Designation: A820/A820M 11

Standard Specification for

Steel Fibers for Fiber-Reinforced Concrete1

This standard is issued under the fixed designation A820/A820M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon () indicates an editorial change since the last revision or reapproval.

3. Terminology
3.1 Definitions of Terms Specific to This Standard:
3.1.1 deformed fiber, na fiber that is bent, flattened, or
roughened to improve mechanical bond to the concrete matrix.
3.1.2 modified fiber, na cold-drawn wire fiber whose
cross-section has been changed from circular by shaving the
wire.
3.1.3 nominal length, nthe length of a deformed fiber,
out-to-out, after being deformed.
3.1.4 range of equivalent diameter, de-r, na set of limits
placed on the equivalent diameter by the specifier. See 8.1.6
and Note 3.
3.2 SymbolsThe following symbols used in this specification are defined as follows:
A = cross-sectional area, in.2 [mm2]
d = diameter, in. [mm]
fu = ultimate tensile strength, psi [MPa]
l = length, in. [mm]
l = l/d = aspect ratio

2. Referenced Documents
2.1 The following documents, of the issue in effect on the
date of material purchase, form a part of this specification to
the extent referenced herein.

2
For referenced ASTM standards, visit the ASTM website, www.astm.org, or
contact ASTM Customer Service at service@astm.org. For Annual Book of ASTM
Standards volume information, refer to the standards Document Summary page on
the ASTM website.
3
Available from American Concrete Institute (ACI), P.O. Box 9094, Farmington
Hills, MI 48333-9094, http://www.concrete.org.
4
Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,
Section D, 700 Robbins Ave., Philadelphia, PA 19111-5098, http://
dodssp.daps.dla.mil.

1
This specification is under the jurisdiction of ASTM Committee A01 on Steel,
Stainless Steel and Related Alloys and is the direct responsibility of Subcommittee
A01.05 on Steel Reinforcement.
Current edition approved Oct. 1, 2011. Published October 2011. Originally
approved in 1985. Last previous edition approved in 2006 as A820/A820M 06.
DOI: 10.1520/A0820_A0820M-11.

*A Summary of Changes section appears at the end of this standard.

Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.

Copyright by ASTM (all rights reserved); Downloaded/printed by

PSS Standard Service - + () - Unit , Block , Andishe Str., Beheshti Str., TEHRAN-IR | ihssnp@gmail.com

--`,``,,``,`,````,,`,,,,,``,,``,-`-`,,`,,`,`,,`---

2.2 ASTM Standards:2

A370 Test Methods and Definitions for Mechanical Testing
of Steel Products
A700 Practices for Packaging, Marking, and Loading Methods for Steel Products for Shipment
C1116/C1116M Specification for Fiber-Reinforced Concrete
2.3 ACI Documents:3
ACI 506.1 Guide to Fiber-Reinforced Shotcrete
ACI 544.1R Committee Report on Fiber-Reinforced Concrete
2.4 U.S. Federal Standards:4
Fed. Std. No. 123 Marking for Shipment (Civil Agencies)
2.5 U.S. Military Standards:4
MIL-STD-129 Marking for Shipment and Storage

1. Scope*
1.1 This specification covers minimum requirements for
steel fibers intended for use in fiber-reinforced concrete. Five
types of steel fibers for this purpose are defined as pieces of
smooth or deformed cold-drawn wire; smooth or deformed cut
sheet; melt-extracted fibers; mill-cut or modified cold-drawn
wire steel fibers that are sufficiently small to be dispersed at
random in a concrete mixture.
1.2 This specification provides for measurement of dimensions, tolerances from specified dimensions, and required
minimum physical properties, and prescribes testing procedures to establish conformance to these requirements.
1.3 In the case of conflict between a requirement of a
product specification and a requirement of this specification,
the product specification shall prevail. In the case of a conflict
between a requirement of the product specification or a
requirement of this specification and a more stringent requirement of the purchase order, the purchase order shall prevail.
The purchase order requirements shall not take precedence if
they, in any way, violate the requirements of the product
specification or this specification; for example, by the waiving
of a test requirement or by making a test requirement less
stringent.
1.4 The values stated in either SI units or inch-pound units
are to be regarded separately as standard. The values stated in
each system may not be exact equivalents; therefore, each
system shall be used independently of the other. Combining
values from the two systems may result in non-conformance
with the standard.

