    Tensile Test Report

    Uploaded by

    GHULAM NABI
    This tensile and bend test report summarizes the results of mechanical tests conducted on an angle sample made of S355J2 steel. The sample passed both the tensile test, achieving a yield strength of 400.076 MPa, tensile strength of 533.193 MPa, and 33.80% elongation, and the bend test at 1.5 and 2 times the thickness. The test was conducted according to ASTM A370 and BSEN 10025 standards and the sample met the material specification requirements for S355J2 steel.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd

    Tensile Test Report

    Uploaded by

    GHULAM NABI
    36 views1 page
    This tensile and bend test report summarizes the results of mechanical tests conducted on an angle sample made of S355J2 steel. The sample passed both the tensile test, achieving a yield strength of 400.076 MPa, tensile strength of 533.193 MPa, and 33.80% elongation, and the bend test at 1.5 and 2 times the thickness. The test was conducted according to ASTM A370 and BSEN 10025 standards and the sample met the material specification requirements for S355J2 steel.

    Original Description:

    TENSILE REPORT

    Copyright

    © © All Rights Reserved

    Available Formats

    PDF, TXT or read online from Scribd

    Did you find this document useful?

    Is this content inappropriate?

    This tensile and bend test report summarizes the results of mechanical tests conducted on an angle sample made of S355J2 steel. The sample passed both the tensile test, achieving a yield strength of 400.076 MPa, tensile strength of 533.193 MPa, and 33.80% elongation, and the bend test at 1.5 and 2 times the thickness. The test was conducted according to ASTM A370 and BSEN 10025 standards and the sample met the material specification requirements for S355J2 steel.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    36 views1 page

    Tensile Test Report

    Uploaded by

    GHULAM NABI
    This tensile and bend test report summarizes the results of mechanical tests conducted on an angle sample made of S355J2 steel. The sample passed both the tensile test, achieving a yield strength of 400.076 MPa, tensile strength of 533.193 MPa, and 33.80% elongation, and the bend test at 1.5 and 2 times the thickness. The test was conducted according to ASTM A370 and BSEN 10025 standards and the sample met the material specification requirements for S355J2 steel.

    Copyright:

    © All Rights Reserved
    Download as PDF, TXT or read online from Scribd
    Download as pdf or txt
    of 1

    E/litrsteels

    TENSILE & BEND TEST REPORT

    Reoort No. : AlclMechl20lSl2Ol Date :02.07.2018

    AIC P.O. No. ASFAN


    Supplier / Manufacturer KOCAER,Turkey.
    Sample Description : Angle
    Material Specification : BSEN 10025 S355J2
    Heat No : 44219
    Test Method : ASTM A 370 OR QWI/8.2.4iTRIQCD/04
    Tvpe of Test : Tensile with Yield & % Elonoation: Bend Test
    Sample Designation 2018-201
    Size Description (mm) 1120X10X12000
    Thickness (mm)
    Width (mm) 29.84
    Cross Sectlon Area (mm') 290.045
    Gauge Length (mm) 96
    Yield Load (KN) 116 040
    Tensile Load (KN) 154.650
    Final Gauge Length (mm) 128.45

    Yield Strength ('MPa) 400.076


    Tensi I e Strength ('M P a ) 533.193
    Yo Elongation 33.80%
    Result OK
    Bend Test (1.5T/2T) Satisfactory

    Reference standard
    The above test was conducted by the test method prescribed in ASTM A 370 OR
    QWU8.2.4/TR/QCD/04 and was found to be soecification of material sDecification BSEN
    10025 S355J2

    Tested By :

    ._-tl
    \--+.n
    Superkisorl

    Format No : QSF /8.2.4ITR/QCD/Ot/06