Abstract
The capacity to propagate magnetic domain walls with spin-polarized currents underpins several schemes for information storage and processing using spintronic devices. A key question involves the internal structure of the domain walls, which governs their response to certain current-driven torques such as the spin Hall effect. Here we show that magnetic microscopy based on a single nitrogen-vacancy defect in diamond can provide a direct determination of the internal wall structure in ultrathin ferromagnetic films under ambient conditions. We find pure Bloch walls in Ta/CoFeB(1ânm)/MgO, while left-handed Néel walls are observed in Pt/Co(0.6ânm)/AlOx. The latter indicates the presence of a sizable interfacial DzyaloshinskiiâMoriya interaction, which has strong bearing on the feasibility of exploiting novel chiral states such as skyrmions for information technologies.
Similar content being viewed by others
Introduction
The recent observation of current-induced domain wall (DW) motion with large velocity in ultrathin (few atomic layers) magnetic wires has opened new opportunities for spintronic devices1. However, there is still no consensus on the underlying mechanisms of DW motion, and several distinct models have been shown to be consistent with experimental observations1,2,3,4,5,6,7. The key to this debate is the DW structure, which can be of Bloch or Néel type, and which dramatically affects the efficiency of the different proposed mechanisms7,8,9. In a wide ultrathin ferromagnetic wire with perpendicular magnetic anisotropy, magnetostatics predicts that the Bloch DW, a helical rotation of the magnetization, is the most stable DW configuration because it minimizes volume magnetic charges10. However, the unexpectedly large current-induced DW velocities, recently observed in ultrathin ferromagnets1, added to the fact that the motion can be found against the electron flow2,3, has cast doubt on this hypothesis and triggered a major academic debate regarding the physical processes at the origin of DW motion4,5,6,7,8,9. Notably, it was recently proposed that Néel DWs with fixed chirality could be stabilized by the DzyaloshinskiiâMoriya interaction (DMI)8, an indirect exchange possibly occurring at the interface between a magnetic layer and a heavy metal substrate with large spin-orbit coupling11. For such chiral DWs, hereafter termed Dzyaloshinskii DWs, a damping-like torque due to spin-orbit terms (spin Hall effect and Rashba interaction) would lead to efficient current-induced DW motion along a direction fixed by chirality8.
In order to validate unambiguously these theoretical predictions, a direct, in situ, determination of the DW structure in ultrathin ferromagnets is required. However, the relatively small number of spins at the wall centre makes direct imaging of its inner structure a very challenging task. So far, only spin-polarized scanning tunnelling microscopy12 and spin-polarized low-energy electron microscopy13 have allowed a direct determination of the DW structure, demonstrating homochiral Néel DWs in Fe double layer on W(110) and in (Co/Ni)n multilayers on Pt or Ir, respectively. However, these techniques are intrinsically limited to model samples because of high experimental constraints, for example bare magnetic surface hence ultrahigh vacuum, and the debate remains open for widely used trilayer systems with perpendicular magnetic anisotropy such as Pt/Co/AlOx (ref. 1), Pt/Co/Pt (ref. 4) or Ta/CoFeB/MgO (ref. 14). Indeed, most experiments aiming to deduce the DW structure and chirality in such trilayer systems have relied on DW motion analysis under additional in-plane applied fields, which is indirect and involves strong assumptions on the DW dynamics2,3,4,14,15. Here we introduce a general method enabling a direct determination of the DW structure in ultrathin ferromagnets under ambient conditions. It relies on local measurements of the stray field distribution above the DW using a scanning nanomagnetometer based on the nitrogen-vacancy (NV) defect in diamond16,17,18. We first apply the method to a Ta/Co40Fe40B20 (1ânm)/MgO magnetic wire and find clear signature of pure Bloch DWs. In contrast, we observe left-handed Néel DWs in a Pt/Co(0.6ânm)/AlOx wire, providing direct evidence for the presence of a sizable DMI in this multilayer stack. This method offers a new path for exploring interfacial DMI in ultrathin ferromagnets and elucidating the physics of DW motion under current.
