JSRNBR e
JSRNBR e
JSRNBR e
This information contained herein is given in good faith but without any guarantee
or warranty and may involve proprietary rights of third parties. Our advice given in
this information does not release you from the obligation to check its validity and
to test our products as to their suitability for the intended process and uses. The
application, use and processing of our products and the products manufactured
by you on the basis of our technical advice are beyond our control and, therefore,
entirely on your own responsibility. Our products are sold only in accordance with
Product Specification separately issued by us.
This printed document uses FSC®-certified paper that includes materials from properly managed forests, printed with vegetable oil ink.
Printed on paper made with wood from forest thinning.“Morino Chonai-Kai” (Forest Neighborhood Association)̶Supporting sound forest management. '14.10 NE 50
About JSR
Chemical Structure and Characteristics of NBR
Since JSR's success as the first Japanese producer of synthetic
rubber in 1960, the company has continued to supply the world The increased bound acrylonitrile content of this copolymer of acrylonitrile and butadiene
market with synthetic rubber in the key categories of NBR, EP, provides improved characteristics such as oil and heat resistance while reducing
SBR, BR, IR, and IIR as an“Integrated manufacturer of synthetic characteristics such as cold resistance.
rubber.”JSR also distills butadiene (a major raw material of Please refer to the following for a description of representative trends:
A special-purpose synthetic rubber that combines extremely high oil resistance with other excellent
properties, including abrasion resistance and heat resistance.
NBR is used in a wide range of applications such as seal parts, hoses, and other automobile parts, as Relationship between Bound Acrylonitrile Content and Oil Resistance
well as in various types of rolls.
40
フューエルホース
Temperature (℃)
-20
Ozone Resistance × × × × ○ ◎ ◎
Alkali Resistance ○ ○ ○ ○ ◎ ◎ ◎
-60
◎: Excellent ○: Good △: Fair ×: Poor
15 20 25 30 35 40 45 50 55
Bound Acrylonitrile Content (%)
1 2
Advantages of JSR NBR Representative JSR NBR Grades and Applications
Mold Fouling Resistance
JSR NBR is based on a polymer design that adjusts non-rubber content and components in order to reduce mold
fouling. Mold fouling resistant grades have significantly less mold fouling, and this contributes to both increase in Ultra High, High-Nitrile Used in applications that require high oil and solvent resistance.
productivity as well as reduction in cleaning costs. (36% or Higher) Main applications:
N215SL Automobile parts, industrial hoses, packing, gaskets, O-rings, oil
Mold Fouling Comparison N220S, N220SH seals, and rolls
Medium High-Nitrile Used in a wide range of general applications that require oil resistance.
(30% or Higher, Lower than 36%) Main applications:
N230S, N230SL, N230SV Automobile parts, industrial hoses, packing, gaskets, O-rings, oil
N237, N237H, N236H seals, rolls, and adhesives
The white, ring-shaped stain and the overall white staining of the surface are both examples of mold fouling.
Medium-Nitrile Used in applications that require more cold resistance and higher
(25% or Higher, Lower than 30%) elasticity than medium high-nitrile.
Compared with the other company’s NBR, JSR NBR show less mold fouling in both ring-shaped staining and overall
N240S, N241, N241H Main applications:
staining.
Automobile parts, industrial hoses, packing, gaskets, O-rings, oil seals, and rolls
[Comparison Conditions]
Mold fouling comparisons are based on three repetitions of vulcanization and molding using the same combination in the NBR compound.
[Vulcanization]
20-minute press vulcanization at 160 ℃
Low-Nitrile (Lower than 25%) Used in applications that require more cold and water resistance
[Combination]
N250S, N250SL, N260S than medium-nitrile, in particular.*
NBR100, zinc oxide 5, stearic acid 1, SRF carbon 60, DOP5, antioxidant RD 1, sulfur 0.5, vulcanization accelerator TET 1.5,
*Excellent water resistance is provided due to differences in polymer design, not AN content.
vulcanization accelerator CZ2, with a total of 176
Main applications:
A Diverse Product Lineup Packing with cold and oil resistance, gaskets, oil seals, and belts
JSR NBR lineup covers wide range of Mooney viscosity and Bound AN content. Due to the differences in the
structure of the polymer, low-AN grades offer superior water resistance in addition cold resistance.
Heat-Resistant Grades Used in applications that require oil and heat resistance.
