The surface fluorination of polypropylene (PP) was performed using F2 and O2 gas mixtures with different F2 gas proportions at 25 °C and 13.3 kPa for 1 h. The surface roughness of the fluorinated PP samples was approximately 1.5 times higher than that of the untreated sample (5 nm). The Fourier-transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS) results showed that the PP-derived bonds (-C-C- and -CHx) decreased because they were converted into polar groups (-C–O, -CHF-, and -CFx), which increased the surface electronegativity of PP. The variation in the F2 gas proportion in the gas mixture significantly affected the hydrophilicity and surface composition of PP. At F2 gas proportions of <70%, the hydrophilicity of the fluorinated PP samples improved. Notably, the hydrophilic and negatively charged PP surface enhanced the dyeing of the polymer with basic methylene blue (MB). In contrast, at F2 gas proportions of >90%, the PP surface became hydrophobic owing to increased hydrophobic -CF3 bonds. Thus, enhanced PP dyeing can be controlled based on the composition of the F2 and O2 gas mixture.

Various colors of clothing originating from synthetic dyes are presently causing serious environmental pollution problems, whereas natural dyes extracted from natural indigo plants help reduce the harm to the environment and extend the sustainable use of clothing. This study focuses on the relation between indigo dyeing colors and the environment on the basis of sustainable design. The results reveal that light colors are considered to conform to the sustainable spirit more than dark colors in different indigo colors. In fact, the recyclable light-colored indigo dyeing t-shirt is beneficial in its reuse. Indigo dyeing fabric can be decomposed by a variety of microorganisms; however, the light-colored indigo dyeing takes a short time. Light colored indigo dyeing is more resource-saving when considering dye, water and electricity costs. The results of colors and environmental protection provide scheme references to consumers or industry for clothing collocation of different indigo dyeing colors for a series of blue clothing and carry out the ideal of the sustainability and co-existence between clothing and natural resources.

The art of dyeing textiles has a long history, as natural dyes have been used since prehis-toric times. With the development of synthetic dyes in the 19th century, the focus shifted from natural to synthetic dyes due to their superior properties. Recently, however, interest in natural dyes has increased again due to environmental and health concerns. Among industrial dyes, heterocyclic dyes, especially azo dyes, are of great importance due to their color brilliance and fastness. This review examines the synthesis, application and analysis of azo dyes, especially heterocyclic dyes. It deals with monoazo, diazo and polyazo dyes and highlights their structures, synthesis methods and fastness properties. In addition, the ecological impact of azo dyes and practical solutions for their synthesis and application are discussed.

The textile processing sector is accountable for the extensive utilisation and pollution of freshwater resources. Due to heightened consumer awareness of environmental legislation regarding freshwater contamination, the textile sector is compelled to review and improve their current water consumption practices. Foan dyeing technique is a highly promising alternative that has the ability to contribute to a more sustainable future. This review paper discussed the current state of foam dyeing technology, highlighting its advantages in terms of re-duced consumption of water and energy, as well as minimal usage of dyes and chemicals compared to conventional methods. The foam configuration allows for more effective application of dyes. As a result, there is a decrease in dye consumption and a reduction in processing time. The process is environmen-tally sustainable since it significantly reduces water pollution. Furthermore, foam dyeing method consumes less energy due to its lower dying temperature need compared to conventional processing technology. Additionally, this paper highlights the continued investigation of foam dyeing on many types of textile substrates (such as fibres, yarns, and fabric) and compositions including cotton, polyester, and their mixtures. In addition, the techno-economic comparison of foam dyeing and conventional dyeing is also given. This review paper addi-tionally endorses the Sustainable Development Goals (SDG 6, clean water and sanitation) by examining the preservation of usable water and the decrease in wastewater discharge through foam dyeing technology. Lastly, the potential advantages of foam dyeing in terms of significantly reducing water consump-tion and the generation of waste in the textile industry were also addressed.

The graphene based highly conductive and flexible devices has received momentous attraction and growth in recent years for potential multifunctional uses. The development of flexible and washable textile sensors, actuators, energy storage and energy harvesting systems. Textile fabrics coated with graphene and conductive polymers have been used for wearable self-powered e-textiles, such as tribo-electric, piezoelectric, and Thermoelectric. Herein this research, 100% woven cotton fabric is Fictionalized with graphene oxide (GO) using industrial-scale cold pad batch dyeing technique for the development of low-grade body heat into self-powered wearable e-textiles. The conductive polymer PEDOT: PSS was coated using layer by layer approach. The study demonstrates that the resultant textile electrodes showed reduced electrical sheet resistance from 2.5 MΩ to 15KΩ, with a reduced graphene oxide and further reduced to (2.5 -12.5 Ω) for conductive polymer. The sheet resistance was decreased with the number of dyeing cycles (10-15) and increased with 20 washing cycles vice versa. The study demonstrates that the sensor response and performance were improved with increasing the content percent of rGO and PEDOT: PSS. The tensile strength of as coated fabric electrodes was improved from (25.0-85.5 mPa) and fabric thickness was increased to (26-38µm) without compromising or influencing the air permeability. The resultant textile electrodes may potentially be used in smart textiles for self-powered flexible wearable generators, sensors, and energy storage. The study demonstrates that the cold pad batch dyeing method is a suitable and effective method for the fabrication of graphene-based textiles.

