Pressure Effect and Specific Heat of RBa2Cu3Ox at Distinct Charge Carrier Concentrations: Possible Influence of Stripes
Authors:
S. I. Schlachter,
U. Tutsch,
W. H. Fietz,
K. -P. Weiss,
H. Leibrock,
K. Grube,
Th. Wolf,
B. Obst,
P. Schweiss,
H. Wuehl
Abstract:
In YBa2Cu3Ox, distinct features are found in the pressure dependence of the transition temperature, dTc/dp, and in DeltaCp*Tc, where DeltaCp is the jump in the specific heat at Tc: dTc/dp becomes zero when DeltaCp*Tc is maximal, whereas dTc/dp has a peak at lower oxygen contents where DeltaCp*Tc vanishes. Substituting Nd for Y and doping with Ca leads to a shift of these specific oxygen contents…
▽ More
In YBa2Cu3Ox, distinct features are found in the pressure dependence of the transition temperature, dTc/dp, and in DeltaCp*Tc, where DeltaCp is the jump in the specific heat at Tc: dTc/dp becomes zero when DeltaCp*Tc is maximal, whereas dTc/dp has a peak at lower oxygen contents where DeltaCp*Tc vanishes. Substituting Nd for Y and doping with Ca leads to a shift of these specific oxygen contents, since oxygen order and hole doping by Ca influences the hole content nh in the CuO2 planes. Calculating nh from the parabolic Tc(nh) behavior, the features coalesce for all samples at nh=0.11 and nh=0.175, irrespective of substitution and doping. Hence, this behavior seems to reflect an intrinsic property of the CuO2 planes. Analyzing our results we obtain different mechanisms in three doping regions: Tc changes in the optimally doped and overdoped region are mainly caused by charge transfer. In the slightly underdoped region an increasing contribution to dTc/dp is obtained when well ordered CuO chain fragments serve as pinning centers for stripes. This behavior is supported by our results on Zn doped NdBa2Cu3Ox and is responsible for the well known dTc/dp peak observed in YBa2Cu3Ox at x=6.7. Going to a hole content below nh=0.11 our results point to a crossover from an underdoped superconductor to a doped antiferromagnet, changing completely the physics of these materials.
△ Less
Submitted 8 March, 2001;
originally announced March 2001.
The Effects of Chemical Doping and Hydrostatic Pressure on Tc of Y(1-y)CayBa2Cu3Ox and NdBa2Cu3Ox Single Crystals
Authors:
S. I. Schlachter,
K. -P. Weiss,
W. H. Fietz,
K. Grube,
H. Leibrock,
Th. Wolf,
B. Obst,
P. Schweiss,
M. Klaeser,
H. Wuehl
Abstract:
We studied Tc of YBa2Cu3Ox (Y123), Y0.89Ca0.11Ba2Cu3Ox (YCa123) and NdBa2Cu3Ox (Nd123) single crystals with various oxygen contents x. Compared to Tc(x) of Y123 the Tc(x) curves of YCa123 are shifted to lower oxygen contents and the maximum transition temperature Tc,max decreases with increasing Ca content whereas in Nd123 Tc(x) is shifted to higher oxygen contents and Tc,max is increased. Accor…
▽ More
We studied Tc of YBa2Cu3Ox (Y123), Y0.89Ca0.11Ba2Cu3Ox (YCa123) and NdBa2Cu3Ox (Nd123) single crystals with various oxygen contents x. Compared to Tc(x) of Y123 the Tc(x) curves of YCa123 are shifted to lower oxygen contents and the maximum transition temperature Tc,max decreases with increasing Ca content whereas in Nd123 Tc(x) is shifted to higher oxygen contents and Tc,max is increased. According to the universal parabolic Tc(nh) behavior the differences in Tc(x)of Y123, YCa123 and Nd123 can be ascribed to different hole concentrations nh in the CuO2 planes caused by doping via changes in chemistry or structure. In order to study the influence of structural changes on Tc we examined the hydrostatic pressure effect dTc/dp (p up to 0.6 GPa). In the underdoped region, at nh=0.11, the examined compounds show a peak in dTc/dp which is very pronounced for systems with well ordered CuO chains. As this peak occurs at the same nh in all investigated systems it is not caused by oxygen ordering, but its origins might be found in a strong influence of lattice deformations on the electronic structure.
△ Less
Submitted 20 December, 1999;
originally announced December 1999.