Roebel cables from REBCO coated conductors: a one-century-old concept for the superconductivity of the future
Authors:
Wilfried Goldacker,
Francesco Grilli,
Enric Pardo,
Anna Kario,
Sonja I. Schlachter,
Michal Vojenciak
Abstract:
Energy applications employing high-temperature superconductors (HTS), such as motors/generators, transformers, transmission lines and fault current limiters, are usually operated in the alternate current (AC) regime. In order to be efficient, the HTS devices need to have a sufficiently low value of AC loss, in addition to the necessary current-carrying capacity. Most applications are operated with…
▽ More
Energy applications employing high-temperature superconductors (HTS), such as motors/generators, transformers, transmission lines and fault current limiters, are usually operated in the alternate current (AC) regime. In order to be efficient, the HTS devices need to have a sufficiently low value of AC loss, in addition to the necessary current-carrying capacity. Most applications are operated with currents beyond the current capacity of single conductors and consequently require cabled conductor solutions with much higher current carrying capacity, from a few kA to up to 20-30 kA for large hydro-generators. A century ago, in 1914, Ludwig Roebel invented a low-loss cable design for copper cables, which was successively named after him. The main idea behind Roebel cables is to separate the current in different strands and to provide a full transposition of the strands along the cable direction. Nowadays, these cables are commonly used in the stator of large generators. Based on the same design concept of their conventional material counterparts, HTS Roebel cables from REBCO coated conductors were first manufactured at the Karlsruhe Institute of Technology (KIT) and have been successively developed in a number of varieties that provide all the required technical features such as fully transposed strands, high transport currents and low AC losses, yet retaining enough flexibility for a specific cable design. In the past few years a large number of scientific papers have been published on the concept, manufacturing and characterization of such cables. Times are therefore mature for a review of those results. The goal is to provide an overview and a succinct and easy-to-consult guide for users, developers, and manufacturers of this kind of HTS cables.
△ Less
Submitted 29 May, 2017; v1 submitted 17 June, 2014;
originally announced June 2014.
-
High current DyBCO-ROEBEL Assembled Coated Conductor (RACC)
Authors:
W. Goldacker,
R. Nast,
G. Kotzyba,
S. I. Schlachter,
A. Frank,
B. Ringsdorf,
C. Schmidt,
P. Komarek
Abstract:
Low AC loss high transport current HTS cables (>1 kA) are required for application in transformers, generators and are considered for future generations of fusion reactors coils. 2G coated conductors are suitable candidates for high field application at quite high operation temperatures of 50-77 K, which is crucial precondition for economical cooling costs. As a feasibility study we present the…
▽ More
Low AC loss high transport current HTS cables (>1 kA) are required for application in transformers, generators and are considered for future generations of fusion reactors coils. 2G coated conductors are suitable candidates for high field application at quite high operation temperatures of 50-77 K, which is crucial precondition for economical cooling costs. As a feasibility study we present the first ROEBEL bar cable of approx. 35 cm length made from industrial DyBCO coated conductor (THEVA GmbH, Germany). Meander shaped ROEBEL strands of 4 mm width with a twist pitch of 180 mm were cut from 10 mm wide CC tapes using a specially designed tool. The strands carried in average 157 Amps/cm-width DC and were assembled to a subcable with 5 strands and a final cable with 16 strands. The 5 strand cable was tested and carried a transport current of > 300 Amps DC at 77 K, equivalent to the sum of the individual strand transport critical currents. The 16 strand cable carried 500 A limited through heating effects and non sufficient stabilisation and current sharing. A pulse current load indicated a current carrying potential of > 1 kA for the 16 strand cable.
△ Less
Submitted 6 October, 2005;
originally announced October 2005.
-
Mechanical properties of reinforced MgB2 wires
Authors:
Wilfried Goldacker,
Sonja I. Schlachter,
Johann Reiner,
Silke Zimmer,
Arman Nyilas,
Helmut Kiesel
Abstract:
For technical application in windings of coils, transformers or motors, a reinforcement of MgB2 wires and tapes is necessary to withstand applied stresses and strains and to avoid cracks in the filaments. Therefore, the response of the superconducting transport currents on applied axial strain in different magnetic background fields was investigated for differently stainless steel reinforced MgB…
▽ More
For technical application in windings of coils, transformers or motors, a reinforcement of MgB2 wires and tapes is necessary to withstand applied stresses and strains and to avoid cracks in the filaments. Therefore, the response of the superconducting transport currents on applied axial strain in different magnetic background fields was investigated for differently stainless steel reinforced MgB2 wires, by means of an axial strain rig. Increased amounts of stainless steel in the sheath caused a stronger decrease of the critical currents in fields above 3 T as a consequence of a changed irreversibility field. Heat treated wires have a quite different mechanical behaviour compared to as-cold-worked wires, but an about 10 times higher transport current level. Tape geometries, having generally higher current carrying capabilities than wires, showed much poorer mechanical properties with a less effective filament precompression from the matrix.