N520, N530 Main applications:
Ultra High/High-AN Automobile parts, industrial hoses, packing, gaskets, O-rings, and oil seals
N640 (Acrylate-Modified)
50.0 ●
●
●
● JSR Grades
Medium High/Medium-AN ● ●
● ● ● ● ● Other Company Grades
●● ●● ● ● ●●
● ●●
40.0 ●
●
●
●
● ● ●
●●
● ●
Resin-Modifying Grades These grades, which offer a high level of compatibility with polyvinyl chloride
● and phenol resin, can also provide excellent properties in terms of
● ● N202S, N210S, T496
● ● ● ●●● ●●
(%)
● ● ●
● ●● ●● ● ● ● ● ●●● PN30A compression set, cold resistance, and other attributes by blending with resin.
● ● ●● ● ●● ● ● ● ● ●● ●● ●
● ● ● ●
●
AN
30.0 ● ●●
● ● ● ● ● ● ●● ●
● ●
●● ● ● ●
●
● ● ●●
● ● ● ●
●
● ●●
20.0 ● ●● Adhesive Grade High levels of both strength and cohesion give this grade excellent
● ● ● ●
●
T4103 properties as an adhesive.
●
Low-AN
10.0
20 30 40 50 60 70 80 90
ML
(1+4)100℃
3 4
JSR NBR Product Lineup Legend:
Product Name
AN / MV
Characteristics
Low-AN
N222SH N221H T4103 N220SH N224SH N232SH N238H N237H N236H N241H
43 / 85 41.5 / 75 41 / 73 41.5 / 80 37 / 70 35 / 77 35 / 77 34 / 72 32 / 72 29 / 75
Press Molding Air/ Heat Resistance Adhesives Applications Mold Fouling Resistance Water Resistance Press Molding Air/ Mold Fouling Resistance Cold Resistance Mold Fouling Resistance
Defect Reduction Mold Releasing Sharp Vulcanization Metal Corrosion Resistance Defect Reduction Sharp Vulcanization, Sharp Vulcanization
Mold Fouling Resistance Properties Heat Resistance
N233
High-MV High-MV High-MV High-MV 30 / 59 High-MV
N202S T496
40 / 57 30 / 56
Medium-Nitrile Low-Nitrile
High-MV
High-Nitrile Medium High-Nitrile Standard Standard
Standard Grade Standard Grade Grade Grade
N220S N232S N230S N237 N210S N241 N240S N250S N260S
41.5 / 56 35 / 54 35/ 56 34 / 56 30 / 54 29 / 56 26 / 56 19.5 / 63 15 / 62
Water Resistance Water Resistance Partial Cross Linking Mold Fouling Resistance Cold Resistance Cold Resistance Cold Resistance
Metal Corrosion Resistance Sharp Vulcanization, PVC Modification Applications Sharp Vulcanization High Rebound Resilience Water Resistance Water Resistance
Heat Resistance Improved Sheet Surface Smoothness Metal Corrosion Resistance Metal Corrosion Resistance
N242S
Gas Permeability
29 / 56
Resistance
Low-MV Mold Fouling Resistance Low-MV
N520 N530 Sharp Vulcanization N640
41 / 51 35 / 52 25 / 50
High-AN
N215SL N222L N230SL N231L N250SL
48 / 45 43 / 45 35 / 42 34 / 45 19.5 / 43
Ultra High Nitrile Mold Fouling Resistance Processability Mold Releasing Cold Resistance
Fuel Oil Resistance Processability Properties Water Resistance
Processability Metal Corrosion Resistance
Low-MV Low-MV
Low
N230SV N239SV
35 / 32 33.5 / 30
5 6
Basic Properties and Characteristics of JSR NBR
*This data indicates representative physical properties, and does not signify product specifications.
*This data indicates representative physical properties, and does not signify product specifications.
[Vulcanization]
20-minute press vulcanization at 160 ℃
[Combination]
NBR100, zinc oxide 5, stearic acid 1, SRF carbon 60, DOP 5, sulfur 0.5, vulcanization accelerator TT 1.5,
vulcanization accelerator C Z2.0, with a total of 175.0
7 8
Typical Properties and Characteristics of Polymer Alloy Series
■JSR NV ■Product Forms
JSR NV is polymer alloy of NBR and polyvinyl chloride (abbreviated as“PVC”below)
that offers high oil and fuel oil resistance as well as excellent ozone resistance.