A820/A820M 11
parent source material or finished fiber; (2) for cut sheet fibers,
Type II, the area calculated from the actual thickness and width
of the parent source material specimen, or if fibers are tested,
the area of each individual fiber calculated from measured
length and weight [mass] of the fiber. See 8.1.5. (3) for
melt-extracted fibers, Type III, or mill-cut fibers, Type IV,
specified by equivalent diameter, the area calculated from the
equivalent diameter of the fibers. See 8.1.5; and (4) for
modified cold drawn wire fibers, Type V, specified by a range of
equivalent diameters, the area of each individual fiber calculated from the measured length and weight [mass] of the fiber.
See 8.1.6. The ultimate tensile load in pounds-force [newtons]
for individual fibers shall be measured to at least three
significant figures. Testing shall be in accordance with Test
Methods and Definitions A370, where applicable.
7.2 Bending Requirements:
7.2.1 Fibers shall withstand being bent around a 0.125 in.
[3.2 mm] diameter pin to an angle of 90 at temperatures not
less than 60F [16C] without breaking.

3.2.1 The subscript n on dimensional units indicates nominal and the subscript e indicates equivalent. Nominal and
equivalent dimensions are calculated from other measurable
dimensions or average weight [mass].
4. Classification
4.1 Five general types of steel fibers are identified in this
specification based upon the product or process used as a
source of the steel fiber material.
4.1.1 Type I, cold-drawn wire.
4.1.2 Type II, cut sheet.
4.1.3 Type III, melt-extracted.
4.1.4 Type IV, mill cut.
4.1.5 Type V, modified cold-drawn wire.
4.2 Fibers shall be straight or deformed.
5. Ordering Information
5.1 It shall be the responsibility of the purchaser to specify
all requirements that are necessary for the product under this
specification. Such requirements to be considered include, but
are not limited to, the following:
5.1.1 ASTM designation and year of issue,
5.1.2 Quantity in pounds or tons [kilograms],
5.1.3 Type or types permissible (4.1),
5.1.4 Diameter or equivalent diameter (8.1.4), or range of
equivalent diameters (8.1.6),
5.1.5 Length or nominal length (3.1.3),
5.1.6 Deformations, if required, and
5.1.7 Whether certification by the manufacturer is required
including whether a report is to be furnished (Section 11).

NOTE 2The bending requirements of this specification provide a

general indication of fiber ductility, as may be important in resisting
breakage during handling and mixing operations. Ductility measures of
fiber-reinforced concrete are outside the scope of this specification; see
ACI 544.1R.

7.2.2 Bend tests shall be conducted on ten randomly selected specimens of finished fibers. It shall be permissible to
perform bend tests manually. At least one test consisting of ten
specimens shall be made for each 5 tons [4 500 kg] of material.
At least 90 % of the specimens must pass the test.
8. Dimensions and Permissible Variations
8.1 Dimensions:
8.1.1 Straight cold-drawn wire (Type I) fibers are specified
by diameter (d) or equivalent (de) and length (l), that establish
a specified aspect ratio, (l), or (le), as (l / d) or (l / de).
8.1.2 Deformed cold-drawn wire (Type I) fibers are specified by the diameter (d) or equivalent diameter (de) and
nominal length after bending (ln). Nominal aspect ratio (ln) is
established as (ln/ d) or (ln/ de).
8.1.3 Cut sheet (Type II) fibers are specified by thickness (t),
width (w), and length (l). Aspect ratio (l) can be computed as:

NOTE 1For information on satisfactory sizes and aspect ratios, see

ACI 544.1R and ACI 506.1, and contact the manufacturers regarding
availability.

