
additional heating stations employing various
materials handling systems.
While many examples of heat treating are
typical, when parts are large and/or geometri-
cally difficult, the presentation to the inductor
may require engineering. For many induction-
hardened parts, rotation during heating equalizes
the heat treating pattern. Some parts, such
as truck steering arms in the shape of the letter
“J,” cannot be rotated 360
due to the J-hookFig. 19 Comparison of temperature distributions with and without profiling for nonrotational heating of a crankshaft
Color Shade Results
(a) (b)
Quantity : Power density W/(cubic m)
Scale / Color
0 / 35.01103E6
Phase (Deg) 0
35.01103E6 / 70.02206E6
70.02206E6 / 105.03309E6
105.03309E6 / 140.04411E6
140.04411E6 / 175.05515E6
175.05515E6 / 210.06618E6
210.06618E6 / 245.0772E6
245.0772E6 / 280.08822E6
280.08822E6 / 315.09923E6
315.09923E6 / 350.11027E6
350.11027E6 / 385.12131E6
385.12131E6 / 420.13232E6
420.13232E6 / 455.14336E6
455.14336E6 / 490.15437E6
490.15437E6 / 525.16541E6
525.16541E6 / 560.17645E6
Color Shade Results
Quantity : Power density W/(cubic m)
Scale / Color
0 / 29.92064E6
Phase (Deg) 0
29.92064E6 / 59.84129E6
59.84129E6 / 89.76194E6
89.76194E6 / 119.68258E6
119.68258E6 / 149.60323E6
149.60323E6 / 139.52387E6
139.52387E6 / 209.44451E6
209.44451E6 / 239.36515E6
239.36515E6 / 269.28579E6
269.28579E6 / 299.20643E6
299.20643E6 / 329.1271E6
329.1271E6 / 359.04774E6
359.04774E6 / 388.96830E6
388.96830E6 / 418.88902E6
418.88902E6 / 448.80966E6
448.80966E6 / 478.7303E6
10 / 865.19256E-6
11 / 970.83917E-6
12 / 1.07649E-3
8 / 03383339E-6
9 / 759.54595E-6
Fig. 20 Comparison of (a) 9.5 mm (⅜ in.) and (b) 12.7 mm (0.5 in.) heat faces for heating of a flat plate
Design and Fabrication of Inductors for Induction Heat Treating / 595
8. interfering with the inductor; yet, to equalize the
hardened pattern, some form of rotation is needed
to equally heat the bearing journal on the end of
the J-hook. To accomplish this, a part holder is
connected to a crank and made to oscillate
through 210
during the hardening cycle, closely
mimicking full rotation.
Large, heavy parts may be application spe-
cific as to their presentation to the inductor,
requiring thoughtful design, materials selection,
and testing to verify the heating results. In some
installations, it is necessary to present the induc-
tor to the part. Complex designs involve robots
moving the inductor along the path to be hard-
ened. The inductor and transformer sometimes
are robotically moved together, while other
times, depending on the power and frequency,
a flexible cable connected to the inductor may
be employed. Other heating applications may
use a handheld induction heating apparatus.
All applications are dependent on the power
required, the size of the part, and the areas to
be heated.
Inductor Structure
For low-frequency and/or high-power-den-
sity induction heat treating applications, the
electrodynamic forces are strong and the induc-
tion coil requires a supplemental mechanical
support structure. A mechanical support struc-
ture also is required if the induction coil is
heavy or manufactured from thin-walled cop-
per tubing. Some common types of inductors
where mechanical supports are used include
single-shot inductors for heating shafts or
stems, multiturn induction coils, induction
coils without rotational symmetry, and applica-
tions where the inductor is heating a surface
that is perpendicular to the buss mounting
plates.
For induction heat treating coils, the
mechanical support components include stud
boards, retainer rings, mounting plates, and
components to connect the coil to quench rings.
In the vast majority of cases, the materials used
for the inductor structure are made from high-
temperature fiber-reinforced plastic compo-
nents. In some extreme cases, such as long sin-
gle-shot coils for axle shaft hardening, a fiber-
reinforced stud board may be additionally sup-
ported by an aluminum housing or channel. In
this case, care should be taken to insulate the
inductor and any studs from the conductive
support housing.
One of the more challenging induction appli-
cations that requires a strong mechanical sup-
port system is rotational crankshaft hardening
with U-shaped inductors (Fig. 23). The distance
from the output of the transformer to the heat-
ing area of the coil must be relatively long to
ensure that the counterweights of the crankshaft
will not hit the transformer. This is a challenge,
because in this style of coil the electrodynamic
forces are high and act in multiple directions.
There also is a mechanical load placed on the
induction coil, because the inductor assembly
is in contact with the part during rotation.
When the crankshaft is cold, the turns are
pulled toward the bearing journal and the side-
walls of the crankshaft. Once the part is above
the Curie point, the forces are reversed, and
the inductor is pushed away from the sidewalls
and away from the bearing diameter.
Due to these multiple challenges, the struc-
ture consists of several parts. Outside the
Color Shade Results
Quantity : Power density W/(cubic m)
Phase (Deg): 0
Scale/Color
0 / 115.86056E6
115.86056E6 / 231.72114E6
231.72114E6 / 347.5817E6
347.5817E6 / 463.44224E6
463.44224E6 / 579.30285E6
579.30285E6 / 695.16339E6
695.16339E6 / 811.02394E6
811.02394E6 / 926.88448E6
926.88448E6 / 1.04275E9
1.04275E9 / 1.15861E9
1.15861E9 / 1.27447E9
1.27447E9 / 1.39033E9
1.39033E9 / 1.50619E9
1.50619E9 / 1.62205E9
1.62205E9 / 1.73791E9
1.73791E9 / 1.85377E9
Fig. 21 Magnetic field and power density distribution for a 12.7 mm (0.5 in.) heat face with Fluxtrol A for heating of
a flat plate
Fig. 22 Surface power density curves for all three cases of flat plate heating
596 / Equipment
9. inductor there typically are two brass or alumi-
num side plates. All of the components are
anchored to the side plates, including the induc-
tion coil. To prevent contact of the inductor
with the part, ceramic or carbide guide shoes
are placed in three places (just after the ends
of the loops and between the two loops) around
the perimeter on both sides of the inductor. The
ceramic guide shoes typically are mounted to
brass or aluminum side plates.
In addition to the guide shoes, the side plates
also help to keep the induction coil in position.
