304l stainless steel
Recently Published Documents

Purpose This paper aims to present the development and experimental study of a fully automated system using a novel laser additive manufacturing technology called laser foil printing (LFP), to fabricate metal parts layer by layer. The mechanical properties of parts fabricated with this novel system are compared with those of comparable methodologies to emphasize the suitability of this process. Design/methodology/approach Test specimens and parts with different geometries were fabricated from 304L stainless steel foil using an automated LFP system. The dimensions of the fabricated parts were measured, and the mechanical properties of the test specimens were characterized in terms of mechanical strength and elongation. Findings The properties of parts fabricated with the automated LFP system were compared with those of parts fabricated with the powder bed fusion additive manufacturing methods. The mechanical strength is higher than those of parts fabricated by the laser powder bed fusion and directed energy deposition technologies. Originality/value To the best knowledge of authors, this is the first time a fully automated LFP system has been developed and the properties of its fabricated parts were compared with other additive manufacturing methods for evaluation.

The present study investigates the electrochemical corrosion response and tribo-behavior of 304L and 316L stainless steel welded by gas metal arc welding (GMAW), which offered a high deposition rate. During this research, the metallurgically prepared welded samples were subjected to a tribological test and a corrosion test. The wear results were favorable for 316L steel, and it showed a lower coefficient of friction than the 304L specimen. These samples also underwent characterization studies, such as X-ray diffractometry (XRD) and scanning electron microscopy (SEM), to identify the different phases obtained on the cooling of the weld pool. Finally, both specimens were compared against their mechanical properties. Owing to the above properties, the 316L sample showed lasting durability, as compared to the 304L steel. The primary compositional difference is the higher presence of molybdenum and chromium in the 316L steel, compared to the 304L stainless steel.

This work aims to optimize the main YAG fiber laser parameters to weld 304L stainless steel plates of 3 mm thick. Different laser powers (2500, 2000, and 1500 W) and speeds (60, 40, and 20 mm/s) were used and merged in heat input, maintaining the defocusing distance at –2 mm to get full penetration. The weld quality and the effect of the laser heat input on the microstructures of the weld and heat-affected zones were investigated. Besides, the fracture strength of the welded joints and hardness distribution through the cross-sections were evaluated. The weld width has a direct relationship with heat input. The laser power of 2800 W produced full penetration joints without any macro defects while reduction in laser power pronounced partial penetration defects. The size of the heat-affected zone in all the processing parameters was very small. The microstructure of the weld zone shows columnar dendrite austenite grains with small arm spacing in most of the welded zone. The size of the dendrites became finer at lower heat input. At a higher heat input, a reasonable amount of lathy equiaxed grains with some delta ferrite occurred. A small amount of delta ferrite was detected in the heat-affected zone, which prevented the crack formation. The hardness of the weld metal was much higher than that of the base metal in all processing parameters and it has a reverse relationship with the heat input. The fracture strength of the welded joints was very close to that of the base metal in the defect-free samples and it increased with decreasing the heat input.

Crevice corrosion has become an important issue of the safety of AISI 304L austenitic stainless steel canister when exposed to the chloride environments located in coastal areas. Moreover, dust deposited on the canister surface may enhance the corrosion effect of 304L stainless steel. In this work, white emery was adopted to simulate the dust accumulated on the as-machined specimen surface. To investigate the effect of deposited white emery, chloride concentration, and relative humidity on the crevice corrosion behavior, an experiment was conducted on 304L stainless steel specimens at 45 °C with 45%, 55%, and 70% relative humidity (RH) for 7000 h. The surface features and crack morphology of the tested 304L stainless steel specimens were examined by SEM equipped with energy-dispersive spectrometry (EDS) and electron back scatter diffraction (EBSD). From the experimental results, a threshold RH for the stress corrosion cracking (SCC) initiation of AISI 304L austenitic stainless steel with different concentrations of chloride was proposed.