... Manoj M. Koranne, James G. Goodwin, Jr.,' and George Marcelin Department of Chemical and... more ... Manoj M. Koranne, James G. Goodwin, Jr.,' and George Marcelin Department of Chemical and Petroelum Engineering, University of Pittsburgh ... Carbon transients were obtained by switching from 12CH4 to "CHI at steady state accompanied by continuous monitoring of the ...
ABSTRACT CO affects H2 activation on supported Pt in the catalyst layers of a PEMFC and significa... more ABSTRACT CO affects H2 activation on supported Pt in the catalyst layers of a PEMFC and significantly degrades overall fuel cell performance. This paper establishes a more fundamental understanding of the effect of humidity on CO poisoning of Pt/C at typical fuel cell conditions (80°C, 2atm). In this work, direct measurements of hydrogen surface concentration on Pt/C were performed utilizing an H2–D2 switch with Ar purge (HDSAP). The presence of water vapor decreased the rate of CO adsorption on Pt, but had very little effect on the resulting CO surface coverage on PtS (θCO) at steady-state. The steady-state θCOs at 80°C for Pt exposed to H2 (PH2=1 atm) and a mixture of H2/H2O (1atm H2, 10%RH) were 0.70 and 0.66ML, respectively. Furthermore, total strongly bound surface hydrogen measured after exposure to H2/H2O was, surprisingly, the sum of the exchangeable surface hydrogen contributed by each component, even in the presence of CO. In the absence of any evidence for strong chemisorption of H2O on the carbon support with/without Pt, this additive nature and seemingly lack of interaction from the co-adsorption of H2 and H2O on Pt may be explained by the repulsion of strongly adsorbed H2O to the stepped-terrace interface at high coverages of surface hydrogen.
A process for hydrocarbon synthesis comprising the step of reacting a synthesis gas in the presen... more A process for hydrocarbon synthesis comprising the step of reacting a synthesis gas in the presence of a cobalt catalyst promoted with palladium.
... Manoj M. Koranne, James G. Goodwin, Jr.,' and George Marcelin Department of Chemical and... more ... Manoj M. Koranne, James G. Goodwin, Jr.,' and George Marcelin Department of Chemical and Petroelum Engineering, University of Pittsburgh ... Carbon transients were obtained by switching from 12CH4 to "CHI at steady state accompanied by continuous monitoring of the ...
ABSTRACT CO affects H2 activation on supported Pt in the catalyst layers of a PEMFC and significa... more ABSTRACT CO affects H2 activation on supported Pt in the catalyst layers of a PEMFC and significantly degrades overall fuel cell performance. This paper establishes a more fundamental understanding of the effect of humidity on CO poisoning of Pt/C at typical fuel cell conditions (80°C, 2atm). In this work, direct measurements of hydrogen surface concentration on Pt/C were performed utilizing an H2–D2 switch with Ar purge (HDSAP). The presence of water vapor decreased the rate of CO adsorption on Pt, but had very little effect on the resulting CO surface coverage on PtS (θCO) at steady-state. The steady-state θCOs at 80°C for Pt exposed to H2 (PH2=1 atm) and a mixture of H2/H2O (1atm H2, 10%RH) were 0.70 and 0.66ML, respectively. Furthermore, total strongly bound surface hydrogen measured after exposure to H2/H2O was, surprisingly, the sum of the exchangeable surface hydrogen contributed by each component, even in the presence of CO. In the absence of any evidence for strong chemisorption of H2O on the carbon support with/without Pt, this additive nature and seemingly lack of interaction from the co-adsorption of H2 and H2O on Pt may be explained by the repulsion of strongly adsorbed H2O to the stepped-terrace interface at high coverages of surface hydrogen.
A process for hydrocarbon synthesis comprising the step of reacting a synthesis gas in the presen... more A process for hydrocarbon synthesis comprising the step of reacting a synthesis gas in the presence of a cobalt catalyst promoted with palladium.
Uploads
Papers by James Goodwin