The document discusses various aspects of rolling processes. It defines rolling as a metalworking process that uses compressive forces exerted by rolls to reduce the thickness or change the cross-section of a workpiece. It describes the basic components of a rolling mill and the functions of rolls. It also discusses types of rolling like flat rolling, shape rolling, ring rolling, and thread rolling. Key differences between hot and cold rolling are explained along with advantages and disadvantages of each. Various products produced from rolling like plates, sheets, strips are also mentioned.
2. ROLLING
Deformation process in which work thickness is reduced by
compressive forces exerted by two opposing rolls
The rolling process (specifically, flat rolling)
3. ROLLING
This is the process of reducing the thickness or
changing the cross-section of a work-piece by
compressive forces exerted by a pair of rotating
rolls. or
The process of plastically deforming
metal by passing it between rolls.
The products are flat products, like: plates &
sheets.
Plates are used for structural applications like
bridges, ships & nuclear vessels.
Sheets (generally 6mm or less in thickness) are
used for automotive, beverage cans, office &
kitchen equipment.
6. CONT……..
• Rolling is the most widely used
forming process, which provides high
production and close control of final
product.
• The metal is subjected to high
compressive stresses as a result of
the friction between the rolls and the metal
surface
8. THE ROLLS
The rotating rolls perform two main functions:
• Pull the work into the gap between them by
friction between work-part and rolls
• Simultaneously squeeze the work to reduce
cross section
9. WHERE
IT
IS
DONE
Rolling mill is a machine or a factoryfor
shaping metal by passing it through
rollers
A rolling mill basically consists of
• rolls
• bearings
• a housing for containing these parts
• a drive (motor) for applying power
to the rolls and controlling the
speed
10. TERMINOLOGY
Bloom is the product of first breakdown
of ingot
(cross sectional area > 230 cm2).
Billet is the product obtained from a
further reduction by hot rolling
(cross sectional area > 40x40 mm2).
Slab is the hot rolledingot
(cross sectional area > 100 cm2 and with
a width ≥ 2 x thickness).
12. TYPES OF ROLLING
• Based on work piece geometry :
– Flat rolling - used to reduce thickness of a rectangular
cross section
– Shape rolling - square cross section is formed into a
shape such as an I-beam
• Based on work temperature :
– Hot Rolling – most common due to the large amount
of deformation required
– Cold rolling – produces finished sheet and plate stock
13. Some of the steel products made in a rolling mill
14. FLAT ROLLING AND ITS
ANALYSIS
R = roller radius
p = roll pressure
L = contact length
θ = contact angle
vr = rollspeed
to = initial plate
thickness
tf = final plate thickness
vo = plate entry speed
vf = plate exitspeed
Side view of flat rolling, indicating before and after thicknesses,
work velocities, angle of contact with rolls, and other features.
15. FLAT ROLLING AND ITS
ANALYSIS
• The work enters the gap between the rolls at a velocity vo and
exits at a velocity vf. Because the volume flow rate is constant
and the thickness is decreasing, vf should be larger than vo.
• The roll surface velocity vr is larger than vo and smaller than vf.
This means that slipping occurs between the work and the rolls.
• Only at one point along the contact length, there is no slipping
(relative motion) between the work and the roll. This point is
called the “Neutral Point” or the “No Slip Point”.
16. FLAT ROLLING AND ITS
ANALYSIS
• In flat rolling, the work is squeezed between two rolls
so that its thickness is reduced by an amount called
the draft:
where
d: draft
to: starting thickness
tf : final thickness
d to t f
17. FLAT ROLLING AND ITS ANALYSIS
• Rolling may not be possible (the sheet will not be pulled) if the
draft is large. The maximum draft for successful rolling per pass
is:
Where:
dmax : maximum draft successful rolling perpass
μ : coefficient of friction
R : roll radius
d 2
R
max
to t f
2
R
of passes
Number
18. Example:- A series of cold rolling operations is to be used to reduce
the thickness of a plate from 50 mm down to 25 mm in a reversing two
high mill. Roll diameter =700 mm and coefficient of friction between
rolls and work = 0.15. The specification is that the draft is to be equal
on each pass.
Determine (a) minimum number of passes required, and
(b) draft for each pass.
Solution
4 passes
3.17
0.15 350
50 - 25
of passes
number 2
2
R
to t f
4
50 - 25
of passes
number
per pass
Draft 6.25 mm
to t f
19. HOT ROLLING
Hot rolling is
a metalworking process that occurs above
the recrystallization temperature of the
material.
Hot rolled metals generally have little directionality
in their mechanical properties and deformation
induced residual stresses.
However, in certain instances non- metallic
inclusions will impart some directionality
20. Also includes
cooling ....
Hot rolling is used mainly to produce sheet metal
or simple cross sections, such as rail tracks.
Non-uniformed cooling will
induce a lot of residual
stresses, which usually occurs
in shapes that have a non-
uniform cross-section, such
as I-beams and H-beams.
APPLICATION
21. Advantages Of Hot Rolling Process
Hot rolling can greatly reduce energy consumption and costs.
The metal plastic deformation is high during hot rolling, and the
deformation resistance is low,
which reduces the energy consumption of metal deformation.
Hot rolling can improve the processing performance of metals and
alloys. That is to say, the coarse grains during foundry are broken, the
cracks are healed, the casting
defects are reduced or eliminated, and the as-cast microstructure is
transformed into a
deformed structure to improve the processing properties of the alloy.
Hot rolling usually uses large ingots and large reduction rolling, which
not only improves
production efficiency, but also creates conditions for increasing rolling
speed and achieving
continuous and automated rolling process.
22. Disadvantages Of Hot Rolling Process
After hot rolling, non-metallic inclusions (mainly
sulfides and oxides, as well as silicates) inside the
steel are pressed into thin
sheets, causing delamination (sandwich).