The inductor typically is held in at least three
places: the ends of each loop by a stud and
G-11 component, and the leads area by a G-11
component. Other components that may be a
part of the structure in crankshaft coils include
leaders to facilitate the coil loading, quench
heads, and side support composites to increase
the rigidity of the assembly.
Coil Leads/Busswork and Contacts
With induction coils, there is an intermediate
body between the coil head (the part where the
induction heat treating process is conducted)
and the heat station, power supply, or quick-
change adapter. This section of the inductor is
referred to as the coil leads or busswork. The
role of the coil leads or busswork is to mechan-
ically and electrically connect the induction coil
head to the power supply. Often, the cooling
water for the coil head also is supplied through
the leads.
Good design practice is that the leads should
be close together, with a piece of synthetic
fluorine-containing resin between them to
electrically separate the two leads from one
another. It also is good practice to make the
height of the busswork significantly longer than
the length of the heat face of the induction coil.
In most cases, the coil leads or busswork
must carry the same current that is in the induc-
tion coil head itself. Because the coil leads/
busswork carry a high-frequency current, the
coil leads generate heat from eddy currents.
The current is drawn to the side of the bussbar
that faces the opposing bussbar by the proxim-
ity effect. The current density in the leads is
inversely proportional to the length of the inter-
face, and hence, the losses are approximately
proportional to the length squared. The proxim-
ity of the two leads to each other primarily influ-
ences the voltage drop in the leads. The closer
the leads are, the lower the inductance of the
leads and hence the lower the voltage drop.
The coil contacts range from simple flared or
compression fittings to machined blocks with
keys to ensure location, depending on the mat-
ing surface. For heat treating environments,
the machined blocks with keys are preferred
for high-power-density and low- or medium-
frequency environments. Compression or flared
fittings should be used only in the case of high-
frequency, lower-power-density applications or
long solenoids with high turn numbers and
low currents.
For the machined block contacts, these sys-
tems can be separated into two classes: standard
bolting connections and quick-change adapters.
For standard bolting connections, there are two
main contact styles: fishtails or Jackson type,
and flat plate. Fishtails consist of a slotted cop-
per bar for adjustment of the vertical height,
with a female key on the back to fix the hori-
zontal position (Fig. 24a). This type of contact
is common for the frequency range of 1 to 30 kHz
in heat treating applications where the coil is
mounted to a transformer. For this style, water
typically is fed from separate water lines to the
induction coil rather than through the heat station
electrical contacts, because the vertical height of
the coil is not always in the same place.
Flat plate contacts typically consist of a flat
plate with two holes for bolts and a hole between
the two bolts for water (Fig. 24b). The water-
cooling hole commonly is slightly recessed
for placement of an O-ring. Flat plate contacts
typically are used for mounting to power supply
or heat station outputs for higher frequencies
(50 to 450 kHz).
Besides bolting contacts, there are several
types of quick-change adapters used in industry
(Fig. 25). All of these systems involve the use
of mechanical keys and a lever to press the con-
tacts flush and fix the position of the coil in a
quick motion. Coil water cooling may or may
not be incorporated into the quick-change
adapter. Separate water cooling typically is
provided to the induction coil in the case of
high power densities or where the quick-change
adapter allows for a variable vertical position.
Quenching Considerations in
Induction Coil Design
In many cases, quenching is done to finalize
the hardening process of steel components,
and it typically is done with water that has a
small percentage of a quench medium. This is
the second half of heat treating; this stage is just
as important as heating. After the part surface is
raised above the austenitizing temperature, it
should be quenched (or rapidly cooled). In most
cases, this should be done immediately after the
austenitizing temperature is reached. The time
before quenching can vary depending on the
composition of the steel. The quench design
must not only remove heat rapidly but uni-
formly as well. The results of nonuniform or
slow quench are nonuniform hardness and
possible overall distortion in the part (or work-
piece). Nonuniform hardness can lead to pre-
mature part failure or cracking. Because of the
importance of uniformity when quenching,
round or symmetrical parts almost always are
Fig. 23 U-shaped crankshaft hardening coil components and assembly
Fig. 24 (a) Fishtail-type and (b) flat plate machined
coil contact types
Design and Fabrication of Inductors for Induction Heat Treating / 597
10. rotated during the quenching process. Other
important considerations for quench design are
the part geometry and how the part is presented
to the quench (i.e., horizontal, vertical, etc.). In
some irregular-shaped parts, rotation is not pos-
sible, or the rotation rate is slowed to help con-
trol the quench. When quenching for surface
hardness, a vigorous or intensive quench usu-
ally is required. Because of this, the quench
usually is done with a series of relatively small
holes. These holes usually have a staggered pat-
tern. The small holes and staggered pattern
result in an intense quenching that helps to
avoid the development of steam pockets. If a
submerge (or dunk) quench is used, a fine layer
of steam usually is developed on the surface;
this steam can act as a barrier or insulator, caus-
ing a slower quench. The size of the individual
quench holes can vary from 1.5 to 5 mm (1=16 to
3=16 in.) diameter, depending on the part size
and geometry. It usually is desirable to keep
these holes as small as possible to keep the
quenching pressure higher, which helps reduce
the steam pocket described earlier. This also
helps to lock in the hardness by fully transform-
ing the martensite. One disadvantage to small
quench holes is that they are more likely to fill
with debris or quench residue; for this reason,
many quench designs for heat treating have
quench holes between 2.5 and 3.2 mm (3=32
and ⅛ in.) diameter.
Figure 26 shows a typical scanning quench
hole arrangement. The hole size is related to the
shaft or workpiece diameter, as well as a quench-
ing area, and the air gap between the quench
block and the workpiece surface (Table 2)
(Ref 9).
The quench design, like the inductor design,
should conform around the part. In some cases,
the quench can be incorporated into the induc-
tor design; in other cases, it is in a separate
quench ring or quench block. This is further
discussed in the section “Styles of Heat Treat-
ing Inductors” in this article. With regard to
the duration of quenching time, quenching typ-
ically takes longer than heating; a rule of thumb
is that the quench should be 1.5 the time of
the heating. With static heating or single-shot
heating, this can be controlled by a timer, either
in the heating station or moved to a quenching
station. To save cycle time, some equipment
has a short quench in the heating station fol-
lowed by another station to finalize the quench-
ing process. With regard to scan heating, the
quench should be designed to have direct
impingement for at least 1.5 the distance of
the heating face of the inductor. When scan-
ning, the quench holes are angled away from
the coil in the same direction that the part is
traveling. This helps to keep the water from
washing back into the inductor, and allows the
water to stay on the part as long as possible.