Results
Principle of the method
To convey the basic idea behind our method, we start by deriving analytical formulae of the magnetic field distribution at a distance d above a DW placed at x=0 in a perpendicularly magnetized film (Fig. 1a). The main contribution to the stray field, denoted by Bâ¥, is provided by the abrupt variation of the out-of-plane magnetization Mz(x)=âMs tanh(x/ÎDW) (ref. 10), where Ms is the saturation magnetization and ÎDW is the DW width parameter. The resulting stray field components can be expressed as
where t is the film thickness. These approximate formulae are valid in the limit of (i) tâªd, (ii) ÎDWâªd and (iii) for an infinitely long DW along the y axis. On the other hand, the in-plane magnetization, with amplitude , can be oriented with an angle Ï with respect to the x axis (Fig. 1b). This angle is linked to the nature of the DW: Ï=±Ï/2 for a Bloch DW, whereas Ï=0 or Ï for a Néel DW. The two possible values define the chirality (right or left) of the DW. The spatial variation of the in-plane magnetization adds a contribution to the stray field, whose components are given by
The net stray field above the DW is finally expressed as
which indicates that a Néel DW (cosÏ=±1) produces an additional stray field owing to extra magnetic charges on each side of the wall. Using equations (1) and (2), we find a maximum relative difference in stray field between Bloch and Néel DWs scaling as âÏ ÎDW/2d. Local measurements of the stray field above a DW can therefore reveal its inner structure, characterized by the angle Ï. This is further illustrated in Fig. 1c,d, which shows the stray field components and for various DW configurations while using d=120ânm and ÎDW=20ânm, which are typical parameters of the experiments considered below on a Ta/CoFeB(1ânm)/MgO trilayer system.
Magnetic field imaging with scanning-NV magnetometry
We now demonstrate the effectiveness of the method by employing a single NV defect hosted in a diamond nanocrystal as a nanomagnetometer operating under ambient conditions16,17,18. Here the local magnetic field is evaluated within an atomic-size detection volume by monitoring the Zeeman shift of the NV defect electron spin sublevels through optical detection of the magnetic resonance. After grafting the diamond nanocrystal on the tip of an atomic force microscope (AFM), we obtain a scanning nanomagnetometer that provides quantitative maps of the stray field emanating from nanostructured samples19,20,21, with a magnetic field sensitivity in the range of 10âμTâHzâ1/2 (ref. 22). In this study, the Zeeman frequency shift ÎfNV of the NV spin is measured while scanning the AFM tip in the tapping mode, so that the mean distance between the NV spin and the sample surface is kept constant with a typical tip oscillation amplitude of a few nanometres20. Each recorded value of ÎfNV is a function of and BNV,â¥, which are the parallel and perpendicular components, respectively, of the local magnetic field with respect to the NV spinâs quantization axis (see Supplementary Note 1). Note that a frequently found approximation is , where gμB/hâ28âGHzâTâ1. This indicates that scanning-NV magnetometry essentially measures the projection of the magnetic field along the NV centreâs axis. The latter is characterized by spherical angles (θ,Ï) measured independently in the (xyz) reference frame of the sample (Fig. 2a).
Calibration of the experiment
We first applied our method to determine the structure of DWs in a 1.5-μm-wide magnetic wire made of a Ta(5ânm)/Co40Fe40B20(1ânm)/MgO(2ânm) trilayer stack (see Supplementary Note 2). This system has been intensively studied in the last years owing to low damping parameter and depinning field23. Before imaging a DW, it is first necessary to determine precisely (i) the distance d between the NV probe and the magnetic layer and (ii) the product Is=Mst, which are both directly involved in equation (3). These parameters are obtained by performing a calibration measurement above the edges of a uniformly magnetized wire, as shown in Fig. 2a. Here we use the fact that the stray field profile Bedge(x) above an edge placed at x=0 can be easily expressed analytically in a form similar to equation (1), which only depends on d and Is. An example of a measurement obtained by scanning the magnetometer across a Ta/CoFeB/MgO stripe is shown in Fig. 2b. The data are fitted with a function corresponding to the Zeeman shift induced by the stray field Bedge(x)âBedge(x+wc), where wc is the width of the stripe (see Supplementary Note 3). Repeating this procedure for a set of independent calibration linecuts, we obtain d=123±3ânm and Is=926±26âμA, in good agreement with the value measured by other methods24.
