Int. J. Mol. Sci. 2009, 10, 3671-3712; doi:10.3390/ijms10093671
OPEN ACCESS
International Journal of
Molecular Sciences
ISSN 1422-0067
www.mdpi.com/journal/ijms
Review
Chemical Interactions and Their Role in the Microphase
Separation of Block Copolymer Thin Films
Richard A. Farrell 1,2,3, Thomas G. Fitzgerald 1,2,4, Dipu Borah 1,2, Justin D. Holmes 1,2,3 and
Michael A. Morris 1,2,3,*
1
2
3
4
Department of Chemistry, University College Cork, Cork, Ireland; E-Mails: r.farell@ucc.ie (R.A.F.);
thomas.g.fitzgerald@intel.com (T.G.F.); d.borah@ucc.ie (D.B.); j.d.holmes@ucc.ie (J.D.H.)
Centre for Research on Adaptive Nanostructures and Nanodevices (CRANN), Trinity College
Dublin, Dublin, Ireland
Tyndall National Institute, The Maltings, Cork, Ireland
Intel Ireland, Leixlip, Co. Kildare, Ireland
* Author to whom correspondence should be addressed; E-Mail: m.morris@ucc.ie;
Tel. 353-21-4902180; Fax: 353-21-4274097.
Received: 6 August 2009 / Accepted: 14 August 2009 / Published: 25 August 2009
Abstract: The thermodynamics of self-assembling systems are discussed in terms of the
chemical interactions and the intermolecular forces between species. It is clear that there
are both theoretical and practical limitations on the dimensions and the structural regularity
of these systems. These considerations are made with reference to the microphase
separation that occurs in block copolymer (BCP) systems. BCP systems self-assemble via a
thermodynamic driven process where chemical dis-affinity between the blocks driving
them part is balanced by a restorative force deriving from the chemical bond between the
blocks. These systems are attracting much interest because of their possible role in
nanoelectronic fabrication. This form of self-assembly can obtain highly regular
nanopatterns in certain circumstances where the orientation and alignment of chemically
distinct blocks can be guided through molecular interactions between the polymer and the
surrounding interfaces. However, for this to be possible, great care must be taken to
properly engineer the interactions between the surfaces and the polymer blocks. The
optimum methods of structure directing are chemical pre-patterning (defining regions on
the substrate of different chemistry) and graphoepitaxy (topographical alignment) but both
centre on generating alignment through favourable chemical interactions. As in all
self-assembling systems, the problems of defect formation must be considered and the
Int. J. Mol. Sci. 2009, 10
3672
origin of defects in these systems is explored. It is argued that in these nanostructures
equilibrium defects are relatively few and largely originate from kinetic effects arising
during film growth. Many defects also arise from the confinement of the systems when
they are ‘directed’ by topography. The potential applications of these materials in
electronics are discussed.
Keywords: block copolymer; intermolecular forces; self-assembly; ordering; structural
regularity; thermodynamics
1. Introduction and Background
Self-assembly (and self-organisation) has become a topic of enormous interest as scientists have
sought to provide chemical methodologies (sometimes called ‘bottom-up’ techniques) to create highly
organised materials at scales beyond the crystallographic dimensions of atoms or simple molecules.
These regular assemblies are expected to have applications as alternatives to photolithography
(particularly when feature sizes are on the nanoscale) or where there might be advantages in high
surface area or regular feature sizes. An example of the latter is the formation of regular sized pores for
selective molecular separations, selective adsorption systems and high activity catalysis. Self-assembly
is used as a term to describe spontaneous processes where nanoscale entities pack into regular
arrangements in order to attain a minimum free energy through minimisation of repulsive and
maximisation of attractive molecular interactions [1]. In self-assembly, defects can be considered as
higher energy states whose concentration can, therefore, be low and this provides a thermodynamic
driving force for the high structural regularity of the aggregate of entities [2]. In the simplest cases the
self-assembling entities might be solid particles and Murray has pioneered the use of ligand chemistry
to generate regular particulate aggregates as a means of enhancing or controlling the physical
properties of the aggregate compared to individual particles [3]. Self-assembly might also be on the
molecular scale involving surface molecules and described as self-assembled monolayers (SAMS) [4]
or involving molecules in solution where the formation of vesicles or micelles provide suitable
examples [5]. Perhaps the most successful and well known self-assembled nanostructured materials is
mesoporous silica which has a number of important commercial applications including catalysis,
material separations and sorbents [6]. The structures are so regular in these materials that the size
monodispersed pore network can act as a template for the growth of regular sized nanoparticles and
nanowires [7].
The term self-assembly has also been applied to processes not involving individual entities but also
has been used to describe processes such as phase separation within a single component (as in the
example described here, block copolymer microphase separation, and this is discussed in depth below).
Phase separation can probably be more correctly described by the related term self-organisation. The
difference between self-assembly and self-organisation can be difficult to differentiate [8]. Very often,
in chemistry especially, self-assembly and self-organisation are used interchangeably and we will
continue this practice in this article. Self-assembly is generally reserved for systems that are driven to
3673
Int. J. Mol. Sci. 2009, 10
equilibrium via physical interactions between entities (a free energy minimum). Self-organisation
refers to a dynamic process where the assembled or organised structure is in a steady state. It is clear
that in organised micelle systems where the lifetime of any individual micelle is relatively short that
the system can be properly described as dynamic and the term self-organisation can be used
appropriately. For BCP systems where a well-defined order-disorder transition is present the term
self-organisation could be used but in many cases these systems reach a true equilibrium and the term
self-assembly can be properly used. There is further confusion because many (but by no means all)
BCP structures are micellar in nature. Assignment and proper description of these terms are beyond the
scope of this article and for this reason the term self-assembly will be generally used as a generic term.
Self-assembly cannot be confused with chemical reactions; it is centred on arrangements of species
mediated by weak, non-covalent, intermolecular forces. Self-organisation can often involve external
mediating or directing forces as well as these weak intermolecular forces [8]. Fundamental to
self-assembly is that a collection of randomly arranged components (or different parts of the same
molecule) interact to form a more regularly arranged system. Note that the term order should be
carefully avoided because this might imply that entropy always decreases in the self-assembly process.
This is not so and in a few examples local entropy effects can outweigh decreasing entropy at larger
scales. This can be the case in micelle formation and e.g., in the case of colloidal self-assembly where
the presence of secondary components (i.e., smaller particles or polymers and inter-particle excluded
volume) can increase entropy through the assembly process [9,10]. It should be noted that the micellar
processes are true self-organisations because the assembly not only results from the intermolecular
forces between the entities but also from interactions between the entities and the solvent [5]. Strong
bonding covalent forces are not usually associated with self-assembly processes but these may be
involved indirectly, most notably in the formation of self-assembled monolayers where a terminal or
head group can provide a strongly bound ‘anchor’ to a substrate surface whilst tail groups interact via
weaker intermolecular forces [11]. Self-assembly is often associated with the merging field of
nanosciences but is a vital part of nature and is e.g., responsible for the folding of nucleic acids into
their functional forms [12].
Below, we examine in detail the microphase separation of block-copolymers describing the
thermodynamics of the process, the type of structures formed, the formation of regular thin films and
how the structures might be directed to define orientation and alignment, Applications of these systems
are also discussed. As discussed above, BCPs can form ordered structures via self-organisation and
self-assembly-although the generic terms self-assembly will be used through the rest of the article.
1.1. The Thermodynamics of Self-Assembly
Self-assembly is an equilibrium process that represents a balance between repulsive and attractive
forces between entities [1]. These forces are manifest as a minimum in potential energy with distance
apart and are discussed further below. This provides a useful framework for understanding and
modelling the microphase separation of BCPs. The thermodynamics of the self-assembly process can
be represented by a simple Gibbs Free Energy equation
ΔGSA = ΔHSA – TΔSSA
(1)
3674
Int. J. Mol. Sci. 2009, 10
where self-assembly is a spontaneous process if ΔGSA is negative. ΔHSA is the enthalpy change of the
process and is largely determined by the potential energy/intermolecular forces between the
assembling entities. ΔSSA is the change in entropy in the process. Since the organisation is generally
(but not always) accompanied by an entropy decrease, for self-assembly to be spontaneous the
enthalpy term must be negative and in excess of the entropy term. The equation shows that the
self-assembly process will become progressively less likely as the magnitude of TΔSSA approaches the
magnitude of ΔHSA and above a critical temperature will not occur.
As regular structural arrangements are observed in self-assembly it is clear that there must be a
balance of attractive and repulsive forces between entities or else an equilibrium distance would not
exist between the particles. Since, for practical reasons, the assembly is generally not at the atomic or
small molecule scale (for practical reasons outlined below) it is generally necessary that both attractive
and repulsive forces are long range interactions (as distinct from short range chemical bonds) if the
separation distance between features is to be in the nanometre range. This can be illustrated using very
simple consideration of the intermolecular forces between the entities. If we assume that the attractive
intermolecular forces can be modelled as an attractive potential between similar point charges (Q), the
potential energy (Vatt) follows a 1/r dependence and can be written as
Vatt = -Q2/4πεor
(2)
where r is the separation of the entities. The repulsive charge can be modelled as Vrep α 1/rn. Assuming
a charge of around 1.37 × 10-19 C and a repulsive constant = 10000 (10-9)n kJ mol-1 the variation in the
total potential-distance curves (Vtot = Vatt + Vrep) as a function of n in the repulsion term can be plotted
(Figure 1A). The curves describe a classic potential energy well with a minimum Vtot at an equilibrium
separation distance between the entities. It is worth noting since RT ~ 2.5 kJ mol-1, that the minimum
value of Vtot must be significantly greater than this to provide a driving force for assembly that
compensates for an entropy decrease (Equation 1). The minimum value of Vtot can be approximately
associated with ΔHSA assuming that there is no volume or temperature change during self-assembly.
The attractive term is long range in nature and the width of the potential energy well that is formed is
defined, in this case, the repulsive term. At n=4 there is a well-defined potential energy minimum. This
is important because it will precisely define an equilibrium distance between entities that is necessary
if structural regularity is going to be high. The effect of increasing n, i.e., increasing the short-range
nature of the repulsive forces, is to reduce the value of the potential energy minimum, increase the
width of the potential energy well and move the minimum to greater distances. The increasing
shallowness of the well is a major problem in terms of generating patterns of high structural regularity
because it ensures a variation in spacing between entities (or features in phase-separated systems
outlined below) can exist with little energy cost.
The effect of increasing the dependence of potential energy with distance, i.e., increasing the
short-range nature of the attractive potential, also has a dramatic effect on the potential energy curve.
This is modelled using a Vatt that follows a 1/rn dependence whilst using a constant repulsive term that
varies as 1/r6. Illustrative data are shown in Figure 1B. Increasing the value of n reduces the value of
the potential energy minimum, increases the width of the potential energy well and moves the
minimum to greater distances as described for the repulsive forces above. However, as n increases the
Int. J. Mol. Sci. 2009, 10
3675
decrease in the value of the potential energy minimum is very considerable such that changing n from
1 to 3 reduces the potential energy minimum by a factor of around ~× 150.
Although these are quite simple calculations they do illustrate some important concepts in
self-assembly on the mesoscale. Firstly, if the entities are to be relatively large distances apart, the
repulsive and attractive forces between the entities will need to be relatively high or the potential
energy will not provide an effective driving force at room temperature. Secondly, as the spacing
between entities or features increases, variations in the separation distance within the self-assembled
structure will increase dramatically and lead to poor structural regularity. Finally, for self-assembly to
be effective, there needs to be a delicate balance of the intermolecular forces and because of this
self-assembly with high structural regularity is not common-place and will require careful molecular or
particle design coupled to optimisation of the process.
Finally, it should be stressed that self-assembly is a spontaneous chemical process where entities or
components within a mixture arrange themselves in a structured manner and these processes take place
in normal chemistry environments e.g., solution mediated. Normally the self-organisation is borne
from an initially disordered system. Importantly the equilibrium low-energy arrangement is reached
from positional fluctuations as a result of thermal effects. Thus, the effective interaction potential
between the entities or components can not exceed thermal energy by too great a factor or else it will
not be possible to minimise positional errors in the in the arrangement. Alternatively, there has to be
enough difference between thermal energy and the interaction potential energy to maintain order
within the pattern. The thermodynamics of defect formation is described below (Figure 1).
Figure 1. Potential energy against distance curves. A—result of increasing the short range
nature of the repulsive forces between entities in a self-assembly process. Note the
increasing width of potential energy well. B—result of increasing the short range nature of
the attractive forces between entities in a self assembly process. Note the dramatic decrease
in the depth of the well.
1.2. The Intermolecular Forces Involved in Self-Assembly
A detailed understanding of the theory of self-assembly is a difficult problem and these difficulties
have been discussed at length [13]. Very many kinds of intermolecular forces can be involved in
self-assembly. These comprise the classic polar forces including ionic, ion-dipole, dipole-dipole and
Int. J. Mol. Sci. 2009, 10
3676
hydrogen-bonding and other variations that can be described as hydrophobic interactions. Π-π
interactions and even weak covalent forces such as coordination forces have been associated with
self-assembly. Π-π interactions have importance in block copolymer self-assembly because of the
potential for stacking leading to supramolecular structures [14]. These latter forces may have particular
relevance because they can accommodate classic inorganic chemistry to be applied to design
systems [15].
Probably, the most important forces in self-assembly are often described as being hydrophobic in
nature and are responsible e.g., for protein folding and micelle formation of amphiphilic block
copolymers in solution [16] and colloidal assembly. A hydrophobic force is essentially an entropic
force but it does have an enthalpic component largely originating from dispersive forces between
molecules [17]. In water, or similar solvents with strong H-bonding type interactions, the introduction
of anon-hydrogen bonding surface (i.e., aggregations of molecules principally interacting via
dispersive and non-electrostatic forces) results in a rearrangement of the system minimise the number
of disrupted hydrogen bonds and maximising the entropy of the system. These arrangements can lead
to ordered assemblies of the hydrophobic components and is the basis of the so called “attraction”
between hydrophobic objects in solution. It should be notes that the attractive force between the
hydrophobic components is balanced by a weak repulsive force when they are close. This repulsion
originates from the water molecules when trapped in very low entropy positions between the
hydrophobic components. In this way, London dispersion or van der Waals forces are important
hydrophobic interactions. Although these are normally associated with being relatively weak in
molecular systems, they become stronger as size and surface area increase.