6. Materials and Manufacture

6.1 The materials and manufacturing methods used shall be
such that the fibers produced conform to the requirements in
this specification.
7. Mechanical Properties
7.1 Tensile Requirements:
7.1.1 At least ten individual tensile tests of randomly
selected finished fibers shall be performed for each 5 tons
[4 500 kg] of product. This is an approximate distribution of
one fiber tensile test per every 0.5 ton [450 kg] of finished
product. The average tensile strength, fu, of each fiber shall not
be less than 50 000 psi [345 MPa]. The tensile strength of any
one of the ten specimens shall not be less than 45 000 psi
[310 MPa]. Where the parent source material consists of sheet
or wire, tensile tests by the manufacturer may be performed on
larger samples of source material. One sample of each different
source material used shall then be tested for each 5 tons
[4 500 kg] of material. The tensile strength of a single sample
of source material shall not be less than 50 000 psi [345 MPa].
7.1.2 The cross-sectional area used to compute fu shall be
carried out to five decimal places, in units of square inches
[square millimetres], and shall be: (1) for drawn wire fibers,
Type I, the area calculated from the actual diameter of the

l 5 l / de

where:
A = tw, and
de = equivalent diameter = =4A / p .
8.1.4 Deformed cut sheet (Type II) fibers are specified by
thickness (t), width (w), and nominal length after deformation
(ln). Nominal aspect ratio (ln) can be computed as follows.
l 5 l n / de

where:
A = tw, and
de = equivalent diameter = =4A / p .
8.1.5 Melt-extracted (Type III) and mill-cut (Type IV) fibers
are specified by equivalent diameter, (de), and length (l), or
nominal length (ln). Equivalent diameter is computed from
measured average nominal length and the weight [mass] of a
known quantity of fibers, based upon 0.284 lb/in.3 [7 865 kg/

--`,``,,``,`,````,,`,,,,,``,,``,-`-`,,`,,`,`,,`---

Copyright by ASTM (all rights reserved); Downloaded/printed by

PSS Standard Service - + () - Unit , Block , Andishe Str., Beheshti Str., TEHRAN-IR | ihssnp@gmail.com

A820/A820M 11
m3] measured to the nearest 2 3 10-6 lb [0.1 mg]. Nominal
aspect ratio, (ln), can be computed as follows:

11. Rejection and Rehearing

11.1 Rejection:
11.1.1 If any test fails to conform to the requirements of this
specification, it shall be cause for rejection of the material
represented by the test. Material that is found to be defective
subsequent to its acceptance at the manufacturers works may
be rejected, and the manufacturer notified.
11.1.2 Rejection of fibers shall be reported to the manufacturer promptly and in writing. Samples representing fibers
rejected by the purchaser shall be preserved until disposition of
the claim has been agreed to between the supplier and the
purchaser.
11.2 RehearingWhen any test fails to meet the requirements of tension, bending, or dimensional tolerances, a retest
shall be allowed. This retest shall be performed on twice the
number of randomly selected specimens originally tested. The
results of the retest shall meet the requirements of this
specification or the lot shall be rejected.

ln 5 l / de, or 5 ln / de

8.1.6 Modified cold-drawn wire fibers (Type V) are specified by a range of equivalent diameters, (de-r), and length (l), or
nominal length (ln). Equivalent diameter is computed as in
8.1.5. A range of nominal aspect ratios, (ln-r) can be computed
as follows:
ln2r 5 l / de2r, or 5 ln / de2r
NOTE 3Specifying a specific diameter or equivalent diameter for
Type V fibers is not applicable as the diameters of many Type V fibers
vary more than 610 % in each lot. Therefore a user should provide the
limits on diameter or equivalent diameter allowable.

8.2 Measurement of Dimensions:

8.2.1 Measurement of dimensions shall be performed on not
less than 10 randomly selected specimens for each test to
establish the average for conformance to specified tolerances.
At least 90 % of the specimens in each test shall meet the
specified tolerances for length, diameter or equivalent diameter, and aspect ratio.
8.2.2 At least one test shall be performed for 5 tons
[4 500 kg] of finished product.
8.3 Permissible Variations:
8.3.1 The length, or nominal length shall not vary from its
specified value more than 610 %.
8.3.2 The diameter, equivalent diameter, or range of equivalent diameters shall not vary from its specified value more than
610 %.
8.3.3 The aspect ratio, nominal aspect ratio, or range of
aspect ratios shall not vary from its specified value more than
615 %.