In either case (static heating or scanning), the
quenching should be done before the surface
of the part falls below the hardening tem-
perature, to ensure that the material is fully
transformed.
Induction Coil Cooling
As discussed earlier, induction heating uses
high currents and high power levels. Because
of this, most heat treating inductors are water
cooled. Some inductors are constructed of
copper tubing that the water flows through.
Other types of inductors are constructed from
machined copper details, with cooling passages
integrated within them. In either case, the pas-
sages must be designed for the intended power
levels and must have maximum water flow with
minimal restrictions.
Thermal degradation is caused by local or
total overheating of the coil head due to eddy
current losses in the copper, magnetic losses
in the flux concentrator, and heat transfer from
the hot surface of the part via convection and
radiation. Overheating can result in copper
cracking or deformation as well as concentrator
material degradation. Copper cracking usually
occurs in heat treating coils with a short cycle
due to thermomechanical stresses, while a grad-
ual coil deformation is more typical for contin-
uous processes (Ref 13, 14, 18, 19). Thermal
effects can strongly increase the effects of elec-
tromagnetic forces and accelerate electrical insu-
lation aging.
Copper overheating is the leading cause of
failure in heavy-loaded heat treating inductors;
this section focuses mainly on this mode of fail-
ure. For consistently manufactured inductors,
copper cracks occur in nearly the same place
on an inductor each time in a certain range of
parts produced. There are several approaches
to increasing coil life: provide additional cooling,
reduce the density of heat sources, or change the
coil design completely.
Additional cooling can be obtained by
increasing the water flow rate, reducing the water
cooling temperature, adjusting the water pocket,
or introducing additional cooling circuits. Water
flow rate is the first step, and it is increased
until the pump output limit is reached. Inductor
manufacturers generally have internal guidelines
related to best practices for water pocket and
cooling circuit design, which have been devel-
oped over the years (Table 1). These guidelines
generally are based on frequency and power
density. Once these standard options have been
exhausted, the next step is to replace the existing
pump with a larger one or to introduce a booster
pump to the system.
Sometimes on very high-power-density coils,
a limit is reached where, even with the best
cooling circuit design and very large pumps,
coil lifetime is still unsatisfactory. At this point,
it is necessary to try to minimize the localized
power density in the weak point of the inductor.
This often is challenging in complex inductors,
Fig. 25 Styles of quick-change adapters. Courtesy of Capital Induction
Fig. 26 Quench hole arrangement for scanning coil.
Source: Ref 9
Table 2 As workpiece diameter increases,
orifice size should increase to help provide
a more uniform quench
Shaft diameter Orifice size
mm in. mm in.
6.5–13 0.25–0.50 1–1.5 0.046–0.063
13–38 0.50–1.50 1.5–2.5 0.063–0.094
38 1.50 3.5–4 0.125–0.156
Source: Ref 9
598 / Equipment
11. because changing this section may have some
effect on the heat pattern in this area of the part,
as well as in the rest of the part.
To determine what high power density is, it is
important to consider the cause of the failure.
The failure mode that can be resolved with water
cooling in high-power induction heat treating
coils is mechanical fatigue caused by thermal
cycling. During each heat treating cycle, the
copper temperature rises as the power is turned
on, primarily due to current in the induction coil.
As the copper temperature increases, the copper
expands. When the power is turned off, the cop-
per rapidly cools and contracts.
Because the eddy currents are distributed non-
uniformly in the copper cross section, the tem-
perature distribution in the copper coil is also
nonuniform. Water in the induction coil removes
heat through forced convection. This means that
the rate of heat removal is directly proportional
to the heat-transfer coefficient and the tempera-
ture difference between the copper and the bulk
water. The heat-transfer coefficient depends on
the velocity of the water, the pressure of the
water (in addition to the effect of pressure on
water flow), and the temperature of the water.
In recent years, computer simulation has pro-
ven an effective tool for estimating thermal
cycles in induction coils during a heat treating
process (Ref 19–21). These recent studies were
made using some combination of electromag-
netic, thermal, and fluid dynamics codes or cor-
relations. With this method, the temperatures
that are the source of the dimensional movement
and stress are predicted. Certain guidelines for
maximum allowable temperatures are used to
ensure good life. It is envisioned that in the
future, these codes could be coupled with struc-
tural, stress, and distortion simulation.
Case Study: Single-Shot Coil Copper
Temperature Prediction
A casestudy using computer simulation to show
typical temperature distributions in a single-shot
induction hardening coil is discussed in this sec-
tion. Flux 2D is used for electromagnetic and
thermal simulation, and analytical calculations
are made for the heat-transfer coefficients. The
influence of pressure (high and low), wall thick-
ness (1, 1.5, and 3 mm, or 0.048, 0.062, and
0.125 in.), current in the coil (5,000, 7,500, and
10,000 A), and frequency (1, 3, and 10 kHz) is con-
sidered. The correlations for heat-transfer coeffi-
cient hold only to approximately 250
C (480
F)
on the interface of the copper wall with the cooling
water, so if this consideration is not met, the tem-
perature in the coil will be less accurate.
The geometry for the study is a 19 mm
(3/4 in.) square copper tube with Fluxtrol A mag-
netic flux concentrator for heating of a 38 mm
(1.5 in.) diameter shaft. The coupling gap used
for the study is 3.2 mm (⅛ in.). To limit the
number of variables, the part is not simulated
during the study. The part is approximated by
a nonmagnetic layer 6.3 mm (¼ in.) thick, with
the properties of steel above the Curie point and
the 25 mm (1 in.) diameter core, which has the
properties of cold low-carbon steel.
Figure 27 shows the temperature distribution
in the coil cross section if the current is 5000 A
at 10 kHz with low pressure and a wall thickness
of 1 mm (0.048 in.) after 10 s of heating. The
temperature is highest in the corners of the heat
face and somewhat lower in the center of the turn.
The concentrator is at a significantly lower tem-
perature, and the localized higher-temperature
areas are due to conduction through the glue to
the concentrator. The maximum temperature is
117
C (243
F). Figure 28 shows the tempera-
tures in the corner and center of the tube versus
time for this case. Nearly the entire temperature
rise in the copper occurs in the first 2 s.
If pressure is doubled, the temperature distri-
bution is that shown in Fig. 29(a). The maxi-
mum temperature in the corner is reduced
to 99
C (210
F). The difference between the
temperature in the corner of the copper and the
center of the heat face is significantly higher.