On the basis of even this very brief review of the role of intermolecular forces in self-assembly, it
is, therefore, not surprising that self-assembly, self-organisation and phase separation are highly
sensitive to environment and substrate effects [18]. It is beyond the scope of this article to explore
these forces in greater details. Instead we will concentrate on the effects of these forces on the
self-organisation or microphase separation of block copolymers and in particular the understanding of
defect formation in these systems.
2. Microphase Separation and Self-Organisation Block Copolymers
Block copolymers have become increasingly more important materials as routine design and
synthesis of these materials has become practical. Block copolymers were developed to essentially
tune the properties of the macromolecule between that of the two blocks individually. The advantage
of using a single macromolecule rather than a blend is that the macroscopic phase separation in
mixtures can not occur. However, the chemical mismatch does lead to microphase separation as
described below. Industrial synthesis of block copolymers (BCPs) was first demonstrated in the 1950s
by scientists at BASF and ICI around the generation of triblock systems of poly(ethylene oxide) and
poly(propylene oxide). Amongst many applications these found widespread use as surfactants,
anti-foaming agents, cosmetic materials and drug release materials [19]. More recently they have
found use as versatile ‘templating agents’ for the generation of ordered nanoporous silicates allowing
precise control of pore diameters [20]. Spandex was the first BCP to be widely known because of its
use in textiles (spandex is an anagram of expands) and was invented by the DuPont chemist J. Shivers
3677
Int. J. Mol. Sci. 2009, 10
[21]. It became apparent that the possibility of forming macromolecules with blocks of differing
chemical properties could yield materials where the interaction of the different blocks would ordain
important physical properties. Many aspects of BCPs have been reviewed in depth [22,23]. This article
will be restricted to discussion of the formation of nanopatterns of these materials in thin film form on
substrates. The nanopatterns are essentially the result of the self-organisation via microphase
separation of the BCP at the surface and not via micelle formation and related phenomena of the BCP
in solution. Lyotropic phases will not be discussed at length here, however, solvent effects can not be
completely ignored because it is convenient and practical (particularly for the thin films discussed
here) that the polymers are solvent cast onto the substrate surface by techniques such as dip- and
spin-coating. Further, a technique known as solvent-annealing or solvent-swelling is becoming
common place as a means of attaining high degrees of structural regularity. This ordering is a result of
the increased mobility within the macromolecule block network related to the decrease in the glass
transition temperature as a result of solvent molecule inclusion [24].
2.1. Intermolecular Forces in Microphase Separation of Block Copolymers
When any two polymers are mixed the result is often phase separation. This phase separation may
not be observed on a macroscopic scale; unlike phase separation in liquids, the process may be
extremely slow because of the mass transport limitations associated with the large number of mers in
the polymer. If ordered systems are observed this process may be properly described as
self-organisation. Very often phase separation in a polymer blend will not be observed until heating to
around the glass temperature when chain mobility is much higher. It is worth noting that even when
the polymers are quite similar chemically, small differences can result in strong repulsive interactions
between the polymers because of the number of units in a chain. The polymer molecular weight will
play a pivotal role in any phase or microphase separation process because it will define both the
strength of the repulsions and chain mobility within the system. The repulsive forces between blocks
will lead to segregation of two polymer components under suitable temperature conditions.
Importantly, there is a practical temperature window such that the temperature should be i) low enough
that the result of intermolecular forces can be expressed despite thermal randomisation and ii) high
enough that phase separation can be achieved in reasonable times.
In block copolymers complete phase separation of the chemically distinct sub-groups can not be
achieved because of the chemical bonds that bind the two blocks. Thus, the chemical immiscibility of
the monomers that would drive a blend of polymers to segregate is counter-balanced by a restorative
entropy cost associated with deformation of the random coil structures of the blocks that occurs during
microphase separation. The result of this balance of repulsive intermolecular forces between blocks
and attractive restoring force is the formation of mesocale regular periodic structures of microphase
separated domains with the structure being formed in order to minimise the contact area between
dissimilar blocks. The term microphase separation is becoming strongly associated with this BCP
self-organisation but can also be seen in mixtures of liquids, metal alloys and ceramic systems.
The thermodynamics of microphase separation can be expressed by modification of Equation 1
Gmix – GPS = ΔGSA = ΔHSA – TΔSSA
(3)
3678
Int. J. Mol. Sci. 2009, 10
where Gmix and GPS represent the free energy of the mixed and phase separated systems respectively.
ΔHSA and ΔSSA represent the enthalpy/entropy changes between the mixed and phase separated states
respectively. It should be noted that the entropy change associated with mixing is usually quite small
because of the random coil confirmation adopted by the polymer blocks. Within the mixed state the
BCP will adopt an unsystematic confirmation of random coils which results in a great many contacts
between the different blocks. The random coil arrangement is the usual structure for macromolecules
because of the possible rotations around the C-C bonds in the polymer backbone. The intermolecular
forces driving the microphase separation process are normally of the hydrophobic type described
above where the attraction of more polar components forces the non-polar components to aggregate.
This segregation of the blocks reduces the number of interactions of the dissimilar blocks thereby
lowering the number of repulsive interactions between chains. The value of ΔHSA is thus always
negative and should result in de-mixing of the blocks. During segregation of the blocks the random
coils become extended decreasing the number of possible configurations and so decreasing entropy.
This results in an entropic restorative force opposing the enthalpy driven phase separation and so phase
separation occurs over very limited distances of the same order as the random coil length.
The intermolecular forces dominant in microphase separation are dispersion forces, polar forces and
hydrogen bonding. These give rise to the balance of repulsive and attractive interactions (‘hydrophobic
forces’) detailed above. The application of the models to explain BCP self-assembly has significant
relevance and has even been used to explain the self-assembly associated with Huntington’s disease
[25]. Dispersion forces become dominant in polymers that contain hydrocarbon groups and although
relatively weak can be quite strong over the volume of the macromolecule. Polar forces are common in
oxygen containing systems such as polyesters and polyethylene oxides. Hydrogen bonding is common
in many systems including polyamides. The strength of the intermolecular forces can be understood by
consideration of a term known as the solubility parameter which was first proposed by Hildebrand [26]
and has been extensively reviewed because of its’ fundamental importance [27-28]. Although this term
is often considered to be a qualitative measure of the propensity of one material to dissolve in another,
the solubility parameter, δ, is a thermodynamic quantity quite specifically defined. The cohesive
energy Ecoh of a substance in a condensed state is defined as the increase in internal energy U per mole
of substance if all of the intermolecular forces with its environment are eliminated. In a solution the
free energy change represents the difference between the condensed (i) and the gas (g) phase states
(ΔU = Ug - Ui). Since the internal energy (ΔU) of a system is the sum of kinetic energy and potential
energy it can be seen that Ecoh is closely related to the strength of the intermolecular forces between the
entities in the condensed state but the kinetic energy component can not be ignored because significant
differences are expected. The Ecoh can be expressed as the cohesive energy (molar volume)
density (ECD)
ECD = Ecoh/Vm
(4)
and the solubility parameter, δ, is defined as
ECD1/2 = δ
(5)
δ = (Ecoh/Vm) 1/2
(6)
And
3679
Int. J. Mol. Sci. 2009, 10
Since ΔU = ΔH + Δ(P Vm)
(7)
i.e., the internal energy change is equal to the change in PV work and the enthalpy change we can
write
δ = ((ΔHvap + RT)/Vm) 1/2
(8)
where ΔHvap is the heat of vaporisation. The solubility parameter should be referred to as the cohesion
parameter when discussing non-liquid materials. The relationship of δ to the intermolecular forces can
be seen using Hansen parameters developed in 1966 [30,31]. Hansen parameters separate the
Hildebrand value into three parts: a dispersion force component, a hydrogen bonding component and a
polar component. The square of the Hansen parameters are additive
δ2 = δd2 + δp2 + δh2
(9)
where δd is the dispersion component, δp is the polar component and δh is the hydrogen bonding
component. Numerical values for the component parameters are estimated by reference to the
non-polar molecule that most closely resembles the molecule of interest (e.g., polyethylene for
polyvinyl chloride). The contribution of polar and hydrogen bonding terms was based simply on other
supporting evidence. Typical Hansen parameters are provided elsewhere [29,30].
The power of the solubility parameters and, in particular, Hansen parameters is that they can be
used to predict the solubility of one component in another particularly through consideration of
δA2 – δB2. If this is close to zero it implies that the molar enthalpies of vaporisation are similar and the
intermolecular forces holding the components in a fluid or solid state similar. For example, if we take
two polymers such that δA2 – δB2 has a significant magnitude then it would be expected that they would
phase separate on mixing. If the components are present as a block copolymer they would be expected
to microphase separate. The Hansen approach suggests that raw Hildebrand values may not provide
adequate understanding in all systems since we would hope that polar and non-polar contributions of
the two components should also be similar for favourable mixing or lese that segregation of
components would be expected on the basis of the hydrophobic forces described above. It should also
be noted that solubility or mixing of polymer components will be very sensitive to even small
differences in the solubility parameter of the components. This is due the square dependence and also
because it is a direct measure of the magnitude of the intermolecular force differences and even when
they are small can be very significant over the whole of the macromolecule. This is described and
illustrated in detail below.
2.2. The Solubility Parameter and the Thermodynamics of Microphase Separation
The thermodynamics of microphase separation in BCPs has been reviewed several times following
the original work of Bates [31]. The theory will not be detailed in depth here except to show how it
relates to intermolecular forces through the solubility parameter. Most of the understanding of
microphase separation of BCPs is centred on a term known as the interaction parameter χ. Assuming a
simple diblock copolymer made up of sub-units A and B, the χ value resulting from the interactions
between block A and block B can be written as
3680
Int. J. Mol. Sci. 2009, 10
χ = zΔw/kT
(10)
and χ is the exchange energy per molecule normalised by the thermal energy kT and is dimensionless.
The number of neighbours surrounding one block is z. Δw is the exchange energy which is the
difference in energy between the interaction between block A and block B and the average of the self
interactions between block A-block A and block B-block B. That is, Δw is the energy cost of taking a
block of A from surrounding A blocks and placing in a B block environment and doing the same for a
B block (from a B environment to an A environment). The interaction parameter can be related
directly to the molar enthalpy change of mixing, ΔHm, by
ΔHm = ƒAƒB χRT
(11)
where ƒA and ƒB are the volume fractions of the blocks. By conventional solution theory and assuming
no volume change on mixing, it can be shown that
χ = Vm(δA – δB)2/RT
(12)
where δA and δB are the solvent parameters (see below) of the two blocks. Therefore
ΔHm = ƒAƒB Vm(δA – δB)2
(13)
This is important because it shows that any block copolymer system where the blocks have
different solubility parameters (i.e., different strengths and forms of intermolecular interactions) will
have a positive enthalpy of mixing and will, thus, have a tendency to microphase separate and
self-assemble provided the entropy change (always a decrease as discussed above) associated with the
process is not too large as to overcome the enthalpy contribution. Flory-Huggins theory has been the
basis for modelling the behaviour of block copolymers since their invention and remains the most used
model to date [32,33] providing a robust basis for the prediction of morphology seen in BCP
microphase separated systems. Using this formulism the configurational entropy of phase separation is
assumed as the only major contribution to energy such that the entropy associated with microphase
separation ΔSm = klnΩ where Ω is the number of possible ways of arranging the system. Via Stirling’s
approximation the entropy change can be written as can be written as
ΔSm/RT = (1/NA)ln ƒA + (1/NB)ln ƒB
(14)
where NA, NB are the degrees of polymerisation of each block such that ƒA = NA/(NA + NB). Since the
entropy decreases in the system on mixing and using Equation 11
ΔGm /RT = ƒAƒB χ + (1/NA)ln ƒA + (1/NB)ln ƒB
(15)
This Equation specifically relates to the mixing process and not phase separation. The implication is
that the free energy of mixing is always likely to be positive bearing in mind the definition of χ given
in Equations 10 and 12. The driving force for self-assembly is the minimisation of the free energy of
mixing by the regular patterns formed by microphase separation. For illustrative purposes consider the
formation of a regular, microphase separated, lamellar phase consisting of alternating stripes of blocks
from a AB block copolymer with ƒA = ƒB. The lamellar structure is a common motif in phase
separation because it is achieved with lowest mass transport limitations. This is particularly important
considering that phase separation is limited by the covalent bonding between blocks and all theories
suggest this is the lowest energy structure for BCPs. A simple schematic of the arrangement can be
3681
Int. J. Mol. Sci. 2009, 10
seen in Figure 2. As can be seen from Equation 3, ordered self-assembly/microphase separation will
occur provided that ΔGSA = Gmix – GPS is negative. The free energy change in forming the lamellar
structure (ΔGSA,L) can be described by modelling Gmix as a sum of AB contacts and GPS as a Hookian
term describing the balance of repulsive enthalpic and attractive/restorative entropic forces (as detailed
above) plus an interfacial term. In this way [31,34] the GPS can be written
GPS = 1.19(χABN)1/3
(16)
and the equilibrium spacing between stripes in the lamellar structure (L) as
L = 1.03a(χAB)1/6N2/3
(17)
Since the sum of simple contacts in the mixed system allows Gmix to be estimated as (χABN)/4 it is
possible to write that for microphase separation to occur Gmix must be greater or equal to GPS and the
minimum condition is
1.19(χABN)1/3 = (χABN)/4
(18)
Thus, for microphase separation χABN must be greater than 10.4. Since χAB is a measure of the
chemical dis-similarity between the units (mers) in the blocks χABN represents the total dis-similarity
over the whole macromolecule. Using Equation 18 the minimum value of (χABN)min to bring about
phase separation is about 10.4. This very simple approach provides a value for (χABN)min which is very
similar to much more complex theories developed by Leibler using self-consistent field theory [35]. A
summary of recent theoretical developments in block copolymer phase separation has been provided
by Grason [36].