Plasticized NR PVC AN
NV CR
PVC SBR Content Content
Oil and Fuel Oil Resistance ◎ ○ × ○ High High
Tensile Strength
Ozone Resistance ◎ ◎ × ○
High High ■Packing Forms
Abrasion Resistance ◎ ○ ◎ ◎ Compression Set
■JSR NE
JSR NE is alloy of NBR and EP that combines the oil resistance of NBR with the weather resistance of EP.
EP AN
NE EP NBR CR Content Content
Ozone Resistance ○ ◎ × ◎ Good Liquid Packing #1 Liquid Packing #2 Sheet Packing
Oil Resistance Poor
Adhesion ○ △ ◎ ◎
Good Liquid product is stored in metal can. Liquid product is stored in Product is wrapped in black
Cold Resistance ○ ◎ △ △ Cold Resistance
Poor It’s Inner capacity is 18 L. metal drum cans. It’s Inner polyethylene bags, which are
Oil Resistance ○ × ◎ ○ Good capacity is 180 L. then banded together.
Ozone Resistance
Metal Corrosion Resistance ◎ ◎ ◎ ×
High
◎: Excellent ○: Good △: Fair ×: Poor Compression Set
Low
*This chart shows typical trends, and does not describe the behavior or
characteristics of all products.
9 10
Typical Properties of JSR NBR Non-vulcanized and Vulcanized Rubber
Raw Polymer Compound (non-vulcanized) Compound (vulcanized)
Mooney Mooney Scorch JSR Mold Curast Mill Flow Rate
Viscosity Extrusion Test 80℃ 100kg IRM901 IRM903
Mooney ML(1+4) Test Test Contraction (Kokashiki Tensile Test
80℃ 25rpm 70 Hours at 120 ℃ 70 Hours at 120 ℃
Grade Viscosity 100℃ ML1-125℃ 160℃ 50℃ Flow Tester) Grade
AN(%)
ML(1+4) Extrusion Extrusion Die
100℃ Vm t5 tc(10) tc(90) (%) Length Volume Swell Q×104 S100 S300 TS Eb HA SCTB SCEB SH △V100 SCTB SCEB SH △V100
(Minutes) (Minutes) (Minutes) (cm/min.) (cc/min.) (%) (cc/sec.) (MPa)(MPa)(MPa) (%)(DuroA) (%) (%) (Point) (%) (%) (%) (Point) (%)
N215SL 48 45 53 23 16 2 8 25 362 381 110 115 4.7 15.8 19.2 430 81 -8 -40 2 -4 -1 -24 -8 6 N215SL
N222SH 43 85 79 52 12 2 6 53 393 433 117 49 4.2 18.1 21.0 390 72 -15 -37 3 -3 -17 -22 -5 7 N222SH
N220SH 41.5 80 81 49 17 2 6 40 328 402 145 35 4.0 18 22.5 430 73 -8 -38 0 -3 -11 -23 -8 8 N220SH
N221H 41.5 75 79 48 19 3 6 39 415 440 115 13 3.3 16.3 21.6 460 70 -3 -31 4 -2 -2 -19 -3 9 N221H
N224SH 37 70 74 44 14 2 5 41 337 366 117 18 3.9 17.5 22.1 410 72 -2 -33 -1 -2 -12 -23 -9 16 N224SH
N220S 41.5 56 62 36 18 2 6 34 407 427 110 115 3.7 17.3 22.7 470 72 0 -39 2 -2 -12 -31 -7 8 N220S
N222L 43 45 52 28 16 2 9 31 337 349 107 170 3.9 15.9 19.7 410 76 0 -33 1 -4 -12 -19 -10 9 N222L
N238H 35 77 78 53 14 2 5 49 247 297 140 30 3.5 16.6 20.3 380 68 9 -14 3 -3 -13 -14 -8 17 N238H
N232SH 35 77 81 52 17 2 7 51 293 322 130 25 3.1 16.6 21.3 410 69 2 -32 1 -3 -15 -16 -8 15 N232SH
N237H 34 72 78 48 20 3 5 43 394 399 103 48 3.3 17.4 22.4 400 70 -7 -30 1 -3 -22 -27 -12 19 N237H
N236H 32 72 79 49 19 2 4 45 393 383 95 83 3.5 17.8 21.8 370 70 -5 -27 1 -1 -23 -25 -12 24 N236H