12. Certification
12.1 Certificate of ComplianceWhen specified in the
purchase order or contract, the producer or supplier shall
furnish a certificate of compliance stating the product was
manufactured, sampled, tested, and inspected in accordance
with this specification (including year of issue) and any other
requirements designated in the purchase order or contract, and
has been found to meet such requirements.
12.2 Test ReportsWhen specified in the purchase order or
contract, test reports shall be furnished to the purchaser
containing the results of all tests required by this specification
(including year of issue), and any other requirements designated in the purchase order or contract.
12.3 A signature or notarization is not required; however,
the document shall clearly identify the organization submitting
the document. Notwithstanding the absence of a signature, the
organization submitting the document is responsible for its
content.
12.4 Copies of the original manufacturers test report shall
be included with any subsequent test report. A certificate of
compliance (or test report) printed from or used in electronic
form from an electronic data interchange (EDI) shall be
regarded as having the same validity as a counterpart printed in
the certifying organizations facility. The content of the EDItransmitted document must conform to any existing EDI
agreement between the purchaser and the supplier.

9. Workmanship, Finish, and Appearance

9.1 Surface Condition:
9.1.1 Seams and surface irregularities shall not be cause for
rejection provided that tensile properties are not less than
requirements of this specification and mixing performance in
concrete is not adversely affected.
9.1.2 Rust, mill scale, or other coatings shall not be cause
for rejection provided that the individual fibers separate when
mixed in concrete in accordance with Specification C1116/
C1116M, and tensile and bending properties are not less than
the requirements of this specification.
10. Inspection

13. Packaging and Package Marking

13.1 Packaging, marking, and loading for shipment shall be
in accordance with Practices A700.
13.2 When specified in the contract or order, and for direct
procurement by or direct shipment to the U.S. government,
marking for shipment, in addition to requirements specified in
the contract or order, shall be in accordance with MIL-STD129 for military agencies and with Fed. Std. No. 123 for civil
agencies.
13.3 The material shall be packaged to provide adequate
protection during normal handling and transportation and each
package shall contain only one type and size of material unless

10.1 Unless otherwise specified in the purchase order or

contract, the manufacturer is responsible for the performance
of all inspection and test requirements specified herein. Except
as otherwise specified in the purchase order or contract, the
manufacturer may use his own or any other suitable facility for
the performance of the inspection and test requirements specified herein unless disapproved by the purchaser. The purchaser
shall have the right to perform any of the inspections and tests
set forth in this specification where such inspections are
deemed necessary to ensure that material conforms to prescribed requirements.
--`,``,,``,`,````,,`,,,,,``,,``,-`-`,,`,,`,`,,`---

Copyright by ASTM (all rights reserved); Downloaded/printed by

PSS Standard Service - + () - Unit , Block , Andishe Str., Beheshti Str., TEHRAN-IR | ihssnp@gmail.com

A820/A820M 11
otherwise agreed upon. The type of packaging and gross
weight [mass] of containers shall, unless otherwise agreed
upon, be at the manufacturers discretion provided that they are
such as to ensure acceptance by common or other carriers for
safe transportation at the lowest rate to the delivery point.
13.4 Each shipping container shall be marked with the
material, size, type, specification designation, net weight
[mass], and the manufacturers name or trademark.

14. Keywords
14.1 acceptance testing; classification; fiber-reinforced concrete; steel fibers; tensile strength; testing procedures

SUMMARY OF CHANGES
Committee A01 has identified the location of selected changes to this standard since the last issue
(A820/A820M 06) that may impact the use of this standard. (Approved Oct. 1, 2011.)

ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned
in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk
of infringement of such rights, are entirely their own responsibility.
This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the
responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should
make your views known to the ASTM Committee on Standards, at the address shown below.
This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,
United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above
address or at 610-832-9585 (phone), 610-832-9555 (fax), or service@astm.org (e-mail); or through the ASTM website
(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/
COPYRIGHT/).

Copyright by ASTM (all rights reserved); Downloaded/printed by

PSS Standard Service - + () - Unit , Block , Andishe Str., Beheshti Str., TEHRAN-IR | ihssnp@gmail.com

--`,``,,``,`,````,,`,,,,,``,,``,-`-`,,`,,`,`,,`---

(1) Revised 1.4, 2.2, 2.3, and Note 1.

(2) Re-positioned the units of measurement throughout the
specification.