2.3. Phase Diagrams
The structure resulting from microphase separation will be dependent only on a limited number of
parameters; the chemical differences between blocks, the degree of polymerisation and the
composition of the BCP. Since the interaction parameter is dependent on temperature, this will also
have an effect. The variation of structure with χABN and composition is normally shown using a phase
diagram and was first theoretically determined by Matsen [34] and is still very widely used to describe
self-assembly in these systems. Only simple diblock systems will be described in detail here and the
reader is referred to phase diagrams for triblock structures [31]. The general form of the theoretical
phase diagram calculated by Matesen agrees well with literature [37]. The phase diagram is separated
into several regions which are characterised by the relative stability of the structures formed and the
dependency of the separation of features or feature size, L, on the degree of polymerisation [38]. For
the symmetric system (i.e., ƒA = ƒB) below χABN ~ 10.5 the system is disordered. Between
χABN = 10.5 and 12.5 the region is known as the weak segregation limit and L is proportional to N0.5.
In the intermediate regime, χABN = 12.5 to 95, L is proportional to N0.72 and above this level (the
strong segregation limit) L is proportional to N0.67. For practical purposes, it is probably best to avoid
the weak segregation limit for creating well-defined block copolymer structures, because although this
gives the smallest feature size, the thermodynamic driving force (as determined by the intermolecular
forces) is small and regions of disorder might be expected because of thermal effects. The strong
Int. J. Mol. Sci. 2009, 10
3682
segregation limit may also afford problems in the commercial use of these materials because the
thermodynamic driving force for microphase separation is becoming so strong that it vastly exceeds
thermal energy and achieving thermal equilibrium (for reduction of disorder) may require extended
annealing. For practical purposes it should also be remembered that as the molecule increases in length
there will be increased rigidity and the glass transition temperature of the systems will increase and
there will be temperature requirements imposed by processing in commercial applications which might
place an upper limit on the time used to attain phase separation.
In the region of the diblock phase diagram where the balance of intermolecular forces results in
microphase separation various structures form within certain composition limits. The phase diagram
first described by Matsen [34] is symmetrical around the mid point of composition ƒA = ƒB = 0.5
although experimentally the system is a little more complex than predicted [39]. This central region
adopts a lamellar structure. As ƒA increases to between 0.6 and 0.7 a bicontinuous gyroid phase of
cubic symmetry consisting of interpenetrating tubules of the B block in A block is formed. This phase
has a relatively narrow stable composition range particularly in the intermediate and strong segregation
ranges. At higher ƒA values there is a composition range where there is a hexagonal arrangement of
block B cylinders in a matrix of A. Finally, the B block adopts an arrangement of body-centred
spheres. Due to its structural complexity and a narrow stability range, the gyroid structure has only
limited applicability and is less well studied. The lamellar and, hexagonal and body-centred structures
have been intensively studied and these are described in Figure 2. Of these the lamellar and hexagonal
structures are most important in terms of patterning electronic materials and generating useful
porous materials.
Figure 2. Schematic showing the most useful microphase separated arrangement of blocks
possible in a diblock copolymer as a function of increasing compositional asymmetry. The
gyroid structure is not shown (see text).
In reality, more complex structures do form because of the complexity of the intermolecular interac
tions in polymers. Grayson has reviewed extensions to theory which allow more complex systems to
be examined [40]. A structure of this type that has received some attention is the hexagonal-perforatedlamellar structure that is metastable and observed at the phase boundary between the lamellar and
cylinder arrangements [41,42]. This perforated phase has become more important in thin film
structures because it can be stabilised by surface reconstruction [43] due to preferential interactions of
Int. J. Mol. Sci. 2009, 10
3683
one block with gas, liquid or substrate interfaces. Hamley has surveyed a great number of diblock
systems and the phases that they form [44].
2.4. Applications of Microphase Separation—SURFACE Pattern Formations
Microphase separation in BCPs is becoming a subject of research for potential commercial
development. Few self-assembling systems can rival the regularity of BCP systems with perhaps only
mesoporous silicates [45] and porous anodic alumina [46] rivalling the polymer systems in the feature
size range of interest and having been shown to offer opportunities for controlled alignment. It can be
seen from the arguments made above that the high regularity of the systems is because the
intermolecular forces that drive the self-assembly are such that highly periodic structures are favoured
and ordering can be attained at practical temperatures. One of the advantages of BCP self-assembly
compared to these inorganic systems is that the film can be ‘annealed’ after their formation to improve
the regularity of the self-assembled structures. Other self-assembled systems such as nanoparticle
superlattices [47] also produce highly regular and sometimes complex structures. However, the
synthesis of size mono- dispersed particles is challenging for all but a few systems and thin films of
these tend to lack thermal and mechanical robustness. BCP systems do have an unrivalled combination
of advantages; thin films can be formed from simple solutions, the resultant films are robust, the
feature size is highly controllable using polymer engineering and the films are readily processed (e.g.,
in pattern transfer where the polymer pattern is transferred to the surface by selective etch processes).
Authors have demonstrated many applications for microphase separated BCP thin films. BCP
micelle systems have found commercial use in applications such as drug delivery but these are not the
focus of the work described here and the reader is directed to some excellent reviews [48,49].
Applications for BCP films in the general area of materials science include solid state battery
electrolytes [50] and membrane separation technologies [51]. Park and co-workers have provided an
extensive review of technologies that might be developed using BCP thin films and these are largely in
the area of development of strategies to develop nanoscale electronics, magnetics and photonics [52].
These ICT focussed technologies include low dielectric materials for electrical insulation and
reduction of crosstalk [53-55], high density magnetic storage media [56] and photonic band gap
crystals [57].
By far the most researched area for use of these materials is as potential alternatives to conventional
mask-based photolithography for fabrication of nanoelectronic circuitry. Photo-lithography has been
the cornerstone of the electronics industry since the advent of the first silicon devices [58,59]. The
photolithographic process has been continually developed to allow the size of devices to be decreased
and the density of devices constantly increased so that individual transistor sizes have shrank from cm
type sizes to around 50 nm. The trend in resolution enhancement was, for many years, achieved by
reducing the dimensions of the mask patterns whilst simultaneously decreasing the wavelength of the
radiation (light) [60]. Currently, techniques such as immersion technologies whereby a liquid (usually
water) is placed directly between the final lens and photoresist surface resulting in a resolution
enhancement defined by the refractive index of the liquid have allowed device engineers to pattern
transfer feature sizes (65 or 45 nm generation) that are actually less than the wavelength of light used
(193 nm) [60]. Device performance is ultimately limited by the density of transistors on the chip [61]
Int. J. Mol. Sci. 2009, 10
3684
and it is clear that patterning requirements will continue to the 32 nm node and beyond. Although
photolithography can potentially be used to create sub-10 nm device structures for high volume
manufacturing processes, it will necessitate the use of deep UV (13 nm) and x-ray sources and these
are associated with high costs and materials implications for the masks and resists [62].
For these reasons, self-assembly may have importance for transistor manufacture beyond the 22 nm
node [63]. The advantages of self-assembly over conventional and non-lithographic methods include:
(i) the reduction of source costs, (ii) elimination of masks and photoresists, (iii) non-existence of
proximity affects, (iv) the possibility of developing 3D patterning techniques, (v) absence of
diffraction restrictions to resolution and (vi) can be used to pattern materials with precision placement
techniques by availing of templating (i.e., deposition of materials within the structure, known as
graphoepitaxy) or a chemical pattern (alternating surface chemistries). The microphase separation of
block copolymers is emerging as the most promising method of assembling highly ordered
nanopatterns at dimensionalities and regularity approaching the future device dimension requirements.
These requirements are extremely challenging for self-assembly and lithography alike and include
sub-nm line edge roughness and sub-4 nm positioning (of a feature expressed from the overlay registry
requirements) accuracy for the 16 nm technology node [64]. The potential application of BCPs in this
area has been extensively reported and reviewed [58,59,65-71]. These reviews also detail the methods
by which the polymer nanopatterns can be processed into active components (i.e., nanowires, nanodots
of semiconducting, magnetic or conducting materials). As briefly outlined above, these are
conveniently divided into two broad areas; pattern transfer where essentially the polymer is used as a
mask within an etch process and templating where active materials are selectively placed at one block
(or the space created by removal of one block). In the remainder of this article we will explore some of
the issues which may prevent implementation of BCP self-assembly as a technology for development
of nanoelectronic circuitry. The issues mainly result for difficulties in controlling or defining the
chemical interactions of the polymer with the substrate and other interfaces.
3. Surface, Interface and Related Effects
The simple theories mentioned above for describing microphase separation relate to the
development of bulk structures from the melt. However, for application in electronics the only
practical means of developing thin films (<100 nm) is deposition from a solvent and, further, once
formed the film is susceptible to boundary, thickness and interface effects which will disturb the
delicate balance of intermolecular forces within the films.
3.1. Surface Interface Effects
Within mobile systems such as BCPS which are heated to around their glass transition temperature
to effect microphase separation, changes in the film structure will occur to minimise surface energies
and maximise bonding interactions with the surface. In block copolymer systems these interactions are
manifest as: 1) preferential wetting layers by segregation of the preferred block to the substrate or
surface, 2) irregular films caused by de-wetting of the film and 3) orientational effects and stability of
unexpected film patterns.
Int. J. Mol. Sci. 2009, 10
3685
Figure 3. Orientational effects in block copolymer thin films upon self-assembly. Dashed
lines indicate the wetting layers. See text for details.
Some examples are shown in Figure 3 (assuming substrate surface effects are dominant and surface
interface effects can be ignored for simplicity). In Figure 3A and 3B two orientations of the same
structure can be seen. In Figure 3A a horizontal orientation of the lamellae occurs if one block is
preferentially favoured at the substrate surface whilst in Figure 3B a vertical orientation occurs as of
both blocks are equally favoured. Similarly for the hexagonal cylinder structure, a substrate surface
that interacts equally with both blocks will favour vertical orientation of cylinders with respect to the
surface (Figure 3C). Whilst favourable interactions of one block with the surface and substrate
interfaces can lead to the formation of wetting layers which will tend to favour a horizontal orientation
to the surface (Figure 3D). In general the block that has lowest surface energy will reside at the
surface. The substrate interactions can also yield complex structures. In Figure 3E strong substrate
interactions with the minority block can lead to a perforated lamellar-like structure. The perforated
lamellar structure is only pseudostable and is best thought of as an intermediate phase between the
hexagonal and lamellar structures [72]. This structure is being observed more frequently in very thin
films largely because of these strong interface effects [73]. The example in Figure 3E might arise if the
substrate favours one of the blocks and the surface energies of both blocks are similar.
Finally, it should be recognised that the interactions of the BCP with the substrate can lead to
complex morphologies on the micron scale. For example, if a surface is hydrophobic and both blocks
in a diblock copolymer are hydrophilic there will be a tendency to form droplets rather than
Int. J. Mol. Sci. 2009, 10
3686
commensurate films as illustrated in Figure 3F where hemispheres of phase separated polymers are
formed [74]. In the case of block copolymers commensurate (flat films of regular thickness) thin films
are defined by the amount of polymer at the surface so that an integer (if the same block resides at the
substrate and the surface interfaces) or half integer (i.e., different blocks at the substrate and the
surface interfaces) number of lamellae are formed [75]. The types of pattern produced are shown in
Figures 4A-4C for a polystyrene-b-poly(methyl methacrylate) (PS-b-PMMA) BCP.
Figure 4. Phase separation of a PS-b-PMMA (symmetric, lamellar forming polymer)
spin-coated thin film as indicated by tapping mode atomic force microscopy. The
molecular weight of both the PS and PMMA blocks is 37 k. As the amount of polymer
increases the morphology shows three distinct forms.
At lower thicknesses isolated islands of BCP are formed but as the amount of polymer increases
these bumps merge and a bicontinuous layer is formed. As an amount of polymer equivalent to a
commensurate layer is approached the film adopts a uniform thickness with a series of holes.
Microphase separation is possible in these structures as shown in Figure 4. It should be noted that
these images are relatively simple. Film thickness plays an important role in determining orientational
effects—e.g., in hexagonal cylinder arrangements whether the cylinders are vertical or parallel to the
surface. In thin films the elastic strain energy associated with forming a parallel arrangement is too
great unless an integer number of layers of cylinders are formed and instead a vertical arrangement is
favoured [76]. In thicker films the strain energy can be more readily accommodated and thickness
dependence is less. In general, very thin films favour vertical (to the surface) alignment of cylinders or
lamellae. This is a challenge for lithographic applications because using the BCP nanopattern to create
wire type structures (from cylinder forming structures) is significantly more difficult than forming
nanodot structures. Because of this dependence of orientation with thickness, complex morphologies
such as hemispheres can show several different orientations within a single object [77].
These substrate effects need to be carefully controlled for applications in lithography where
orientational control, alignment control and film regularity are pre-requisites for transferring patterns
over large areas. Note here that orientation is used to describe direction of the BCP features relative to
the surface plane (i.e., vertical or horizontal) whilst alignment refers to determination of direction
within the surface plane (to an azimuthal direction). The most obvious method of providing ideal or
neutral surfaces is to manipulated the chemical interactions between the BCP and the substrate such
Int. J. Mol. Sci. 2009, 10
3687
that they do not differentiate between the blocks. Random block copolymer thin films (i.e., where
relatively short chains of each block provide a random distribution of composition) or self-assembled
monolayers (SAMS) have provided a useful approach for this surface chemical modification. SAM
methods have produced interesting results and orientational control has been demonstrated [78]. One
of the more attractive features of the SAM chemistry is that for optimisation of BCP film quality it is
necessary to achieve exact monolayer coverages of the SAM or polymer brush and this is readily
achieved in SAMS by relatively simple methods. Polymer brush chemistry, largely developed by
Russell, Hawker and their co-workers [79], also provides almost ideally chemically tailored surfaces
for BCP self-assembly but obtaining very uniform surface coatings is more problematical than for
SAMs, a typical example of a brush layer is shown in Figure 5. The importance of good brush
chemistry for generating ‘perfect’ self-assembly has been shown by Nealey [80] and is demonstrated
in Figure 5. Here a symmetric PS-b-PMMA block copolymer has been deposited onto a bare (100)
silicon substrate and a brush modified version of the same surface. It can be seen that the unmodified
surface, Figure 5B, produces little regular assembly because of poor polymer wetting characteristics.