Figure 29(b) shows the temperature distribution
if the wall thickness is increased to 1.5 mm
(0.062 in.). The maximum copper temperature
is slightly higher, 102
C (216
F). If the wall
thickness is increased to 3 mm (0.125 in.), the
maximum temperature increases to approxi-
mately 111
C (232
F) (Fig. 29c).
All of these temperatures are what could
be considered reasonable, and a long copper
lifetime would be expected based on the tem-
peratures. If the current is increased to 7500 A,
the differences between the results are much
more apparent. Figure 30 shows the tempera-
ture distributions for the same cases shown in
Fig. 27 and 29 with the higher current. Now
the temperature of the copper wall contacting
the water for the low-pressure, 1 mm (0.048 in.)
wall (Fig. 30a) is above the threshold where the
correlations hold. This means that there is danger
of vapor blanket formation and very short coil
lifetime. It also is important to note that the
maximum temperature shifts to the center of
the tube instead of the corners. This is a sign that
there is insufficient cooling, and increasing the
water pressure can significantly increase the
coil lifetime.
When pressure is increased, the temperature
on the internal walls of the copper tubing
drops to manageable levels (Fig. 30b). The max-
imum temperature again is in the corners of the
copper tube instead of the center. However, the
level of the copper temperature in the corners
remains elevated (225
C, or 437
F). For the
thicker walls, the temperatures are 230 and 263
C
(446 and 505
F), respectively (Fig. 30c, d).
This means that in each cycle, the copper in the
corners of the tubing expands more than twice as
much as for the case of the lower current. When
power is turned off, the tubing contracts to its
original shape. At these temperatures, there is
the potential that the coil lifetime may not be
satisfactory.
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
22.72733 / 28.59668
28.59668 / 34.46604
34.46604 / 40.3354
40.3354 / 46.20475
46.20475 / 52.0741
52.0741 / 57.94347
57.94347 / 63.81282
63.81282 / 69.68217
69.68217 / 75.55153
75.55153 / 81.42089
81.42089 / 87.29025
87.29025 / 93.1596
93.1596 / 99.02896
99.02896 / 104.89832
104.89832 / 110.76767
110.76767 / 116.63702
Fig. 27 Temperature distribution in the induction coil with 1 mm (0.048 in.) wall thickness, 10 kHz frequency, 5000 A
current, and low-pressure cooling
Design and Fabrication of Inductors for Induction Heat Treating / 599
12. If frequency is reduced but the current re-
mains 7500 A, the coil temperatures are reduced
significantly (Fig. 31). For the case of the 1 mm
(0.048 in.) wall with low pressure, the maximum
temperature is reduced to 178
C (352
F)
(Fig. 31a). The temperature in the corners is
significantly lower than in the center. If pres-
sure is increased, the copper temperature is
reduced to 133
C (271
F) (Fig. 31b). How-
ever, the maximum temperature is still in the
central sections of the copper rather than
the corners. This is due to the wall thickness
of the copper being less than optimal (1.6d).
The low copper thickness increases resistance
and losses in the central section of the coil.
When the wall thickness is increased to
1.5 mm (0.062 in.), the copper temperature is
reduced to 114
C (237
F) (Fig. 31c). The
central temperature of the winding also is
reduced relative to the corners. The maximum
in temperature lies just inside the edge of the
water cooling, implying slightly less than opti-
mal wall thickness. For the case of the 3 mm
(0.125 in.) wall, the maximum temperature
goes up again to 125
C (257
F) (Fig. 31d).
The maximum now is clearly in the corners.
The temperature in the center of the tube
actually is lower for this case. The rise in max-
imum temperature is due to it being a farther
distance from the water cooling.
The losses in the copper tubing are nearly the
same for these two cases (3 kHz; 1.5 and 3 mm,
or 0.062 and 0.125 in., wall thickness) and just
under 20% lower than for the 1 mm (0.048 in.)
wall thickness. The optimal wall thickness and
hence the maximum current-carrying capacity for
3 kHz would lie between these two thicknesses.
At 1 kHz, 10,000 A was used for compari-
son, because at lower frequencies it is natural
to have higher currents (Fig. 32). For the
1 mm (0.048 in.) wall thickness and low pres-
sure, temperature in the copper clearly is exces-
sive, and there is a significant gradient from the
center to the corners (Fig. 32a). As pressure is
increased, the temperature is marginal (230
C,
or 446
F, wall temperature), and there is still
a significant gradient from center to edge
(Fig. 32b). This is because the wall thickness
is significantly less than optimal.
For the 1.5 mm (0.062 in.) wall thickness, the
maximum temperature declines to approxi-
mately 144
C (291
F) (Fig. 32c). Losses in
the copper are nearly 40% lower than for the
1 mm (0.048 in.) wall thickness. The tempera-
ture distribution across the face is nearly flat,
implying that the wall thickness is less than
optimal. For the 3 mm (0.125 in.) wall thick-
ness, the maximum temperature is only 100
C
(212
F), and the location is the corners
(Fig. 32d). The losses in the 3 mm (0.125 in.)
wall thickness are approximately 30% lower
than for the 1.5 mm (0.062 in.) wall thickness.
Another factor related to water cooling of
induction coils is the water temperature. The
temperature of the induction coil is influenced
in two ways by the water temperature. It is clear
that the lower the water temperature, the cooler
the induction coil, because the cooling method
is convection. If the water temperature was
lowered by 10
C (18
F), then it would be
expected that the maximum temperature in the
copper also would be 10
C (18
F) lower.
Because the temperature change (DT) of the
copper would be the same, one would expect
that the magnitude of the copper movement
would be the same, and coil lifetime would be
also. However, this is not true, because the
coefficient of thermal expansion of copper is
not constant with temperature (Fig. 33). As
temperature rises, the coefficient of thermal
expansion of copper continues to rise (Ref 22).
This means that the higher the temperature, the
larger the movement for the same DT.
In reality, the DT of the copper is not the
same. It actually is slightly less, because the cop-
per electrical resistivity rises with temperature.
Therefore, the losses in the copper are lower,
and the resulting DT smaller. This overrides the
fact that the heat-transfer coefficient of water is
slightly lower at lower temperature (Ref 23).
The last factor to consider with water cooling
of inductors is the water quality. The best fluid
for cooling induction coils in heat treating
applications is pure, demineralized water. Pure
water has a naturally high heat-transfer coeffi-
cient. Almost all additives have a negative
effect on the heat-transfer capability.
