    Aluminium 2014 t6 2014 t651

    Uploaded by

    Agung Sapto Aji
    This document provides information on the aluminum alloy 2014-T6/T651, including its typical composition, physical and mechanical properties, thermal properties, and processing details. The alloy contains aluminum (90.4-95 wt%), copper (3.9-5 wt%), magnesium (0.8 wt%), and silicon (0.5-1.2 wt%) as its major components. It has a density of 2.8 g/cc, ultimate tensile strength of 483 MPa, hardness of 155 HV, and melting point range of 507-638°C. The alloy is heat treated with annealing at 413°C, solutionizing at 502°C, and aging at either 160°C or 171°C

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Aluminium 2014 t6 2014 t651

    Uploaded by

    Agung Sapto Aji
    321 views3 pages
    This document provides information on the aluminum alloy 2014-T6/T651, including its typical composition, physical and mechanical properties, thermal properties, and processing details. The alloy contains aluminum (90.4-95 wt%), copper (3.9-5 wt%), magnesium (0.8 wt%), and silicon (0.5-1.2 wt%) as its major components. It has a density of 2.8 g/cc, ultimate tensile strength of 483 MPa, hardness of 155 HV, and melting point range of 507-638°C. The alloy is heat treated with annealing at 413°C, solutionizing at 502°C, and aging at either 160°C or 171°C

    Original Description:

    Metalurgi

    Original Title

    aluminium-2014-t6-2014-t651

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This document provides information on the aluminum alloy 2014-T6/T651, including its typical composition, physical and mechanical properties, thermal properties, and processing details. The alloy contains aluminum (90.4-95 wt%), copper (3.9-5 wt%), magnesium (0.8 wt%), and silicon (0.5-1.2 wt%) as its major components. It has a density of 2.8 g/cc, ultimate tensile strength of 483 MPa, hardness of 155 HV, and melting point range of 507-638°C. The alloy is heat treated with annealing at 413°C, solutionizing at 502°C, and aging at either 160°C or 171°C

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    321 views3 pages

    Aluminium 2014 t6 2014 t651

    Uploaded by

    Agung Sapto Aji
    This document provides information on the aluminum alloy 2014-T6/T651, including its typical composition, physical and mechanical properties, thermal properties, and processing details. The alloy contains aluminum (90.4-95 wt%), copper (3.9-5 wt%), magnesium (0.8 wt%), and silicon (0.5-1.2 wt%) as its major components. It has a density of 2.8 g/cc, ultimate tensile strength of 483 MPa, hardness of 155 HV, and melting point range of 507-638°C. The alloy is heat treated with annealing at 413°C, solutionizing at 502°C, and aging at either 160°C or 171°C

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 3

    Aluminum 2014-T6; 2014-T651

    Subcategory: 2000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal
    Close Analogs: none
    Composition Notes: A Zr + Ti limit of 0.20 percent maximum may be used with this alloy designation for
    extruded and forged products only, but only when the supplier or producer and the purchaser have
    mutually so agreed. Agreement may be indicated, for example, by reference to a standard, by letter, by
    order note, or other means which allow the Zr + Ti limit.
    Aluminum content reported is calculated as remainder.
    Composition information provided by the Aluminum Association and is not for design.
    Key Words: Aluminium 2014-T651; UNS A92014; ISO AlCu4SiMg; BS H15 (UK); CSA CS41N (Canada);
    AA2014-T651, DIN AlCuSiMn; NF A-U4SG (France)
    Component

    Wt. %

    Al

    90.4 - 95

    Cr

    Max 0.1

    Cu

    3.9 - 5

    Fe

    Max 0.7

    Wt.
    %
    0.2 Mg
    0.8
    0.4 Mn
    1.2
    Max
    Other, each
    0.05
    Max
    Other, total
    0.15

    Component

    Component
    Si
    Ti
    Zn

    Wt.
    %
    0.5 1.2
    Max
    0.15
    Max
    0.25

    Material Notes: Data points with the AA note have been provided by the Aluminum Association, Inc. and
    are NOT FOR DESIGN
    Physical Properties
    Density
    Mechanical Properties

    Metric
    2.8 g/cc
    Metric

    English
    0.101 lb/in
    English

    Comments
    AA; Typical
    Comments

    Hardness, Brinell

    135

    135

    AA; Typical; 500 g


    load; 10 mm ball

    Hardness, Knoop

    170

    170

    Hardness, Rockwell A

    50,50

    50,50

    Hardness, Rockwell B

    82

    82

    Hardness, Vickers

    155

    155

    Ultimate Tensile Strength

    483 MPa

    70000 psi

    CRP MECCANICA S.r.l.