However, in the brush modified surface, Figure 5C, discrete lines are observed due to vertical
orientation of the lamellar. These surfaces are often described as neutral—the term being used to
indicate a surface wet by both blocks equally.
3.2. Solvent Interface Effects
The second interface of importance in polymer thin film formation is frequently a polymer thin
film–solvent interface. For convenience polymer thin films are formed by conventional coating
techniques (such as spin-coating or dip-coating) from polymer solutions. During solvent
annealing/swelling the process of solution is complex. In the first part of the process solvent penetrates
the macromolecular network forcing the individual molecules apart. This process results in an
expansion in volume of the polymer and in thin films is associated with a thickness change which can
often be revealed as a distinct colour change. This is known as polymer swelling. In high solvent
concentrations the limited availability of polymer results in eventual complete separation of the chains
and solution occurs. Where the amount of solvent is limited (e.g., in solvent atmospheres or limited
solubility), complete solution will not occur. The basis of polymer swelling, solution [81] and kinetics
[82] has been described. In microphase separated BCP systems the chemical interactions between the
polymer and the solvent can usually be ignored. This is because the system is usually heated at
temperatures around the glass transition temperature but below the order-disorder temperature in
vacuum to obtain the most ideal ordering possible and thereby minimising the total free energy of the
system. In these treatments it is generally thought that solvent within the matrix will be rapidly
removed compared to usual heating times. This may not be true for glassy polymers such as
polystyrene heated well below the glass transition temperature. Recent work has shown that solvent
may be retained in thin polystyrene films for extended periods [83]. Even in cases where polymer is
removed by post-processing, interactions of the polymer may have a profound effect because of two
effects. Firstly, the BCP with two distinct chemical blocks may form in solution. These micelles may
have enough rigidity or mass transport limitations such that they survive and heating of the resultant
thin film and examples are given below. Secondly, a technique known as solvent annealing is attaining
Int. J. Mol. Sci. 2009, 10
3688
popularity for bringing about microphase separation as an alternative to or in combination with
vacuum heating.
Figure 5. (A) cross-sectional TEM image of a random copolymer brush layer applied to a
silicon substrate. The overlayer is a PS-b-PMMA BCP applied above it. The Au and Cr
shown form pattern for graphoepitaxial alignment (see below). (B) a tapping mode AFM
image of a lamellar forming PS-b-PMMA system on bare silicon whilst (C) is the same
polymer on a well-defined brush layer.
Solvent annealing as an alternative to thermal annealing was proposed by Libera et al. [23] where
microphase separation of a cylinder forming polystyrene-b-polybutadiene-b-polystyrene (PS-b-PB-bPS) triblock copolymer was achieved using a solvent exposure technique. This method has since been
extended to a variety of other copolymer systems including polystyrene-b-poly(2-vinylpyridine)-bpoly(t-butyl methacrylate) [84], polystyrene-b-polyisoprene [85] and most recently polyisoprene-bpolylactide [86]. The most extensive work in this area has focused on the formation of a hexagonal
arrangement of cylinders of the minor block component (PEO) in a PS matrix for an asymmetric
PS-b-PEO diblock system. Russell et al. [87,88] have been at the forefront in refining this approach to
enhance control over the lateral order in hexagonally close packed cylindrical microdomains in thin
films. This technique works by lowering the glass transition temperature of the polymer because of
solvent molecules that penetrate the macromolecular matrix separating the molecules, increasing the
system volume and increasing mobility within the system. The lowering of the glass transition
temperature as a function of even relatively small solvent content can be relatively large [89].
Although, polymer swelling apparatus can be quite complex (e.g., flow-through, pressure control) it
can be effected by simple placement of samples in a beaker and exposing them to a solvent vapour
pressure. The advantages of the methodology can be shorter processing temperatures and enhanced
thermal separation from the order-disorder temperature.
Int. J. Mol. Sci. 2009, 10
3689
The rationalisation of solvent effects in these systems can be achieved using the concept of solvent
parameters introduced earlier. The solvent parameter arose from Hildebrand and Scott’s work on
describing a series of rules to explain the solubility of solids and gases and as such can be used to
define whether a substance in any physical sate is soluble in a solvent [90]. In Hildebrand’s original
work, the solvent parameter was used as a measure of the cohesive energy which has fundamental
importance because it is a direct measure of the strength of the chemical bond holding the molecules
together in the liquid. This chemical bond strength is given directly by the square of the solvent
parameter which yields the cohesive energy density (as detailed above). The cohesive energy density
was originally described as the internal pressure of a fluid as used in the classic non-ideal gas equation
and for small molecules (that obey Raoults’s Law in similarly simple solvents) can be approximated
by the heat of vaporisation per unit volume. In this way the solvent parameter is a direct measure of the
intermolecular interactions that exist in a fluid and in turn explains the series of physical properties
described as colligative. By addition of a solute to a solvent the intermolecular forces between solvent
molecules are disrupted and thus any properties dependent on these weak chemical interactions will be
altered (to a first approximation) by amounts proportional to the amount of solute not specific
chemical interactions between the solute and the solvent molecules. The description of the solvent
parameter given here shows that these colligative properties relate to establishment of the chemical
equilibrium liquid solution and the pure solvent. Colligative properties such as vapour pressure,
freezing point depression, boiling point elevation and osmotic pressure are thus defined as those
properties that do not depend on the nature of the solute but only on the amount added.
The practical importance of the solubility parameter is that it allows prediction of whether one
material is soluble in another. This is because unless the type and magnitude of the intermolecular
interactions between different molecules in solution are similar there will be no tendency for the solute
and solvent molecules to intermix and thereby reduce the free energy of the system. The tendency for
solvation is often described on the basis of "complementary matching" and an interaction parameter χ
defined by expressions equivalent to Equation 12. It is generally accepted that for solubility the χ value
must be less than 0.5 or the differences in solubility parameter no greater than about 5 (J cm-3)1/2.
When a BCP is placed in a solvent careful consideration of the solvent chemistry must be considered.
Where the blocks are chemically distinct and one block has a solubility parameter close to that of the
solvent, micellisation may occur although this is a very complex process [5]. Since these properties are
colligative, the BCP will only truly dissolve in the solvent if the total solubility parameter (given by a
simple volume ratio of the blocks and their individual δ values) is close to the solubility parameter of
the solvent. However, it should be remembered that solubility parameters, since they depend on the
intermolecular forces between molecules, can be strongly dependent on temperature. This coupled to
low solution concentrations (such that the concentration is below the critical micelle concentrations
[5]) can ensure that solutions are not micellised even where δ values might suggest this is possible.
Polystyrene-b-poly(4-vinylpyridine) (PS-P4VP) is one system where strong micellisation is known
to occur [91]. The micelles formed are stable enough to survive solvent removal during thin film
formation. Figure 6 represents a series of AFM images of a symmetric PS-b-P4VP block copolymer
(Polymer Source Inc.) of composition MnPS = 20,000 g mol-1, MnP4VP = 19,000 g mol-1 dissolved in
toluene, spin-coated onto a Si(100) surface and then solvent annealed in a series of solvents and
solvent mixtures such that a range of solvent parameters could be probed. Microphase separated
Int. J. Mol. Sci. 2009, 10
3690
structures are only observed upon solvent annealing in toluene/ethanol, tetrahydrofuran/ethanol,
ethanol/chloroform and toluene/methanol mixtures that closely match the solvent parameter of the
BCP (~23.0 MPa1/2). In all other cases the patterns seen are typical of hemispherical micelles and
related morphologies on the substrate. It should be noted that PS-P4VP is molecularly dispersed in this
solvent [92]. These data demonstrate that choice of solvent and a fundamental understanding of the
chemical interactions between the solvent and the components of the BCP are pivotal in determing the
ideal conditions for generation of long range order in microphase separated BCP systems.
Figure 6. Tapping mode AFM images of 60 nm (average film thickness) thick PS-b-P4VP
thin films following film deposition and annealing in various solvents and mixtures. The
solvent parameter (MPa1/2) ranges from 18 to 38 (water=48).
In a similar way that the chemical interactions of the BCP with the substrate surface can define
orientation of features, the same type of control can be exerted by the surface-solvent interactions
particularly in solvent annealing processing of these films. Because of the sensitivity of the BCP
structure to even small changes in solvent parameter even relatively small changes in annealing
conditions can cause dramatic changes in film structure. Poly(styrene-b-ethylene oxide) (PS-b-PEO) is
a system which has been shown to be amenable to both orientational control and improvement in
long-range ordered phase separation by the solvent annealing method [87,88]. Russell and his
co-workers have explained a vertical orientation of cylinders in this system as a result of a ‘field’
effect where the evaporation of solvent molecules during solvent annealing leads to preferable vertical
orientation of the cylinders. Recent work by our group demonstrates that orientational effects can also
be controlled by careful control of the solvent parameter [93]. In this work it was suggested that the
change in solubility parameter of a toluene/water mixture with temperature (due to changes in the
vapour pressure of each of the co-solvents with temperature) was sufficient to select between an
atmosphere that favoured both blocks at the surface (defining a vertical cylinder orientation) to one
that favoured one block only (favouring a wetting layer of one selective block and a parallel
orientation).
Int. J. Mol. Sci. 2009, 10
3691
Figure 7. A—theoretically predicted model of polymer film development via spin-coating
at an isolated topographically patterned channel in a substrate surface. The grey areas
indicate the channel walls. B and C show sinusoidal variations in block copolymer polymer
film thickness as observed by cross-sectional electron microscopy. B—PS-b-PI-b-PS
spin-coated at deep trenches in a silicon substrate (SEM). C—PS-b-PEO at shallow
trenches formed by creation of gold lines at a silicon substrate (TEM).
3.3. Solvent Casting Effects
It should also be noted that the structure of films can be strongly dependent on the method of
deposition, for example, in the case of spin coating onto topographically patterned surfaces. The
practice and theory of spin-coating onto flat substrates is well-established [94,95] and the methodology
is used practically to produce conventional photoresist thin films [96] and in more complex polymer
systems [97]. As described below, regular topographically patterned substrates have considerable
application for the selective alignment of polymer nanostructures in one azimuthal direction. However,
the effects of this surface topography on the morphology of polymer films by spin-coating have been
little explored. Recent theoretical work has suggested that substrate topography can have an important
effect, giving rise to capillary waves and ridges [98]. Theoretical modelling of a typical polymer thin
film formed by spin-coating solution across an isolated channel formed on a flat substrate surface is
shown in Figure 7 [99]. The edge of the channel gives rise to positive film excursions in the film
height at the channel wall and negative excursions in the polymer thickness within the film. Where a
number of channels are placed closely together, the result is a sinusoidal variation in film thickness
across the topography and this can be seen experimentally as shown in Figure 7B and 7C [99].
Because of the variation in thickness across the surface and the effect of thickness on feature
orientation in microphase separated thin films, this can have a profound effect on structure [99].
Careful consideration to these effects will need to be considered because such film morphologies will
make pattern transfer a difficult process.
Int. J. Mol. Sci. 2009, 10
3692
4. Alignment of Microphase Separated BCP Features
The microphase separation of BCPs produces regular structures but the size of the region where the
pattern formed displays high regularity is dependent on the thermodynamics and kinetics that describe
the phase separation process. Often the patterns have ‘domain’ like morphologies where each domain
maps a region where the phase separated microstructure has a well-defined arrangement that is highly
periodic. The neighbouring domains will have the same periodic microstructures but within each
domain alignment of features will be random. Domain sizes can range from tens of nm to micron
dimensions. Typical examples are given in Figure 8. The presence of grain boundary type structures
can arise for three main reasons. Firstly, during microphase separation, the ordered structure will
nucleate at many points and these ordered regions will grow until a grain boundary wall is formed.
Secondly, extrinsic defects such as substrate defects or impurities can precipitate domain structures.
Finally, there will be an equilibrium number of all types of defects governed by the thermodynamics
(as described below). For non-equilibrium structures (arising from defects and/or growth mechanisms)
the grains can be extended (coarsened) by annealing and defect annihilation. However, domain size
increase will occur only slowly and has been shown to follow a t0.25 power law [101] and for practical
purposes (i.e., extended process time) it is unlikely that thermal annealing could be used to generate a
single macroscopic sized domain. Further, the alignment of features would be random. For practical
use in electronics the feature alignment direction must be strictly controlled to allow subsequent
lithographic steps to define device and interconnect structures. Thus, in recent years, control of
alignment in these nanopatterns has been of pivotal importance.
4.1. Pattern Alignment Control
Several methods have been adapted to control feature alignment direction in thin films of these
systems. Here, alignment is defined relative to an azimuthal direction on the substrate. This alignment
control is often referred to as directed self-assembly and has been reviewed several times
[52,71,102,103]. The techniques used to effect alignment control of the microphase separated
structures include electric fields [104-106]. With careful design of the electrodes used to generate the
applied fields the films can show alignment areas of >1 cm2 [107]. Flow fields have also been widely
used and shear forces have been shown to preferentially align structures [108-110]. Long-range
alignment aided by a directional crystallisation process has also showed significant promise for this
application [111]. In this technique a molten crystalline organic material is used as the solvent for the
BCP and during processing the polymer microdomains align in the direction of growth of the organic
crystallites [112]. However, two techniques have become dominant because the methodology may be
transferable to industrial environments for generation of large area aligned nanopatterns. These are
chemical patterning and graphoepitaxy.
Int. J. Mol. Sci. 2009, 10
3693
Figure 8. Tapping mode AFM phase images (A, B and C) and SEM (D, following
selective etching to remove one block) showing typical microphase separated BCP
structures formed in 50 nm thick films at silicon substrates. A shows cylindrical
arrangement of PS-b-PEO with the PEO cylinders orientated perpendicular to the surface.
B is the same material with a parallel (to the substrate surface) arrangement of cylinders.
C is a polystyrene-b-polymethylmethacrylate (PS-b-PMMA) lamellar system and D is a
PS-b-PMMA cylinder forming system with a vertical alignment of PMMA cylinders
vertical to silicon substrate surface. In C and D a random PS-b-PMMA neutral brush layer
as described earlier was used to provide a neutral wetting layer. Grain boundaries between
areas of uniform alignment can be readily observed.
