Fabrication and Characterization of Graphene-Barium Titanate-Graphene layered capacitors by spin coating at low processing temperatures
Authors:
M. S. Habib,
S. F. U. Farhad,
N. I. Tanvir,
M. S. Alam,
M. N. A. Bitu,
M. S. Islam,
S. Islam,
N. Khatun,
M. S Hossain
Abstract:
Barium titanate, BaTiO3 (BT), materials have been synthesized by two different routes: one ball-mill-derived (BMD) nanopowder and another precursor-derived (PCD) BT synthesis method were used separately to fabricate BT thin films on stainless steel (SS) and quartz substrates by spin coating. Then thin films from both synthesis routes were characterized by Ultraviolet-Visible-Near Infrared (UV-Vis-…
▽ More
Barium titanate, BaTiO3 (BT), materials have been synthesized by two different routes: one ball-mill-derived (BMD) nanopowder and another precursor-derived (PCD) BT synthesis method were used separately to fabricate BT thin films on stainless steel (SS) and quartz substrates by spin coating. Then thin films from both synthesis routes were characterized by Ultraviolet-Visible-Near Infrared (UV-Vis-NIR) Spectroscopy, Field-Emission Scanning Electron Microscopy (FE-SEM), X-ray Diffractometry (XRD), Raman Spectroscopy, and Four-point collinear probe; all carried out at room temperature. Our studies revealed that the PCD synthesis process did not produce the BT phase even under the 900^0C air-annealing condition. In contrast, a homogeneous BT thin film has been formed from the BMD-BT nanopowder. The optical band gap of BMD-BT thin films was found in the 3.10 - 3.28 eV range. Finally, a Graphene-Barium Titanate-Graphene (G-BT-G) structure was fabricated on a SS substrate by spin coating at processing temperatures below 100^0C and characterized by two different pieces of equipment: a Potentiostat/Galvanostat (PG-STAT) and a Precision Impedance Analyzer (PIA). The G-BT-G structure exhibited a capacitance of 8 nF and 7.15 nF, a highest dielectric constant of 800 and 790, and a low dielectric loss of 4.5 and 5, investigated by PG-STAT and PIA equipment, respectively.
△ Less
Submitted 17 June, 2023;
originally announced June 2023.
-
Effect of Substrate Surface on the Wide Bandgap SnO2 Thin Films Grown by Spin Coating
Authors:
Md. Nur Amin Bitu,
Nazmul Islam Tanvir,
Suravi Islam,
Syed Farid Uddin Farhad
Abstract:
Tin (IV) oxide (SnO2) sols have been synthesized from SnCl2.2H2O precursor solution by applying two different processing conditions. The prepared sols were then deposited on UV-Ozone treated quartz and soda lime glass (SLG) substrates by spin coating. The as-synthesized film was soft-baked at about 100 deg. C. for 10 min. This process was repeated five times to get a compact film, followed by air-…
▽ More
Tin (IV) oxide (SnO2) sols have been synthesized from SnCl2.2H2O precursor solution by applying two different processing conditions. The prepared sols were then deposited on UV-Ozone treated quartz and soda lime glass (SLG) substrates by spin coating. The as-synthesized film was soft-baked at about 100 deg. C. for 10 min. This process was repeated five times to get a compact film, followed by air-annealing at 250 deg. C. for 2 hours. The pristine and annealed films were characterized by UV-Vis-NIR spectroscopy, Grazing Incident X-Ray Diffraction (GIXRD), and Field Emission Scanning Electron Microscope (FESEM). The effect of the substrate surface was investigated by measuring the contact angles with De-Ionized (DI) water. UV-Ozone treatment of substrate provides a cleaner surface to grow a homogeneous film. The electrical resistivity of annealed thin films was carried out by a four-point-collinear probe employing the current reversal technique and found in the range of approx. 2x10^3 to 3x10^3 Ohm-cm. Film thickness was found in the range of approx. 137-285 nm, measured by a stylus profilometer. UV-VIs-NIR Transmission data revealed that all the thin film samples showed maximum (82-89) % transmission in the visible range. The optical bandgap of the thin films was estimated to be approx. 3.75-4.00 eV and approx. 3.78-4.35 eV for the films grown on SLG and quartz substrates, respectively.
△ Less
Submitted 29 January, 2023; v1 submitted 20 September, 2022;
originally announced September 2022.
-
Spherical and Rod-shaped Gold Nanoparticles for Surface Enhanced Raman Spectroscopy
Authors:
Md. Shaha Alam,
Syed Farid Uddin Farhad,
Nazmul Islam Tanvir,
Md. Nur Amin Bitu,
Mohammad Moniruzzaman,
Mahmuda Hakim,
Md Aftab Ali Shaikh
Abstract:
Raman Spectroscopy offers an in-situ, rapid, and non-destructive characterization tool for chemical analysis of diverse samples with no or minimal preparation. However, due to the inherent weak signal of conventional Raman spectroscopy, surface plasmon resonance features of noble metal nanoparticles have been utilized to conduct Surface Enhanced Raman Spectroscopy (SERS) in detecting trace label c…
▽ More
Raman Spectroscopy offers an in-situ, rapid, and non-destructive characterization tool for chemical analysis of diverse samples with no or minimal preparation. However, due to the inherent weak signal of conventional Raman spectroscopy, surface plasmon resonance features of noble metal nanoparticles have been utilized to conduct Surface Enhanced Raman Spectroscopy (SERS) in detecting trace label contaminants in foods and foodstuffs. In this effort, we synthesized gold nanoparticles (AuNPs) by reduction of chloroauric acid (HAuCl4) with sodium citrate dehydrate. We prepared different sizes of AuNPs at a fixed temperature (100 oC) but with varying pHs of 4 and 8. The as-synthesized AuNPs were characterized by UV-Vis spectroscopy, dynamic light scattering (DLS), and Field Emission Scanning Electron Microscopy (FE-SEM). FE-SEM micrographs revealed spherical AuNPs with an average diameter of approx. 55 nm and rod-shaped AuNPs with an average length of approx. 170 nm for sample synthesis at pH 8 and 4, respectively. The effectiveness of the as-prepared AuNPs for SERS is tested by detecting Rhodamine 6G diluted at a trace level. This study suggests that plasmonic nanoparticles coupled with SERS have great potential for broad applications in detecting other trace amounts of hazardous chemicals in foods and foodstuffs.
△ Less
Submitted 1 October, 2022; v1 submitted 19 September, 2022;
originally announced September 2022.