Minerals are especially bad. Over time, they
tend to fall out of solution and build up on the
wall of the copper tubing. This has two nega-
tive effects. First, the mineral layer reduces
the cross section for water flow. The mineral
layer also creates a barrier for heat transfer,
causing the temperature of the copper to rise.
If water containing minerals is used, over time
the copper temperature continues to rise and
reach a critical level, resulting in an inductor
failure. With this type of cooling fluid, the
induction coil must be cleaned and flushed on
a regular interval.
Styles of Heat Treating Inductors
As stated previously, induction heat treating
coils come in many shapes and sizes. An excel-
lent source for photos of induction heat treat-
ing coils is the book Practical Induction Heat
Treating by Richard Haimbaugh (Ref 5). These
photos are included in Steel Heat Treating Fun-
damentals and Processes, Volume 4A of ASM
Handbook, 2013, so they are not repeated here.
Skills for Heat Treating Inductor
Construction
Copper is a unique metal associated with
an ancient skills trade—coppersmithing. While
training as either a craftsman or an artisan, a
student coppersmith would apprentice under a
journeyman to learn the character and manipu-
lation of this metal. Although the United States
has assimilated the coppersmith into other skilled
trades, coppersmithing is still a recognized trade
throughout the industrialized world.
The tools and skills of a coppersmith are ide-
ally matched to the metal; however, is a copper-
smith by trade needed to build a copper
inductor? The answer is no; yet, the skills of a
coppersmith must be learned in the process of
building heat treating inductors, along with a
familiarity of high-power electrical circuits.
Basic Skills
Because copper has a characteristic of being
easily formed into complex shapes, a craftsman
handy with tools, a soldering iron, and a propane
torch is able to build a good basic inductor. In
the process of forming, copper work hardens;
yet, when heated to a dull red and quenched in
water, it again forms easily. Basic inductors are
made of readily available copper tubing wound
Fig. 28 Temperature dynamics during heating at critical points with 1 mm (0.048 in.) wall thickness, 10 kHz frequency,
5000 A current, and high-pressure cooling
600 / Equipment
13. around a forming mandrel. Copper tubing pro-
vides a convenient path necessary to cool the
copper. Depending on the induction power supply
configuration, simple electrical connections may
be brass pipe fittings—either flair or compres-
sion, although flair is preferred—or copper tabs
that are soldered to the tube, as mentioned
previously. Electrical soft solder is sufficient
at power requirements of 10 kW or less.
Advanced Skills
A classically trained machinist is the usual
tradesman employed to build heat treating
inductors. A suitable candidate has the ability,
dexterity, and patience for modelmaking. Most
will have difficulty machining copper unless
instruction is provided in the use of special
cutting tools, speeds, feeds, and coolant specific
to this metal. Much of the work in building
complex inductors involves a quantity of small
parts and various materials that require machin-
ing, forming, silver brazing, and assembly. Heat
treating inductors usually are built one at a
time, and one machinist may do all of the work.
A simple machine shop consisting of a floor
model milling machine, lathe, band-type table
saw, a ventilated brazing table with torches,
and assembly bench with a variety of hand tools
makes a suitable work area.
Most inductors are best built from design
prints. A good print package has a bill of material,
details of all components, and an assembly and
inspection form. In some cases, the inductor may
be built by reverse engineering the original. The
following should be considered during the con-
struction of heat treating inductors:
Machining: Most of the raw material in a
typical heat treating inductor is in the form
of electrolytic copper sheet, plate or round.
Due to the gummy nature of the metal, cutters,
feeds, speeds, and coolant specifically design-
ed for copper are advised for milling, drilling,
and turning operations.
Fabrication: Many parts may be needed
to complete a heat treating inductor as-
sembly. Some of these parts are fit to provide
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
21.3703 / 26.22846
26.22846 / 31.08662
31.08662 / 35.94477
35.94477 / 40.80293
40.80293 / 45.66109
45.66109 / 50.51925
50.51925 / 55.37741
55.37741 / 60.23556
60.23556 / 65.09372
65.09372 / 69.95189
69.95189 / 74.81004
74.81004 / 79.6682
79.6682 / 84.52635
84.52635 / 89.38452
89.38452 / 94.24268
94.24268 / 99.10083
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
22.26987 / 27.27455
27.27455 / 32.27923
32.27923 / 37.28391
37.28391 / 42.28858
42.28858 / 47.29326
47.29326 / 52.29794
52.29794 / 57.30262
57.30262 / 62.3073
62.3073 / 67.31197
67.31197 / 72.31666
72.31666 / 77.32133
77.32133 / 82.32601
82.32601 / 87.3307
87.3307 / 92.33537
92.33537 / 97.34005
97.34005 / 102.34473
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
29.39038 / 34.47861
34.47861 / 39.56684
39.56684 / 44.65507
44.65507 / 49.74329
49.74329 / 54.83152
54.83152 / 59.91975
59.91975 / 65.00798
65.00798 / 70.09621
70.09621 / 75.18443
75.18443 / 80.27267
80.27267 / 85.36089
85.36089 / 90.44912
90.44912 / 95.53735
95.53735 / 100.62558
100.62558 / 105.71381
105.71381 / 110.80203
(a)
(b)
(c)
Fig. 29 Temperature distribution in the induction coil with wall thicknesses of (a) 1 mm (0.048 in.), (b) 1.5 mm (0.062 in.), and (c) 3 mm (0.125 in.) with 10 kHz frequency, 5000
A current, and high-pressure cooling
Design and Fabrication of Inductors for Induction Heat Treating / 601
14. covers for cooling chambers and ancillary con-
nections that involve cooling or quench or
both. Integrity of fit is necessary to provide
watertight and quality electrical connections.
Silver brazing: While some fuel gases are
best suited for silver brazing, choosing an
appropriate fuel, such as methyl-acetylene-
propadiene gas, to mix with compressed
oxygen may be subject to limited availabil-
ity. Torch heat must be sufficient to maintain
silver brazing temperatures throughout the
copper mass. A variety of torch tips are
needed, along with flux and 1.5 mm (0.06 in.)
silver brazing rod. The silver content of the
brazing rod best suited for inductor construc-
tion is at 5 to 45%. Silver brazing is a skill
that can be difficult; however, with practice,
patience, and perseverance, the technique can
be mastered.
Repair Skills
Copper inductors sometimes are subjected to
the extreme conditions of induction heat treat-
ing: electromagnetic stress, intense heat, oily
smoke, steam, dirt, and grime. The effects on
copper can be severe, resulting in deterioration
and fatigue of the inductor and, ultimately, the
heat treating process. Inductor maintenance
is essential. Cleaning the inductor with soap,
water, and a soft plastic brush, along with regu-
lar inspection of the copper and components,
alerts the induction operator to deterioration
and performance issues.