△ Less
Submitted 27 November, 2002;
originally announced November 2002.
-
Influence of the Preparation Process on Microstructure, Critical Current Density and Tc of MgB2 Powder-In-Tube Wires
Authors:
S. I. Schlachter,
W. Goldacker,
J. Reiner,
S. Zimmer,
B. Liu,
B. Obst
Abstract:
MgB2 wires and tapes suffer from a limitation of the transport current densities, especially at low field, due to an unsufficient thermal stabilization caused by hot spots from a non-homogeneous microstructure, the presence of secondary phases and voids. For the preparation of MgB2 wires and tapes two different precursor routes, using MgB2 (ex-situ process) or Mg + B (in-situ process) are applie…
▽ More
MgB2 wires and tapes suffer from a limitation of the transport current densities, especially at low field, due to an unsufficient thermal stabilization caused by hot spots from a non-homogeneous microstructure, the presence of secondary phases and voids. For the preparation of MgB2 wires and tapes two different precursor routes, using MgB2 (ex-situ process) or Mg + B (in-situ process) are applied. The in-situ approach allows variation of many parameters in the wire preparation and the improvement of this approach is the central topic of this paper. We present an improved in-situ approach, the characterization of the filament microstructure, effects from stoichiometry and the corresponding superconducting properties. The transport current capability of such in-situ wires could be improved to the level of the reference ex-situ wires.
△ Less
Submitted 28 October, 2002;
originally announced October 2002.
-
Mechanically Reinforced MgB2 Wires and Tapes with High Transport Currents
Authors:
W. Goldacker,
S. I. Schlachter,
H. Reiner,
S. Zimmer,
B. Obst,
H. Kiesel,
A. Nyilas
Abstract:
In this contribution, different concepts for mechanically reinforced MgB2 wires with high transport currents are presented and characterised. It is shown that the achieved critical transport currents depend strongly on the conductor concept, the choice of the precursor route and the applied treatment method.
In this contribution, different concepts for mechanically reinforced MgB2 wires with high transport currents are presented and characterised. It is shown that the achieved critical transport currents depend strongly on the conductor concept, the choice of the precursor route and the applied treatment method.
△ Less
Submitted 29 April, 2002;
originally announced April 2002.
-
Influence of mechanical reinforcement of MgB2 wires on the superconducting properties
Authors:
W. Goldacker,
S. I. Schlachter
Abstract:
Monofilamentary MgB2-wires with a mechanical tough Nb/Cu/steel or Fe/steel sheath were prepared and characterized. The steel content was varied to investigate the reinforcement effect and the consequences for the superconducting properties of the wires, which were heat treated to achieve dense and homogeneous filaments. The use of Nb as first sheath layer, having a smaller thermal expansion coef…
▽ More
Monofilamentary MgB2-wires with a mechanical tough Nb/Cu/steel or Fe/steel sheath were prepared and characterized. The steel content was varied to investigate the reinforcement effect and the consequences for the superconducting properties of the wires, which were heat treated to achieve dense and homogeneous filaments. The use of Nb as first sheath layer, having a smaller thermal expansion coefficient than MgB2, requires the application of higher amounts of steel to achieve compressive pre-stress on the filament in comparison to Fe as first wall material. With raised steel content in the sheath the critical transport currents show field dependent significant critical current and irreversibility field degradations. First Ic vs. axial stress and strain experiments confirmed this observation of pre-stress induced degradations. Consequences for improved wires and for future applications will be discussed.
△ Less
Submitted 11 October, 2001;
originally announced October 2001.