Bloch DW structure in a Ta/CoFeB/MgO wire
Having determined all needed parameters, it is now possible to measure the stray field above a DW (Fig. 2c) and compare it with the theoretical prediction, which only depends on the angle Ï that characterizes the DW structure. To this end, an isolated DW was nucleated in a wire of the same Ta/CoFeB/MgO film and imaged with the scanning-NV magnetometer under the same conditions as for the calibration measurements. The resulting distribution of the Zeeman shift ÎfNV is shown in Fig. 2d together with the AFM image of the magnetic wire. Within the resolving power of our instrument, limited by the probe-to-sample distance d~120ânm (ref. 20), the DW appears to be straight with a small tilt angle with respect to the long axis of the wire, determined to be 2±1°. Taking into account this DW spatial profile, the stray field above the DW was computed for (i) Ï=0 (right-handed Néel DW), (ii) Ï=Ï (left-handed Néel DW) and (iii) ϱÏ/2 (Bloch DW). Here we used the micromagnetic OOMMF software25,26 rather than the analytical formula described above in order to avoid any approximation in the calculation (see Supplementary Note 4). The computed magnetic field distributions were finally converted into Zeeman shift distribution, taking into account the quantization axis of the NV spin. A linecut of the experimental data across the DW is shown in Fig. 2e, together with the predicted curves in the three above-mentioned cases. Excellent agreement is found if one assumes that the DW is purely of Bloch-type. The same conclusion can be drawn by directly comparing the full two-dimensional theoretical maps to the data (Fig. 2d,f). As described in detail in Supplementary Note 5, all sources of uncertainty in the theoretical predictions were carefully analysed, yielding the 1-s.e. intervals shown as shaded areas in Fig. 2e. On the basis of this analysis, we find a 1-s.e. upper limit |cosÏ|<0.07. This corresponds to an upper limit for the DMI parameter DDMI, as defined in ref. 8, of |DDMI|<0.01âmJâmâ2 (see Supplementary Note 5). This result was confirmed on a second DW in the same wire. In addition, the measurements were reproduced for different projection axes of the NV probe. The results are shown in Fig. 3 for four NV defects with different quantization axes, showing excellent agreement between experiment and theory if one assumes a Bloch-type DW. These experiments provide an unambiguous confirmation of the Bloch nature of the DWs in our sample, but are also a striking illustration of the vector mapping capability offered by NV microscopy, allowing for robust tests of theoretical predictions.
We conclude that there is no evidence for the presence of a sizable interfacial DMI in a Ta(5ânm)/Co40Fe40B20(1ânm)/MgO trilayer stack. This is in contrast with recent experiments reported on similar samples with different compositions, such as Ta(5ânm)/Co80Fe20(0.6ânm)/MgO (refs 3, 27) and Ta(0.5ânm)/Co20Fe60B20(1ânm)/MgO (refs 14), where a significant deviation towards Néel DWs was inferred from current-induced DW motion experiments. We note that contrary to these studies, our method indicates the nature of the DW at rest, in a direct manner, without any assumption on the DW dynamics. Our results therefore motivate a systematic study of the DW structure as a function of the composition of the trilayer stack.
Left-handed Néel DW structure in a Pt/Co/AlOx wire
In a second step, we explored another type of sample, namely a Pt(3ânm)/Co(0.6ânm)/AlOx(2ânm) trilayer grown by sputtering on a thermally oxidized silicon wafer (see Supplementary Note 2). The observation of current-induced DW motion with unexpectedly large velocities in this asymmetric stack has attracted considerable interest in the recent years1. Here the DW width is ÎDWâ6ânm, leading to a relative field difference between Bloch and Néel cases of â8% at a distance dâ120ânm. We followed a procedure similar to that described above. After a preliminary calibration of the experiment, a DW in a 500-nm-wide magnetic wire was imaged (Fig. 4a,b) and linecuts across the DW were compared with theoretical predictions (Fig. 4c). Here the experimental results clearly indicate a Néel-type DW structure with left-handed chirality. The same result was found for two other DWs. This provides direct evidence of a strong DMI at the Pt/Co interface, with a lower bound |DDMI|>0.1âmJâmâ2. This result is consistent with the conclusions of recent field-dependent DW nucleation experiments performed in similar films28. In addition, we note that the observed left-handed chirality, once combined with a damping-like torque induced by the spin-orbit terms, could explain the characteristics of DW motion under current in this sample7.