Repair skills are advanced. The inductor is
cleaned, disassembled, and inspected for deterio-
ration of copper as well as for leaks and cracks.
Cosmetic repairs such as straightening bent com-
ponents usually can be made without annealing
the copper. Ancillary components such as flux
intensifiers, brackets, guides, and quench units
are cleaned and inspected for damage and are
repaired or replaced.
Cracks in a copper inductor can result from
any of the following: cyclic fatigue, differen-
tial cooling of the copper, resistive braze
joints, and abuse. Cracks often are repaired
with silver braze. Although this patch may be a
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
26.80051 / 42.98555
42.98555 / 59.17058
59.17058 / 75.35562
75.35562 / 91.54066
91.54066 / 107.72571
107.72571 / 123.91074
123.91074 / 140.09578
140.09578 / 156.28082
156.28082 / 172.46587
172.46587 / 188.65089
188.65089 / 204.83594
204.83594 / 221.02098
221.02098 / 237.20601
237.20601 / 253.39107
253.39107 / 269.57611
269.57611 / 285.76114
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
23.08636 / 35.74352
35.74352 / 48.40069
48.40069 / 61.05785
61.05785 / 73.715
73.715 / 86.37217
86.37217 / 99.02933
99.02933 / 111.68649
111.68649 / 124.34365
124.34365 / 137.00079
137.00079 / 149.65796
149.65796 / 162.31512
162.31512 / 174.97227
174.97227 / 187.62944
187.62944 / 200.28659
200.28659 / 212.94376
212.94376 / 225.60092
Color Shade Results
(a) (b)
(d)(c)
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
22.30582 / 35.28288
35.28288 / 48.25994
48.25994 / 61.2361
61.2361 / 74.21406
74.21406 / 87.19112
87.19112 / 100.16818
100.16818 / 113.14524
113.14524 / 126.12231
126.12231 / 139.09935
139.09935 / 152.07642
152.07642 / 165.05348
165.05348 / 178.03053
178.03053 / 191.0076
191.0076 / 203.98465
203.98465 / 216.96172
216.96172 / 229.93878
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
38.29016 / 52.3344
52.3344 / 66.37862
66.37862 / 80.42286
80.42286 / 94.46709
94.46709 / 108.51132
108.51132 / 122.55556
122.55556 / 136.59979
136.59979 / 150.64403
150.64403 / 164.68826
164.68826 / 178.7325
178.7325 / 192.77672
192.77672 / 206.82095
206.82095 / 220.86519
220.86519 / 234.90942
234.90942 / 248.95366
248.95366 / 262.99789
Fig. 30 Temperature distribution in the induction coil with (a) 1 mm (0.048 in.) wall thickness, 10 kHz frequency, 7500 A current, and low-pressure cooling; (b) 1 mm (0.048 in.)
wall thickness, 10 kHz frequency, 7500 A current, and high-pressure cooling; (c) 1.5 mm (0.062 in.) wall thickness, 10 kHz frequency, 7500 A current, and high-pressure
cooling; and (d) 3 mm (0.125 in.) wall thickness, 10 kHz frequency, 7500 A current, and high-pressure cooling
602 / Equipment
15. cost-effective repair, it is seldom permanent. In
a robust process, the copper inductor should be
replaced at an appropriate time/life interval.
Attachment of Magnetic Flux
Controllers
It has been explained that flux controllers are
needed to direct the current flow for specific
induction heating applications. Attaching them
to the inductor requires careful handling so
that they are properly placed and secure.
Misplacement or loss of any portion of a magnetic
flux controller may result in a nonconforming
processed part. Magnetic flux controllers are fre-
quency dependent and made from either a silicon
steel, soft magnetic ferrite, or a soft magnetic
composite. Attaching these materials to an induc-
tor can present a challenge to the designer/builder.
The following are a few examples.
Silicon Steel Laminations
This material is supplied in a variety of
grades, thicknesses, and finishes. Its usual form
is a thin sheet with an insulating layer on both
sides. It is first designed to a specific shape, then
die stamped or machined and to fit the inductor.
The most common shape is a rectangular or
square “C” form. The laminations are stacked
side by side onto the inductor in such a way as
to expose that portion of the copper to the part
being heated. Copper tabs of the same shape
are silver brazed onto the inductor at various
intervals in order to support the stack. Securing
the stack is achieved by either gluing with a
high-temperature epoxy or by mechanically
clamping it to the inductor. Various clamping
methods are used. The most common is the
use of a semirigid glass epoxy circuit board
(a) (b)
(d)(c)
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
23.992 / 33.64118
33.64118 / 43.29035
43.29035 / 52.93953
52.93953 / 62.58871
62.58871 / 72.23788
72.23788 / 81.88705
81.88705 / 91.53623
91.53623 / 101.18541
101.18541 / 110.83459
110.83459 / 120.48376
120.48376 / 130.13293
130.13293 / 139.78212
139.78212 / 149.43129
149.43129 / 159.08047
159.08047 / 168.72964
168.72964 / 178.37881
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
21.77783 / 28.7492
28.7492 / 35.72057
35.72057 / 42.69193
42.69193 / 49.6633
49.6633 / 56.63467
56.63467 / 63.60603
63.60603 / 70.5774
70.5774 / 77.54877
77.54877 / 84.52013
84.52013 / 91.4915
91.4915 / 98.46287
98.46287 / 105.43423
105.43423 / 112.4056
112.4056 / 119.37697
119.37697 / 126.34834
126.34834 / 133.3197
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
22.64523 / 28.33354
28.33354 / 34.02185
34.02185 / 39.71016
39.71016 / 45.39847
45.39847 / 51.08678
51.08678 / 56.77509
56.77509 / 62.46339
62.46339 / 68.1517
68.1517 / 73.84001
73.84001 / 79.52832
79.52832 / 85.21663
85.21663 / 90.90494
90.90494 / 96.59325
96.59325 / 102.28156
102.28156 / 107.96986
107.96986 / 113.65817
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
29.76266 / 35.69722
35.69722 / 41.63177
41.63177 / 47.56632
47.56632 / 53.50088
53.50088 / 59.43542
59.43542 / 65.36998
65.36998 / 71.30453
71.30453 / 77.23909
77.23909 / 83.17365
83.17365 / 89.10819
89.10819 / 95.04275
95.04275 / 100.9773
100.9773 / 106.91185
106.91185 / 112.84641
112.84641 / 118.78096
118.78096 / 124.71552
Fig. 31 Temperature distribution in the induction coil with (a) 1 mm (0.048 in.) wall thickness, 3 kHz frequency, 7500 A current, and low-pressure cooling; (b) 1 mm (0.048 in.)
wall thickness, 3 kHz frequency, 7500 A current, and high-pressure cooling; (c) 1.5 mm (0.062 in.) wall thickness, 3 kHz frequency, 7500 A current, and high-pressure
cooling; and (d) 3 mm (0.125 in.) wall thickness, 3 kHz frequency, 7500 A current, and high-pressure cooling
Design and Fabrication of Inductors for Induction Heat Treating / 603
16. material, such as G-10, that is cut and fit to
the back of the stack and is fastened at both ends.