N230S 35 56 60 35 17 2 5 44 382 407 113 60 3.2 16.2 22.1 440 70 -13 -38 0 1 -12 -21 -10 16 N230S
N232S 35 54 66 41 18 2 5 46 322 352 118 39 3.6 18.4 22.5 390 70 -7 -30 2 -4 -22 -27 -10 17 N232S
N237 34 56 63 37 19 3 4 59 349 349 90 64 2.8 13.7 18.3 430 68 4 -28 2 -3 -8 -14 -8 17 N237
N233 32 59 68 44 20 3 6 30 446 337 63 90 3 14.4 19.7 470 69 -2 -26 2 -1 -13 -16 -10 17 N233
N230SL 35 42 47 26 17 2 5 43 432 411 90 80 3.2 15.3 20.2 420 70 -3 -31 0 -3 -17 -21 -13 16 N230SL
N231L 34 45 48 28 21 3 5 46 415 400 93 49 3.0 14.4 19.9 430 68 -11 -38 0 0 -27 -31 -12 19 N231L
N230SV 35 32 40 20 18 2 5 45 455 420 60 96 2.6 12.4 18.0 480 68 5 -26 -1 -3 -9 -15 -12 15 N230SV
N239SV 33.5 30 39 29 15 2 5 31 341 293 69 370 3.6 13.3 17.8 470 69 2 -31 -1 -1 -10 -16 -14 21 N239SV
N241H 29 75 82 53 14 2 5 43 333 342 165 15 3.6 16.7 21.4 390 69 -4 -26 -1 1 -29 -29 -12 26 N241H
N242S 29 56 65 43 14 2 5 30 437 348 71 109 3.3 15.4 19.1 400 69 -4 -20 -1 0 -16 -12 -15 23 N242S
N241 29 56 64 39 15 2 5 44 363 355 96 70 3.4 15.3 19.7 400 70 6 -22 -3 0 -21 -22 -15 27 N241
N240S 26 56 61 39 17 2 4 42 417 372 78 65 3.2 15.1 19.7 400 68 -10 -28 0 1 -20 -23 -18 34 N240S
N250S 19.5 63 70 46 22 3 5 46 303 335 121 25 3.4 15.9 18.1 340 67 -1 -19 -7 6 -34 -32 -17 54 N250S
N260S 15 62 67 45 16 3 5 47 255 309 139 91 2.7 12.4 16.6 320 64 -14 -18 -10 16 -48 -43 -20 85 N260S
N250SL 19.5 43 56 39 21 3 5 37 344 274 70 251 3.2 14.6 17.6 370 68 -5 -18 -6 6 -45 -35 -25 57 N250SL
N520 41 51 67 40 6 1 3 31 387 396 104 56 3.9 14.1 20.4 520 72 -5 -44 3 -2 -7 -27 -5 10 N520
N530 35 52 58 38 6 1 3 41 358 376 112 54 3.3 12.9 19.7 470 70 11 -24 2 -1 -14 -19 -11 17 N530
N640 25 50 41 26 18 3 8 59 311 408 160 95 3.6 ー 14.8 300 63 -4 -31 2 -5 -12 -13 -9 14 N640
N202S 40 57 97 80 13 3 6 1 749 409 2 35 6.6 ー 14.9 260 75 -10 -32 2 -4 -7 -23 -5 10 N202S
T496 30 56 91 83 13 2 5 3 432 177 5 507 5.5 ー 11 170 74 21 -24 -1 0 -1 -8 -10 20 T496
N210S 30 54 99 80 11 2 5 9 600 343 14 10 7.1 ー 14.4 180 72 -8 -26 3 -1 -32 -33 -6 23 N210S
T4103 41 73 69 51 13 2 6 52 272 363 161 6 3.5 17.3 21.9 420 70 -17 -40 3 -3 -9 -21 -2 7 T4103
NV80G Medium 65 74 45 17 3 6 33 464 376 62 74 6.0 18.0 20.9 400 76 2 -34 1 -5 -2 -16 -13 19 NV80G
NV72G Medium High 75 86 48 19 3 6 19 417 357 73 40 12.7 19.6 19.9 370 86 19 -31 2 -5 6 -13 -12 13 NV72G
NV73G Medium High 68 68 39 19 3 6 16 437 372 70 70 10.6 18.7 19.3 400 82 15 -48 7 -9 9 -22 -6 7 NV73G
NV75G Medium 68 72 46 17 3 5 20 550 402 46 105 10.5 19.0 20.6 370 82 11 -42 5 -8 -13 -21 -11 13 NV75G
NV76G Medium 60 67 43 17 3 6 15 610 397 30 95 9.6 18.3 18.7 340 82 10 -39 6 -9 4 -18 -9 10 NV76G
NV60G High 63 67 36 17 2 8 12 496 398 61 115 13.1 ー 17.4 290 88 26 -43 9 -8 23 -20 2 0 NV60G
*This data indicates representative physical properties, and does not signify product specifications.