    Sede Legale e Amministrativa/Headquarters and Administration Office
    Via Cesare Della Chiesa 21 - 41126 Modena
    Tel./Phone +39-059-330544/821135/826025
    Fax +39-059-822071/381148
    C.F./ P.IVA/Registro Imprese Modena IT00782680367 (VAT number)
    Capitale sociale Euro 564.000 i. v.

    Converted from
    Brinell Hardness
    Value
    Converted from
    Rockwell B
    Converted from
    Brinell Hardness
    Value
    AA; Typical

    Tensile Yield Strength

    414 MPa

    60000 psi

    Elongation at Break

    13 %

    13 %

    Modulus of Elasticity

    72.4 GPa

    10500 ksi

    Modulus of Elasticity

    73.1 GPa

    10600 ksi

    Compressive Strength
    Compressive Modulus

    470 MPa
    73.8 GPa

    68200 psi
    10700 ksi

    Notched Tensile Strength

    414 MPa

    60000 psi

    Ultimate Bearing Strength

    889 MPa

    129000 psi

    Bearing Yield Strength

    662 MPa

    96000 psi

    Poisson's Ratio

    0.33

    0.33

    Fatigue Strength

    124 MPa

    18000 psi

    Fracture Toughness

    19 MPa-m

    17.3 ksi-in

    Machinability

    70 %

    70 %

    Shear Modulus
    Shear Strength
    Electrical Properties

    28 GPa
    290 MPa
    Metric

    4060 ksi
    42000 psi
    English

    Electrical Resistivity

    4.32e-006 ohm-cm 4.32e-006 ohm-cm

    AA; Typical
    AA; Typical; 1/2 in.
    (12.7 mm) Diameter
    In Tension
    AA; Typical; Average
    of tension and
    compression.
    Compression modulus
    is about 2% greater
    than tensile modulus.

    2.5 cm width x 0.16


    cm thick side-notched
    specimen, Kt = 17.
    Edge distance/pin
    diameter = 2.0
    Edge distance/pin
    diameter = 2.0
    AA; 500,000,000
    cycles completely
    reversed stress; RR
    Moore
    machine/specimen
    KIC; TL orientation.
    0-100 Scale of
    Aluminum Alloys
    AA; Typical
    Comments
    AA; Typical at 68F

    Thermal Properties

    Metric

    English

    Comments

    CTE, linear 68F

    23 m/m-C

    12.8 in/in-F

    AA; Typical; Average


    over 68-212F range.

    CTE, linear 250C

    24.4 m/m-C

    Specific Heat Capacity

    0.88 J/g-C

    Thermal Conductivity

    154 W/m-K

    Average over the


    range 20-300C
    Estimated from
    0.21 BTU/lb-F
    trends in similar Al
    alloys.
    1070 BTU-in/hr-ft-F AA; Typical at 77F
    13.6 in/in-F

    CRP MECCANICA S.r.l.


    Sede Legale e Amministrativa/Headquarters and Administration Office
    Via Cesare Della Chiesa 21 - 41126 Modena
    Tel./Phone +39-059-330544/821135/826025
    Fax +39-059-822071/381148
    C.F./ P.IVA/Registro Imprese Modena IT00782680367 (VAT number)
    Capitale sociale Euro 564.000 i. v.

    Melting Point

    507 - 638 C

    945 - 1180 F

    Solidus
    Liquidus
    Processing Properties

    507 C
    638 C
    Metric

    945 F
    1180 F
    English

    Annealing Temperature

    413 C

    775 F

    Solution Temperature

    502 C

    935 F

    Aging Temperature

    160 C

    320 F

    Aging Temperature

    171 C

    340 F

    References are available for this material.


    Source: MatWeb, The Online Materials Database

    CRP MECCANICA S.r.l.


    Sede Legale e Amministrativa/Headquarters and Administration Office
    Via Cesare Della Chiesa 21 - 41126 Modena
    Tel./Phone +39-059-330544/821135/826025
    Fax +39-059-822071/381148
    C.F./ P.IVA/Registro Imprese Modena IT00782680367 (VAT number)
    Capitale sociale Euro 564.000 i. v.

    AA; Typical range


    based on typical
    composition for
    wrought products 1/4
    inch thickness or
    greater. Eutectic
    melting is not
    eliminated by
    homogenization.
    AA; Typical
    AA; Typical
    Comments

    Sheet, plate, wire,


    rod, bar, shapes,
    tube; 18 hr at
    temperature
    Forgings; 10 hr at
    temperature