SC-81Ni2M
FLUX CORED ARC WELDING CONSUMABLE
FOR WELDING OF LOW-TEMPERATURE
SERVICE STEEL

HYUNDAI WELDING CO., LTD.

 SC-81Ni2M

AWS A5.29 E81T1-Ni2M

v Specification
EN ISO 17632-A T 46 6 2Ni P M 2 H5

JIS Z3313 T 55 6 T1-1 M A-N5 H5

v Applications SC-81Ni2M is a titania type flux cored wire for welding of low-temperature
service steel.

v Characteristics SC-81Ni2M is titania type flux cored wire for all position welding with
on Usage Ar+CO2 gas mixture shielding. This wire provide excellent notch
toughness at low temperature down to -60℃.

v Note on Usage 1. Proper preheating(50~150℃) and interpass temperature must

be used in order to release hydrogen which may cause cracking
in weld metal when electrodes are used for medium and heavy
plates

2. Use Ar+20~25% CO2 gas

3. Original packaging until ready for use should remain.

4. Remaining after use so that you can be protected from moisture

and re-packaging plastic, etc. should be kept in the room and
as soon as possible should be used.
 SC-81Ni2M

Mechanical Properties
& Chemical Composition of All Weld Metal

v Welding Conditions Method by AWS Spec.

Diameter(mm) : 1.2mm

Shielding Gas : Ar+20% CO2

Flow Rate(ℓ /min.) : 20

Amp./ Volt. : 270~280 / 29~30

Stick-Out(mm) : 20~25

Pre-Heat(℃) : R.T .

Interpass Temp.(℃) : 150±15

Polarity : DC(+)
[ Joint Preparation & Layer Details ]

v Mechanical Properties of all weld metal

CVN Impact Test

Consumable Tensile Test
(Joule)

YS(Mpa) TS(MPa) EL(%) -60℃ -80℃

SC-81Ni2M
600 645 24.8 90 50

AWS A5.29
≥ 470 550~690 ≥ 19 ≥27J at –40℃
E81T1-Ni2M

v Chemical Analysis of all weld metal(wt%)

Consumable C Si Mn P S Ni

SC-81Ni2M 0.06 0.24 1.15 0.010 0.010 2.25

AWS A5.29
≤0.12 ≤0.80 ≤1.50 ≤0.03 ≤0.03 1.75∼2.75
E81T1-Ni2M

This information is provided solely for the purpose of confirming product conformance with applicable standards. The serviceability of a product or
structure utilizing this type of information is and must be the sole responsibility of the builder/user. Many variables beyond the control of HYUNDAI
WELDING CO., LTD. affect the results obtained in applying this type of information. These variables include, but are not limited to, welding procedure,
shielding gas, plate chemistry and temperature, weldment design, fabrication methods and service requirements.
 SC-81Ni2M

Mechanical Properties
& Chemical Composition of All Weld Metal

v Welding Conditions Method by AWS Spec.

Diameter(mm) : 1.4mm

Shielding Gas : Ar+20% CO2

Flow Rate(ℓ /min.) : 20

Amp./ Volt. : 300~310 / 29~30

Stick-Out(mm) : 20~25

Pre-Heat(℃) : R.T .

Interpass Temp.(℃) : 150±15

Polarity : DC(+)
[ Joint Preparation & Layer Details ]

v Mechanical Properties of all weld metal

CVN Impact Test

Consumable Tensile Test
(Joule)

YS(Mpa) TS(MPa) EL(%) -60℃ -80℃

SC-81Ni2M
585 640 25.4 85 46

AWS A5.29
≥ 470 550~690 ≥ 19 ≥27J at –40℃
E81T1-Ni2M

v Chemical Analysis of all weld metal(wt%)