[Vulcanization]
20-minute press vulcanization at 160 ℃
[Combination]
NBR 100, zinc oxide 5, stearic acid 1, SRF carbon 60, DOP 5, sulfur 0.5, vulcanization accelerator TT 1.5,
vulcanization accelerator CZ 2.0, with a total of 175.0
11 12
Typical Properties JSR NBR Vulcanized Rubber
Raw Polymer Compound (non-vulcanized) Compound (vulcanized)
Fuel Oil C Fuel Oil(*1)
C/ Distilled Aging Test Compression Set Tearing Permanent Rebound Ozone
Fuel Oil B Ethanol Water Test set at Brittle Low-Temperature Degradability Test
48 Hours 48 Hours 70 Hours 70 Hours of Air Heat Aging Test(*2) Flex Test (*2)
Mooney 48 Hours at 40 ℃ Angle 200% Resilience Temperature Torsion Test 50 ppm
Grade Viscosity at 40 °C at 40 °C at 70 °C at 120 ° C 70 Hours Type Elongation (*2)
5 Hours at 40 ℃ Grade
AN(%)
ML(1+4) Occurrence Growth 2→
100℃ SCTB SCEB SH △V100 △V100 △V100 △V100 ACTB ACEB AH 100℃ 120℃ TR TSE R (Thousand 15 mm Tb t10 t100 Static 20%
Dynamic
0 to 20%
(%) (%) (Point) (%) (%) (%) (%) (%) (%) (Point) CS(%) CS(%)(KN/m) (%) (%) Times) (Thousand (℃) (℃) (℃) Elongation Elongation
Times)
N215SL 48 45 -29 -23 -21 16 31 48 3 1 -39 3 22 32 48 5 6 20 3 -8 -4 -11 C-3 C-3 N215SL
N222SH 43 85 -40 -32 -12 20 32 55 3 2 -28 6 15 19 51 3 18 9 1 -18 -12 -19 C-2 B-2 N222SH
N220SH 41.5 80 -41 -38 -13 20 33 58 2 6 -33 4 12 17 54 3 18 20 3 -18 -15 -19 C-3 C-3 N220SH
N221H 41.5 75 -52 -44 -12 23 39 60 2 6 -31 7 13 19 53 3 21 24 5 -17 -15 -22 C-3 C-3 N221H
N224SH 37 70 -46 -41 -14 28 47 68 2 5 -35 4 13 20 50 4 30 15 2 -26 -21 -26 C-3 C-3 N224SH
N220S 41.5 56 -37 -37 -14 20 34 59 2 5 -40 6 13 19 53 3 18 20 4 -18 -15 -23 C-3 C-3 N220S
N222L 43 45 -39 -30 -18 20 33 57 3 14 -24 3 17 24 51 7 13 15 2 -16 -12 -19 C-3 C-3 N222L
N238H 35 77 -67 -57 -11 29 49 78 2 3 -24 6 12 18 52 3 37 ー 5 -31 -22 -28 C-3 C-3 N238H
N232SH 35 77 -51 -46 -10 28 50 75 1 4 -29 6 11 15 46 3 37 ー 3 -31 -22 -28 C-3 C-3 N232SH
N237H 34 72 -61 -53 -12 30 52 90 2 4 -25 5 10 14 49 3 37 20 2 -28 -25 -29 C-3 C-3 N237H
N236H 32 72 -63 -55 -13 34 60 90 2 -1 -34 6 10 16 48 3 39 50 2 -32 -25 -31 C-3 C-3 N236H
N230S 35 56 -54 -47 -14 28 52 81 2 7 -36 6 12 18 52 3 34 30 7 -29 -23 -29 C-3 C-3 N230S
N232S 35 54 -55 -45 -12 28 50 88 1 6 -27 6 12 19 51 2 34 10 3 -27 -23 -27 C-3 C-3 N232S
N237 34 56 -52 -43 -12 30 50 79 2 7 -29 7 10 14 43 2 44 ー 5 -34 -25 -31 C-3 C-3 N237
N233 32 59 -56 -52 -12 35 62 88 2 11 -24 5 11 16 53 2 44 30 3 -31 -28 -34 C-3 C-3 N233
N230SL 35 42 -56 -48 -14 28 50 82 2 0 -40 6 13 18 52 3 33 20 5 -28 -24 -30 C-3 C-3 N230SL