It is practical to stack laminations around
the outside or inside of an inductor loop. Installed
onto circular inductors, the laminations radiate
from the center point, leaving noticeable gaps,
especially on small, circular inductors; yet, with
careful design, this can be minimized.
Soft Magnetic Composites and
Sintered Ferrites
These products are engineered and manufac-
tured for specific induction applications. Because
sintered ferrites are brittle and difficult to
machine, their use mainly has been limited to
transformer applications. Soft magnetic compo-
sites, however, have been designed specifically
for the induction heating industry. These products
are engineered to be used at the common power-
supply frequencies. They are manufactured in
various block sizes, are easily machined, and
fit to the inductor. Both iron ferrites and
soft magnetic composites are attached to the
inductor, either mechanically with bolts and
screws or with glue. The product literature
describes their use in induction heating applica-
tions (Ref 13).
Integrity Procedures prior to
Production
This section includes discussion on flux and
oxide removal, leak and flow checking, silver
plating, and electrical parameter measurement.
Flux and Oxide Removal
After brazing, the induction coil copper has flux
near the braze joints, along with oxidation from
the high-temperature brazing process. Prior to
assembly, the flux and oxides should be removed.
(a) (b)
(d)(c)
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
28.14111 / 49.29983
49.29983 / 70.45855
70.45855 / 91.61726
91.61726 / 112.77598
112.77598 / 133.93469
133.93469 / 155.0934
155.0934 / 176.25212
176.25212 / 197.41084
197.41084 / 218.56955
218.56955 / 239.72827
239.72827 / 260.88699
260.88699 / 282.04572
282.04572 / 303.20441
303.20441 / 324.36313
324.36313 / 345.52185
345.52185 / 366.68057
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
23.12088 / 36.80721
36.80721 / 50.49354
50.49354 / 64.17987
64.17987 / 77.8662
77.8662 / 91.55252
91.55252 / 105.23886
105.23886 / 118.92519
118.92519 / 132.61151
132.61151 / 146.29784
146.29784 / 159.98418
159.98418 / 173.6705
173.6705 / 187.35683
187.35683 / 201.04317
201.04317 / 214.72949
214.72949 / 228.41582
228.41582 / 242.10214
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
23.82666 / 31.32733
31.32733 / 38.8271
38.8271 / 46.32866
46.32866 / 53.82932
53.82932 / 61.32999
61.32999 / 68.83066
68.83066 / 76.33132
76.33132 / 83.83199
83.83199 / 91.33265
91.33265 / 98.83332
98.83332 / 106.33398
106.33398 / 113.83465
113.83465 / 121.33532
121.33532 / 128.83597
128.83597 / 136.33664
136.33664 / 143.83731
Color Shade Results
Quantity : Temperature Deg. Celsius
Time (s.) : 10 Phase (Deg): 0
Scale / Color
29.53604 / 34.54433
34.54433 / 39.5526
39.5526 / 44.56089
44.56089 / 49.56918
49.56918 / 54.57746
54.57746 / 59.58574
59.58574 / 64.59402
64.59402 / 69.60231
69.60231 / 74.6106
74.6106 / 79.61887
79.61887 / 84.62716
84.62716 / 89.63544
89.63544 / 94.64372
94.64372 / 99.65201
99.65201 / 104.66029
104.66029 / 109.66858
Fig. 32 Temperature distribution in the induction coil with (a) 1 mm (0.048 in.) wall thickness, 1 kHz frequency, 10,000 A current, and low-pressure cooling; (b) 1 mm (0.048 in.)
wall thickness, 1 kHz frequency, 10,000 A current, and high-pressure cooling; (c) 1.5 mm (0.062 in.) wall thickness, 1 kHz frequency, 10,000 A current, and high-pressure
cooling; and (d) 3 mm (0.125 in.) wall thickness, 1 kHz frequency, 10,000 A current, and high-pressure cooling
604 / Equipment
17. The first step in the process is to place the
induction coil under hot (70 to 80
C, or 150 to
180
F) running water. Hot water helps to
remove the bulk of the flux remaining from the
brazing process. It also is recommended to flow
the hot water through the water-cooling passages
of the inductor to remove flux that could be built
up on the inside of the tube and obstructing the
passage.
After the hot water cleaning, the next step
in the process is to sandblast the inductor to
remove the oxides. The sandblasting process
also removes the remaining flux from the induc-
tor. After sandblasting, a fine glass beading pro-
cess should be used to improve the surface
condition of the inductor.
After glass beading, the copper is clean. If left
this way, the inductor oxidizes in air and change
color. It is good practice to spray the surface of
the induction coil (with the exception of the
electrical contacts) with a clear coat varnish.
The varnish inhibits copper oxidation.
In some cases with heavily loaded heat treat-
ing inductors, a low-temperature tempering at
200
C (400
F) for several hours or a higher-
temperature annealing process in air is per-
formed. This tempering process removes the
stresses from manufacturing and oxidizes the
copper to a dark orange (tempering) or a dark
brown (annealing). From this state, the copper
does not oxidize further, and it is not necessary
to apply a clear coat varnish.
Leak and Flow Checking
After cleaning the induction coil, it is neces-
sary to ensure that it is leaktight and that the
water passages are not clogged. Leak checking
of the induction coil typically is done by sub-
merging the induction coil in a tank of water
and applying high-pressure shop air. The test
should be conducted for several minutes. If
bubbles appear, the coil must be sent back to the
coil builder to repair the leak. In some special
atmosphere heat treating applications, a water
leak is especially dangerous. In these instances,
helium leak checking should be performed.
After leak checking, the induction coil
should be connected to water lines. With a spe-
cific pressure applied, the flow rate of the water
through the induction coil should be measured.
