Shot Peenning and Grit Blasting Effect On Surface Integrity PDF
Shot Peenning and Grit Blasting Effect On Surface Integrity PDF
Shot Peenning and Grit Blasting Effect On Surface Integrity PDF
ABSTRACT
This paper describes influence of factors such as particle size (0.55-2.2 mm), particle
velocity (15-35 mls) and work hardness on surface integrity. Hardness, residual
stress and crystal transformation of areas affected by shot peening or grit blasting
are examined. In order to clarify the influences of those factors on the surface
integrity, a medium carbon steel (C:0.45%, 180HV) and an austenitic stainless steel
(SUS304, 210HV) were peened by a centrifugal type peening machine using cast
steel particles (650-800HV). The following results were obtained: (1) Shot peening
maximum hardness is lower while depth of work-hardened layer is thicker. (2)
Compressive residual stresses on the peened surface are larger than that of grit
blasting. (3) Critical thickness of shot peening is about 50% thicker than that of grit
blasting. (4)Strain-induced transformation happens with shot peening and grit
blasting.
SUBJECT INDEX
Surface integrity, hardness distribution, residual stress, critical thickness, strain
induced transformation
INTRODUCTION
Shot peening and grit blasting are cold working processes where the worked material
is peened with spherical shots or non-spherical grits to introduce compressive
residual stresses and work hardening or alternatively to remove surface layers. Shot
peening improves the mechanical properties such as fatigue (Drechsler et al, 1999),
stress corrosion cracking (Kirk, Render, 1999) and so on (Watanabe et al, 1999).
Shot peening is therefore widely used in many industries such as aircraft, automobile
and machines. Grit blasting produces stock removal and affected layer
simultaneously by impact of the grit on work material (Kock et all 1984).
Surface integrity is a concept including hardness alternations, residual stresses,
plastic deformations, heat-affected zone, recrystallization and so on. It influences
strength of work materials for fatigue, stress corrosion cracking, wear and so on
(Takazawa, 1989). Although shot peening and grit blasting techniques are widely
used in many industries, systematic studies on surface integrity are very few.
In order to clarify the influences of those factors on surface integrity, a medium
carbon steel (C:0.45%, 180HV) and an austenitic stainless steel (SUS304, 210HV)
were peened by a centrifugal type peening machine using 4 different cast steel
TECHNOLOGICAL ASPECTS
METHODS
Experimental conditions on shot peening (SP), grit blasting (GB), work material
and residual stress measurement are shown in Tablel. Hardness was measured on
the perpendicular section using a micro Vickers hardness tester. Hardness distributions
were obtained from averaging data measured on the three positions in the same depth
from the peened surface. Stock removal which is the important factor in grit blasting was
measured using a digital balance whose sensitivity is 0.1 mg. Half-width values are the
average obtained from six different inlet angle of X-ray on the residual stress
measurement.
Work: Material
X-Ray diffraction
Residual stress measurement
RESULTS
Hardness distribution
Figure 1 shows hardness distributions of cross section after blasting to medium
carbon steel. Shot peening maximum hardness is lower while depth of workhardened layer is thicker. This, therefore, means that the deformation in the
hardened layer of grit blasted material is different from that of shot peened one as
illustrated in Fig. 2.
Stock removal
In blasting process, numerous shots or grits are blasted with centrifugal force. The
total area of dents increase with blasting time till full coverage. Although stock
removal does not appear in shot peened material during the peened time in this
experiment, in case of grit blasting, it increases with blasting time as shown in Fig.3.
Stock removal is also influenced significantly by the blasting angle. Figure 4 shows
the influences of normal velocity and of tangential component on stock removal. It
shows the results obtained from two experiments. In the first one blasting angle is
variable with a constant normal velocity. In the second one normal velocity is variable
with a normal blasting angle. Nevertheless normal component of grit velocity is the
same. Stock removal on the oblique blasting is larger than that on normal blasting.
Half width
The broadening of half width means the increase of the scatter of the micro strain
in crystal, and its change is similar to the hardness one. Figure 5(a) shows the
influence of blasting time on half width. Half width values produced by shot
peening and grit blasting increase rapidly with blasting time. They reach saturated
values near full coverage times. The influences of kinetic energy of a particle on
the half width are very small as shown in Fig. 6(a). As their values in shot peening
are always less than in grit blasting. These results mean that the deformation level
of surface layer produced by shot peening is lower than those produced by grit
blasting as illustrated in Fig. 2.
Residual stresses
Figure 5(b) shows the influence of peening time on surface residual stresses
induced by shot peening and grit blasting. In early stage, they also increase rapidly
like half width. Then they approach saturated values when over 80 % of area is
peened. In case of grit blasting, the compressive stresses decrease slightly after
the maximum value, owing to the stock removal.
TECHNOLOGICAL ASPECTS
w-w
404
Transformation of crystal
Figure 11 shows the X-ray diffraction patterns on as-annealed, grit blasted and
shot peened. The peak neighbored on 149 degree shows that the structure of the
annealed material is clearly austenite. After blasting, the height of the peak
decreases and another peak arises neighbored on 156 degree, which is the peak
of (211) plain of alpha-Fe. This result suggests that strain-induced transformation
happened due to blasting. Figure 12 shows the austenite volume distribution
changed by shot peening, and also the volume in the affected layer decrease
owing to the strain-induced transformation.
TECHNOLOGICAL ASPECTS
CONCLUSIONS
Hardness distribution produced by blasting is different for those points:
(1) Shot peening maximum hardness is lower while depth of work-hardened layer
is thicker.
(2) Compressive residual stresses induced by shot peening is larger than the one
induced by grit blasting owing to stock removal.
(3) Critical thickness produced by shot peening is about 50% thicker than those c
grit blasting.
(4) Strain-induced transformation happens by shot peening and grit blasting.
REFERENCES
Drechsler, A., et al: Effect of Shot Peening and Roller Burnishing on Fatigue
Performance of Various Titanium Alloys, Proc. ICSP7, Warsaw, Poland, (1999)
145.
Kirk, D., Render P.E.: Effects of Peening on Stress Corrosion Cracking in Carbon
Steel, Proceedings of ICSP7, Warsaw, Poland, (1999) 167.
Kock, G.H., et al: Effect of grit blasting on the stress corrosion cracking behavior of
line pipe steel, J. National Association of Corrosion Engineers, 23,IO (1984) 20.
Takazawa, K.: Surface Integrity, J. Japan Society for Precision Engineering, 55, 10
(1989) 1772.
Watanabe, Y., et al: An Effect of Peening on Fretting Fatigue, Proc. ICSP7, ICSP7,
Warsaw, Poland, (1999) 145.