-
Mechanically reinforced MgB2 wires and tapes with high transport currents
Authors:
R. Nast,
S. I. Schlachter,
S. Zimmer,
H. Reiner,
W. Goldacker
Abstract:
Monofilamentary MgB2-wires with a 2- or 3-component sheath containing mechanical reinforcing stainless steel (SS) were prepared and characterized. In direct contact to the superconductor Nb, Ta or Fe was used. For a selection of samples with a Fe and Fe/SS sheath, we investigated the transport critical current behaviour in magnetic fields changing systematically the geometrical shape from a roun…
▽ More
Monofilamentary MgB2-wires with a 2- or 3-component sheath containing mechanical reinforcing stainless steel (SS) were prepared and characterized. In direct contact to the superconductor Nb, Ta or Fe was used. For a selection of samples with a Fe and Fe/SS sheath, we investigated the transport critical current behaviour in magnetic fields changing systematically the geometrical shape from a round wire to a flat tape. A strong increase of the current densities in flat tapes was observed and possible reasons for this are discussed. Reinforcing the sheath in the outer layer with different amounts of stainless steel leads to a systematic field dependent decrease of the transport critical current density with increasing steel amount. This is an indication for a pre-stress induced degradation of the critical currents in MgB2 wires and first Ic-stress-strain experiments seem to confirm this observation and interpretation.
△ Less
Submitted 28 August, 2001;
originally announced August 2001.
-
High Pressure Studies of Tc and Lattice Parameters of MgB2
Authors:
S. I. Schlachter,
W. H. Fietz,
K. Grube,
W. Goldacker
Abstract:
We performed ac-susceptibility measurements of magnesium diboride powder samples under pure hydrostatic pressures up to 0.4 GPa and under quasi-hydrostatic pressure conditions up to 8 GPa in a helium gas pressure cell and a diamond-anvil cell (DAC), respectively. Furthermore, the DAC has been used to investigate the lattice compression by X-ray diffraction. Under helium gas pressure the supercon…
▽ More
We performed ac-susceptibility measurements of magnesium diboride powder samples under pure hydrostatic pressures up to 0.4 GPa and under quasi-hydrostatic pressure conditions up to 8 GPa in a helium gas pressure cell and a diamond-anvil cell (DAC), respectively. Furthermore, the DAC has been used to investigate the lattice compression by X-ray diffraction. Under helium gas pressure the superconducting transition temperature shows a linear decrease dTc/dp = -1.13 K/GPa. The pressure effect is fully reversible with a return to the initial Tc of 37.5 K after pressure release. In the diamond-anvil cell the application of pressure leads to a stronger Tc-decrease than in the helium gas pressure cell, and after the release of pressure a degradation effect with lower Tc and a broader transition compared to the first measurement at ambient pressure occurs. Such degradation may be explained by shear stresses and uniaxial pressure components, which cannot be avoided in a DAC at low temperatures. Considering the anisotropic AlB2-type structure with alternating honeycomb boron and magnesium layers, MgB2 seems to be very sensitive to such non-hydrostatic pressure components, which would explain the spread of dTc/dp values reported in the literature.
△ Less
Submitted 27 August, 2001; v1 submitted 10 July, 2001;
originally announced July 2001.
-
High transport currents in mechanically reinforced MgB2 wires
Authors:
W. Goldacker,
S. I. Schlachter,
S. Zimmer,
H. Reiner
Abstract:
We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self field. The reproducibility of the measured transport currents was excellent and not depending on the wire diameter. Using different precursors, commercial react…
▽ More
We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self field. The reproducibility of the measured transport currents was excellent and not depending on the wire diameter. Using different precursors, commercial reacted powder or an unreacted Mg/B powder mixture, a strong influence on the pinning behaviour and the irreversibility field was observed. The critical transport current density showed a nearly linear temperature dependency for all wires being still 52 kA/cm^2 at 20 K and 23 kA/cm^2 at 30 K. Detailed data for Jc(B,T) and Tc(B) were measured.
△ Less
Submitted 5 July, 2001; v1 submitted 12 June, 2001;
originally announced June 2001.