4.2. Chemical Patterning
Chemical patterning, as the name suggests, involves pre-patterning the substrate surface with
chemical functionality that selectively chemically interacts with one block. The microphase separated
structure will then tend to align to the pre-pattern. Provided that the feature size of the chemically
patterned substrate surface is matched to the feature size of the polymer pattern then the chemical
interactions between the blocks and the substrate can be such as to produce almost ideal pattern of
polymer. If the pattern dimensions are not matched then the surface will form defects to minimise the
chemical strain. The incommensurability of the BCP feature size and the pre-pattern has been explored
Int. J. Mol. Sci. 2009, 10
3694
[114] and evolution of unusual structures shown [115]. The laboratories of Russell and Nealey
pioneered this approach. Russell used a form of metal-metal oxide striped patterned substrates (formed
by oblique metal deposition onto grooved surfaces) to demonstrate the possibility for preferred
alignment control in PS-b-PMMA lamellar forming systems [116]. Nealey extended this work
significantly by developing chemical patterns based around various forms of lithography to generate
exceptionally well-ordered and aligned BCP microphase separated structures. Initially, extreme
ultraviolet interferometric lithography was used to pattern a self-assembled monolayer of
octadecyltrichlorosilane and other similar SAMs [117]. The radiation causes the formation of hydroxyl
and aldehyde linkages in the SAM modifying the chemical activity in the exposed region [118]. Using
x-ray interference lithography to chemically modify a PS-r-PMMA brush layer in a patterned manner,
the Nealey group were able to show almost defect free alignment of lamellar forming PS-b-PMMA
[119,120]. These lithographic approaches to chemical patterning show that the sort of feature size and
structure requirements for generation of future generations of electronic circuitry can be attained via
these bottom-up methodologies. However, since they are based around a pre-patterning method which
in itself needs advanced lithographies, the usefulness and practicality of these combined techniques
requires careful attention and already advances are being made. Cheng et al. used a technique known
as ‘sparse’ chemical patterning where the frequency of the chemical pattern is increased by subsequent
BCP patterning [120]. Ruiz et al. have also successfully used this type of method [121]; however an
important advance reported was the use of an e-beam to write the sparse patterns [12] and this makes a
significant contribution in simplifying the ease of processing these structures for potential delivery of a
manufacturable technology.
4.3. Graphoepitaxy for Patterning
The other method used to generate highly ordered BCP nanopatterns with controlled alignment is
graphoepitaxy where surface topography is used to direct the BCP structure. The term graphoepitaxy
was originally coined to describe how a substrate topographic periodicity can be used to control the
crystallographic alignment of thin films [122] and the technique evolved to become a popular method
for defining highly crystalline polymer films [123]. It is generally accepted that strain imposed by the
topography is the origin of the alignment effects, however, chemical interactions of the BCP with the
topography (as outlined below) also play an important role in influenceing the alignment process. The
advantage of graphoepitaxial techniques for BCP nanopattern development is that a single relatively
large substrate feature such as a channel can be used to direct the BCP nanopattern with precise
alignment into almost single crystal-like periodicity within the topographically defined feature.
Fasolka et al. were the first researchers to show that corrugated substrate surfaces could be used to
direct the development of microphase separated block copolymers [77]. These authors used a simple
off-cut silicon substrate to generate a saw-tooth topography and this was sufficient to generate regular
BCP periodicity. Segalman was the first author to demonstrate that designer topography (in this work
channels or rectangular cross-section separated by flat terraces or mesas and examples provided here
will refer only to this shape) could be used to generate aligned, to the edge of the channel, nanopatterns
of extremely high periodicity [124]. Segalaman’s ground-breaking work not only demonstrated the
possibility of this methodology for control of BCP structures but also reported the possibility of
Int. J. Mol. Sci. 2009, 10
3695
unusual edge effects due to varying film thickness as well as proposing a mechanism for alignment. It
was suggested that alignment occurs via nucleation at the channel walls and that, below a critical
channel width, a single domain structure could be formed.
Segalman’s original work was based around aligned sphere forming polystyrene-b-poly
(2-vinylpyridine) (PS-b-PVP) diblock copolymers. The work has progressed very quickly and reached
a high level of sophistication (see for example the review by Segalman [71]). Work reported to date
has demonstrated alignment of both horizontal and vertical orientations of cylinder forming systems
[52,56,126,127] and sphere forming [124,128,129] systems. One area of considerable importance has
been the development ‘sparse’ surface topographies which minimise the size of the topographical
features and considerably reduce the mesa contribution. Ross and co-workers have developed this
technique to align vertical cylinders or spheres so that a low density of ‘posts’ guide the structure
whilst being almost indistinguishable in terms of position, size and chemistry from a feature in the
BCP nanopatterns [130]. These sphere and vertical cylinder structures can be used to create column or
nanodot structures by pattern transfer or templating methods.
In terms of emerging electronic structures or interconnect arrangements, the formation of parallel
nanowires at a substrate has become an important challenge. So-called FIN-FET structures consisting
of several nanowires controlled through a single gate has become an important topic of research [131].
There has, therefore, been considerable work on the controlled alignment of lamellar (stripes
orientated vertically to surface plane, Figure 3B) and cylinder (parallel to surface plane, Figure 3D)
forming BCPs where coupling these techniques with templating and/or pattern transfer can transform
these structures into nanowire arrays. PS-b-PMMA is of particular interest because of the etch
characteristics of this system [132]. This has provided the motivation of much of Nealey’s work
outlined above in terms of chemical patterning. However, precise control of alignment using
graphoepitaxy is not as facile for these structures as for the vertical cylinder and sphere geometries.
Authors have ascribed the preferential alignment of topographical patterns due to e.g., the flow
forces developed as material is drawn from the substrate surface into channels and grooves [133],
however, it is now apparent that wetting phenomena at walls, grooves and wells dominate any such
process particularly at equilibrium [132,134]. For the lamellar stripe forming systems ensuring the
vertical alignment of lamellae requires surface neutralisation. However, application of the brush also
neutralises the walls and no preferred alignment of the blocks parallel to the channel wall occurs as
shown in Figure 9(A).
Figure 9. Lamellar (A) and hexagonal cylinder (B, C and D) forming arrangements of
PS-b-PMMA in topographically patterned substrates. See text for details.
Int. J. Mol. Sci. 2009, 10
3696
Various strategies for circumnavigating these problems have been suggested including side wall
modification [134] and using cylinder forming PS-b-PMMA at the base of the channel to form a
chemical pattern to guide the lamellar phase [135]. In a similar way, the cylinder forming systems also
require interface tailoring however, this is somewhat easier because of the ideal parallel orientation
and alignment is favoured by modifying both the base of a feature and the sidewalls to be selective to
the majority block. This is shown explicitly in Figure 9. In Figure 9B the hexagonal cylinder forming
PS-b-PMMA (PS as the major block) shows little alignment in channels created in silicon substrates.
However, by creating the channel structure in a siloxane surface (Figure 9C) and Si3N4 (Figure 9D) PS
wetting at the surface interfaces is favoured and alignment is improved.
Figure 10. 2D Tapping mode AFM phase images of PS-PI-PS thin films prepared from
0.7 wt% solutions of polymer in toluene on channel cut topographically defined substrates
(433 nm channels) after annealing at about 400 K for (a) 0 h, (b) 1 h, (c) 1½ h, (d) 2 h,
(e) 2½ h and (f) 3 h.
Int. J. Mol. Sci. 2009, 10
3697
It is also pointed out that forming parallel (to the surface plane) cylinder arrangements offers some
further challenges compared to vertical arrangements. Film thickness and transfer of polymer to the
channels can present a number of experimental difficulties. Suh et al. [76] studied orientation effects in
cylinder forming block copolymer films in detail and it is now generally accepted that vertical
orientation of the cylinders is favoured for very thin films because the parallel arrangement can only be
sustained with inclusion of elastic strain in the structure at low dimension (this strain effectively
reduces with thickness). This is important because only single layers of cylinders are required if the
pattern is to be used for creation of devices since multilayer structures can not be readily filled or
transferred to the substrate by etch methods. Some recent data (Figure 10, AFM tapping mode phase
images) show the importance of the relationship between film thickness and orientation in
topographical substrates. The cylinder forming PS-b-PI-b-PS system on Si(100) substrates has a strong
tendency to form parallel arrangements of cylinders because chemical interactions with both the
substrate and the surface interface strongly favour PS wetting layers [136]. If sufficient BCP is
spin-coated onto a channel cut surface to just fill channels (433 nm, 60 nm deep) so as to form a single
layer of PI cylinders (light lines) in a PS matrix the as coated surface (Figure 10A) is an isotropic
distribution of polymer across mesas and channels. Heating at about 400 K brings about phase
separation and transfer of material from the mesas into the channels. After 1 h the material has formed
a vertical cylinder arrangement in the channels (Figure 10B). Although the parallel arrangement is
favoured by interface effects, teh strain energy associated by not being able to form a complete layer of
cylinders leads to a vertical arrangement [76]. Further heating periods lead to more complete filling of
channels and eventual formation of a well ordered parallel arrangement of cylinders (Figure 10F). It is
important to note that alignment and orientation is nucleated at the channel edge (Figure 10C)
presumably because of polymer interactions with the side wall. The alignment also proceeds via a
disordered a structure as can be seen in Figure 10D and E. It is clear from these data that mass
transport and redistribution of polymer (towards an equilibrium distribution) requires careful study on
these topographic surfaces.
5. Defect Formation
In a self-assembled structure there are likely to be reasonable concentrations of defects. This is
suggested in Equation 1, ΔGSA = ΔHSA – TΔSSA, because in most cases the thermodynamic driving
force for self-assembly is provided by weak intermolecular interactions and is usually of the same
order of magnitude as the entropy term. Practically, for any self-assembling system to reach the
minimum free energy configuration there must be enough thermal energy to allow the mass transport
of the self-assembling moieties [1]. In these circumstances, obtaining defect free self-assembly over
macroscopic areas is improbable. A self-assembled nanopatterned surface is likely to show a number
of distinct irregularities or defects and these can take many forms as outlined below. The origins of
these defects are manifold but each defect comes with an energy cost because it disrupts the
arrangement of the polymer blocks which provides a free energy minimum within the film.
3698
Int. J. Mol. Sci. 2009, 10
5.1. Intrinsic Defects in Block Copolymer Nanopatterned Surfaces
An intrinsic defect in a thin film can be defined a defect that is formed within the film without
undue influence of the substrate. The formation of a perfect pattern is reliant on favourable
thermodynamic limitations and kinetics. At any temperature there will be an ‘equilibrium’
concentration of defects governed by a Bolzmann distribution. There will also be a ‘non-equilibrium’
(or kinetic) concentration of defects as pattern formation is reliant on material mass transport and this
may require process times beyond experimental limitations and defects may be ‘frozen’ in.
5.1.1. Equilibrium Defects
As above, the thermodynamically defined concentration of defects originates from a balance of
configurational entropy and the energy cost associated with the defect. These defects are ‘statistical’ in
nature and while individual defects may have limited lifetimes a population of them will always exist
at a concentration defined by conditions.
The thermodynamics of defects in fully equilibrated systems is well understood but care must be
taken to separate the free energy defining self-assembly and pattern formation from the free energy of
defect formation so that the role of intermolecular forces can be well understood. For defect formation
the free energy of single defect formation is given by
ΔGDF = ΔHDF – TΔSDF
(19)
The enthalpy term, ΔHDF, does not necessarily reflect the intermolecular forces between blocks—it
is the energy cost associated with disrupting the pattern and may be thought of as a region where
optimum arrangement does not occur and the reduction of enthalpy associated with ideal self-assembly
is not realised. For example, a system of hexagonally packed cylinders may exhibit defect regions of
lamellar structure. The enthalpy of defect formation is partially related to the enthalpic difference
between the two structural arrangements and this might be much less than the intermolecular forces
between blocks. If the difference in enthalpy of two different arrangements is small a relatively high
equilibrium concentration of defects might be expected compared to one where the enthalpy difference
is large. The entropy difference now reflects the order change between the prefect and defective
structural arrangement. Note here that the enthalpy cost of creating a defect is not only determined by
the respective differences in structural arrangement but also by strain energy (due to tensile and
compressive forces that are associated with defect insertion) as well as any interfacial effects arising
from intermolecular interactions in the areas around the defect . If ΔGDF is negative there will be a
finite number of defects in the system and the concentration will be given by
N/N0 = exp (-ΔEact/RT) [137]
(20)
N is the number of defects in a matrix of N0 self-assembled moieties or features and ΔEact is the
activation energy of defect formation. The activation energy ΔEact should not be confused with ΔHDF.
The activation energy represents energy difference between the initial ideally arranged state and a
transition state towards the defective structure.
3699
Int. J. Mol. Sci. 2009, 10
Figure 11. (A)–(C) Free energy of defect formation as a function of defect concentration
(as ratio of defects to total number of features) for three different activation energies for
defect formation. (D) Free energy of defect formation versus defect concentration at
various channel widths.
Equation 19 can be used to estimate the defect concentration by use of the Boltzmann formula to
estimate entropy S [137]
S = klnW
(21)
where W is the number of ways of arranging n defects over N possible features within a system of
periodic structure. W can be written
W = N!/((N-n )!n!)
(22)
and using Stirling’s approximation we can write that
ln N! ~ N ln N – N
(23)
so that
TΔSDF = kT[N ln N – n ln n – (N – n) ln (N-n)]
(24)
ΔGDF(n) = nΔHDF – kT[N ln N – n ln n – (N – n) ln (N-n)]
(25)
and
where ΔGDF(n) represents the free energy cost of forming n defects in the system. This formulism
allows a plot of free energy against n/N, the defect ratio, as shown in Figure 11. Three plots
(Figures 11A-C) are shown for defect formation energies of what might be expected for a BCP system
Int. J. Mol. Sci. 2009, 10
3700
e.g., Hammond et al. [138] have measured the defect formation energy in a PS-b-P2VP system at
around 30 kJ mol-1. Although these are simple calculations they illustrate the salient features of
equilibrium defect formation. At low defect concentrations defect formation is entropy driven until a
critical concentration of defects allows the activation energy term to compensate for entropy. There is
usually an equilibrium defect density indicated at the minimum free energy. As might be expected, as
the activation energy for defect formation increases this equilibrium defect density. At high activation
energy values (e.g., 30 kJ mol-1) and low temperature (300 K) there is no thermodynamic driving force
for defect formation and the data suggests that in BCP systems it should be possible to form highly
regular structures.