N231L 34 45 -60 -51 -16 31 56 94 2 7 -30 6 15 20 48 3 38 30 8 -29 -26 -30 C-3 C-3 N231L
N230SV 35 32 -54 -48 -13 27 47 80 2 6 -33 4 14 19 47 3 33 ー 11 -29 -24 -30 C-3 C-3 N230SV
N239SV 33.5 30 -56 -52 -17 34 58 91 2 6 -34 5 13 19 51 3 37 20 14 -35 -20 -29 C-3 C-2 N239SV
N241H 29 75 -60 -54 -14 39 69 97 2 7 -24 3 12 18 51 3 48 10 2 -37 -31 -36 C-3 C-3 N241H
N242S 29 56 -57 -54 -13 40 71 99 2 -1 -32 6 11 16 51 3 49 26 1 -39 -31 -38 C-3 C-3 N242S
N241 29 56 -59 -53 -16 43 73 95 2 13 -23 4 14 21 49 3 48 15 3 -39 -31 -36 C-3 C-3 N241
N240S 26 56 -62 -56 -16 48 84 102 3 -1 -36 7 13 21 47 2 50 20 3 -40 -34 -41 C-3 C-3 N240S
N250S 19.5 63 -65 -58 -16 69 109 119 1 -11 -35 5 12 19 45 3 58 30 2 -51 -42 -50 C-3 C-3 N250S
N260S 15 62 -64 -59 -18 96 145 152 1 -5 -28 4 14 18 42 1 57 2 1 -62 -51 -58 C-2 C-3 N260S
N250SL 19.5 43 -67 -66 -14 72 120 131 0 -10 -40 6 12 18 41 2 54 31 1 -49 -44 -52 C-3 C-3 N250SL
N520 41 51 -40 -33 -14 23 30 59 2 12 -28 5 13 20 52 3 15 30 15 -15 -14 -19 C-3 C-3 N520
N530 35 52 -49 -41 -15 31 50 81 2 15 -19 5 12 18 51 3 30 30 10 -27 -21 -27 C-3 C-3 N530
N640 25 50 -59 -49 -12 33 61 105 2 21 -15 5 12 18 39 2 35 60 2 -26 -25 -30 C-2 A-2 N640
N202S 40 57 -67 -56 -11 23 36 59 1 12 -31 5 12 17 28 ー 20 1 1 -19 -13 -19 C-2 ー N202S
T496 30 56 -68 -65 -10 34 59 81 1 -49 -10 5 9 14 15 ー 39 5 1 -23 -25 -33 C-3 C-3 T496
N210S 30 54 -72 -57 -11 34 49 79 1 8 -30 9 11 17 26 ー 37 1 1 -27 -25 -32 C-3 C-3 N210S
T4103 41 73 -51 -46 -12 22 36 58 2 9 -26 7 11 17 49 3 22 29 2 -19 -15 -22 C-3 C-3 T4103
NV80G Medium 65 -47 -43 -16 28 54 77 2 3 -35 2 23 30 53 6 36 20 2 -33 -26 -36 NC B-2 NV80G
NV72G Medium High 75 -30 -20 -19 21 39 63 2 17 -44 3 35 45 61 9 11 15 2 -16 -8 -19 NC NC NV72G
NV73G Medium High 68 -25 -19 -15 14 32 54 2 16 -47 7 34 43 56 8 14 15 5 -21 -12 -29 NC NC NV73G
NV75G Medium 68 -37 -31 -16 20 42 64 2 8 -32 3 32 44 53 10 22 20 2 -29 -20 -34 NC NC NV75G
NV76G Medium 60 -29 -18 -16 18 39 58 2 13 -27 4 32 40 50 10 22 70 2 -34 -22 -35 NC NC NV76G
NV60G High 63 -24 -17 -16 14 24 37 3 27 -35 4 42 49 54 12 9 15 2 -10 -9 -19 NC NC NV60G
(*1)Fuel oil C/ethanol blend ratio = 80/20 (*2)30 minute thick press vulcanization *This data indicates representative physical properties, and does not signify product specifications.
[Vulcanization]
20-minute press vulcanization at 160 ℃
[Combination]
NBR 100, zinc oxide 5, stearic acid 1, SRF carbon 60, DOP 5, sulfur 0.5, vulcanization accelerator TT 1.5,
vulcanization accelerator CZ 2.0, with a total of 175.0
13 14