Weldability of Materials

Download as docx, pdf, or txt
Download as docx, pdf, or txt
You are on page 1of 5
At a glance
Powered by AI
The passage discusses various types of materials that can be welded and focuses on the weldability of carbon-manganese steels and low alloy steels. It describes different types of imperfections that can occur during welding and factors that influence the risk of these imperfections.

The main types of imperfections that can occur in welds are porosity, solidification cracking, hydrogen cracking, and reheat cracking. Other imperfections like lamellar tearing and liquation cracking are less common with modern steels and consumables.

The risk of porosity occurring in welds is influenced by factors like poor gas shielding, surface contamination, insufficient deoxidants in the parent metal or consumables, and the oxygen content of rimming steels. Thorough cleaning of the joint area and protection of the arc from draughts can reduce porosity.

Weldability of materials

Job Knowledge 19
In arc welding, as the weld metal needs mechanical properties to match the parent metal, the
welder must avoid forming defects in the weld. Imperfections are principally caused by:

poor welder technique;

insufficient measures to accommodate the material or welding process;

high stress in the component.


Techniques to avoid imperfections such as lack of fusion and slag inclusions, which result from
poor welder techniques, are relatively well known. However, the welder should be aware that the
material itself may be susceptible to formation of imperfections caused by the welding process.
In the materials section of the Job Knowledge for Welders, guidelines are given on material
weldability and precautions to be taken to avoid defects.

Material types
In terms of weldability, commonly used materials can be divided into the following types:

Steels

Stainless steels

Aluminium and its alloys

Nickel and its alloys

Copper and its alloys

Titanium and its alloys

Cast iron
Fusion welding processes can be used to weld most alloys of these materials, in a wide range of
thickness. When imperfections are formed, they will be located in either the weld metal or the
parent material immediately adjacent to the weld, called the heat affected zone (HAZ). As
chemical composition of the weld metal determines the risk of imperfections, the choice of filler
metal may be crucial not only in achieving adequate mechanical properties and corrosion
resistance but also in producing a sound weld. However, HAZ imperfections are caused by the
adverse effect of the heat generated during welding and can only be avoided by strict adherence
to the welding procedure.
This part of the materials section of Job Knowledge for Welders considers the weldability of
carbon-manganese (C-Mn) steels and low alloy steels.

Imperfections in welds
Commonly used steels are considered to be readily welded. However, these materials can be at
risk from the following types of imperfection:


porosity;

solidification cracking;

hydrogen cracking;

reheat cracking.
Other fabrication imperfections are lamellar tearing and liquation cracking but using modern
steels and consumables, these types of defects are less likely to arise.
In discussing the main causes of imperfections, guidance is given on procedure and welder
techniques for reducing the risk in arc welding.

Porosity
Porosity is formed by entrapment of discrete pockets of gas in the solidifying weld pool. The gas
may originate from poor gas shielding, surface contaminants such as rust or grease, or
insufficient deoxidants in the parent metal (autogenous weld), electrode or filler wire. A
particularly severe form of porosity is 'wormholes', caused by gross surface contamination or
welding with damp electrodes.
The presence of manganese and silicon in the parent metal, electrode and filler wire is beneficial
as they act as deoxidants combining with entrapped air in the weld pool to form slag. Rimming
steels with a high oxygen content, can only be welded satisfactorily with a consumable which
adds aluminium to the weld pool.
To obtain sound porosity-free welds, the joint area should be cleaned and degreased before
welding. Primer coatings should be removed unless considered suitable for welding by that
particular process and procedure. When using gas shielded processes, the material surface
demands more rigorous cleaning, such as by degreasing, grinding or machining, followed by final
degreasing, and the arc must be protected from draughts.

Solidification cracking
Solidification cracks occur longitudinally as a result of the weld bead having insufficient strength
to withstand the contraction stresses within the weld metal. Sulphur, phosphorus, and carbon
pick up from the parent metal at high dilution increase the risk of weld metal (solidification)
cracking especially in thick section and highly restrained joints. When welding high carbon and
sulphur content steels, thin weld beads will be more susceptible to solidification cracking.
However, a weld with a large depth to width ratio can also be susceptible. In this case, the
centre of the weld, the last part to solidify, will have a high concentration of impurities increasing
the risk of cracking.
Solidification cracking is best avoided by careful attention to the choice of consumable, welding
parameters and welder technique. To minimise the risk, consumables with low carbon and
impurity levels and relatively high manganese and silicon contents are preferred. High current
density processes such as submerged-arc and CO 2 , are more likely to induce cracking. The
welding parameters must produce an adequate depth to width ratio in butt welds, or throat
thickness in fillet welds. High welding speeds also increase the risk as the amount of segregation
and weld stresses will increase. The welder should ensure that there is a good joint fit-up so as
to avoid bridging wide gaps. Surface contaminants, such as cutting oils, should be removed
before welding.