5.1.2. Non-Equilibrium Defects
Practically, there are few examples of defect free microphase separation of BCP thin film systems.
As these films are normally prepared by non-equilibrium methods such as spin- or dip-coating the
microphase separated structure evolves by either thermal or solvent annealing and defects are
introduced (nucleation of microphase separated regions) or removed by growth kinetics. Through the
annealing cycle phase separated regions will nucleate in various places, grow and increase in order
[138-141].
Due to the nature of the chemical interactions between blocks and the relatively high glass
transition temperatures coupled to low meting points and low order-disorder temperatures, the
temperature window for annealing out these non-equilibrium defects may be rather small and the
defects may be essentially kinetically stable). Extended heating times well-separated from the
order-disorder temperature may be required to remove defects and practically (because of local and
large area mass transport limitations) equilibrium may not be achieved even after inordinately long
annealing periods and non-equilibrium defects will be present. This is largely due to the requirement
for defect annihilation associated with coarsening of the randomly orientated grain structure that
results from the kinetics of nucleation and growth of phase separated regions [101]. Thus, although
ΔGDF may be positive for many BCP systems, implying no defects should be formed if the system
attains complete equilibrium, in practice this is unlikely. In many cases a clear distinction of
equilibrium defects and non-equilibrium defects can not be practically achieved. The advent of
advanced force microscopy methods facilitates defect studies without causing damage to the sample
[142-144]. Of particular importance are in situ AFM methods that allow real time data collection
during pattern evolution [144].
5.2. Extrinsic Defects in Block Copolymer Nanopatterned Surfaces
It is highly unlikely that a true minimum energy configuration of a BCP film on a flat substrate
(which may be a defect free arrangement) can be achieved in practice because of the effects outlined
above. However, if the pattern can be aligned to a substrate feature (through favourable chemical
interactions) then random grain orientations can be avoided and the requirement for defect annihilation
during grain coarsening can be removed and ideally ordered arrangements may be achieved.
Int. J. Mol. Sci. 2009, 10
3701
Graphoepitaxy and chemical patterning as described above offer a means of aligning patterns and thus
potentially provide a solution to problems associated with forming defect free films. It thus seems
necessary that these bottom-up techniques for patterned surface formation are combined with a
top-down lithographic method in order to achieve ideal arrangements. Chemical pre-patterning of
surfaces has shown great potential in this regard [119-121,145]. The main drawback of the chemical
patterning methodology is a requirement to pre-pattern on the same length scale as the phase separated
BCP feature size and this requires very advanced lithographic methods. One innovative approach to
the problem of developing and use of advanced lithography is to use the assembly of another block
copolymer film which can be readily aligned through favourable interactions with substrate features
(see below). This polymer film is then subsequently used to chemically pattern the BCP of interest.
This approach has been used with a cylinder forming PS-b-PMMA system to form a chemical pattern
for development of well-ordered lamellar forming PS-b-PMMA [135].
Low defect concentrations in BCP phase separated structures have been reported using
graphoepitaxial methods. As discussed above, in favourable circumstances the topographically
patterned surfaces align and orientate the phase separated BCP structure through interactions between
the surfaces and one or both blocks. These interactions force the BCP structure into registry and single
grain structures. There are many examples in the literature of graphoepitaxial defined single grain
structures [126-128,132,135,136,146-151]. Various authors report that the defect nature of these
directed structures are largely insensitive to the match between polymer feature spacing and channel
width (commensurability) except that as width increases there is a corresponding increase in the
number of polymer features within the topography. It is of course noted that the polymer structure will
exhibit strain (i.e., the spacing between features will stretch or compress) so as to fit an integer number
of features across the topography such that strain is minimised. As shown by Ross and co-workers
[128] the energy of the system will be minimum at the trench width at which commensurability occurs
(i.e., width = n polymer feature spacings, n = an integer) but will increase at higher or lower values.
The strain energy will be at a maximum when the trench width is equivalent to n + ½ polymer
feature spacings).
However, Nealey has noted that the defect concentration within the phase separated polymer
structure is highly dependent on the degree of commensurability with a strong correlation observed for
the cylinder forming PS-b-PMMA system. We observed similar effects in the cylinder forming
PS-b-PEO system as shown in Figure 12 and defect free single grain structures were a rarity except at
obviously commensurate trench widths (e.g., 390 and 560 nm). The difference between these studies
and other systems probably lies in the deformability of the polymer blocks. Analysis of the data in
figure 12 suggests a number of other points. Firstly, relatively small amounts of strain around narrower
trench widths can relatively easily precipitate defects and defect concentrations are relatively high. As
the width increases the defect concentration observed apparently decreases until at very high widths it
increases again. We explain these observations in the following manner. The BCP energy is dominated
by block-block and block-interface interactions so that filling of the topography and maximising the
number of features within the topography are the most important factors. When the channel width and
phase separated feature spacing is incommensurate, strain energy (highly dependent on the polymer
properties) results and an ideal pattern can only be achieved if this strain energy is less than the total
energy recoverable from changes in structure and defect formation. Thus, as width increases it
Int. J. Mol. Sci. 2009, 10
3702
becomes easier to maintain ideal single grain, defect free structures because the strain is distributed
over a larger polymer volume and so is proportionally less. At very large channel widths nucleation
can occur at both side walls leaving an area at centre where defects must form to allow volume fill.
Figure 12. SEM images of etched cylinder forming PS-b-PEO (PEO removed) in
rectangular trenches (60 nm depth and width as shown) of various widths. The white
circles show various defects present including grain boundaries, dislocations and point
defects. See text for further details.
If this description is correct there should be a minimum channel width where no equilibrium defects
should be observed since the introduction of strain energy would raise the total energy of the system
excessively. This can be modelled in the same way as described above except that the activation
energy for defect formation (a value of 16 kJ mol-1 was used) is effectively increased by an
incommensurate strain energy of 4 kJ mol-1. It was further assumed that this incommensurate strain
was dispersed over the volume of polymer in the channel. The results are shown in Figure 11(D) which
illustrates that even when defect formation is favourable, that there is a critical dimension when there
should be no equilibrium defects formed. Figure 13 provides experimental support for this model. In
the narrowest channel widths of 20 nm, there is an almost ideal arrangement of BCP structure.
Figure 13(C) provides clear evidence that the majority of defects observed in graphoepitaxy result
form the strain introduced by the channels. Here, a cylinder forming PS-b-PEO polymer was
spin-coated to create material at the channel mesas and within the channel. The BCP structure within
the channel is highly defective with the defect motifs seen above clearly visible. Also the expected
hexagonal pattern is not exhibited uniformly and an unexpected cubic arrangement is observed in
places as a result of the imposed strain. However, at the mesas, an almost ideal structure is seen. This
can be explained by the fact that any strain caused by incommensurity can be relived by a slight
expansion of the film.
Int. J. Mol. Sci. 2009, 10
3703
Figure 13. SEM images of etched cylinder forming PS-b-PEO (PEO removed) in
rectangular trenches (60 nm depth and widths of 175 (A), 120 (B) and 390 (C) nm).
Polymer was deposited to just fill channels in (A) and (B) but was overfileld in (C) to
allow phase separation at the mesas.
6. Concluding Remarks
The microphase separation of block copolymers shows a great deal of promise as a means of
generating regular nanopatterns at surfaces. They may, therefore, find application as a means to novel
nanomaterials and nanoelectronics device structures. The possible formation of these patterns is
thermodynamically determined by the strength of the chemical interactions which is balanced by
entropy considerations. Polymer composition determines the structural arrangement whilst molecular
weight and the physical properties determine the kinetics of the phase separation process. However, in
thin film form the chemical interactions between the blocks and their environment, i.e., the interfaces
that surround them, must also be carefully considered so that the microphase structure exhibits
controlled alignment and orientation. The use of surface engineering to control the chemical
interactions with the surface and chemical pre-patterning are strict needs if the requirements for
long-range order and periodicity are to be met. Like all self-assembly processes, defect chemistry is
important and these systems can exhibit a number of defects originating from thermodynamic and
kinetic limitations. However, recent work suggests that defect-free patterns over macroscopic
dimensions may be achievable.
Int. J. Mol. Sci. 2009, 10
3704
Acknowledgements
The authors would like to acknowledge SFI grant 03-IN3-I375 and the SFI CRANN CSET grant
which supported this work. The authors would like to thank Intel Ireland for provision and
development of patterned wafers under the Adaptive Grid Substrate CRANN programme. We would
also thank SFI though the National Access Programme at the Tyndall National Institute. Intel are also
thanked for electron microscopy. Several co-workers are also acknowledged; N Petkov, C O’ Mahony
S O’Driscoll and B Kosmala as contribution to the data presented here.
References
1.
2.
3.
4.
5.
6.
7.
8.
9.
10.
11.
12.
13.
14.
15.
16.
Whitesides, G.M.; Grzybowski, B. Self-assembly at all scales. Science 2002, 295, 2418-2421.
Whitesides, G.M.; Mathias, J.P.; Seto, C.T. Molecular self-assembly and nanochemistry: A
chemical strategy for the synthesis of nanostructures. Science 1991, 254, 1312-1319.
Murray, C.B.; Kagan, C.R.; Bawendi, M.G. Self-organization of CdSe nanocrystallites into
three-dimensional quantum dot superlattices. Science 1995, 270, 1335.
Schwarz, D.K. Mechanisms and kinetics of self-assembled monolayer formation. Annu. Rev.
Phys. Chem. 2001, 52, 107-137.
Svenson, S. Controlling surfactant self-assembly. Curr. Opin. Colloid Interface Sci. 2004, 9,
201-212.
Kresge, C.T.; Leonowicz, M.E.; Roth, W.J.; Vartuli, J.C.; Beck, J.S. Ordered mesoporous
molecular sieves synthesized by a liquid-crystal mechanism. Nature 1992, 359, 710-712.
Holmes, J.D.; Morris, M.A.; Ryan, K.M. Self Assembly—The Future, 1st ed.; Robinson, B.H.,
Ed.; Elsevier: Amsterdam, The Netherlands, 2003; Chapter 2, p. 175.
Misteli, T. The concept of self-organization in cellular architecture. J. Cell Biol. 2001, 155,
181-185.
Care, C.M.; Dalby, T. Packing entropy in micelle self-assembly. Europhys. Lett. 1999, 45, 38-42.
Yodh, A.G.; Lin, K.-H.; Crockery, J.C.; Dinsmorez, A.D.; Verma, R.; Kaplan, P.D. Entropically
driven self-assembly and interaction in suspension. Phil. Trans. R. Soc. Lond. A 2001, 359,
921-937.
Huie, J.C. Guided molecular self-assembly: A review of recent efforts. Smart Mater. Struct. 2003,
12, 264-271.
Neidle, S. Oxford Handbook of Nucleic Acid; Structure Oxford University Press: Oxford,
UK, 1999.
Ninham, B. Self Assembly; Robinson, B.H., Ed.; IOS Press: Amsterdam, The Netherlands, 2003;
p. 11.
Würthner, F. Perylene bisimide dyes as versatile building blocks for functional supramolecular
architectures. Chem. Commun. 2004, 14, 1574.
Olenyuk, B.; Whiteford, J.A.; Fechtenkotter, A.; Stang, P.J. Self-assembly of nanoscale
cuboctahedra by coordination chemistry. Nature 1990, 398, 796-799.
Lindgård, P.-A. Reflections on the protein-folding problem. J. Phys.: Condens. Matter 2003, 15,
S1779-S1786.
Int. J. Mol. Sci. 2009, 10
17.
18.
19.
20.
21.
22.
23.
24.
25.
26.
27.
28.
29.
30.
31.
32.
33.
34.
35.
36.
37.
3705
Israelachivili, J. Intermolecular and surface forces, 2nd ed; Academic Press: NY, USA, 1991;
pp. 1-130.
Leclère, Ph.; Surin, M.; Brocorens, P.; Cavallini, M.; Biscarini, F.; Lazzaroni, R. Supramolecular
assembly of conjugated polymers: From molecular engineering to solid-state properties. Mater.
Sci. Eng. R 2006, 55, 1-56.
D’Errico, G. Encyclopaedia of Surface and Colloid Science; Somasundaran, P., Ed.; CRC Press:
Boca Raton, FL, USA, 2006; pp. 3840-3848.
Ryan, K.M.; Coleman, N.R.B.; Lyons, D.M.; Morris, M.A.; Steytler, D.C.; Heenan, R.K.;
Holmes, J.D. Control of pore morphology in mesoporous silica synthesized from triblock
copolymer templates. Langmuir 2002, 18, 4996-5001.
Carraher, C.E., Jr. Introduction to Polymer Chemistry; CRC Press: New York, NY, USA, 2007.
Hamley, I.W. Developments in Block Copolymer Science and Technology; Wiley: Hoboken, NJ,
USA, 2004.
Lazzari, M.; Liu, G.; Lecommandoux, S. Block Copolymers in Nanoscience; Wiley-VCH.
Weinheim: Berlin, DE, Germany, 2006.
Kim, G.; Libera, M. Microstructural development in solvent-cast polystyrene-polybutadienepolystyrene (SBS) triblock copolymer thin films. Macromolecules 1998, 31, 2569-2577.
Burke, G.M.; Woscholski, R.; Yaliraki, S.N. Differential hydrophobicity drives self-assembly in
Huntington's disease. Proc. Nat. Acad. Sci. USA 2003, 100, 13928-13933.
Hildebrand, J.H. The Solubility of Non-Electrolytes; Reinhold Publishing Corporation: New York,
NY, USA, 1936.
Burke, J. Solubility parameters: Theory and application. AIC Book and Paper Group Annual
1984, 3, 13-58.
Barton, A.F.M. Handbook of Polymer-liquid Interaction Parameters and Solubility Parameters;
CRC Press: Boca Raton, FL, USA, 1990.
Hansen, C.M. The three dimensional solubility parameter key to paint component affinities: 1.