-
Pressure Effect and Specific Heat of RBa2Cu3Ox at Distinct Charge Carrier Concentrations: Possible Influence of Stripes
Authors:
S. I. Schlachter,
U. Tutsch,
W. H. Fietz,
K. -P. Weiss,
H. Leibrock,
K. Grube,
Th. Wolf,
B. Obst,
P. Schweiss,
H. Wuehl
Abstract:
In YBa2Cu3Ox, distinct features are found in the pressure dependence of the transition temperature, dTc/dp, and in DeltaCp*Tc, where DeltaCp is the jump in the specific heat at Tc: dTc/dp becomes zero when DeltaCp*Tc is maximal, whereas dTc/dp has a peak at lower oxygen contents where DeltaCp*Tc vanishes. Substituting Nd for Y and doping with Ca leads to a shift of these specific oxygen contents…
▽ More
In YBa2Cu3Ox, distinct features are found in the pressure dependence of the transition temperature, dTc/dp, and in DeltaCp*Tc, where DeltaCp is the jump in the specific heat at Tc: dTc/dp becomes zero when DeltaCp*Tc is maximal, whereas dTc/dp has a peak at lower oxygen contents where DeltaCp*Tc vanishes. Substituting Nd for Y and doping with Ca leads to a shift of these specific oxygen contents, since oxygen order and hole doping by Ca influences the hole content nh in the CuO2 planes. Calculating nh from the parabolic Tc(nh) behavior, the features coalesce for all samples at nh=0.11 and nh=0.175, irrespective of substitution and doping. Hence, this behavior seems to reflect an intrinsic property of the CuO2 planes. Analyzing our results we obtain different mechanisms in three doping regions: Tc changes in the optimally doped and overdoped region are mainly caused by charge transfer. In the slightly underdoped region an increasing contribution to dTc/dp is obtained when well ordered CuO chain fragments serve as pinning centers for stripes. This behavior is supported by our results on Zn doped NdBa2Cu3Ox and is responsible for the well known dTc/dp peak observed in YBa2Cu3Ox at x=6.7. Going to a hole content below nh=0.11 our results point to a crossover from an underdoped superconductor to a doped antiferromagnet, changing completely the physics of these materials.
△ Less
Submitted 8 March, 2001;
originally announced March 2001.
-
Compressibility and thermal expansion of YBa2Cu3Ox
Authors:
K. Grube,
H. Leibrock,
W. H. Fietz,
S. I. Schlachter,
A. I. Rykov,
S. Tajima,
P. Schweiss,
B. Obst,
H. Wuehl
Abstract:
The linear compressibilities and the thermal expansion of an untwinned, nearly optimal doped YBa2Cu3O6.94 single crystal were measured along the three crystallographic axes with a high-resolution dilatometer mounted in a high-pressure cell. The measurements were performed in a temperature range from 50 K to 320 K under hydrostatic gas pressure of maximal 0.65 GPa. At a temperature of 300 K the m…
▽ More
The linear compressibilities and the thermal expansion of an untwinned, nearly optimal doped YBa2Cu3O6.94 single crystal were measured along the three crystallographic axes with a high-resolution dilatometer mounted in a high-pressure cell. The measurements were performed in a temperature range from 50 K to 320 K under hydrostatic gas pressure of maximal 0.65 GPa. At a temperature of 300 K the measured bulk modulus is reduced and shows a very strong enhancement under increasing pressure due to pressure-induced oxygen ordering. This ordering process can also be related to a glass transition seen in the thermal expansion above 225 K. At lower temperatures, when oxygen ordering is frozen, the bulk modulus is increased and shows a significantly reduced enhancement under pressure. This pressure dependence, however, is still anomalous high, probably caused by bonds of extremely different compressibilities within the unit cell. The widely spread literature data of the bulk modulus can be explained by this high pressure dependence.
△ Less
Submitted 20 December, 1999;
originally announced December 1999.