Hydrogen cracking
A characteristic feature of high carbon and low alloy steels is that the HAZ immediately adjacent
to the weld hardens on welding with an attendant risk of cold (hydrogen) cracking. Although the
risk of cracking is determined by the level of hydrogen produced by the welding process,
susceptibility will also depend upon several contributory factors:


material composition (carbon equivalent);

section thickness;

arc energy (heat) input;

degree of restraint.
The amount of hydrogen generated is determined by the electrode type and the process. Basic
electrodes generate less hydrogen than rutile electrodes (MMA) and the gas shielded processes
(MIG and TIG) produce only a small amount of hydrogen in the weld pool. Steel composition and
cooling rate determines the HAZ hardness. Chemical composition determines material
hardenability, and the higher the carbon and alloy content of the material, the greater the HAZ
hardness. Section thickness and arc energy influences the cooling rate and hence, the hardness
of the HAZ.
For a given situation therefore, material composition, thickness, joint type, electrode
composition and arc energy input, HAZ cracking is prevented by heating the material. Using
preheat which reduces the cooling rate, promotes escape of hydrogen and reduces HAZ hardness
so preventing a crack-sensitive structure being formed; the recommended levels of preheat for
various practical situations are detailed in the appropriate standards e.g. BS EN1011-2:2001. As
cracking only occurs at temperatures slightly above ambient, maintaining the temperature of the
weld area above the recommended level during fabrication is especially important. If the
material is allowed to cool too quickly, cracking can occur up to several hours after welding,
often termed 'delayed hydrogen cracking'. After welding, therefore, it is beneficial to maintain
the heating for a given period (hold time), depending on the steel thickness, to enable the
hydrogen to diffuse from the weld area.
When welding C-Mn structural and pressure vessel steels, the measures which are taken to
prevent HAZ cracking will also be adequate to avoid hydrogen cracking in the weld metal.
However, with increasing alloying of the weld metal e.g. when welding alloyed or quenched and
tempered steels, more stringent precautions may be necessary.
The risk of HAZ cracking is reduced by using a low hydrogen process, low hydrogen electrodes
and high arc energy, and by reducing the level of restraint. Practical precautions to avoid
hydrogen cracking include drying the electrodes and cleaning the joint faces. When using a gas
shielded process, a significant amount of hydrogen can be generated from contaminants on the
surface of the components and filler wire so preheat and arc energy requirements should be
maintained even for tack welds.

Reheat cracking
Reheat or stress relaxation cracking may occur in the HAZ of thick section components, usually
of greater than 50mm thickness. The more likely cause of cracking is embrittlement of the HAZ
during high temperature service or stress relief heat treatment.
As a coarse grained HAZ is more susceptible to cracking, low arc energy input welding
procedures reduce the risk. Although reheat cracking occurs in sensitive materials, avoidance of
high stresses during welding and elimination of local points of stress concentration, e.g. by
dressing the weld toes, can reduce the risk.

Weldability of steel groups


PD CEN ISO/TR 15608:2005 identifies a number of steels groups which have similar
metallurgical and welding characteristics. The main risks in welding these groups are:
Group 1. Low carbon unalloyed steels, no specific processing requirements, specified
minimum yield strength R eH 460N/mm 2 .

For thin section, unalloyed materials, these are normally readily weldable. However, when
welding thicker sections with a flux process, there is a risk of HAZ hydrogen cracking, which will
need increased hydrogen control of the consumables or the use of preheat.
Group 2. Thermomechanically treated fine grain steels and cast steels with a specified
miniumum yield strength R eH > 360N/mm 2 .
For a given strength level, a thermomechanically processed ( TMCP) steel will have a lower alloy
content than a normalised steel, and thus will be more readily weldable with regard to avoidance
of HAZ hydrogen cracking and the achievement of maximum hardness limits. However, there is
always some degree of softening in the HAZ after welding TMCP steels, and a restriction on the
heat input used, so as not to degrade the properties of the joint zone (e.g. 2.5kJ/mm limits for
15mm plate).
Group 3. Quenched and tempered steels and precipitation hardened steels (except
stainless steels), ReH>360N/mm2
These are weldable, but care must be taken to adhere to established procedures, as these often
have high carbon contents, and thus high hardenability, leading to a hard HAZ susceptibility to
cracking. As with TMCP steels, there maybe a restriction on heat input or preheat to avoid
degradation of the steel properties.
Groups 4, 5 and 6. Chromium-molybdenum and chromium-molybdenum-vanadium
creep resisting steels.
These are susceptible to hydrogen cracking, but with appropriate preheat and low hydrogen
consumables, with temper bead techniques to minimise cracking, the steels are fairly weldable.
Postweld heat treatment is used to improve HAZ toughness in these steels.
Group 7. Ferritic, martensitic or precipitation hardened stainless steels.
When using a filler to produce matching weld metal strength, preheat is needed to avoid HAZ
cracking. Postweld heat treatment is essential to restore HAZ toughness.
Group 8. Austenitic stainless steels.
These steels do not generally need preheat, but in order to avoid problems with solidification or
liquation cracking upon welding, the consumables should be selected to give weld metal with a
low impurity content, or if appropriate, residual ferrite in the weld metal.
Group 9. Nickel alloy steels, Ni10%.
These have a similar weldability to Groups 4, 5 & 6.
Group 10. Austenitic ferritic stainless steels (duplex).
In welding these steels, maintaining phase balance in the weld metal and in the HAZ requires
careful selection of consumables, the absence of preheat and control of maximum interpass
temperature, along with minimum heat input levels, as slow cooling encourages austenite
formation in the HAZ.
Group 11. High carbon steels.
These steels will be less weldable owing to their increased carbon content with respect to Group
1. It is likely that care over the choice of consumables and the use of high preheat levels would
be needed.

It is important to obtain advice before welding any steels that you do not have experience in.

References
1.

BS EN 1011-2:2001 'Welding - recommendations for welding of metallic materials - part


2: Arc welding of ferritic steels' British Standards Institution, March 2001.
2.
PD CEN ISO/TR 15608:2005 'Welding - guidelines for a metallic material grouping
system' British Standards Institution, October 2005.
This Job Knowledge article was originally published in Connect, July/August 1996. It has been