Discussion
In conclusion, we have shown how scanning-NV magnetometry enables direct discrimination between competing DW configurations in ultrathin ferromagnets. This method, which is not sensitive to possible artifacts linked to the DW dynamics, will help clarify the physics of DW motion under current, a necessary step towards the development of DW-based spintronic devices. In addition, this work opens a new avenue for studying the mechanisms at the origin of interfacial DMI in ultrathin ferromagnets, by measuring the DW structure while tuning the properties of the magnetic material14,29. This is a key milestone in the search for systems with large DMI that could sustain magnetic skyrmions30.
Additional information
How to cite this article: Tetienne, J.-P. et al. The nature of domain walls in ultrathin ferromagnets revealed by scanning nanomagnetometry. Nat. Commun. 6:6733 doi: 10.1038/ncomms7733 (2015).
References
Miron, I. M. et al. Fast current-induced domain-wall motion controlled by the Rashba effect. Nat. Mater. 10, 419â423 (2011) .
Ryu, K.-S., Thomas, L., Yang, S.-H. & Parkin, S. Chiral spin torque at magnetic domain walls. Nat. Nano 8, 527â533 (2013) .
Emori, S., Bauer, U., Ahn, S.-M., Martinez, E. & Beach, G. S. D. Current-driven dynamics of chiral ferromagnetic domain walls. Nat. Mater. 12, 611â616 (2013) .
Haazen, P. P. J. et al. Domain wall depinning governed by the spin Hall effect. Nat. Mater. 12, 299â303 (2013) .
Kim, J. et al. Layer thickness dependence of the current-induced effective field vector in Ta/CoFeB/MgO. Nat. Mater. 12, 240â245 (2013) .
Garello, K. et al. Symmetry and magnitude of spin-orbit torques in ferromagnetic heterostructures. Nat. Nanotechnol. 8, 587â593 (2013) .
Martinez, E., Emori, S. & Beach, G. S. D. Current-driven domain wall motion along high perpendicular anisotropy multilayers: the role of the Rashba field, the spin Hall effect, and the Dzyaloshinskii-Moriya interaction. Appl. Phys. Lett. 103, 072406 (2013) .
Thiaville, A., Rohart, S., Jué, E., Cros, V. & Fert, A. Dynamics of Dzyaloshinskii domain walls in ultrathin magnetic films. Europhys. Lett. 100, 57002 (2012) .
Brataas, A. & Hals, K. M. D. Spin-orbit torques in action. Nat. Nano 9, 86â88 (2014) .
Hubert, A. & Schäfer, R. Magnetic Domains Springer Verlag (1998) .
Crépieux, A. & Lacroix, C. Dzyaloshinsky-Moriya interactions induced by symmetry breaking at a surface. J. Magn. Magn. Mater. 182, 341â349 (1998) .
Meckler, S. et al. Real-space observation of a right-rotating inhomogeneous cycloidal spin spiral by spin-polarized scanning tunneling microscopy in a triple axes vector magnet. Phys. Rev. Lett. 103, 157201 (2009) .
Chen, G. et al. Tailoring the chirality of magnetic domain walls by interface engineering. Nat. Commun. 4, 2671 (2013) .
Torrejon, J. et al. Interface control of the magnetic chirality in CoFeB/MgO heterostructures with heavy metal underlayers. Nat. Commun. 5, 4655 (2014) .
Je, S.-G. et al. Asymmetric magnetic domain-wall motion by the Dzyaloshinskii-Moriya interaction. Phys. Rev. B 88, 214401 (2013) .
Taylor, J. M. et al. High-sensitivity diamond magnetometer with nanoscale resolution. Nat. Phys. 4, 810â816 (2008) .