Cotton cationization with low molecular-weight/polymeric cationic modifiers allows the effective dyeing of fabrics with reactive dyes under salt-free and more environmentally-friendly conditions. The current work focuses on the spectroscopic study of the intermolecular interactions, which dictate the physicochemical process associated with dyeing. Water-soluble copolymers of vinyl benzyl chloride and vinyl benzyl triethylammonium chloride (VBCTEAM) have been used as cellulose cationic modifiers. Dye uptake was assessed using Remazol Brilliant Blue and Novacron Ruby dyes. The study involves ATR-FTIR, UV-Vis, fluorescence and XPS spectroscopy. The results of binary polymer-rich dye-polymer aqueous solutions or dye-polymer precipitates at stoichiometric charge-ratio revealed that the sulfonate/sulfate anions of the dyes interact with the cationic VBCTEAM units of the polymer via electrostatic interactions. Moreover, the comparative study of unmodified/modified dyed cotton indicates that the dye reactive sites remain unaffected for cationized cotton, suggesting that electrostatic interactions are the main driving force for the high dyeing performance observed.

Usually, the two-bath dyeing process using disperse dyes and reactive dyes separately was employed for the dyeing of PC blends. The cost of the double bath, dyeing cycle, energy consumption and chemical consumption is quite higher than the one-step or single bath dyeing methods. In this study, the one-bath dyeing process using one kind of dye was investigated. Polyester cotton blends dyed in one-bath one-step dyeing methods with disperse dye after surface modifications of cotton by acetylation methods were studied. Surface modification of cotton was carried out using fibrous acetylation methods. The effect of acetic anhydride and time on percent acetyl content at room temperature was studied. Modified polyester/cotton was carried out in HTHP dyeing machine incorporates with different dye concentrations and dyeing temperature. Surface chemistry, thermal decomposition property and moisture regain of modified polyester/ cotton blend are evaluated. The color strength of the dyed fabrics and their fastness properties to washing, light, and rubbing as well as tear strength and abrasion resistance were evaluated. The effect of dye concentration and temperature color strength, tensile strength warp and weft direction was assessed. The optimum value for surface modification was obtained with a concentration of acetylation agent 16% and time of reaction 2.5 hours, gave percent acetylation of 34. An FTIR spectrum shows acetylation resonance. The experiment result of dyeing showed that the optimum value was obtained with dye concentration above 1% at a temperature of 120oC, warp tensile strength decreased by 12% and weft tensile strength was decreased by 9% from the control half-bleached fabric. Results of this study showed that a one-step one-bath dyed modified polyester/cotton blend with disperse dye fabric presents good fastness property compared with conventional two-bath dyed fabric as well as colour strength values.

Natural dyes offer a bio-based opportunity to support attractive coloration to textile fabrics made from natural fibers like cotton, wool, hemp and many other materials. They can be part of a strategy to realize fully bio-based textile materials and clothing. Following this statement, the actual study investigates the use of wood extracts for dyeing of cotton fabrics. Actually extract powders of Logwood (Haematoxylon campechianum L.), Brazilwood (Caesalpinia spp.), and Quebracho wood (Schinopsis lorentzii) are used. The dyeing process is modified using different mordants based on iron and aluminum salts. These mordants are applied in pre-, meta- or post-mordant procedures. Color and fastness properties of prepared textile samples are determined by spectroscopic measurements, color measurements, washing procedures and Xenotest for measuring the light fastness. Finally, a broad range of different colorations can be realized by different combinations of wood extracts and mordanting procedures. A good wash fastness is reached for some color shades. For reaching good wash fastness, pre- and meta-mordanting procedures are more advantageous compared to post-mordanting. However, the light fastness of realized samples is only moderate to low. In conclusion, it can be stated that dyes from wood extracts are excellent materials to dye natural fibers if they are combined with the right mordanting agent in pre- or meta-mordanting procedures. The actual study is therefore a good proof-of-concept for the realization of fully bio-based colored textile materials.

Textile industry is one of the major industries responsible for environmental pollution globally. This is mainly due to the use of synthetic dyes, toxic ingredients and solvents for dy-ing/treatments/protocols of textiles. Replacement of those non ecofriendly ingredients would be a very challenging target to develop novel sustainable textile dying strategies. Using biobased and bioactive pigments, antibacterial ingredients and especially natural solvents are recently pointed out as substances to included in the related formulations. In this study the dyeing ability of the crude gel prodigiosin produced by non-pathogenic bacteria Serratia plymuthica as a natural pigment was investigated on various multifiber fabrics at different condition (temperature and pH) and by using salts (NaOH and Na2S2O4) and alternative mordants (a conventional: FeSO4 and a new bio-mordant: L-Cysteine (L-Cys)) in the recipes with different compositions and especially replacing of organic solvent with a new type of gel-based Choline chloride (ChCl) : Lactic acid (LA) (1 : 2) deep eutectic solvents (DES) as a dyeing medium. For determination of the dying process performances, the color strength (K/S value) of dyed fabric and the dyeing equalization (dE) parameters were evaluated. The fastness properties of the dyed fabrics which displayed as a higher K/S value and good dE were evaluated. The nylon fabrics dyed with 3.0% owf L-Cys at pH = 8.3 improved the color fastness to washing, while the gel-based ChCl : LA (1 : 2) DES dyebath provided a better color fastness to light. Moreover, the nylon fabrics under these conditions exhibited remarkable anti-microbial activity against Staphylococcus aureus (S. aureus) and Pseudomonas aeruginosa (P. aeruginosa). As conclusion, the use of the crude gel prodigiosin pigment revealed an advantageous ability to dye the textile materials, responding to consumers' demand for more ecological and sustainable products. Furthermore, the natural reducing agent L-Cys, never tested before as a bio-mordant, and the use of gel-based DES as a dyeing medium demonstrated enhanced colorimetric and antibacterial properties on dyed nylon with crude gel prodigiosin pigment.