The delamination greatly deteriorates the tensile
properties of the steel in the thickness direction,
and it is possible that interlinear tearing occurs
when the weld is shrunk.
The local strain induced by weld shrinkage often
reaches several times the yield point strain and is
much larger than the strain caused by the load.
Residual stress caused by uneven cooling.
23. The residual stress is the internal
self-phase equilibrium stress without
external force.
The hot-rolled steel of various
sections has such residual stress.
The larger the section size of the
general section steel, the larger the
residual stress.
Although the residual stress is self-
phase-balanced, it still has some
influence on the performance of
steel members under external force.
24. Such as deformation, stability, fatigue and other aspects may
have adverse effects.
Hot rolling does not control the mechanical properties required
for the product accurately, and the microstructure and
properties of the hot rolled product are not uniform.
The strength index is lower than that of the cold work
hardened product, and higher than the fully annealed product,
the
plasticity index is higher than that of the cold work hardened
product, and lower than the fully annealed product.
The thickness of the hot rolled product is difficult to control
and the control precision is relatively poor; the rough Ra value
of
the surface of the hot rolled product is generally 0.5 to 1.5 μm.
Therefore, hot rolled products are generally used as blanks for
cold rolling.
25. COLD ROLLING
Cold rolling occurs with the
metal below its
recrystallization temperature
(usually at room temperature).
It also improves the surface finish and
holds tighter tolerances.
Due to smaller size of the workpieces
and their greater strength than hot
rolled stock, four-high or cluster mills
are used.
Commonly cold-rolled products include
sheets, strips and rods; products being
smaller than the same products that are
hot rolled.
30. Advantages Of Cold Rolling Process
No heating required
Better surface finish obtained
Superior dimension control
Better reproducibility and
interchangeability of parts
Improved strength properties
Directional properties can be
minimized
31. Disadvantages Of Cold Rolling Process
Higher forces required for deformation
Heavier and more powerful equipment
required
Less ductility available
Metal surfaces must be clean and scale-free
Strain hardening occurs (may require
intermediate anneals)
Imparted directional properties may be
detrimental
May produce undesirable residual stresses
32. Application Of Cold Rolling Process
▪
Foil- The Thickness is less than 0.2 mm, used
mainly in the packaging industry Foil is also used
for building insulation, electrical applications and
in the printing industry.
Sheet-Thickness ranges from 0.2 mm and 6mm,
used for a wide variety of industry including
construction where it is used in aluminum siding
and roofing. Sheet is also used in transport sectors
for making automobile body panels, airframes etc.
Plate-It is the rolled product, which is over 6mm
in thickness. It also has a number of applications
including airframes, defence vehicles and
structural components in building
38. CONTINOUS
The objective is to decrease the
thickness of the metal with an
increase in length and with little
increase in width.
39. TRANSVERSE
•Using circular wedge rolls.
•Heated bar is cropped to
length and
fed in transversely between
rolls.
•Rolls are revolved in one
direction.
40. SECTION OR SHAPE
Flat slap is progressively bent into complex shapes
Suitable for producing moulded sections such as irregular
shaped channels and trim.
41. SHAPE-ROLLING OPERATIONS
• Various shapes can be produced by shape rolling
– Bars
– Channels
– I-beams
– Railroad rails
• Roll-pass design requires considerable experience in
order to avoid external and internal defects
42. RING
A specialized type of hot rolling that increases the
diameter of a ring
The resulting grain structure is circumferential, which
gives better mechanical properties
43. RING ROLLING
Deformation process in which a thick-walled ring of smaller diameter
is rolled into a thin walled ring of larger diameter
• As thick-walled ring is compressed, deformed metal elongates,
causing diameter of ring to be enlarged
• Hot working process for large rings and cold working process for
smaller rings
• Applications: ball and roller bearing races, steel tires for railroad
wheels, and rings for pipes, pressure vessels, and rotating
machinery
• Advantages: material savings, ideal grain orientation,
strengthening through cold working
44. RING ROLLING
Ring rolling used to reduce the wall thickness and increase
the diameter of a ring:
(1) start, and (2) completion of process
45. CONTINOUS CASTING
AND HOT ROLLING
• Metal is melted, cast and hot rolled continuously
through a series of rolling mills within the same
process.
46. THREAD
• Rolled threads are produced in a single pass at speeds
far in excess of those used to cut threads.
• Dies are pressed against the surface of cylindrical
blank. As the blank rolls against the in-feeding die
faces, the material is displaced to form the roots of
the thread, and the displaced material flows radially
outward to form the thread's crest.
47. THREAD ROLLING
Bulk deformation process used to form threads on cylindrical parts
by rolling them between two dies
• Most important commercial process for mass producing bolts and
screws
• Performed by cold working in thread rolling machines
• Advantages over thread cutting (machining):
– Higher production rates
– Better material utilization
– Stronger threads due to work hardening
– Better fatigue resistance due to compressive stresses
introduced by rolling
50. Defects in Rolled Products:
Some of the common defects in rolled products are given
below:
(i) Edge Cracking:
Edge cracking generally occurs in rolled ingots, slabs, or
plates. This is due to, either limited ductility of the work metal
or uneven deformation, especially at the edges.
(ii) Folds:
Folds are a defect generally occurs in plate rolling. This is
caused if the reduction per pass is too small.
(iii) Alligatoring:
Alligatoring is the defect, usually occurs in the rolling of slabs
(particularly aluminum and alloys). In this defect, the work
piece splits along a horizontal plane on exit, with the top and
bottom. This defect always occurs when the ratio of slab
thickness to the length of contact fall within the range of 1.4
to 1.65. Fig. 2.15. Shows the defect of Alligatoring.