-
The Effects of Chemical Doping and Hydrostatic Pressure on Tc of Y(1-y)CayBa2Cu3Ox and NdBa2Cu3Ox Single Crystals
Authors:
S. I. Schlachter,
K. -P. Weiss,
W. H. Fietz,
K. Grube,
H. Leibrock,
Th. Wolf,
B. Obst,
P. Schweiss,
M. Klaeser,
H. Wuehl
Abstract:
We studied Tc of YBa2Cu3Ox (Y123), Y0.89Ca0.11Ba2Cu3Ox (YCa123) and NdBa2Cu3Ox (Nd123) single crystals with various oxygen contents x. Compared to Tc(x) of Y123 the Tc(x) curves of YCa123 are shifted to lower oxygen contents and the maximum transition temperature Tc,max decreases with increasing Ca content whereas in Nd123 Tc(x) is shifted to higher oxygen contents and Tc,max is increased. Accor…
▽ More
We studied Tc of YBa2Cu3Ox (Y123), Y0.89Ca0.11Ba2Cu3Ox (YCa123) and NdBa2Cu3Ox (Nd123) single crystals with various oxygen contents x. Compared to Tc(x) of Y123 the Tc(x) curves of YCa123 are shifted to lower oxygen contents and the maximum transition temperature Tc,max decreases with increasing Ca content whereas in Nd123 Tc(x) is shifted to higher oxygen contents and Tc,max is increased. According to the universal parabolic Tc(nh) behavior the differences in Tc(x)of Y123, YCa123 and Nd123 can be ascribed to different hole concentrations nh in the CuO2 planes caused by doping via changes in chemistry or structure. In order to study the influence of structural changes on Tc we examined the hydrostatic pressure effect dTc/dp (p up to 0.6 GPa). In the underdoped region, at nh=0.11, the examined compounds show a peak in dTc/dp which is very pronounced for systems with well ordered CuO chains. As this peak occurs at the same nh in all investigated systems it is not caused by oxygen ordering, but its origins might be found in a strong influence of lattice deformations on the electronic structure.
△ Less
Submitted 20 December, 1999;
originally announced December 1999.
-
Structure and Tc of Y0.8Ca0.2Ba2Cu3O6.92 under High Pressure
Authors:
Walter H. Fietz,
Frank W. Hornung,
Kai Grube,
Sonja I. Schlachter,
Thomas Wolf,
Bernhard Obst,
Peter Schweiss
Abstract:
The lattice parameters and Tc of Y1-yCayBa2Cu3Ox have been determined under pressure up to 10 GPa using a diamond anvil cell. The results are used to test the extended charge transfer model that connects the pressure effect on Tc to an intrinsic dTc,max/dp and a pressure induced hole doping dnh/dp, the latter being caused by charge transfer from the CuO chains to the CuO2 planes. dnh/dp and dTc,…
▽ More
The lattice parameters and Tc of Y1-yCayBa2Cu3Ox have been determined under pressure up to 10 GPa using a diamond anvil cell. The results are used to test the extended charge transfer model that connects the pressure effect on Tc to an intrinsic dTc,max/dp and a pressure induced hole doping dnh/dp, the latter being caused by charge transfer from the CuO chains to the CuO2 planes. dnh/dp and dTc,max/dp are usually assumed to be constant with respect to pressure p. However, our experiments show that the usage of this model gives a poor description of the experimental Tc(p) values. We connected the extended charge transfer model to the pressure induced changes of the compressibilities. With this ansatz the calculated Tc(p) values show an excellent agreement with the experimentally determined values.
△ Less
Submitted 20 December, 1999;
originally announced December 1999.
-
The Effect of Chemical Doping and Hydrostatic Pressure on Tc of Y1-yCayBa2Cu3Ox Single Crystals
Authors:
S. I. Schlachter,
W. H. Fietz,
K. Grube,
Th. Wolf,
B. Obst,
P. Schweiss,
M. Klaeser
Abstract:
We performed susceptibility measurements on Y1-yCayBa2Cu3Ox single crystals under high He pressure. For each Ca content various samples with different oxygen contents have been prepared to probe the influence of Ca on Tc(x), dTc/dp(x) and Tc,max. Starting from the parabolic Tc(nh) behavior we calculated nh values from Tc and Tc,max for each sample. It is shown that in the overdoped region dTc/dp…
▽ More
We performed susceptibility measurements on Y1-yCayBa2Cu3Ox single crystals under high He pressure. For each Ca content various samples with different oxygen contents have been prepared to probe the influence of Ca on Tc(x), dTc/dp(x) and Tc,max. Starting from the parabolic Tc(nh) behavior we calculated nh values from Tc and Tc,max for each sample. It is shown that in the overdoped region dTc/dp can be described by a pressure induced charge transfer with dnh/dp = 3.7E-3 [1/GPa] and a dTc,max/dp value of 0.8 K/GPa, irrespective of the Ca content. In the underdoped region additional pressure effects lead to a peak in dTc/dp at approximately 0.11 holes/CuO2 plane. However, with increasing Ca content this peak is strongly depressed. This is explained in terms of an increasing disorder in the CuO chain system due to doping. Deviations in dTc/dp at very low nh values can be assigned to the ortho II ordering in the CuO chain system.
△ Less
Submitted 20 December, 1999; v1 submitted 17 December, 1999;
originally announced December 1999.