Consumable C Si Mn P S Ni

SC-81Ni2M 0.06 0.22 1.17 0.010 0.010 2.22

AWS A5.29
≤0.12 ≤0.80 ≤1.50 ≤0.03 ≤0.03 1.75∼2.75
E81T1-Ni2M

This information is provided solely for the purpose of confirming product conformance with applicable standards. The serviceability of a product or
structure utilizing this type of information is and must be the sole responsibility of the builder/user. Many variables beyond the control of HYUNDAI
WELDING CO., LTD. affect the results obtained in applying this type of information. These variables include, but are not limited to, welding procedure,
shielding gas, plate chemistry and temperature, weldment design, fabrication methods and service requirements.
 SC-81Ni2M

Welding Efficiency

v Deposition Rate & Efficiency

Welding Conditions
Consumable
Deposition Efficiency(%) Deposition Rate(kg/hr)
(size)
Amp.(A) Volt.(V)

230 26 84~86 3.2

SC-81Ni2M
280 30 85~87 4.4
1.2mm
330 33 86~88 5.1

250 27 83~85 3.0

SC-81Ni2M
300 31 84~86 4.2
1.4mm
350 35 85~87 4.9

Deposition efficiency Deposition rate

Remark =(Deposited metal weight/ =(Deposited metal weight/
Wire weight used)×100 Welding time,min.)×60

* Shielding Gas : Ar+20%CO2

This information is provided solely for the purpose of confirming product conformance with applicable standards. The serviceability of a product or
structure utilizing this type of information is and must be the sole responsibility of the builder/user. Many variables beyond the control of HYUNDAI
WELDING CO., LTD. affect the results obtained in applying this type of information. These variables include, but are not limited to, welding procedure,
shielding gas, plate chemistry and temperature, weldment design, fabrication methods and service requirements.
 SC-81Ni2M

Diffusible Hydrogen Content

v Welding Conditions

Diameter(mm) : 1.2 Amps(A) / Volts(V) : 270 / 29

Shielding Gas : Ar+20%CO2 Stick-Out(mm) : 20~25

Flow Rate(ℓ/min.) : 20 Welding Speed : 30 cpm
Welding Position : 1G Current Type & Polarity : DC(+)

v Hydrogen Analysis Using Gas Chromatography Method

Hydrogen Evolution Time : 72 hrs Analysis Temp. : 25 ℃

Evolution Temp. : 25 ℃ Exposure Condition : 80%RH-25℃

Barometric Pressure : 780 mm-Hg

v Result(㎖/100g Weld Metal)

X1 X2 X3 X4

3.31 3.51 3.23 3.41

Average Hydrogen Content 3.4 ㎖ / 100g Weld Metal

This information is provided solely for the purpose of confirming product conformance with applicable standards. The serviceability of a product or
structure utilizing this type of information is and must be the sole responsibility of the builder/user. Many variables beyond the control of HYUNDAI
WELDING CO., LTD. affect the results obtained in applying this type of information. These variables include, but are not limited to, welding procedure,
shielding gas, plate chemistry and temperature, weldment design, fabrication methods and service requirements.
 SC-81Ni2M

Proper Welding Condition

v Welding Conditions

Wire Dia. (mm)

Shielding
Consumable Welding Position
Gas 1.2mm 1.4mm

Flat 130~300 Amp 270~330 Amp

100% V-up
SC-81Ni2M 170~230 Amp 180~240 Amp
CO2 Over head

V-down 150~300 Amp 170~320 Amp

v AUTHORIZED APPROVAL DETAILS

Register of shipping & size(mm)

Welding
position
DNV LR BV

VY46MS(H5) SA5Y46 HHH

All Pending
1.2~1.4 1.2~1.4

This information is provided solely for the purpose of confirming product conformance with applicable standards. The serviceability of a product or
structure utilizing this type of information is and must be the sole responsibility of the builder/user. Many variables beyond the control of HYUNDAI
WELDING CO., LTD. affect the results obtained in applying this type of information. These variables include, but are not limited to, welding procedure,
shielding gas, plate chemistry and temperature, weldment design, fabrication methods and service requirements.