Balasubramanian, G. et al. Nanoscale imaging magnetometry with diamond spins under ambient conditions. Nature 455, 648â651 (2008) .
Rondin, L. et al. Magnetometry with nitrogen-vacancy defects in diamond. Rep. Prog. Phys. 77, 056503 (2014) .
Rondin, L. et al. Stray-field imaging of magnetic vortices with a single diamond spin. Nat. Commun. 4, 2279 (2013) .
Tetienne, J.-P. et al. Quantitative stray field imaging of a magnetic vortex core. Phys. Rev. B 88, 214408 (2013) .
Tetienne, J.-P. et al. Nanoscale imaging and control of domain-wall hopping with a nitrogen-vacancy center microscope. Science 344, 1366â1369 (2014) .
Rondin, L. et al. Nanoscale magnetic field mapping with a single spin scanning probe magnetometer. Appl. Phys. Lett. 100, 153118 (2012) .
Burrowes, C. et al. Low depinning fields in Ta-CoFeB-MgO ultrathin films with perpendicular magnetic anisotropy. Appl. Phys. Lett. 103, 182401 (2013) .
Vernier, N. et al. Measurement of magnetization using domain compressibility in CoFeB films with perpendicular anisotropy. Appl. Phys. Lett. 104, 122404 (2014) .
Donahue, M. J. & Porter, D. G. OOMMF User's Guide, Version 1.0 Interagency Report NISTIR 6376 National Institute of Standards and Technology (1999) .
Rohart, S. & Thiaville, A. Skyrmion confinement in ultrathin film nanostructures in the presence of Dzyaloshinskii-Moriya interaction. Phys. Rev. B 88, 184422 (2013) .
Emori, S. et al. Spin Hall torque magnetometry of Dzyaloshinskii domain walls. Phys. Rev. B 90, 184427 (2014) .
Pizzini, S. et al. Chirality-induced asymmetric magnetic nucleation in Pt/Co/AlOx ultrathin microstructures. Phys. Rev. Lett. 113, 047203 (2014) .
Ryu, K.-S., Yang, S.-H., Thomas, L. & Parkin, S. S. P. Chiral spin torque arising from proximity-induced magnetization. Nat. Commun. 5, 3910 (2014) .
Fert, A., Cros, V. & Sampaio, J. Skyrmions on the track. Nat. Nano 8, 152â156 (2013) .
Acknowledgements
This research has been partially funded by the European Communityâs Seventh Framework Programme (FP7/2007â2013) under Grant Agreement no. 611143 (Diadems) and no. 257707 (Magwire), the French Agence Nationale de la Recherche through the projects DIAMAG and Esperado, and by C'Nano Ile-de-France (NanoMag).
Author information
Authors and Affiliations
Contributions
S.R. and A.T. conceived the idea of the study. J.-P.T., T.H., L.J.M. and V.J. performed the experiments, analysed the data and wrote the manuscript. L.H.D, K.G., J.-P.A., G.G., L.V. and B.O. prepared the samples. All authors discussed the data and commented on the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-8, Supplementary Tables 1-3, Supplementary Notes 1-5 and Supplementary References (PDF 2407 kb)
Rights and permissions
About this article
Cite this article
Tetienne, JP., Hingant, T., MartÃnez, L. et al. The nature of domain walls in ultrathin ferromagnets revealed by scanning nanomagnetometry. Nat Commun 6, 6733 (2015). https://doi.org/10.1038/ncomms7733
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms7733
This article is cited by
-
Simultaneous magnetic field and field gradient mapping of hexagonal MnNiGa by quantitative magnetic force microscopy
Communications Physics (2023)
-
Imaging ferroelectric domains with a single-spin scanning quantum sensor
Nature Physics (2023)
-
Stabilization and racetrack application of asymmetric Néel skyrmions in hybrid nanostructures
Scientific Reports (2023)
-
Proximity-induced chiral quantum light generation in strain-engineered WSe2/NiPS3 heterostructures
Nature Materials (2023)
-
Off-resonant detection of domain wall oscillations using deterministically placed nanodiamonds
npj Spintronics (2023)
Comments
By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.