For every induction coil, a minimum flow rate
should be defined. If the flow rate does not meet
this minimum level, it means that the cooling
channel is obstructed. The obstruction must be
removed before the induction coil can be
shipped; therefore, the induction coil should
be sent back to the coil builder.
Silver Plating
Silver plating of the induction coil contacts
typically is done after cleaning. The main role
of silver plating is to act as a corrosion inhibitor
for the electrical contacts. Corrosion increases
the contact resistance and can lead to premature
induction coil failure.
Silver plating materials can come in liquid,
paste, or powder form. Liquid silver plating solu-
tion from HM Products Inc. is most commonly
used in the trade. The solution is either brushed
or rubbed onto the contact area. After application,
the contact area is flushed with water. If the sur-
faceis not flushed with water shortly after applica-
tion, the silver carrier corrodes the contacts, and a
green oxide formation occurs. Care should be
taken while using the silver plating materials,
because most of them contain sodium cyanide,
which is a toxic material.
Electrical Parameter Measurement
On some induction coils, such as cast or
potted inductors, it is not possible to physically
see or mechanically inspect all of the critical
dimensions of the induction coil. Also, on induc-
tion coils with magnetic flux controllers, it is not
practical to count the number of laminations, or
it may be difficult to determine if the correct soft
magnetic composite material grade was used.
To ensure that the induction coil perfor-
mance is consistent with other induction coils
built to that print, coil electrical parameter mea-
surements should be made prior to shipping.
The best inspection method involves measur-
ing the inductance or impedance and the resis-
tance of the induction coil with the component
it is designed to heat at the frequency of the
heating. If this is not possible, valuable informa-
tion can be obtained about the coil consistency
from a measurement of the inductance without
a part.
Devices capable of measuring coil inductance
or impedance and resistance (LCR meters) at a
selectable frequency typically cost several thou-
sand dollars and are available from a number
of manufacturers. For inductance measurement
only, less-expensive devices are available. At
the time of this writing, one such device that
works well, the L/C Meter IIB, is manufactured
by Almost All Digital Electronics and costs
under $200 (Ref 24). Over time, new devices
will come to the market with even better charac-
teristics for induction coil quality control.
REFERENCES
1. A. Muhlbauer, History of Induction Heat-
ing and Melting, Vulcan Verlag GmbH,
Huyssenallee, Essen, Germany, 2008
2. H.B. Osborne, Jr., Induction Heating and
Hardening, Part A, American Society for
Metals, Metals Park, OH, 1977
3. V.P. Vologdin and B.N. Romanov, Device
for Hardening Crankshafts Using HF Cur-
rents, USSR Patent 48416, filed Dec 16,
1935, issued 1936
4. V.P. Vologdin, Induction Surface Harden-
ing, Oborongiz, Moscow, 1947
5. R.E. Haimbaugh, Practical Induction Heat
Treating, ASM International, Materials
Park, OH, 2001
6. C.A. Tudbury, Basics of Induction Heating,
Vol 1, John F. Rider, New York, NY, 1960
7. S.L. Semiatin and D.E. Stutz, Induction
Heat Treatment of Steel, American Society
for Metals, Metals Park, OH, 1986
8. M.G. Lozinskiy, Industrial Applications
of Induction Heating, Pergamon Press,
Oxford, London, New York, 1969
9. V. Rudnev et al.,Handbook of Induction Heat-
ing, Marcel Dekker, New York, NY, 2003
10. R.C. Goldstein et al., “Virtual Prototyping
of Induction Heat Treating,” 25th ASM
Heat Treating Society Conference, Sept
14–17, 2009 (Indianapolis, IN)
0
20
200 400
Temperature, K
600 800
15
10
Coefficientofthermalexpansion
Thermal expansion of copper data
5
0
Fig. 33 Temperature dependence of the coefficient of thermal expansion of copper. Source: Ref 22
Design and Fabrication of Inductors for Induction Heat Treating / 605
18. 11. J. Cai et al., Integration of Induction Heat
Treat Simulation into Manufacturing Cycle,
J. Heat Treat. Prog., Vol 3 (No. 2), 2003
12. V.S. Nemkov, Modeling of Induction
Hardening Processes, Handbook of Ther-
mal Process Modeling of Steel, C.H. Gur
and J. Pan, Ed., CRC Press, 2009
13. W.I. Stuehr and D. Lynch, “How to
Improve Inductor Life,” 23rd ASM Heat
Treating Society Conference, Sept 25–28,
2005 (Pittsburgh, PA)
14. W.I. Stuehr and D. Lynch, “How to
Improve Inductor Life, Part II,” 24th ASM
Heat Treating Society Conference, Sept
17–19, 2007 (Detroit, MI)
15. Ajax Tocco Magnethermic, http://www.
ajaxtocco.com/default.asp?ID=134
16. V.S. Nemkov and R.C. Goldstein, Design
Principles for Induction Heating and
Hardening, Chap. 15, Handbook of Metal-
lurgical Process Design, G. Totten, K.
Funatani, and L. Xie, Ed., Marcel Dekker,
New York, NY, 2004
17. V.S. Nemkov, Resource Guide for Induction
Heating, CD-R, Fluxtrol Inc., 2006
18. V.I. Rudnev, Systematic Analysis of Induc-
tion Coil Failure, Parts 1–11, Heat Treat.
Prog. Mag., Aug 2005–Sept/Oct 2007
19. H. Svendsen and S.T. Hagen, “Thermo-
Mechanical Fatigue Life Estimation of
Induction Coils,” International Scientific
Colloquium on Modeling of Electromagnetic
Processing, Oct 27–29, 2008 (Hannover,
Germany)
20. R.C. Goldstein and V.S. Nemkov, “Influ-
ence of Cooling Conditions on Induction
Coil Temperatures,” International Sympo-
sium on Heating by Internal Sources
(Padua, Italy), 2007
21. H. Svendsen and S.T. Hagen, “Temperature
Distribution in Selected Cross-Sections of
Induction Heating Coils,” International
Symposium on Heating by Internal Sources
(Padua, Italy), 2007
22. Case Studies in Process Modeling, Engi-
neering Statistics Handbook, NIST/
SEMATECH, http://www.itl.nist.gov/div898/
handbook/pmd/section6/pmd6.htm
23. Fluxtrol, Inc. internal documents
24. L/C Meter IIB, Almost All Digital Elec-
tronics, http://aade.com/lcmeter.htm
606 / Equipment