This document provides information on the material 30MnVS6, including its chemical composition, applications, processing details, and mechanical properties. Key points:
- It is a dispersion hardening ferritic-pearlitic cold heading steel used for parts requiring strengths from 800-1000 MPa without final heat treatment.
- The chemical composition includes 0.30% C, 0.65% Si, 1.50% Mn, and microalloying elements Cr, Ti, V, and N.
- It is hot formed between 1220-1280°C then gains strength from cold drawing and strain hardening operations without quenching or tempering.
- As rolled properties include a 0.2%
This document provides information on the material 30MnVS6, including its chemical composition, applications, processing details, and mechanical properties. Key points:
- It is a dispersion hardening ferritic-pearlitic cold heading steel used for parts requiring strengths from 800-1000 MPa without final heat treatment.
- The chemical composition includes 0.30% C, 0.65% Si, 1.50% Mn, and microalloying elements Cr, Ti, V, and N.
- It is hot formed between 1220-1280°C then gains strength from cold drawing and strain hardening operations without quenching or tempering.
- As rolled properties include a 0.2%
Original Description:
This gives the material specification used in producing Ball pins.
This document provides information on the material 30MnVS6, including its chemical composition, applications, processing details, and mechanical properties. Key points:
- It is a dispersion hardening ferritic-pearlitic cold heading steel used for parts requiring strengths from 800-1000 MPa without final heat treatment.
- The chemical composition includes 0.30% C, 0.65% Si, 1.50% Mn, and microalloying elements Cr, Ti, V, and N.
- It is hot formed between 1220-1280°C then gains strength from cold drawing and strain hardening operations without quenching or tempering.
- As rolled properties include a 0.2%
This document provides information on the material 30MnVS6, including its chemical composition, applications, processing details, and mechanical properties. Key points:
- It is a dispersion hardening ferritic-pearlitic cold heading steel used for parts requiring strengths from 800-1000 MPa without final heat treatment.
- The chemical composition includes 0.30% C, 0.65% Si, 1.50% Mn, and microalloying elements Cr, Ti, V, and N.
- It is hot formed between 1220-1280°C then gains strength from cold drawing and strain hardening operations without quenching or tempering.
- As rolled properties include a 0.2%
Saarstahl - 30MnVS6 (27MnSiVS6) - Saarform 900 Material No.:
1.1302 (1.5232)
German standard:
DIN EN 10267
International steel grades:
BS: AFNOR: SAE: Material group: Dispersion hardening ferritic-pearlitic cold heading steel C Si Mn P S Cr Ti V N Chemical composition: (typical analysis at Saarstahl in %) 0,30 0,65 1,50 <0,020 <0,025 0,15 0,02 0,12 0,015
Deviation in chemical composition on request Application: Micro-alloyed ferritic-pearlitic cold heading steel owing its properties to temperature-controlled rolling and the addition of micro-alloying elements. The mechanical properties required in the finished part are obtained by a specifically matched combination of as-rolled strength and the strain hardening effects of the drawing reduction and the strain-hardening operation. Use for short and long-shaft ball points, threaded and heavy duty an- chor bolts of strength class 800 to 1000 MPa without final quenching and tempering after cold forging. Hot forming and heat treatment: Furnace temperature before hot forming:
1220 - 1280C
Mechanical properties: As rolled
Diameter d [mm] 5 - 30 0,2% proof stress Rp0,2 [N/mm] about 500 Tensile strength Rm [N/mm] 720 - 820 Fracture elongation A5 [%] 20 Reduction of area Z [%] 50 Microstructure: about 50 % ferrite, balance pearlite