Solvents, plasticizers, polymers, and resins. J. Paint Technol. 1967, 39, 104-117.
Hansen, C.M. The universality of the solubility parameter concept. Ind. Eng. Chem. Prod. Res.
Dev.1969, 8, 2-11.
Bates, F.S. Polymer-polymer phase behaviour. Science 1991, 251, 898-905.
Flory, P.J. Thermodynamics of high polymer solutions. J. Chem. Phys. 1942, 10, 51-61.
Huggins, M.L. Theories of solutions of high polymers. J. Am. Chem. Soc. 1942, 74, 1712-1719.
Matsen, M.W.; Bates, F.S. Unifying weak- and strong-segregation block copolymer theories.
Macromolecules 1996, 28, 1091-1098.
Leibler, L. Theory of microphase separation in block copolymers. Macromolecules 1980, 13,
1602-1617.
Grason, G.M. The packing of soft materials: Molecular asymmetry, geometric frustration and
optimal lattices in block copolymer melts. Phys. Rep. 2006, 433, 1-64.
Khandpur, A.K.; Förster, S.; Bates, F.S.; Hamley, I.W.; Ryan, A.J.; Bras, W.; Almdal, K.;
Mortensen, K. A small-angle neutron scattering study of orientational order in the nematic phase
of a thermotropic liquid crystal. Macromolecules 1995, 28, 8796-8806.
Int. J. Mol. Sci. 2009, 10
38.
39.
40.
41.
42.
43.
44.
45.
46.
47.
48.
49.
50.
51.
52.
53.
54.
3706
Melenkevitz, J.; Muthukumar, M. Density functional theory of lamellar ordering in diblock
copolymers. Macromolecules 1991, 24, 4199-4205.
Bates, F.S.; Fredrickson, G.H. Block copolymers—Designer soft materials. Phys. Today 1998,
52, 32-38.
Grason, G.M. Continuous crystallization in hexagonally ordered materials. Phys. Rev. Letts.
2008, 101, 105702-105706.
Hajduk, D.A.; Takenouchi, H.; Hillmyer, M.A.; Bates, F.S.; Vigild, M.E.; Almdal, K. Stability of
the perforated layer (PL) phase in diblock copolymer melts. Macromolecules 1997, 30,
3788-3795.
Hamley, I.W.; Koppi, K.A.; Rosedale, J.H.; Bates, F.S.; Almdal, K.; Mortensen, K. Hexagonal
mesophases between lamellae and cylinders in a diblock copolymer melt. Macromolecules 1993,
26, 5959-5970.
Knoll, A.; Horvat, A.; Lyakhova, K.S.; Krausch, G.; Sevink, G.J.A.; Zvelindovsky, A.V.;
Magerle, R. Phase behavior in thin films of cylinder-forming block copolymers. Phys. Rev. Letts.
2002, 89, 035501-035505.
Castelletto, V.; Hamley, I.W. Morphologies of block copolymer melts. Current Opinion in Sol.
State Mater. Sci. 2004, 8, 426-438.
Rice, R.; Arnold, D.C.; Shaw, M.T.; Lacopina, I.; Quinn, A.J.; Amenitsch, H.; Holmes, J.D.;
Morris, M.A. Ordered mesoporous silicate structures as potential templates for nanowire growth.
Adv. Funct. Mater. 2007, 17, 133-141.
Petkov, N.; Platschek, B.; Morris, M.A.; Holmes, J.D.; Bein, T. Oriented growth of metal and
semiconductor nanostructures within aligned mesoporous channels. Chem. Mater. 2007, 19,
1376-1381.
Pileni, M.P. Nanocrystal self-assemblies: Fabrication and collective properties. J. Phys. Chem. B
2001, 105, 3358-3371.
Lodge, T.P. Block copolymers: Past successes and future challenges. Macromol. Chem. Phys.
2003, 204, 265-273.
Fasolka, M.; Mayes, A.M. Block copolymer thin films—Physics and applications. Ann. Rev.
Mater. Res. 2001, 31, 323-355.
Soo, P.P.; Huang, B.Y.; Jang, Y.I.; Chiang, Y.M.; Sadoway, D.R.; Mayes, A.M. Rubbery block
copolymer electrolytes. J. Electrochem. Soc. 1999, 146, 32-37.
Ulbricht, M. Advanced functional polymer membranes. Polymer 2006, 47, 2217-2262.
Park, C.; Yoon, J.; Thomas, E.L. Enabling nanotechnology with self assembled block copolymer
patterns. Polymer 2003, 44, 6725-6760.
Chen, V.Z.H.; Hoffman, J.; Lee, V.Y.; Latrou, H.; Avgeropoulus, A.; Hadjichristidis, N.; Miller,
R.D.; Thomas, E.L. Ordered bicontinuous nanoporous and nanorelief ceramic films from self
assembling polymer precursors. Science 1999, 286, 1716-1719.
Farrell, R.A.; Petkov, N.; Cherkaoui, K.; Hurley, P.; Amenitsch, H.; Holmes, J.D.; Morris, M.A.
Thin and continuous films with controlled bi- and tri-modal porosities by embedment of zeolite
nanoparticles in a mesoporous Matrix. J. Mat. Chem. 2008, 18, 2213-2220.
Int. J. Mol. Sci. 2009, 10
55.
56.
57.
58.
59.
60.
61.
62.
63.
64.
65.
66.
67.
68.
69.
70.
71.
72.
73.
3707
Farrell, R.A.; Cherkaoui, K.; Petkov, N.; Amenitsch, H.; Holmes, J.D.; Hurley, P.K.; Morris,
M.A. Physical and electrical properties of low dielectric constant self-assembled mesoporous
silica thin films. Microelectron. Reliab. 2007, 47, 759-763.
Cheng, J.Y.; Ross, C.A.; Chan, V.Z.H.; Thomas, E.L.; Robb, G.H.; Lammertink, R.G.H.; Vancso,
G.J. Formation of a cobalt magnetic dot array via block copolymer lithography. Adv. Mater.
2001, 13, 1174-1178.
Edrington, A.C.; Urbas, A.M.; DeRege, P.; Chen, C.X.; Swager, T.M.; Hadjichristidis, N.;
Xenidou, M.; Fetters, L.J.; Joannopoulos, J.D.; Fink, Y.; Thomas, E.L. Polymer-based photonic
crystals. Adv. Mater. 2001, 13, 421-425.
Pease, R.F.; Chou, S.Y. Lithography and other patterning techniques for future electronics. Pro.
IEEE 2008, 96, 248-270.
Del Campo, A.; Artz, E. Fabrication approaches for generating complex micro- and nanopatterns
on polymeric surfaces. Chem. Rev. 2008, 108, 911-945.
Bloomstein, T.M.; Marchant, M.F.; Deneault, S.; Hardy, D.E.; Rothschild, M. 22-NM immersion
interference lithography. Opt. Express 2006, 14, 6434-6443.
Davari, B.; Dennard, R.H.; Shahidi, G.G. CMOS scaling for high performance and low powerthe next ten years. Proc. IEEE 1995, 83, 595-606.
ITRS roadmap 2005 [Online]. Available: http://www.itrs.net/ (accessed August 7, 2009).
Whitesides, G.M.; Mathias, J.P.; Seto, C.T. Molecular self-assembly and nanochemistry—A
chemical strategy for the synthesis of nanostructures. Science 1991, 254, 1312-1319.
Hillenius, S.; Herr, D.; Weitzman, B.; Welser, J. SRC collaborations paving the way. IEEE
Nanotechnol. Mag. 2007, 1, 6-12.
Jeong, S.J.; Xia, G.; Kim, B.H.; Shin, D.O.; Kwon, S.H.; Kang, S.W.; Kim, O.S. Universal block
copolymer lithography for metals, semiconductors, ceramics, and polymers. Adv. Mater. 2008,
20, 1898-1904.
Yamaguchi, T.; Yamaguchi, H. Block copolymer lithography toward 16-nm-technology nodes
and beyond. NTT Tech. Rev. 2006, 4, 17-24.
Stoykovich, M.P.; Nealey, P.F. Block copolymers and conventional lithography. Mater.Today
2006, 9, 20-29.
Cheng, J.Y.; Sanders, D.P.; Kim, H.C.; Sundberg, L.K. Integration of polymer self-assembly for
lithographic application. Proc. SPIE 2008, 6921, 692127/1-692127/8.
Aizawa, M.; Buriak, J.M. Block copolymer templated chemistry for the formation of metallic
nanoparticle arrays on semiconductor surfaces. Chem. Mater. 2007, 19, 5090-5101.
Krishnamoorthy, S.; Hinderling, C.; Heinzelmann, H. Nanoscale patterning with block
copolymers. Mater. Today 2002, 9, 40-47.
Segalman, R.A. Patterning with block copolymer thin films. Mater. Sci. Eng. R 2005, 48,
191-226.
Qi, S.; Wang, Z.G. On the nature of the perforated layer phase in undiluted diblock copolymers.
Macromolecules 1997, 30, 4491-4497.
Knoll, A.; Lyakhova, K.S.; Horvat, A.; Krausch, G.; Sevink, G.J.A.; Zvelindovsky, A.V.;
Magerle, R. Direct imaging and mesoscale modelling of phase transitions in a nanostructured
fluid. Nat. Mater. 2004, 3, 886-891.
Int. J. Mol. Sci. 2009, 10
74.
75.
76.
77.
78.
79.
80.
81.
82.
83.
84.
85.
86.
87.
88.
89.
90.
91.
92.
3708
Seo, Y.A.; Kim, E.; Kwon, S.Y.; Jing, H.; Shin, K. AFM study of phase-separated morphology
in immiscible blend thin films. Ultramicroscopy 2008, 10, 1186-1190.
Green, P.F.; Limary, R. Block copolymer thin films: Pattern formation and phase behaviour.
Adv. Colloid Interface Sci. 2001, 94, 53-81.
Suh, J.Y.; Kim, Y.S.; Lee, H.H. Parallel and vertical morphologies in block copolymers of
cylindrical domains. J. Chem. Phys. 1998, 108, 1253-1256.
Fasolka, M.J.; Harris, D.J.; Mayes, A.M.; Yoon, M.; Mochrie, S.G.J. Observed substrate
topography-mediated lateral patterning of diblock copolymer films. Phys. Rev. Lett. 1997, 79,
3018-3021.
Sohn, B.H.; Yun, S.H. Perpendicular lamellae induced at the interface of neutral self-assembled
monolayers in thin diblock copolymer films. Polymer 2002, 43, 2507-2512.
Mansky, P.; Liu, Y.; Huang, E.; Russell, T.P.; Hawker, C.J. Controlling polymer-surface
interactions with random copolymer brushes. Science 1997, 275, 1458-1460.
In, I.; La, Y.H.; Park, S.M.; Nealey, P.F.; Gopalan, P. Side-chain-grafted random copolymer
brushes as neutral surfaces for controlling the orientation of block copolymer microdomains in
thin films. Langmuir 2006, 22, 7855-7860.
Sperling, L.H. Introduction to Physical Polymer Science, 4th ed.; Wiley: Hoboken, NJ, USA,
2006.
Schott, H. Swelling kinetics of polymers. J. Macromol. Sci. Part B 1992, 3, 1-9.
Fukunaga, K.; Elbs, H.; Magerle, R.; Krausch, G. Large-scale alignment of ABC block
copolymer microdomains via solvent vapor treatment. Macromolecules 2000, 33, 947-953.
Niu, S.J.; Saraf, R.F. Stability of order in solvent-annealed block copolymer thin films.
Macromolecules 2003, 36, 2428-2440.
Cavicchi, K.A.; Russell, T.P. Solvent annealed thin films of asymmetric polyisoprenepolylactide diblock copolymers. Macromolecules 2001, 40, 1181-1186.
Lin, Z.; Kim, D.H.; Wu, X.; Boosahda, L.; Stone, D.; LaRose, L.; Russell, T.P. A rapid route to
arrays of nanostructures in thin films. Adv. Mater. 2002, 14, 1373-1376.
Kim, S.H.; Misner, M.J.; Xu, T.; Kimura, M.; Russell, T.P. Highly oriented and ordered arrays
from block copolymers via solvent evaporation. Adv. Mater. 2004, 16, 226-231.
Gutierrez, M.H.; Ford, W.T. The glass-to-gel transition in solvent-swollen polystyrene networks.
J. Polym. Sci., Part B: Polym. Chem. 2003, 24, 655-663.
Hildebrand, J.H.; Scott, R.L. The Solubility of Nonelectrolytes, 3rd ed.; Reinhold Publishing
Corporation: New York, NY, USA, 1950.
Tassin, J.F.; Siemans, R.L.; Tang, W.T.; Hadziioannou, G.; Swalen, J.D.; Smith, B.A. Kinetics
of adsorption of block copolymers revealed by surface plasmons. J. Phys. Chem. 1989, 93,
2106-2111.
Cheng, F.; Yang, X.; Peng, H.; Chen, D.; Jing, M. Well-controlled formation of polymeric
micelles with a nanosized aqueous core and their applications as nanoreactors. Macromolecules
2007, 40, 8007-8014.
Fitzgerald, T.G.; Farrell, R.A.; O’Driscoll, S.; O’Mahony, C.T.; Holmes, J.D.; Morris, M.A.
Orientation and translational control of PS-b-PEO/PS thin films via solvent annealing and
graphoepitaxy techniques. e-J. Surf. Sci. Nanotech. 2009, 7, 741-745.
Int. J. Mol. Sci. 2009, 10
93.
3709
Scriven, L.E. Physics and applications of dip coating and spin coating. Mater. Res. Soc. Symp.
Proc. 1998, 121, 717-729.
94. Liquid Film Coating: Scientific Principles and Their Technological Implications, 1st ed.; Kistler,
S.F., Schweizer, P.M., Eds.; Chapman and Hall: London, UK, 1997.
95. Weill, A.; Francou, J.M.; Dechenaux, E. Photoresist spin coating mechanism related to polymer
solution rheology. Microelectron. Eng. 1987, 6, 427-431.
96. Yimsiria, P.; Mackley, M.R. Spin and dip coating of light-emitting polymer solutions: Matching
experiment with modelling. Chem. Eng. Sci. 2006, 61, 3496-3505.
97. Matar, O.K.; Sisoev, G.M.; Lawrence, C.J. Thin film flow over spinning discs: The effect of
surface topography and flow rate modulation. Chem. Eng. Sci. 2008, 63, 2225-2232.
98. Fitzgerald, T.G.; Farrell, R.A.; O'Driscoll, S.; O'Mahony, C.T.; Holmes, J.D.; Morris, M.A.
Orientation and translational control of PS-b-PEO/PS thin films via solvent annealing and
graphoepitaxy techniques. e-J. Surf. Sci. Nanotech. 2009, 7, 471-475.
99. Fitzgerald, T.G.; Farrell, R.A.; Petkov, N.; Shaw, M.T.; Charpin, J.; Gleeson, J.P.; Holmes, J.D.;
Morris, M.A. A study on the combined effects of solvent evaporation and polymer flow upon
block copolymer self-assembly and alignment on topographic patterns. Langmuir, in press.
100. Perlich, J.; Körstgens, V.; Metwalli, E.; Schulz, L.; Georgii, R.; Müller-Buschbaum, P. Solvent
content in thin spin-coated polystyrene homopolymer films. Macromolecules 2009, 42, 337-344.
101. Harrison, C.; Adamson, H.; Cheng, Z.; Sebastian, J.M.; Sethuraman, S.; Huse, D.A.; Register,
A.; Chaikin, P.M. Mechanisms of ordering in striped patterns. Science 2000, 290, 1558-1560.
102. Darling, S.B. Directing the self-assembly of block copolymers. Prog. Polym. Sci. 2007, 32,
1152-1204.
103. Kim, H.C.; Hinsberg, W.D. Surface patterns from block copolymer self-assembly. J. Vac. Sci.
Technol. A 2008, 26, 1369-1382.
104. Thurn-Albrecht, T.; DeRouchey, J.; Russell, T.P.; Kolb, R. Pathways toward electric field
induced alignment of block copolymers. Macromolecules 2002, 35, 8106-8110.
105. Amundsen, K.; Helfand, E.; Quan, X.N.; Hudson, S.D.; Smith, S.D. Alignment of lamellar block
copolymer microstructure in an electric field. 2. Mechanisms of alignment. Macromolecules
1994, 27, 6559-6570.
106. Morkved, T.L.; Lu, M.; Urbas, A.M.; Ehrichs, E.E.; Jaeger, H.M.; Mansky, P.; Russell, T.P.
Local control of microdomain orientation in diblock copolymer thin films with electric fields.
Science 1996, 273, 931-933.
107. Mansky, P.; DeRouchey, J.; Mays, J.; Pitsikalis, M.; Morkved, T.; Russell, T.P. Large-area
domain alignment in block copolymer thin films using electric fields. Macromolecules 1998, 31,
4399-4401.
108. Angelescu, D.E.; Waller, J.H.; Adamson, D.A.; Deshpandle, P.; Chou, S.Y.; Register, R.A.;
Chaikin, P.M. Macroscopic orientation of block copolymer cylinders in single-layer films by
shearing. Adv. Mater. 2004, 16, 1736-1740.
109. Kimura, M.; Misner, M.J.; Xu, T.; Kim, S.H.; Russell, T.P. Long-range ordering of diblock
copolymers induced by droplet pinning. Langmuir 2003, 19, 9910-9913.
110. Petermann, J.; Gohil, R.M. New method for the preparation of high modulus thermoplastic films.
J. Mater. Sci. 1979, 14, 2260-2264.
Int. J. Mol. Sci. 2009, 10
3710
111. Park, C.; Rosa, C.D.; Thomas, E.L. Large area orientation of block copolymer microdomains in
thin films via directional crystallization of a solvent. Macromolecules 2001, 34, 2602-2606.
112. Park, C.; Rosa, C.D.; Lotz, B.; Fetters, L.J.; Thomas, E.L. Molecular and microdomain
orientation in semicrystalline block copolymer thin films by directional crystallization of the
solvent and epitaxy. Macromol. Chem. Phys. 2003, 204, 1514-1523.
113. Kim, S.O.; Solak, H.H.; Stoykovich, M.P.; Ferrier, N.J.; de Pablo, J.J.; Nealey, P.F. Epitaxial
self-assembly of block copolymers on lithographically defined nanopatterned substrates. Nature
2003, 424, 411-414.
114. Chen, H.; Chakrabarti, J. Morphology of thin block copolymer films on chemically patterned
substrates. J. Chem. Phys. 1998, 108, 6897-6905.
115. Pereira, G.G.; Williams, D.R.M. Diblock copolymer thin film melts on striped, heterogeneous
surfaces: Parallel, perpendicular and mixed lamellar morphologies. Macromolecules 1999, 32,
758-764.
116. Rockford, I.; Liu, Y.; Mansky, P.; Russell, T.P.; Yoon, M.; Mochrie, S.G.J. Polymers on
nanoperiodic, heterogeneous surfaces. Phys. Rev. Lett. 1999, 82, 2602-2605.
117. Peters, R.D.; Yang, X.M.; Wang, Q.; de Pablo, J.J.; Nealey, P.F. Combining advanced
lithographic techniques and self-assembly of thin films of diblock copolymers to produce
templates for nanofabrication. J. Vac. Sci. Tech. B 2000, 18, 3530-3534.
118. Kim, T.K.; Yang, X.M.; Peters, R.D.; Sohn, B.H.; Nealey, P.F. Chemical modification of selfassembled monolayers by exposure to soft X-rays in air. J. Phys. Chem. B 2000, 104, 7403-7410.
119. Stoykovich, M.P.; Müller, M.; Kim, S.O.; Solak, H.H.; Edward, E.W.; de Pablo, J.J.; Nealey,
P.F. Directed assembly of block copolymer blends into nonregular device-oriented structures.
Science 2005, 308, 1442-1446.
120. Cheng, J.Y.; Rettner, C.T.; Sanders, D.P.; Kim, H.C.; Hinsberg, W.D. Dense self-assembly on
sparse chemical patterns: Rectifying and multiplying lithographic patterns using block
copolymers. Adv. Mater. 2008, 20, 3155-3158.
121. Ruiz, R.; Kang, H.; Detcheverry, F.A.; Dobisz, F.; Kercher, D.; Albrecht, T.R.; de Pablo, J.J.;
Nealey, P.F. Density multiplication and improved lithography by directed block copolymer
assembly. Science 2008, 321, 936-939.
122. Smith, H.I.; Flanders, D.C. Orientated crystal-growth on amorphous substrates using artificial
surface-relief gratings. Appl. Phys. Letts. 1978, 32, 349-350.
123. Whittmann, J.C.; Smith, P. Highly orientated thin-films of poly(tetrafluoroethylene) as a
substrate for orientated growth of materials. Nature 1991, 353, 414-417.
124. Segalman, R.A.; Yokoyama, H.; Kramer, E.J. Graphoepitaxy of spherical domain block
copolymer films. Adv. Mater. 2001, 13, 1152-1155.
125. Cheng, J.Y.; Ross, C.A.; Thomas, E.L.; Smith, H.I.; Vancso, G.J. Fabrication of nanostructures
with long-range order using block copolymer lithography. Appl. Phys. Lett. 2002, 81, 3657-3659.
126. Xiao, S.; Yang, X.M.; Edwards, E.W.; La, W.H.; Nealey, P.F. Graphoepitaxy of cylinderforming block copolymers for use as templates to pattern magnetic metal dot arrays.
Nanotechnology 2005, 16, S324-S329.
Int. J. Mol. Sci. 2009, 10
3711
127. Chen, F.; Akasaka, S.; Inoue, T.; Takenaka, M.; Hasegawa, H.; Yoshida, H. Ordering cylindrical
microdomains for binary blends of block copolymers with graphoepitaxy. Macromol. Rapid
Commun. 2007, 28, 2137-2144.
128. Cheng, J.Y.; Mayes, A.M.; Ross, C.A. Nanostructure engineering by templated self-assembly of
block copolymers. Nat. Mater. 2004, 3, 823-828.
129. Bosworth, J.K.; Paik, M.Y.; Ruiz, R.; Schwartz, E.L.; Huang, J.Q.; Ko, A.W.; Smilgies, D.M.;
Black, C.T.; Ober, C.K. Control of self-assembly of lithographically patternable block copolymer
films. ACS Nano 2008, 2, 1396-1402.
130. Bita, I.; Yang, J.K.W.; Jung, Y.S.; Ross, C.A.; Thomas, E.L.; Berggren, K.K Graphoepitaxy of
self-assembled block copolymers on two-dimensional periodic patterned templates. Science
2008, 321, 939-943.
131. Rudenko, T.; Kilchytska, V.; Collaert, N.; Nazarov, A.N.; Jurczak, M.; Flandre, D. Electrical
characterization and special properties of FINFET structures. In Nanoscaled Semiconductor-OnInsulator Structures and Devices, 1st ed.; Springer Verlag: Berlin, Germany, 2007.
132. Black, C.T.; Ruiz, Z.; Bretya, G.; Cheng, J.Y.; Colburn, M.E.; Guarini, K.W.; Kim, H.C.; Zhang,
Y. Polymer self assembly in semiconductor microelectronics. IBM J. Res. Dev. 2007, 51,
605-633.
133. Segalman, R.A.; Schaefer, K.E.; Fredrickson, G.H.; Kramer, E.J.; Mogonov, S. Topographic
templating of islands and holes in highly asymmetric block copolymer films. Macromolecules
2003, 36, 4498-4506.
134. Park, S.M.; Stoykovich, M.P.; Ruiz, R.; Zhang, Y.; Black, C.T.; Nealey, P.F. Directed assembly
of lamellae-forming block copolymers by using chemically and topographically patterned
substrates. Adv. Mater. 2007, 19, 607-611.
135. Ruiz, R.; Sandstrom, R.L.; Black, C.T. Induced orientational order in symmetric diblock
copolymer thin films. Adv. Mater. 2007, 19, 587-591.
136. Fitzgerald, T.G.; Borsetto, F.; O’Callaghan, J.M.; Kosmala, B.; Shaw, M.T.; Holmes, J.D.;
Morris, M.A. Polymer nanostructures in sub-micron lithographically defined channels: Filmthickness effects on structural alignment of a small feature size polystyrene-polyisoprenepolystyrene block copolymer. Soft Matter. 2007, 2, 916-921.
137. Scheel, H.J.; Fukuda, T. Crystal Growth Technology, 1st ed.; John Wiley & Sons, Inc.: London,
UK, 2003.
138. Hammond, M.R.; Cochran, E.; Fredrickson, G.H.; Kramer, E.J. Temperature dependence of
order, disorder, and defects in laterally confined diblock copolymer cylinder monolayers.
Macromolecules 2005, 38, 6575-6585.
139. Chastek, T.Q.; Lodge, T.P. Twinning and growth kinetics of lamellar grains in a diblock
copolymer solution. J. Polym. Sci., Part B: Polym. Phys. 2005, 44, 405-412.
140. Harrison, C.; Angelescu, D.E.; Trawick, M.; Zhengdong, C.; Huse, D.A.; Chaikin, P.M.; Vega,
D.A.; Sebastian, J.M.; Register, R.A.; Adamson, D.H. Pattern coarsening in a 2D hexagonal
system. Europhys. Lett. 2004, 67, 800-806.
141. Segalman, R.A.; Hexemer, A.; Kramer, E.J. Edge effects on the order and freezing of a 2D Array
of block copolymer spheres. Phys. Rev. Letts. 2003, 91, 196101/1-4.
Int. J. Mol. Sci. 2009, 10
3712
142. Hahm, J.; Lopes, W.A.; Jaeger, H.M.; Sibener, S.J. Defect evolution in ultrathin films of
polystyrene-block-polymethylmethacrylate diblock copolymers observed by atomic force
microscopy. J. Chem. Phys. 1998, 109, 10111-10114.
143. Hahm, J.; Sibener, S.J. Time-resolved atomic force microscopy imaging studies of asymmetric
PS-b-PMMA ultrathin films: Dislocation and disclination transformations, defect mobility, and
evolution of nanoscale morphology. J. Chem. Phys. 2001, 114, 4730-4740.
144. Tsarkova, L.; Horvat, A.; Krausch, G.; Zvelindovsky, A.V.; Sevink, G.J.A.; Magerle, R. Defect
evolution in block copolymer thin films via temporal phase transitions. Langmuir 2006, 22,
8089-8095.
145. Stoykovich, M.P.; Kang, H.; Daoulas, K.C.; Liu, G.; Liu, C.C.; de Pablo, J.J.; Müller, M.; Nealey,
P.F. Directed self-assembly of block copolymers for nanolithography: Fabrication of isolated
features and essential integrated circuit geometries. ACS Nano 2007, 1, 168-175.
146. Roerdink, M.; Hempenius, M.A.; Gunst, U.; Arlinghaus, H.F.; Vancso, G.J. Substrate wetting
and topographically induced ordering of amorphous PI-b-PFS block-copolymer domains. Small
2007, 3, 1415-1423.
147. Welander, A.M.; Nealey, P.F.; Cao, H.; Bristol, R. Impact of trench width roughness on the
graphoepitaxial assembly of block copolymers. J. Vac. Sci. Tech. B 2008, 26, 2484-2488.
148. Park, S.M.; Craig, G.S.W.; La, Y.K.; Nealey, P.F. Morphological reconstruction and ordering in
films of sphere-forming block copolymers on striped chemically patterned surfaces.
Macromolecules 2008, 41, 9124-9129.
149. Huck, W.T.S. Effects of nanoconfinement on the morphology and reactivity of organic materials.
Chem. Comm. 2005, 41, 4143-4148.
150. Black, C.T. Self-aligned self assembly of multi-nanowire silicon field effect transistors. Appl.
Phys. Lett. 2005, 87, 163116.
151. Ruiz, R.; Ruiz, N.; Sandstrom, R.L.; Black C.T. Local defectivity control of 2D self-assembled
block copolymer patterns. Adv. Mater. 2007, 19, 2157-2162.
© 2009 by the authors; licensee Molecular Diversity Preservation International, Basel, Switzerland.
This article is an open-access article distributed under the terms and conditions of the Creative
Commons Attribution license (http://creativecommons.org/licenses/by/3.0/).